CN107986747A - The aging crack ceramic and its manufacture craft of no glaze decoration - Google Patents
The aging crack ceramic and its manufacture craft of no glaze decoration Download PDFInfo
- Publication number
- CN107986747A CN107986747A CN201711029685.2A CN201711029685A CN107986747A CN 107986747 A CN107986747 A CN 107986747A CN 201711029685 A CN201711029685 A CN 201711029685A CN 107986747 A CN107986747 A CN 107986747A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic
- glaze
- aging crack
- aging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to ceramic fabrication technique field, is specifically related to a kind of the aging crack ceramic and its manufacture craft of no glaze decoration.The blank raw material for the aging crack ceramic that this kind is decorated without glaze includes：Laterite, feldspar, smolmitza, quartz, spodumene, kaolin, di-iron trioxide.The aging crack ceramic of no glaze decoration provided by the invention, surface does not have to glaze water and decorates and expose coarse base substrate, and natural cracking is formed on ceramic body surface, and the lines of cracking gos deep into ceramic body, it is beautiful with the similar effect being corroded, textural effect；When this kind makes without the aging crack ceramic that glaze is decorated, the natural cracking of billet surface is caused by inside and outside contraction difference, but crackle is not through ceramic body, the normal use of ceramic is not influenced, this kind provides a kind of brand-new ceramic decoration method without the aging crack ceramic that glaze is decorated, to promoting the development of ceramic product with positive meaning and with positive economic benefit.
Description
Technical field
The present invention relates to ceramic fabrication technique field, be specifically related to a kind of no glaze decoration aging crack ceramic and
Its manufacture craft.
Background technology
It is traditional to ceramic product with the continuous improvement of people's living standards, aesthetic requirement is also constantly changing
Slight improvement is carried out in shape or pattern, existing design level can not be broken through, lack innovation, it is difficult to adapt to consumer and look for novelty
Seek the demand of change.
To solve the above problems, occur the ceramic decoration of a variety of crack effects, such as application publication number on the market
The disclosed ceramic product production methods with crackle glaze paint of CN102503565A, such as application publication number are CN 105906211A
Preparation method, low-temperature cracks glaze and the use as disclosed in application publication number is CN105294173A of the disclosed colored crack ceramic of kind
Its low-temperature cracks glaze ceramic prepared and preparation method etc.；Ceramics are shown to decorate by the glazing effect of crackle.
The ceramic surface of existing crackle decoration is decorated by glaze paint cracking, and tiny split is formed in glaze layer
Line, it makes ceramic have specific artistic effect and get the favour of people, its formation mechenism is the expansion system using glaze
Number is more than the coefficient of expansion of base, and when ceramics cool down, the contraction of glaze is more than base, and causes glaze layer that cracking, the difference shunk occurs
Bigger, the degree of cracking is also bigger；Glaze it is elastic smaller, cracking also can be bigger.Face checking provides a kind of brand-new ceramics dress
Decorations method, but the effect of only glaze paint cracking lacks three-dimensional sense, therefore the effect of existing only glaze paint crackle, needs further to be changed
Into.
The content of the invention
In order to solve the deficiencies in the prior art, the present invention provides a kind of no glaze decoration aging crack ceramic and its
Manufacture craft.
To achieve the above object, the technical solution adopted by the present invention is as follows：The aging crack ceramic of no glaze decoration, its
It is characterized in that, the blank raw material component of the aging crack ceramic without glaze decoration is as follows：35-45 parts of laterite, feldspar
15-20 parts, 10-15 parts of smolmitza, 10-15 parts of quartz, 5-10 parts of spodumene, 5-10 parts of kaolin, 1-5 parts of di-iron trioxide.
Optimization, the blank raw material component of the aging crack ceramic without glaze decoration is as follows：37 parts of laterite, feldspar 20
Part, 15 parts of smolmitza, 13 parts of quartz, 6 parts of spodumene, 7 parts of kaolin, 2 parts of di-iron trioxide.
Optimization, the blank raw material component of the aging crack ceramic without glaze decoration is as follows：41 parts of laterite, feldspar 18
Part, 13 parts of smolmitza, 12 parts of quartz, 7 parts of spodumene, 6 parts of kaolin, 3 parts of di-iron trioxide.
Optimization, the blank raw material component of the aging crack ceramic without glaze decoration is as follows：42 parts of laterite, feldspar 16
Part, 12 parts of smolmitza, 11 parts of quartz, 8 parts of spodumene, 7 parts of kaolin, 4 parts of di-iron trioxide.
