CN108166318A - 可提高离型纸剥离效果的专用涂料 - Google Patents

可提高离型纸剥离效果的专用涂料 Download PDF

Info

Publication number
CN108166318A
CN108166318A CN201711406198.3A CN201711406198A CN108166318A CN 108166318 A CN108166318 A CN 108166318A CN 201711406198 A CN201711406198 A CN 201711406198A CN 108166318 A CN108166318 A CN 108166318A
Authority
CN
China
Prior art keywords
release paper
remover
white oil
peeling effect
improved
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711406198.3A
Other languages
English (en)
Inventor
周兴
冯春军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiaxing Baichuan Special Paper Industry Co Ltd
Original Assignee
Jiaxing Baichuan Special Paper Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiaxing Baichuan Special Paper Industry Co Ltd filed Critical Jiaxing Baichuan Special Paper Industry Co Ltd
Priority to CN201711406198.3A priority Critical patent/CN108166318A/zh
Publication of CN108166318A publication Critical patent/CN108166318A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种可提高离型纸剥离效果的专用涂料，由以下重量分数的原料制成：100%的PP颗粒、5‑10‰的白油以及5‑10‰的剥离剂在260‑300℃的温度下混合均匀制成。通过在常规的PP涂料中增加白油和剥离剂，在260‑300℃的温度下利用白油使剥离剂更好与PP颗粒混合均匀并溶入PP的分子间隔内，从而降低离型纸的剥离力。

Description

可提高离型纸剥离效果的专用涂料
技术领域
本发明涉及离型纸的涂料，具体涉及一种可提高离型纸剥离效果的专用涂料。
背景技术
现有以原纸为基材制成的用于印花转移的离型纸，通常都具有以下结构，原纸，在原纸一个表面涂一层涂料形成涂料层，涂料层上压花。目前该类离型纸在印花转移过程中，印花转移次数较少，且离型纸在印花转移过程中剥离力大，导致在使用过程中剥离后有残留，剥离不彻底，导致离型纸和载体报废，降低了离型纸的使用寿命，增加了生产成本。
发明内容
本发明针对现有技术的状况，提供了一种可提高离型纸剥离效果的专用涂料，通过在常规的PP涂料中增加白油和剥离剂，在260-300℃的温度下利用白油使剥离剂更好与PP颗粒混合均匀并溶入PP的分子间隔内，从而降低离型纸的剥离力。
为解决上述技术问题，本发明采用的一个技术方案是：可提高离型纸剥离效果的专用涂料，由以下重量分数的原料制成：100%的PP颗粒、5-10‰的白油以及5-10‰的剥离剂在260-300℃的温度下混合均匀制成。
作为上述方案的优选，由以下重量分数的原料制成：100%的PP颗粒、5‰的白油以及5‰的剥离剂在260-300℃的温度下混合均匀制成。
作为上述方案的优选，由以下重量分数的原料制成：100%的PP颗粒、10‰的白油以及10‰的剥离剂在260-300℃的温度下混合均匀制成。
本发明的有益效果是：通过在常规的PP涂料中增加白油和剥离剂，在260-300℃的温度下利用白油使剥离剂更好与PP颗粒混合均匀并溶入PP的分子间隔内，从而降低离型纸的剥离力，在本发明的方案中，剥离力低于15N。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。
可提高离型纸剥离效果的专用涂料，由以下重量分数的原料制成：100%的PP颗粒、5-10‰的白油以及5-10‰的剥离剂在260-300℃的温度下混合均匀制成。
剥离剂和PP具有相溶性，在白油的加入下，可使得剥离剂在260-300℃的温度下与PP混合均匀的同时有效溶入PP的分子间隔内，从而提高剥离效果。
对于本领域的技术人员来说，依然可以对前述各实施例所记载的技术方案进行修改，或对其中部分技术特征进行等同替换，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (3)

1.可提高离型纸剥离效果的专用涂料，其特征在于，由以下重量分数的原料制成：100%的PP颗粒、5-10‰的白油以及5-10‰的剥离剂在260-300℃的温度下混合均匀制成。
2.如权利要求1所述的可提高离型纸剥离效果的专用涂料，其特征在于，由以下重量分数的原料制成：100%的PP颗粒、5‰的白油以及5‰的剥离剂在260-300℃的温度下混合均匀制成。
3.如权利要求1所述的可提高离型纸剥离效果的专用涂料，其特征在于，由以下重量分数的原料制成：100%的PP颗粒、10‰的白油以及10‰的剥离剂在260-300℃的温度下混合均匀制成。
CN201711406198.3A 2017-12-22 2017-12-22 可提高离型纸剥离效果的专用涂料 Pending CN108166318A (zh)