CN106045475A - Method for preparing pearl porcelain sand from blank waste and pearl porcelain sand creative ceramic - Google Patents
Method for preparing pearl porcelain sand from blank waste and pearl porcelain sand creative ceramic Download PDFInfo
- Publication number
- CN106045475A CN106045475A CN201610373667.5A CN201610373667A CN106045475A CN 106045475 A CN106045475 A CN 106045475A CN 201610373667 A CN201610373667 A CN 201610373667A CN 106045475 A CN106045475 A CN 106045475A
- Authority
- CN
- China
- Prior art keywords
- sand
- pearl
- porcelain sand
- porcelain
- base substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of daily and decoration ceramic manufacturing, in particular to pearl porcelain sand creative ceramic and a method for preparing pearl porcelain sand from blank waste. The method includes the steps of waste recovering, drying, breaking, shaping, adhering, fire forming and the like. Pearl porcelain sand is prepared from ceramic blank waste, raw materials are saved, the manufacturing process is simple, and the waste recovery procedure is simplified; the pearl porcelain sand is arranged on the creative ceramic, the granularity of the pearl porcelain sand can be changed according to the design demands, the distribution relation, density and surface layer glazing color of the pearl porcelain sand particles can all be changed according to the design demands, the pearl porcelain sand is remarkable in artistic effect, people can feel obvious granular texture when touching the pearl porcelain sand, the pearl porcelain sand can be used for manufacturing different granular forms such as snowflakes, sand beach, wheat ears and rainwater, various options are provided for a designer, and diversified creation effects are achieved.
Description
Technical field
The present invention relates to daily and decorative porcelain manufacturing technology field, be specifically related to a kind of PEARL CHINA sand intention pottery and
Utilize the method that base substrate waste material prepares PEARL CHINA sand.
Background technology
Ceramic is implements conventional in daily household machine decorative display, and traditional ceramics glaze produces light at ceramic surface
Sliding, gentle visual effect, is widely used on all kinds of ceramic product.But along with improving constantly of people's living standard, to day
With the aesthetic requirement of, decorating ceramic articles also in constantly change, occurring in that on the market multiple increases graininess at ceramic surface
Protruding decorative effect, forms snowflake, the wheat head, sandy beach etc. at ceramic surface and has artistic effect ingenious.
Existing, the making increasing granular ornament at ceramic surface generally has two ways, and one is by base substrate table
Face is prefabricated into grainy surface, forms by a firing after applying glaze, and owing to base substrate particle surface is provided with glaze, therefore this is prepared
The particle effect gone out is inconspicuous and lacks texture；The another kind of glaze that passes through embodies, such as application publication number CN on ceramic body
The preparation method of a kind of snowflake glaze decorative daily-use pottery disclosed in 104150966 A and prepared product thereof, this kind of snowflake glaze
There is in glaze short grained glaze, put on and after burning till on base substrate, form point-like cover-coat enamel as snowflake, in this kind of glaze
Grain to adsorb the particle diameter of therefore granule on glaze and be restricted, and granule can only random arrangement and density cannot realize accurately controlling
System；Existing two kinds of decorating method, all cannot fully show the effect of graininess ornament, all cannot be accurate in processing technique
Meet the design concept of designer.
Additionally, pottery can cut out leftover bits during base substrate, existing generally leftover bits are reclaimed again system
Becoming base slurry, which reclaims clout, secondary operations complex procedures, reclaims clout added value low；If therefore can set according to intention
The demand of meter, and according to the problem in existing Production of Ceramics, it is provided that one can realize blank and recycle, and produces and has uniqueness
Artistic effect, the PEARL CHINA sand intention ceramic of high added value necessarily have positive society and economic benefit.
Summary of the invention
In order to overcome the deficiencies in the prior art, the invention provides and a kind of utilize ceramic body waste material to prepare PEARL CHINA sand
Method.
