CN107775776A - Imitative in a kind of ancient building covers lotus baluster column and its manufacture craft - Google Patents
Imitative in a kind of ancient building covers lotus baluster column and its manufacture craft Download PDFInfo
- Publication number
- CN107775776A CN107775776A CN201710936488.2A CN201710936488A CN107775776A CN 107775776 A CN107775776 A CN 107775776A CN 201710936488 A CN201710936488 A CN 201710936488A CN 107775776 A CN107775776 A CN 107775776A
- Authority
- CN
- China
- Prior art keywords
- lotus
- imitative
- baluster column
- weight
- baluster
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Lotus baluster column and its manufacture craft are covered the invention discloses imitative in a kind of ancient building, manufacture craft comprises the following steps：(1) parent part is made as model gypsum to cover the true part of lotus baluster column；(2) outer mold is made；(3) parent part is placed among outer mold and covered with silica gel, mould in silica gel is made；(4) iron oxide pigment uniform mixing is added with cement, adds stone dry powder, water and water reducer and be well mixed, cement building stones are made；(5) mould in silica gel is placed in outer mold, mould in silica gel is filled with cement building stones；(6) imitate and cover the maintenance of lotus baluster column semi-finished product；(7) imitate and cover lotus baluster column semi-finished product blasting treatment, dry；(8) imitate and cover lotus baluster column semi-finished product outer surface and do old processing；(9) it is imitative cover to spray stone protectant on lotus baluster column semi-finished product and be made imitative cover lotus baluster column finished product.The imitative manufacture craft for covering lotus baluster column in a kind of ancient building of the present invention, cheap, the imitative of wide material sources can be made and cover lotus baluster column.
Description
Technical field
Lotus baluster column and its manufacture craft are covered the present invention relates to imitative in a kind of ancient building, belongs to building in the style of the ancients manufacturing technology neck
Domain.
Background technology
It is the decoration in ancient building to cover lotus baluster column, is usually used in Gu Qiaozhong.It is located in a small piece of land surrounded by water in the Er Dou villages of Huzhou City of Zhejiang Province
It is equipped with that to cover lotus baluster column six right between the breast board of Shou Changqiao on river.It is documented that Shou Changqiao was built between the Southern Song Dynasty's salty pure year, away from the present
There is the history of more than 700 years, there is high cultural relic building to be worth.Cover lotus baluster column to form using the stone engraving of monoblock, cover lotus
The true part of baluster column has been historical relic, is not easy obtain more.The imitative lotus baluster column that covers in building in the style of the ancients is typically formed using stone machine engraving at present,
Imitative 28 petals for covering lotus baluster column are not that chisel is made by hand, but are mechanically cut out, and lines seem abnormal sharp with profile
It is clearly demarcated with corner angle, lose natural, graceful and poised mellow and full ancient rhythm.The stone resource that modern stone exploitation is enabled to be utilized is fewer and fewer, and
Ecology can be destroyed again, and the cost of labor of stone engraving is very high, and product qualified rate is low.It is therefore it provides a kind of cheap, wide material sources
It is imitative to cover lotus baluster column and its production technology has become urgent need.
The content of the invention
Lotus baluster column and its manufacture craft are covered the technical problem to be solved in the present invention is to provide imitative in a kind of ancient building, can be given birth to
Production is cheap, the imitative requirement covered lotus baluster column, meet in building in the style of the ancients of wide material sources.
In order to solve the above technical problems, the imitative manufacture craft for covering lotus baluster column in a kind of ancient building of the present invention, described imitative
The manufacture craft for covering lotus baluster column comprises the following steps：
(1) to cover the true part of lotus baluster column as model in ancient building, with gypsum with 1：1 ratio, which makes to imitate, covers lotus baluster column mother
Part；
(2) do kind of a mould with the imitative lotus baluster column parent part that covers, make can accommodate imitate cover lotus baluster column parent part be unlikely to deform and two panels is opened
The outer mold of conjunction；
(3) outer mold is placed on the plane, imitative will covers lotus baluster column parent part and flat down and be placed among outer mold, covered imitative
Covered on lotus baluster column parent part with silica gel and silica gel fills up the inner space of outer mold to level, outer mold is removed after silica gel solidification
Mould in silica gel is made, by the dimidiation placed in the middle of mould in silica gel, takes out to imitate and covers lotus baluster column parent part；
(4) iron oxide pigment uniform mixing is added close to the true part color of lotus baluster column is covered with cement, add stone dry powder, water
It is well mixed with water reducer, cement building stones is made；
(5) outer mold is inverted in the plane, the concave surface that flats down of mould in silica gel is placed in outer mold upward, used
The cement building stones mixed fill in silica gel forming and hardening in mould；
(6) the imitative lotus baluster column semi-finished product that cover in silica gel in mould are taken out to be conserved；
(7) by conserved it is imitative cover lotus baluster column semi-finished product carry out sandblasting make its outer surface coarse, place drying；
(8) the imitative outer surface for covering lotus baluster column semi-finished product is carried out doing old processing with hairbrush；
(9) do after old processing it is imitative cover to spray stone protectant on lotus baluster column semi-finished product and be made imitative cover lotus baluster column finished product.
