CN107471421A - A kind of three color Inorganic artificial stones and its manufacture method - Google Patents
A kind of three color Inorganic artificial stones and its manufacture method Download PDFInfo
- Publication number
- CN107471421A CN107471421A CN201710811538.4A CN201710811538A CN107471421A CN 107471421 A CN107471421 A CN 107471421A CN 201710811538 A CN201710811538 A CN 201710811538A CN 107471421 A CN107471421 A CN 107471421A
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic
- colors
- manufacture method
- artificial stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of three color Inorganic artificial stones and its manufacture method, the component of the three colors Inorganic artificial stone and the mass fraction of component are as follows：White portland cement：15 25 parts；The quartz sand of 16 26 mesh：15 30 parts；The quartz sand of 26 50 mesh：10 20 parts；The quartz sand of 40 120 mesh：10 30 parts；High-performance water reducing agent：57 parts；Water：58 parts；901 glue：8 15 parts；Inorganic pigment：12 parts.The three color Inorganic artificial stones and its manufacture method of the present invention; organic material is substituted with inorganic material; the problem of not only solving environmental protection; the pattern of artificial stone produced can also be made no longer dull; there is depth to have shallow; and three kinds of colors have the effect to interpenetrate, can also produce the Inorganic artificial stone close to natural stone pattern.
Description
Technical field
The present invention relates to artificial stone field, is specially a kind of three color Inorganic artificial stones and its manufacture method.
Background technology
Artificial stone is that one kind passes through vacuum casting or compression molding by natural ore powder, high performance resin and natural pigment
Mineral-filled polymer composite, can be widely applied to public building and house decoration field, be one kind without radiation
Contact scar, the repeatable environmental protection utilized, green novel building house decorative material.Artificial stone uses binding agent according to itself
Difference, inorganic type artificial stone and the major class of resin type artificial stone two can be divided into.Wherein resin type artificial stone can be a large amount of with its
Use and bring environmental protection problem, and the major defect of the artificial stone of inorganic type be the product of camber stone material and moulding class all
It can not process, what it is available for moulding production is that ordinary cement adds glass fibre, and its outward appearance is concrete grey true qualities, regardless of moulding
Application all, which must be carried out, to its surface can just produce Inorganic artificial stone more attractive in appearance.
The content of the invention
In order to overcome above mentioned problem, the present invention provides a kind of three color Inorganic artificial stones and its manufacture method, by specific
Dispensing suppresses the manufacture method of pattern with three kinds of colors simultaneously, substitutes organic material with inorganic material, the artificial stone produced
Pattern is no longer dull, has depth to have shallow, three kinds of colors have the effect to interpenetrate, can also produce close to the inorganic of natural stone pattern
Artificial stone.
The technical solution adopted by the present invention is：A kind of three color Inorganic artificial stones, the group of the three colors Inorganic artificial stone are provided
Divide and the mass fraction of component is as follows：White portland cement：15-25 parts；The quartz sand of 16-26 mesh：15-30 parts；26-50 mesh
Quartz sand：10-20 parts；The quartz sand of 40-120 mesh：10-30 parts；High-performance water reducing agent：5-7 parts；Water：5-8 parts；901 glue：
8-15 parts；Inorganic pigment：1-2 parts.
Present invention also offers a kind of manufacture method of three colors Inorganic artificial stone, methods described includes step：
S1, all components are weighed into 3 agitator tanks according to percentage by weight respectively, by stirring the feed opening of pot bottom thing
Material is delivered on conveyer belt；
After S2, the material transmission to pair roller, it is resent to agitator disk and is stirred；
Material after S3, stirring carries out cloth as conveyer belt continues to be sent to distribution device and expects mould；
S4, the mould after cloth is delivered to vacuum press progress thin plate compacting, deliver to maintenance area after the material forming and supported
Shield, finally carry out water mill polishing.
Further, the constituent content of 3 agitator tanks is 1 in the ground step 1：2：3, and the group of 3 agitator tanks
Inorganic pigment in point is different color.
Further, using the rotating speed control blanking velocity of agitating paddle in the step S1, the rotating speed is 0-80rpm.
Further, in the step S2, the time of agitator disk stirring is the 30-60 seconds.
Further, the distribution device in the step S3 is wolf's fang shape distribution device.
Further, the maintenance area in the step S4 is that normal temperature conserves area, and curing time is 7 days.
Compared with prior art, three color Inorganic artificial stones and its manufacture method of the invention, substituted with inorganic material organic
Material, the problem of not only solving environmental protection, moreover it is possible to make the pattern of artificial stone produced no longer dull, have it is deep have it is shallow, and
Three kinds of colors have the effect to interpenetrate, can also produce the Inorganic artificial stone close to natural stone pattern.
The manufacturing process of the present invention is simple, and production efficiency is high, seldom produces waste material, waste water, and three colors that it is produced are inorganic
The physical and chemical performances such as the abrasion-proof corrosion-proof of artificial stone, resistance to compression, anti-folding, finish are reached natural granite level.