For achieving the above object, the invention provides a kind of method utilizing base substrate waste material to prepare PEARL CHINA sand, its feature
It is, comprises the steps:
Waste recovery, collects the base substrate leftover bits under being excised in ceramic body manufacturing process；
Step 2, is dried, base substrate leftover bits dried for standby；
Step 3, broken, according to the particle diameter needed for decoration, the porcelain sand base substrate that dried base substrate leftover bits are ground into；
Step 4, setting, porcelain sand granule base substrate puts into easy fired in kiln, it is thus achieved that porcelain sand biscuit；
Step 5, pastes, by porcelain sand biscuit gluing on ceramic body；
Step 6, forms by a firing, and has the ceramic body of porcelain sand biscuit to put in kiln to form by a firing by glutinous, it is thus achieved that with treasure
The ceramic of pearl porcelain sand effect.
Further, in step 6, the temperature that forms by a firing of ceramic body is higher than the easy fired of porcelain sand biscuit body in step 4
Temperature.
Further, in step 4, the easy fired temperature of porcelain sand biscuit is 600-800 DEG C.
Further, in step 6, the temperature that forms by a firing of ceramic body is 1000-1200 DEG C.
Further, glazing on first ceramic body in step 5, porcelain sand biscuit by glaze gluing on ceramic body.
Further, the method that base substrate waste material prepares PEARL CHINA sand is utilized, it is characterised in that:
Further, after porcelain sand biscuit gluing is on ceramic body, porcelain sand biscuit is executed one layer of glaze again.
Further, the glazing mode of the glaze on porcelain sand biscuit is glaze spraying.
Further, imposing on the glaze on ceramic body is different glaze from the glaze imposed on porcelain sand biscuit.
A kind of PEARL CHINA sand intention pottery, including ceramic body and the glaze layer being located on ceramic body, it is characterised in that:
Described ceramic body is provided with above-mentioned PEARL CHINA sand.
Further, PEARL CHINA sand is externally provided with one layer of glaze layer.
From the above-mentioned description of this invention, the invention provides the manufacture method of PEARL CHINA sand and there is PEARL CHINA sand
Intention pottery, this kind of PEARL CHINA sand utilizes ceramic body waste material to prepare, and has saved raw material, processing technology is simple, simplify waste material
Recovery process；
This kind of PEARL CHINA sand is located on intention pottery, and the particle diameter of porcelain sand granule can convert according to the needs of design, and
The arrangement relation of porcelain sand granule, density, the glaze colours on top layer all can be changed according to design requirement, and its artistic effect is obvious, tactile
Touching with obvious granule texture, can be used for making the different particle shapes such as snowflake, sandy beach, the wheat head, rainwater, this kind is designer
Provide multiple choices, it is achieved various intention effect.
Detailed description of the invention
Below by way of detailed description of the invention, the invention will be further described.
A kind of method utilizing base substrate waste material to prepare PEARL CHINA sand, it is characterised in that comprise the steps:
Step 1, waste recovery, collect the base substrate leftover bits under being excised in ceramic body manufacturing process；
Step 2, is dried, base substrate leftover bits dried for standby；
Step 3, broken, according to the particle diameter needed for decoration, the porcelain sand base substrate that dried base substrate leftover bits are ground into；
Step 4, setting, porcelain sand granule base substrate puts into easy fired in kiln, it is thus achieved that porcelain sand biscuit, the low temperature of porcelain sand biscuit
Firing temperature is 600-800 DEG C；
Step 5, paste, glazing on ceramic body, porcelain sand biscuit by glaze gluing on ceramic body；
Step 6, forms by a firing, and has the ceramic body of porcelain sand biscuit to put in kiln to form by a firing by glutinous, it is thus achieved that with treasure
The ceramic of pearl porcelain sand effect, the temperature that forms by a firing of ceramic body is higher than the easy fired temperature of porcelain sand biscuit body in step 4
Degree, the temperature that forms by a firing of ceramic body is 1000-1200 DEG C.
After step 5 completes, after porcelain sand biscuit gluing is on ceramic body, porcelain sand biscuit is executed one layer of glaze again, should
Layer glaze preferred glazing mode be glaze spraying, put on the glaze on porcelain sand biscuit can ensure the porcelain firm gluing of sand biscuit in
It can be again porcelain sand glazing on ceramic body.
