CN103159467A - Archaized tile with gorge grains and production method for same - Google Patents
Archaized tile with gorge grains and production method for same Download PDFInfo
- Publication number
- CN103159467A CN103159467A CN 201110408126 CN201110408126A CN103159467A CN 103159467 A CN103159467 A CN 103159467A CN 201110408126 CN201110408126 CN 201110408126 CN 201110408126 A CN201110408126 A CN 201110408126A CN 103159467 A CN103159467 A CN 103159467A
- Authority
- CN
- China
- Prior art keywords
- tile
- clay
- blank
- antique imitation
- imitation tiles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an archaized tile with gorge grains and a production method for the same. The archaized tile is characterized in that the components needed by blank preparation comprise potassium feldspar A, potassium feldspar B, soda feldspar A, soda feldspar B, soda feldspar C, potassium-soda feldspar A, pyrophyllite, talcum, flint clay, clay A and clay B. The production method for the archaized tile with gorge grains comprises the steps of selecting raw material for each component of a blank, ball-milling to prepare slurry, spraying to prepare powder, distributing the raw materials by a plurality of tubes; pressing by a large-tonnage press, drying, forming a dry blank, glazing clouds, polishing glazes, printing, firing in a roller kiln at a high temperature of 1200 DEG C, polishing and edging, performing a super-bright process, and finally obtaining the finished products, grading, packaging and warehousing. The production process disclosed by the invention combines a super-bright process technology for polished tile and a glazing and printing technology for archaized tile, so that the surface lines of the ceramic tile are randomly changed; and vertical and horizontal grains are distributed on the surface of the tile like a natural gorge, thus the archaized tile has an artistic effect and is comfortable in touch sense.
Description
Technical field
the present invention relates to a kind of Antique Imitation Tiles and production technique thereof, particularly relate to a kind of Antique Imitation Tiles and production technique thereof with valley texture.
Background technology
antique Imitation Tiles has been commonly referred to as the glaze decorative block, and its base substrate can be porcelain, and this is main flow; Shi porcelain, thin Shi and Shi matter are also arranged; Glaze take inferior light as main; Tone be take yellow, coffee color, garnet, ashen, grey, grey black etc. as main; The culture that Antique Imitation Tiles is contained, historical connotation and abundant decoration technique make its ceramic tile main product that becomes European & American Market, have also obtained at home development rapidly.Along with the development of personalized consumption, the human consumer has also had higher requirement to the personalization of house decoration.
traditional Antique Imitation Tiles product, very large expressive space is being arranged aspect color and sense of touch, its personalized characteristic also is well received by consumers, all the time, it is the main manifestations mode that the concavo-convex imitative stone mill face of dumb light is take in the performance of the texture of product surface, in order to make Antique Imitation Tiles reach natural and tripping decorative effect, " valley " technology is arisen at the historic moment, the valley technology has been taken into account the mature technology of polished tile and Antique Imitation Tiles, and make the two effective combination, combine the polishing technology of polished tile and the glaze line technology of Antique Imitation Tiles, make the brick face have the brightness of polished tile concurrently, the texture performance is more three-dimensional, surface touches the natural effects with obvious raised grain, the three-dimensional performance mode of product is stronger.
for the satisfying the market consumers demand, people are in the urgent need to the Antique Imitation Tiles with valley texture of polytypic more.
Summary of the invention
the object of the invention is to solve the technical problem of this series products of domestic production, and developed a kind of Antique Imitation Tiles and production technique thereof with valley texture.This Antique Imitation Tiles series product application with valley texture of the present invention's exploitation combines the super clean bright Technology of polished tile and glazing and the printing technique of Antique Imitation Tiles, and have breakthrough on the basis of the two combination, belong to the edge new technology, the breakthrough point of technology is on glaze line and glossing, on glazing line, comprise and use the cloud glaze spraying, the mill glaze, get ready, hang husky, the rubber roll stamp, for the glaze that strengthens Antique Imitation Tiles antifouling, wear resisting property, the transparent of minute three spraying abrasion-proofs on concavo-convex imitative stone mill face, after burning till, glaze adopts full technique of throwing, by throwing glaze, make the brick face produce special aesthetic effect.Make the surface detail random variation of ceramic tile, texture in length and breadth is just like the surface that is distributed in brick in natural valley, and existing artistic effect sense of touch again is comfortable.
technical solution of the present invention is: this Antique Imitation Tiles with valley texture is characterized in that the blank of this Antique Imitation Tiles is prepared required component and weight percent thereof:
a potassium felspar sand 12-17%,
b potassium felspar sand 11-15%,
a albite 9-13%,
b albite 7-12%,
c albite 3-5%,
a potassium albite 9-11%,
agalmatolite 18-25%,
talcum 3-5%,
flint clay 1-3%,
a clay 9-12%,
b clay 12-16%.