As the improvement of the present invention, mould thinnest part thickness is 1-3 centimetres in silica gel in the step (3).
As the improvement of the present invention, mould thinnest part thickness is 1 centimetre in silica gel in the step (3).
As the improvement of the present invention, iron oxide pigment weight is the 0.1-0.3% of cement weight in the step (4), stone
Head dry powder weight is 2-3 times of cement, and the weight of water is the 30-50% of cement weight, and the weight of water reducer is cement weight
5%.
As the improvement of the present invention, iron oxide pigment weight is the 0.2% of cement weight in the step (4), and stone is done
Powder weight is 2 times of cement, and the weight of water is the 40% of cement weight, and the weight of water reducer is the 5% of cement weight.
As the improvement of the present invention, the particle diameter of stone dry powder is 10-120 mesh in the step (4).
As the improvement of the present invention, the particle diameter of stone dry powder is 60-100 mesh in the step (4).
As the improvement of the present invention, the imitative lotus baluster column that covers conserve the fully hardened time as 7 days in the step (6).
As the improvement of the present invention, imitate that to cover the time that lotus baluster column is dried be 2 days in the step (7).
In order to solve the above technical problems, one kind of the present invention is imitative to cover lotus baluster column, the imitative lotus baluster column cement that covers adds oxygen
Change iron pigment uniform mixing close to the true part color of lotus baluster column is covered, add that stone dry powder, water and water reducer are well mixed to be made, its
Outer surface is roughened, does old processing, and is sprayed with stone protectant, and iron oxide pigment weight is the 0.1-0.3% of cement weight,
Stone dry powder weight is 2-3 times of cement, and the weight of water is the 30-50% of cement weight, and the weight of water reducer is cement weight
5%, the particle diameter of stone dry powder is 10-120 mesh.
The imitative manufacture craft for covering lotus baluster column in a kind of ancient building of the present invention, the imitative manufacture craft bag for covering lotus baluster column
Include following steps：(1) to cover the true part of lotus baluster column as model in ancient building, with gypsum with 1：1 ratio, which makes to imitate, covers lotus baluster column
Parent part；(2) do kind of a mould with the imitative lotus baluster column parent part that covers, make can accommodate imitate cover lotus baluster column parent part be unlikely to deform and two panels folding
Outer mold；(3) outer mold is placed on the plane, imitative will covers lotus baluster column parent part and flat down and be placed among outer mold, covered imitative
Covered on lotus baluster column parent part with silica gel and silica gel fills up the inner space of outer mold to level, outer mold is removed after silica gel solidification
Mould in silica gel is made, by the dimidiation placed in the middle of mould in silica gel, takes out to imitate and covers lotus baluster column parent part；(4) added and aoxidized with cement
The uniform mixing of iron pigment adds stone dry powder, water and water reducer and is well mixed close to the true part color of lotus baluster column is covered, and cement is made
Building stones；(5) outer mold is inverted in the plane, the concave surface that flats down of mould in silica gel is placed in outer mold upward, with mixing
Good cement building stones fill in silica gel forming and hardening in mould；(6) take out imitative in mould in silica gel and cover lotus baluster column semi-finished product
Conserved；(7) by conserved it is imitative cover lotus baluster column semi-finished product carry out sandblasting make its outer surface coarse, place drying；(8) hair is used
Brush and the imitative outer surface for covering lotus baluster column semi-finished product is carried out doing old processing；(9) sprayed after doing old processing in imitative cover on lotus baluster column semi-finished product
Upper stone protectant, which is made to imitate, covers lotus baluster column finished product, the imitative manufacture craft for covering lotus baluster column in a kind of ancient building of the invention, energy
Production is cheap, the imitative requirement covered lotus baluster column, meet in building in the style of the ancients of wide material sources.