A kind of manufacture craft of the aging crack ceramic of no glaze decoration, makes the aging crack of above-mentioned no glaze decoration
Ceramic, comprises the following steps that：
Step 1, biscuit powder is prepared, the particle diameter of biscuit powder is 0.3-0.5mm；
Step 2, base substrate slurry is made in the material component for the aging crack ceramic decorated according to no glaze；
Step 3, ceramic body is made in base substrate slurry made from step 2；
Step 4, when ceramic body moisture content is 30-45%, biscuit powder prepared by step 1 is sprinkling upon on ceramic body；
Step 5, after ceramic body moisture content is 3-5%, kiln kiln roasting type is put into, firing temperature is 1150 ± 50
℃。
Further, the raw material components of biscuit powder are as follows in step 1：Kaolin 45-50, quartz 20-30, white clouds soil 15-
20th, feldspar 5-10, zirconium oxide 1-5.
Further, the raw material components of biscuit powder are as follows：Kaolin 48, quartz 22, white clouds soil 17, feldspar 9, zirconium oxide 4.
Further, in step 1, prepared by biscuit powder comprises the following steps that：
S1, weighs mixing according to the material component of biscuit powder, adds water for ball milling that slurry is made；
S2, by above-mentioned slurry agitation it is uniform after be transferred to comminutor, open comminutor and be granulated, is made up of comminutor
Biscuit particle；
S3, after biscuit particle drying, is put into kiln and forms by a firing acquisition ceramic particle；
S4, the ceramic particle after shaping obtain biscuit powder through crushing, sieving.
Further, the firing temperature of ceramic particle is 1200-1250 DEG C.
The aging crack ceramic of no glaze decoration provided by the invention, surface does not have to glaze water and decorates and expose coarse base
Body, and natural cracking is formed on ceramic body surface, the lines of cracking gos deep into ceramic body, has the similar effect being corroded
Fruit, textural effect are beautiful；When this kind makes without the aging crack ceramic that glaze is decorated, selected specific blank raw material and biscuit
Powder so that ceramic body has stronger plasticity while with the shrinkage ratio of biscuit powder in critical range, when high-moisture percentage
Dry biscuit powder is sprinkled on ceramic body, is fired after its drying, base substrate table is caused by inside and outside contraction difference
The natural cracking in face, but crackle is not through ceramic body, does not influence the normal use of ceramic, the nature that this kind is decorated without glaze
Crack ceramic product provides a kind of brand-new ceramic decoration method, to promote ceramic product development have positive meaning and
And there is positive economic benefit.
Embodiment
Below by way of embodiment, the invention will be further described.
The aging crack ceramic of no glaze decoration, it is characterised in that the described aging crack ceramic system without glaze decoration
The blank raw material component of product is as follows：35-45 parts of laterite, 15-20 parts of feldspar, 10-15 parts of smolmitza, 10-15 parts of quartz, spodumene
5-10 parts, 5-10 parts of kaolin, 1-5 parts of di-iron trioxide.
Specific embodiment one：
The aging crack ceramic of no glaze decoration, the blank raw material component of the aging crack ceramic without glaze decoration
It is as follows：37 parts of laterite, 20 parts of feldspar, 15 parts of smolmitza, 13 parts of quartz, 6 parts of spodumene, 7 parts of kaolin, 2 parts of di-iron trioxide.
Specific embodiment two：
The aging crack ceramic of no glaze decoration, the blank raw material component of the aging crack ceramic without glaze decoration
It is as follows：41 parts of laterite, 18 parts of feldspar, 13 parts of smolmitza, 12 parts of quartz, 7 parts of spodumene, 6 parts of kaolin, 3 parts of di-iron trioxide.
Specific embodiment three：
The aging crack ceramic of no glaze decoration, the blank raw material component of the aging crack ceramic without glaze decoration
It is as follows：42 parts of laterite, 16 parts of feldspar, 12 parts of smolmitza, 11 parts of quartz, 8 parts of spodumene, 7 parts of kaolin, 4 parts of di-iron trioxide.
The manufacture craft of the aging crack ceramic of no glaze decoration, make described in above-mentioned any one without glaze decoration
Aging crack ceramic, comprises the following steps that：
Step 1, biscuit powder is prepared, the raw material components of wherein biscuit powder are as follows：Kaolin 45-50, quartz 20-30, white clouds
Native 15-20, feldspar 5-10, zirconium oxide 1-5, it is preferred that kaolin 48, quartz 22, white clouds soil 17, feldspar 9, zirconium oxide 4,
S1, weighs mixing according to the material component of biscuit powder, adds water for ball milling that slurry is made,
S2, by above-mentioned slurry agitation it is uniform after be transferred to comminutor, open comminutor and be granulated, is made up of comminutor
Biscuit particle,
S3, after biscuit particle drying, is put into kiln and forms by a firing acquisition ceramic particle through 1200-1250 DEG C,
S4, the ceramic particle after shaping obtain the biscuit powder that particle diameter is 0.3-0.5mm through crushing, sieving；
Step 2, base substrate slurry is made in the material component for the aging crack ceramic decorated according to no glaze；
Step 3, ceramic body is made in base substrate slurry made from step 2；
Step 4, when ceramic body moisture content is 30-45%, biscuit powder prepared by step 1 is sprinkling upon on ceramic body；
Step 5, after ceramic body moisture content is 3-5%, kiln kiln roasting type is put into, firing temperature is 1150 ± 50
℃。
Using the aging crack ceramic decorated made from the above method without glaze, surface does not have to glaze water and decorates and expose thick
Rough base substrate, and natural cracking is formed on ceramic body surface, the lines of cracking gos deep into ceramic body, has similar rotten
The effect of erosion, textural effect are beautiful；When this kind makes without the aging crack ceramic that glaze is decorated, selected specific blank raw material
With biscuit powder so that ceramic body has stronger plasticity while with the shrinkage ratio of biscuit powder in critical range, when height contains
Dry biscuit powder is sprinkled on the ceramic body of water rate, is fired after its drying, is caused by inside and outside contraction difference
The natural cracking of billet surface, but crackle is not through ceramic body, does not influence the normal use of ceramic, and this kind is decorated without glaze
Aging crack ceramic provide a kind of brand-new ceramic decoration method, to promoting the development of ceramic product with positive
Meaning and there is positive economic benefit.