the blank of this Antique Imitation Tiles is prepared required Chemical Composition and content
SiO
2
58.00--68.00％，
AL
2
O
3
12.00--17.00％，
Fe
2
O
3
<1.50％，
TiO
3
<2.25％，
CaO <3.50％，
MgO 1.5-3％，
K
2
O 0.80-1.30％，
Na
2
O 3.90-5.60％，
I.L <1.2％。
this preparation method with Antique Imitation Tiles of valley texture that the present invention provides, be characterized in by selected raw material, ball milling, the operations such as preparation, multitube cloth, great tonnage press compacting, drying, multiple colour printing technique, roller kiln burn till, edging, super clean bright technique form.Its Raw, on the basis of basic powder, has increased the application of dry granular material and special material, and the application mix technology is processed to adapt to the needs of production to raw material; On glazing line, mainly adopt cloud glaze spraying, mill glaze, get, hang the techniques such as sand, rubber roll stamp ready; For the product water-intake rate is controlled at below 0.5%, reach the state of complete vitreous, firing temperature is brought up to more than 1200 ℃.The antifouling ability of ceramic tile through processing like this improves greatly, and greatly reduces production cost.In addition, to the surface of ceramic tile, adopt the special techniques such as burn into sandblast to carry out the post-production processing, also can make Antique Imitation Tiles produce personalized decorative effect.
compared with prior art, the invention has the beneficial effects as follows:
1, break through the intrinsic impression of traditional Antique Imitation Tiles dumb light flour milling, surface gloss is high, and the brick face is penetrating, bright, and the texture performance is more clear.
2, brick face performance color surging force is strong, and texture and transparent merge mutually, and unique texture is ready to appear, has natural stereoeffect.
3, brick face superficial makings is crisscross, touches and has obvious convex-concave texture, and the natural effects of true reappearance lithotome, bring strong natural artistic treat.
The accompanying drawing explanation
fig. 1 is process flow sheet of the present invention.
Embodiment
Embodiment
this blank with Antique Imitation Tiles of valley texture is prepared required component and weight percent thereof:
a potassium felspar sand 12%, B potassium felspar sand 11%, A albite 9%, B albite 7%,
c albite 3%, A potassium albite 9%, agalmatolite 18%, talcum 3%,
flint clay 1%, A clay 9%, B clay 12 %.The clay surplus.
this blank with Antique Imitation Tiles of valley texture is prepared required Chemical Composition and content
AL
2
O
3
12.00％， Fe
2
O
3
1.0％，TiO
3
2.2％，CaO 3.0％，
MgO 1.5％，K
2
O 0.80％，Na
2
O 3.90％，I.L 1.0％。SiO
2
surplus.
the selected raw material of each component, ball milling slurrying by blank, spray pulverization, multitube cloth, great tonnage press compacting, drying, formation dry body, cloud glazing, the mill glaze, stamp, 1200 ℃ of high temperature of roller kiln burn till, polishing edging, super clean bright technique, finally obtain finished product classification packing warehouse-in.
this technical indicator with Antique Imitation Tiles of valley texture that the present invention provides sees the following form:
the technical indicator contrast table
Claims (3)
1. the Antique Imitation Tiles with valley texture is characterized in that the blank of this Antique Imitation Tiles is prepared required component and weight percent thereof:
A potassium felspar sand 12-17%,
B potassium felspar sand 11-15%,
A albite 9-13%,
B albite 7-12%,
C albite 3-5%,
A potassium albite 9-11%,
Agalmatolite 18-25%,
Talcum 3-5%,
Flint clay 1-3%,
A clay 9-12%,
B clay 12-16%.
2. the Antique Imitation Tiles with valley texture according to claim 1, is characterized in that the blank of this Antique Imitation Tiles is prepared required Chemical Composition and content
SiO
2 58.00--68.00％，
AL
2O
3 12.00--17.00％，
Fe
2O
3 <1.50％，
TiO
3 <2.25％，
CaO <3.50％，
MgO 1.5-3％，
K
2O 0.80-1.30％，
Na
2O 3.90-5.60％，
I.L <1.2％。
3. the preparation method with Antique Imitation Tiles of valley texture according to claim 1, it is characterized in that the selected raw material of each component, the ball milling slurrying of blank, spray pulverization, multitube cloth, great tonnage press compacting, drying, formation dry body, cloud glazing, the mill glaze, stamp, 1200 ℃ of high temperature of roller kiln burn till, polishing edging, super clean bright technique, finally obtain finished product classification packing warehouse-in.