Embodiment
A kind of imitative manufacture craft for covering lotus baluster column in ancient building, the imitative manufacture craft for covering lotus baluster column include following step
Suddenly：
(1) to cover the true part of lotus baluster column as model in ancient building, with gypsum with 1：1 ratio, which makes to imitate, covers lotus baluster column mother
Part；
(2) do kind of a mould with the imitative lotus baluster column parent part that covers, make can accommodate imitate cover lotus baluster column parent part be unlikely to deform and two panels is opened
The outer mold of conjunction；
(3) outer mold is placed on the plane, imitative will covers lotus baluster column parent part and flat down and be placed among outer mold, covered imitative
Covered on lotus baluster column parent part with silica gel and silica gel fills up the inner space of outer mold to level, outer mold is removed after silica gel solidification
Mould in silica gel is made, by the dimidiation placed in the middle of mould in silica gel, takes out to imitate and covers lotus baluster column parent part；
(4) iron oxide pigment uniform mixing is added close to the true part color of lotus baluster column is covered with cement, add stone dry powder, water
It is well mixed with SM high efficiency water reducing agents, cement building stones is made；
(5) outer mold is inverted in the plane, the concave surface that flats down of mould in silica gel is placed in outer mold upward, used
The cement building stones mixed fill in silica gel forming and hardening in mould；
(6) the imitative lotus baluster column semi-finished product that cover in silica gel in mould are taken out to be conserved；
(7) by conserved it is imitative cover lotus baluster column semi-finished product carry out sandblasting make its outer surface coarse, place drying；
(8) the imitative outer surface for covering lotus baluster column semi-finished product is carried out doing old processing with hairbrush；
(9) do after old processing it is imitative cover to spray stone protectant on lotus baluster column semi-finished product and be made imitative cover lotus baluster column finished product.
As the improvement of the present invention, mould thinnest part thickness is 1-3 centimetres in silica gel in the step (3).
As the improvement of the present invention, mould thinnest part thickness is 1 centimetre in silica gel in the step (3).
As the improvement of the present invention, iron oxide pigment weight is the 0.1-0.3% of cement weight in the step (4), stone
Head dry powder weight is 2-3 times of cement, and the weight of water is the 30-50% of cement weight, and the weight of water reducer is cement weight
5%.
As the improvement of the present invention, iron oxide pigment weight is the 0.2% of cement weight in the step (4), and stone is done
Powder weight is 2 times of cement, and the weight of water is the 40% of cement weight, and the weight of water reducer is the 5% of cement weight.
As the improvement of the present invention, the particle diameter of stone dry powder is 10-120 mesh in the step (4).
As the improvement of the present invention, the particle diameter of stone dry powder is 60-100 mesh in the step (4).
As the improvement of the present invention, the imitative lotus baluster column that covers conserve the fully hardened time as 7 days in the step (6).
As the improvement of the present invention, imitate that to cover the time that lotus baluster column is dried be 2 days in the step (7).
Sand blasted surface roughening processing is carried out to the imitative lotus baluster column semi-finished product that cover conserved in the step (7), using shifting
Dynamic formula sand-blasting machine (China Patent No. 201620178238.8) carries out blasting treatment, makes its outer surface coarse.It can certainly adopt
Blasting treatment is carried out with other similar abrasive blast equipments, makes its outer surface coarse.
The imitative outer surface for covering lotus baluster column semi-finished product is carried out doing old processing with hairbrush in the step (8), using a kind of people
Make stone plate surface processing unit (China Patent No. 201620233525.4) to carry out doing old processing, its outer surface pearl not exactly round in shape reason is seemed certainly
So.It can certainly carry out doing old processing using other similar artificial stone plate's surface processing equipments, make its outer surface pearl not exactly round in shape reason aobvious
Derived from right.
The imitative of the imitative manufacture craft making for covering lotus baluster column in a kind of above-mentioned ancient building covers lotus baluster column, and described imitate covers lotus
Baluster column cement adds iron oxide pigment uniform mixing close to the true part color of lotus baluster column is covered, and it is high to add stone dry powder, water and SM
It is well mixed obtained to imitate water reducer, its outer surface is roughened, does old processing, and is sprayed with stone protectant, iron oxide pigment weight
The 0.1-0.3% for cement weight is measured, stone dry powder weight is 2-3 times of cement, and the weight of water is the 30- of cement weight
50%, the weight of water reducer is the 5% of cement weight, and the particle diameter of stone dry powder is 10-120 mesh.
Because the object for covering the true part ortho states of lotus baluster column has been historical relic, and it is not easy obtain more.Lotus baluster column is covered to carve using the stone of monoblock
Quarter is formed, and the product for using modern Product Process to make lacks the ancient rhythm of original paper, and the exploitation of modern stone is enabled to be utilized
Stone resource it is fewer and fewer, and ecology can be destroyed again, the cost of labor of stone engraving is very high, and product qualified rate is low.And this
The imitative lotus baluster column that covers of invention is made of cement building stones mixture, wide material sources, is made simply, cost is cheap, is made and met with this
Contemporary environmental protection, energy-conservation, efficient policy, there is the ancient rhythm of traditional object.
