CN108169053A - 一种钢渣全铁含量检测方法 - Google Patents

一种钢渣全铁含量检测方法 Download PDF

Info

Publication number
CN108169053A
CN108169053A CN201711355651.2A CN201711355651A CN108169053A CN 108169053 A CN108169053 A CN 108169053A CN 201711355651 A CN201711355651 A CN 201711355651A CN 108169053 A CN108169053 A CN 108169053A
Authority
CN
China
Prior art keywords
slag
iron content
detection method
content detection
iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711355651.2A
Other languages
English (en)
Inventor
李明
周颂红
张高峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Xinxing Ductile Iron Pipes Co Ltd
Original Assignee
Wuhu Xinxing Ductile Iron Pipes Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Xinxing Ductile Iron Pipes Co Ltd filed Critical Wuhu Xinxing Ductile Iron Pipes Co Ltd
Priority to CN201711355651.2A priority Critical patent/CN108169053A/zh
Publication of CN108169053A publication Critical patent/CN108169053A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种钢渣全铁含量检测方法，包括以下步骤：(1)将钢渣试样烘干；(2)将烘干的钢渣试样进行研磨；(3)对研磨好的钢渣试样通过振动筛进行筛分；(4)使用磁铁对筛上物进行吸附，吸附物收集称重，此部分为钢渣中的单质铁部分；(5)将筛上物未吸附部分与筛下物混合收集称重，此部分钢渣中的氧化铁部分；(6)从而检测单质铁和氧化铁含量。该钢渣全铁含量检测方法操作简便快捷，能够准确地检测出钢渣精粉中全铁含量，并提高了检测效率、降低了检测成本。

