CN108017937A - 用于硅烷改性聚醚密封胶碳酸钙的制备方法 - Google Patents
用于硅烷改性聚醚密封胶碳酸钙的制备方法 Download PDFInfo
- Publication number
- CN108017937A CN108017937A CN201711349632.9A CN201711349632A CN108017937A CN 108017937 A CN108017937 A CN 108017937A CN 201711349632 A CN201711349632 A CN 201711349632A CN 108017937 A CN108017937 A CN 108017937A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- modified polyether
- seal glue
- silane modified
- polyether seal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
名称 | 质量份数 |
硅烷改性聚醚 | 100 |
增塑剂(DOP) | 60 |
填料(碳酸钙) | 160 |
增白剂(TiO2) | 20 |
触变剂(氢化蓖麻油) | 5 |
酚抗氧化剂 | 1 |
氨基丙基二甲氧基甲基硅烷 | 1 |
催化剂 | 1 |
碳酸钙型号 | 胶粒黏度/Pa·S | 拉伸强度/MPa | 断裂伸长率/% |
实施例1 | 1600 | 2.3 | 410 |
实施例2 | 1850 | 2.8 | 390 |
实施例3 | 1780 | 2.5 | 430 |
对比例 | 1650 | 2.3 | 380 |
Claims (10)