It should be noted that embodiment is only the explanation and illustration to technical solution of the present invention, should not be by it
The restriction to technical solution of the present invention is interpreted as, it is any only to make what is locally changed using the substantive content of the invention of the present invention, should
Fall within the scope of protection of the present invention.
Claims (10)
- A kind of 1. imitative manufacture craft for covering lotus baluster column in ancient building, it is characterised in that：The imitative manufacture craft for covering lotus baluster column Comprise the following steps：(1) to cover the true part of lotus baluster column as model in ancient building, with gypsum with 1：1 ratio, which makes to imitate, covers lotus baluster column parent part；(2) do kind of a mould with the imitative lotus baluster column parent part that covers, make can accommodate imitate cover lotus baluster column parent part be unlikely to deform and two panels folding Outer mold；(3) outer mold is placed on the plane, imitative will covers lotus baluster column parent part and flat down and be placed among outer mold, covered lotus imitative and hope Covered on post parent part with silica gel and silica gel fills up the inner space of outer mold to level, removing outer mold after silica gel solidification is made Mould in silica gel, by the dimidiation placed in the middle of mould in silica gel, take out to imitate and cover lotus baluster column parent part；(4) iron oxide pigment uniform mixing is added close to the true part color of lotus baluster column is covered with cement, add stone dry powder, water and subtract Aqua is well mixed, and cement building stones are made；(5) outer mold is inverted in the plane, the concave surface that flats down of mould in silica gel is placed in outer mold upward, with mixing Cement building stones fill in silica gel forming and hardening in mould；(6) the imitative lotus baluster column semi-finished product that cover in silica gel in mould are taken out to be conserved；(7) by conserved it is imitative cover lotus baluster column semi-finished product carry out sandblasting make its outer surface coarse, place drying；(8) the imitative outer surface for covering lotus baluster column semi-finished product is carried out doing old processing with hairbrush；(9) do after old processing it is imitative cover to spray stone protectant on lotus baluster column semi-finished product and be made imitative cover lotus baluster column finished product.
- 2. the imitative manufacture craft for covering lotus baluster column in a kind of ancient building according to claim 1, it is characterised in that：The step Suddenly mould thinnest part thickness is 1-3 centimetres in silica gel in (3).
- 3. the imitative manufacture craft for covering lotus baluster column in a kind of ancient building according to claim 2, it is characterised in that：The step Suddenly mould thinnest part thickness is 1 centimetre in silica gel in (3).
- 4. the imitative manufacture craft for covering lotus baluster column in a kind of ancient building according to claim 1, it is characterised in that：The step Suddenly iron oxide pigment weight is the 0.1-0.3% of cement weight in (4), and stone dry powder weight is 2-3 times of cement, the weight of water For the 30-50% of cement weight, the weight of water reducer is the 5% of cement weight.
- 5. the imitative manufacture craft for covering lotus baluster column in a kind of ancient building according to claim 4, it is characterised in that：The step Suddenly iron oxide pigment weight is the 0.2% of cement weight in (4), and stone dry powder weight is 2 times of cement, and the weight of water is cement The 40% of weight, the weight of water reducer are the 5% of cement weight.
- 6. the imitative manufacture craft for covering lotus baluster column in a kind of ancient building according to claim 1, it is characterised in that：The step Suddenly the particle diameter of stone dry powder is 10-120 mesh in (4).
- 7. the imitative manufacture craft for covering lotus baluster column in a kind of ancient building according to claim 6, it is characterised in that：The step Suddenly the particle diameter of stone dry powder is 60-100 mesh in (4).
- 8. the imitative manufacture craft for covering lotus baluster column in a kind of ancient building according to claim 1, it is characterised in that：The step Suddenly the imitative lotus baluster column that covers conserve the fully hardened time as 7 days in (6).
- 9. the imitative manufacture craft for covering lotus baluster column in a kind of ancient building according to claim 1, it is characterised in that：The step Suddenly imitate that to cover the time that lotus baluster column is dried be 2 days in (7).
- 10. imitative the imitative of manufacture craft making for covering lotus baluster column in a kind of a kind of ancient building according to claim 1 covers lotus Baluster column, it is characterised in that：The imitative lotus baluster column cement that covers adds iron oxide pigment uniform mixing close to covering the true part face of lotus baluster column Color, adds stone dry powder, water and water reducer are well mixed is made, and its outer surface is roughened, does old processing, and is sprayed with stone material Protective agent, iron oxide pigment weight are the 0.1-0.3% of cement weight, and stone dry powder weight is 2-3 times of cement, the weight of water For the 30-50% of cement weight, the weight of water reducer is the 5% of cement weight, and the particle diameter of stone dry powder is 10-120 mesh.