Description

一种钢渣全铁含量检测方法
技术领域
本发明涉及钢渣处理技术领域，尤其是涉及一种钢渣全铁含量检测方法。
背景技术
转炉钢渣经棒磨、磁选，生产出品位50％左右的优质钢渣精粉，可做为烧结的原料，达到资源回收利用的效果。
钢渣精粉中铁的存在形式有两种：铁的氧化物和单质金属铁。单质铁通常以球状、块状形状存在，因为颗粒硬度高、延展性好，在样品制备过程中很难被粉碎，导致检验结果偏差大。目前钢渣精粉全铁含量没有国家标准分析方法，现行的一些检测方法均存在可重复性差，或者检测成本高的问题。
发明内容
针对现有技术不足，本发明所要解决的技术问题是提供一种钢渣全铁含量检测方法，以达到检测快速准确的目的。
为了解决上述技术问题，本发明所采用的技术方案为：
该钢渣全铁含量检测方法，包括以下步骤：
(1)将钢渣试样烘干；
(2)将烘干的钢渣试样进行研磨；
(3)对研磨好的钢渣试样通过振动筛进行筛分；
(4)使用磁铁对筛上物进行吸附，吸附物收集称重，此部分为钢渣中的单质铁部分；
(5)将筛上物未吸附部分与筛下物混合收集称重，此部分钢渣中的氧化铁部分；
(6)从而检测单质铁和氧化铁含量。
其中，
所述步骤(1)之前，将钢渣试样进行缩分操作。
所述步骤(1)中的烘干在100-110℃的烘箱内烘干。
所述步骤(2)中，使用磨粉机研磨120s以上。
所述步骤(3)中，利用40目振动筛进行筛分。
所述步骤(4)中，吸附时在磁铁上包裹塑料袋。
本发明与现有技术相比，具有以下优点：该钢渣全铁含量检测方法操作简便快捷，能够准确地检测出钢渣精粉中全铁含量，并提高了检测效率、降低了检测成本。
具体实施方式
下面通过对实施例的描述，对本发明的具体实施方式作进一步详细的说明。
适用于钢渣中全铁含量的检测方法，包括破碎制样、钢渣分离和元素含量测定三个主程序，从而可以经济、快速、准确地测定钢渣中的全铁含量。
钢渣试样经缩分、烘干、研磨、筛分，并使用磁铁吸附，使钢种精粉中的单质铁和氧化铁有效分离。分别检测单质铁和氧化铁的质量分数和全铁含量，从而计算出钢渣精粉中的全铁含量。检测快速准确。
钢渣全铁含量检测方法具体操作步骤如下：
将钢渣试样进行缩分操作；
将钢渣试样在100-110℃的烘箱内烘干；
将烘干的钢渣试样使用磨粉机研磨120s以上；
利用40目振动筛对研磨好的钢渣试样通过振动筛进行筛分；
使用磁铁对筛上物进行吸附，吸附物收集称重，此部分为钢渣中的单质铁部分；
将筛上物未吸附部分与筛下物混合收集称重，此部分钢渣中的氧化铁部分；
从而检测单质铁和氧化铁含量。
其中，吸附时在磁铁上包裹塑料袋，便于收集吸附物，操作简便。
本发明的具体实例为：
(1)钢渣精粉试样使用二分器进行缩分，至料盒剩余试样为200g左右为止；(2)将缩分后的试样放在105℃±5℃的烘箱内经两小时以上烘干至恒重，取出冷却至室温；(3)试样全部倒入磨粉机料钵，使用磨粉机研磨120s以上，使单质铁有效分离；4)研磨好的试样使用40目标准筛振筛60s以上。(5)使用磁铁对筛上物进行吸附(注意吸附时在磁铁上包裹塑料袋)，吸附物收集称重(m1)，此部分认为是钢渣精粉中的单质铁部分；(6)将筛上物未吸附部分与筛下物混合，称重(m2)，此部分认为是钢渣精粉中的氧化铁部分；倒入料钵继续研磨60-120s，至粒度达到200目左右。
单质铁中全铁含量以经验数据85.8％计，氧化铁中的全铁含量(TFe2％)使用GB6730.65《铁矿石全铁含量的测定三氯化钛还原重铬酸钾滴定法(常规方法)》测定。
钢渣精粉中全铁含量(TFe％)计算公式为：
TFe％＝85.8％*m1/(m1+m2)+TFe2％*m2/(m1+m2)。
本发明为对钢铁企业钢渣精粉中全铁含量检测的新型检测方法，实践证明有效地提高了检测效率和准确性，降低了检验成本。
上面对本发明进行了示例性描述，显然本发明具体实现并不受上述方式的限制，只要采用了本发明的构思和技术方案进行的各种非实质性的改进，或未经改进将本发明的构思和技术方案直接应用于其它场合的，均在本发明的保护范围之内。

Claims (6)

1.一种钢渣全铁含量检测方法，其特征在于：所述钢渣全铁含量检测方法包括以下步骤：
(1)将钢渣试样烘干；
(2)将烘干的钢渣试样进行研磨；
(3)对研磨好的钢渣试样通过振动筛进行筛分；
(4)使用磁铁对筛上物进行吸附，吸附物收集称重，此部分为钢渣中的单质铁部分；
(5)将筛上物未吸附部分与筛下物混合收集称重，此部分钢渣中的氧化铁部分；
(6)从而检测单质铁和氧化铁含量。
2.如权利要求1所述钢渣全铁含量检测方法，其特征在于：所述步骤(1)之前，将钢渣试样进行缩分操作。
3.如权利要求1所述钢渣全铁含量检测方法，其特征在于：所述步骤(1)中的烘干在100-110℃的烘箱内烘干。
4.如权利要求1所述钢渣全铁含量检测方法，其特征在于：所述步骤(2)中，使用磨粉机研磨120s以上。
5.如权利要求1所述钢渣全铁含量检测方法，其特征在于：所述步骤(3)中，利用40目振动筛进行筛分。
6.如权利要求1所述钢渣全铁含量检测方法，其特征在于：所述步骤(4)中，吸附时在磁铁上包裹塑料袋。
CN201711355651.2A 2017-12-16 2017-12-16 一种钢渣全铁含量检测方法 Pending CN108169053A (zh)