A kind of PEARL CHINA sand intention pottery, including ceramic body and the glaze layer being located on ceramic body, on ceramic body
Being provided with PEARL CHINA sand, PEARL CHINA sand is externally provided with one layer of glaze layer, and according to design needs, imposing on the glaze on porcelain sand biscuit can be with pottery
Glaze on porcelain base substrate is identical or different, to meet the effect of ceramic.
Above-mentioned PEARL CHINA sand utilizes ceramic body waste material to prepare, and has saved raw material, processing technology is simple, simplify waste material returns
Receive flow process；
This kind of PEARL CHINA sand is located on intention pottery, and the particle diameter of porcelain sand granule can convert according to the needs of design, and
The arrangement relation of porcelain sand granule, density, the glaze colours on top layer all can be changed according to design requirement, and its artistic effect is obvious, tactile
Touching with obvious granule texture, can be used for making the different particle shapes such as snowflake, sandy beach, the wheat head, rainwater, this kind is designer
Provide multiple choices, it is achieved various intention effect
Above are only a specific embodiment of the present invention, but the design concept of the present invention is not limited thereto, all profits
With this design, the present invention is carried out the change of unsubstantiality, the behavior invading scope all should be belonged to.
Claims (10)
1. one kind utilizes the method that base substrate waste material prepares PEARL CHINA sand, it is characterised in that: comprise the steps:
Step 1, waste recovery, collect the base substrate leftover bits under being excised in ceramic body manufacturing process；
Step 2, is dried, base substrate leftover bits dried for standby；
Step 3, broken, according to the particle diameter needed for decoration, the porcelain sand base substrate that dried base substrate leftover bits are ground into；
Step 4, setting, porcelain sand granule base substrate puts into easy fired in kiln, it is thus achieved that porcelain sand biscuit；
Step 5, pastes, by porcelain sand biscuit gluing on ceramic body；
Step 6, forms by a firing, and has the ceramic body of porcelain sand biscuit to put in kiln to form by a firing by glutinous, it is thus achieved that with PEARL CHINA
The ceramic of sand effect.
The method utilizing base substrate waste material to prepare PEARL CHINA sand the most according to claim 1, it is characterised in that: described step 6
The temperature that forms by a firing of middle ceramic body is higher than the easy fired temperature of porcelain sand biscuit body in step 4.
The method utilizing base substrate waste material to prepare PEARL CHINA sand the most according to claim 2, it is characterised in that: described step 4
The easy fired temperature of middle porcelain sand biscuit is 600-800 DEG C.
4. according to utilizing, described in Claims 2 or 3, the method that base substrate waste material prepares PEARL CHINA sand, it is characterised in that: described step
In rapid 6, the temperature that forms by a firing of ceramic body is 1000-1200 DEG C.
The method utilizing base substrate waste material to prepare PEARL CHINA sand the most according to claim 1, it is characterised in that: in step 5 first
Glazing on ceramic body, porcelain sand biscuit by glaze gluing on ceramic body.
The method utilizing base substrate waste material to prepare PEARL CHINA sand the most according to claim 5, it is characterised in that: described porcelain sand element
After base gluing is on ceramic body, porcelain sand biscuit is executed one layer of glaze again.
The method utilizing base substrate waste material to prepare PEARL CHINA sand the most according to claim 6, it is characterised in that: described porcelain sand element
The glazing mode of the glaze on base is glaze spraying.
8. according to utilizing, described in claim 6 or 7, the method that base substrate waste material prepares PEARL CHINA sand, it is characterised in that execute described in:
Glaze on ceramic body is different glaze from the glaze imposed on porcelain sand biscuit.
9. a PEARL CHINA sand intention pottery, including ceramic body and the glaze layer being located on ceramic body, it is characterised in that: institute
State ceramic body and be provided with in claim 1-7 the PEARL CHINA sand described in any one.
10. according to the PEARL CHINA sand intention pottery described in claim 9, it is characterised in that: described PEARL CHINA sand is externally provided with one layer of glaze
The bed of material.