The specific embodiment of the present invention is above are only, but the design concept of the present invention is not limited thereto, all profits
The change of unsubstantiality is carried out to the present invention with this design, the behavior for invading the scope of the present invention should all be belonged to.
Claims (9)
1. the aging crack ceramic without glaze decoration, it is characterised in that the described aging crack ceramic without glaze decoration
Blank raw material component it is as follows：35-45 parts of laterite, 15-20 parts of feldspar, 10-15 parts of smolmitza, 10-15 parts of quartz, spodumene 5-
10 parts, 5-10 parts of kaolin, 1-5 parts of di-iron trioxide.
2. the aging crack ceramic of no glaze decoration according to claim 1, it is characterised in that described this is decorated without glaze
Aging crack ceramic blank raw material component it is as follows：37 parts of laterite, 20 parts of feldspar, 15 parts of smolmitza, quartzy 13 parts, lithium
6 parts of pyroxene, 7 parts of kaolin, 2 parts of di-iron trioxide.
3. the aging crack ceramic of no glaze decoration according to claim 1, it is characterised in that described this is decorated without glaze
Aging crack ceramic blank raw material component it is as follows：41 parts of laterite, 18 parts of feldspar, 13 parts of smolmitza, quartzy 12 parts, lithium
7 parts of pyroxene, 6 parts of kaolin, 3 parts of di-iron trioxide.
4. the aging crack ceramic of no glaze decoration according to claim 1, it is characterised in that described this is decorated without glaze
Aging crack ceramic blank raw material component it is as follows：42 parts of laterite, 16 parts of feldspar, 12 parts of smolmitza, quartzy 11 parts, lithium
8 parts of pyroxene, 7 parts of kaolin, 4 parts of di-iron trioxide.
5. a kind of manufacture craft of the aging crack ceramic of no glaze decoration, make require described in 1-4 any one without glaze
The aging crack ceramic of decoration, comprises the following steps that：
Step 1, biscuit powder is prepared, the particle diameter of biscuit powder is 0.3-0.5mm；
Step 2, base substrate slurry is made in the material component for the aging crack ceramic decorated according to no glaze；
Step 3, ceramic body is made in base substrate slurry made from step 2；
Step 4, when ceramic body moisture content is 30-45%, biscuit powder prepared by step 1 is sprinkling upon on ceramic body；
Step 5, after ceramic body moisture content is 3-5%, kiln kiln roasting type is put into, firing temperature is 1150 ± 50 DEG C.
6. the manufacture craft of the aging crack ceramic of no glaze decoration according to claim 5, it is characterised in that described
The raw material components of biscuit powder are as follows in step 1：Kaolin 45-50, quartz 20-30, white clouds soil 15-20, feldspar 5-10, zirconium oxide
1-5。
7. the manufacture craft of the aging crack ceramic of no glaze decoration according to claim 6, it is characterised in that described
The raw material components of biscuit powder are as follows：Kaolin 48, quartz 22, white clouds soil 17, feldspar 9, zirconium oxide 4.
8. the manufacture craft of the aging crack ceramic without glaze decoration according to claim 6 or 7, it is characterised in that
In the step 1, prepared by biscuit powder comprises the following steps that：
S1, weighs mixing according to the material component of biscuit powder, adds water for ball milling that slurry is made；
S2, by above-mentioned slurry agitation it is uniform after be transferred to comminutor, open comminutor and be granulated, biscuit is made by comminutor
Particle；
S3, after biscuit particle drying, is put into kiln and forms by a firing acquisition ceramic particle；
S4, the ceramic particle after shaping obtain biscuit powder through crushing, sieving.
9. the manufacture craft of the aging crack ceramic of no glaze decoration according to claim 8, it is characterised in that described
The firing temperature of ceramic particle is 1200-1250 DEG C.