Compared with existing organic artificial's stone and natural stone, the service life of the three colors Inorganic artificial stone is longer, uses model
Enclose also wider.
Embodiment
For the ease of the understanding of those skilled in the art, the present invention provides technical side of the specific examples below to the present invention
Case is described in further detail.
Embodiment 1
The present invention provides a kind of three color Inorganic artificial stones, and the component of the three colors Inorganic artificial stone and the mass fraction of component are such as
Under：White portland cement：15 parts；The quartz sand of 16-26 mesh：15 parts；The quartz sand of 26-50 mesh：10 parts；The stone of 40-120 mesh
Sand：10 parts；High-performance water reducing agent：5 parts；Water：6 parts；901 glue：8 parts；Inorganic pigment：1 part.
The present invention also provides a kind of manufacture method of three colors Inorganic artificial stone, and methods described includes step：
S1, all components are weighed into 3 agitator tanks according to percentage by weight respectively, the constituent content of 3 agitator tanks 1 is 1：2：
3, and the color of the inorganic pigment in the component of 3 agitator tanks is navy blue, black and Dark grey, then passes through agitator tank
The feed opening of bottom, blanking velocity is controlled using the rotating speed of agitating paddle, material is delivered on conveyer belt, the rotating speed is 10rpm；
After S2, the material transmission to pair roller, it is resent to agitator disk and is stirred, the time of stirring is 30 seconds；
Material after S3, stirring carries out cloth as conveyer belt continues to be sent to distribution device and expects mould, and the distribution device is
Wolf's fang shape distribution device；
S4, the mould after cloth is delivered to vacuum press progress thin plate compacting, normal temperature maintenance area is delivered to after the material forming and is entered
The maintenance of 7 days behavior phases, finally carry out water mill polishing.
The three color Inorganic artificial stones and its manufacture method of the present invention, organic material is substituted with inorganic material, not only solved
The problem of environmental protection, moreover it is possible to make the pattern of artificial stone produced no longer dull, have it is deep have it is shallow, and three kinds of colors have it is mutual
The effect of infiltration, it can also produce the Inorganic artificial stone close to natural stone pattern.
The manufacturing process of the present invention is simple, and production efficiency is high, seldom produces waste material, waste water, and three colors that it is produced are inorganic
The physical and chemical performances such as the abrasion-proof corrosion-proof of artificial stone, resistance to compression, anti-folding, finish are reached natural granite level.
Embodiment 2
The present invention provides a kind of three color Inorganic artificial stones, and the component of the three colors Inorganic artificial stone and the mass fraction of component are such as
Under：White portland cement：18 parts；The quartz sand of 16-26 mesh：30 parts；The quartz sand of 26-50 mesh：20 parts；40-120 purposes
Quartz sand：30 parts；High-performance water reducing agent：5 parts；Water：6.5 part；901 glue：10 parts；Inorganic pigment：2 parts.
The present invention also provides a kind of manufacture method of three colors Inorganic artificial stone, and methods described includes step：
S1, all components are weighed into 3 agitator tanks according to percentage by weight respectively, the constituent content of 3 agitator tanks 1 is 1：2：
3, and the color of the inorganic pigment in the component of 3 agitator tanks is light yellow, white and light brown, then passes through agitator tank
The feed opening of bottom, blanking velocity is controlled using the rotating speed of agitating paddle, material is delivered on conveyer belt, the rotating speed is 80rpm；
After S2, the material transmission to pair roller, it is resent to agitator disk and is stirred, the time of stirring is 60 seconds；
Material after S3, stirring carries out cloth as conveyer belt continues to be sent to distribution device and expects mould, and the distribution device is
Wolf's fang shape distribution device；
S4, the mould after cloth is delivered to vacuum press progress thin plate compacting, normal temperature maintenance area is delivered to after the material forming and is entered
The maintenance of 7 days behavior phases, finally carry out water mill polishing.
The three color Inorganic artificial stones and its manufacture method of the present invention, organic material is substituted with inorganic material, not only solved
The problem of environmental protection, moreover it is possible to make the pattern of artificial stone produced no longer dull, have it is deep have it is shallow, and three kinds of colors have it is mutual
The effect of infiltration, it can also produce the Inorganic artificial stone close to natural stone pattern.
The manufacturing process of the present invention is simple, and production efficiency is high, seldom produces waste material, waste water, and three colors that it is produced are inorganic
The physical and chemical performances such as the abrasion-proof corrosion-proof of artificial stone, resistance to compression, anti-folding, finish are reached natural granite level.
Embodiment 3
The present invention provides a kind of three color Inorganic artificial stones, and the component of the three colors Inorganic artificial stone and the mass fraction of component are such as
Under：White portland cement：19 parts；The quartz sand of 16-26 mesh：22.5 parts；The quartz sand of 26-50 mesh：15 parts；40-120 purposes
Quartz sand：15 parts；High-performance water reducing agent：5.5 part；Water：7.5 part；901 glue：11.5 parts；Inorganic pigment：1.5 part.
The present invention also provides a kind of manufacture method of three colors Inorganic artificial stone, and methods described includes step：
S1, all components are weighed into 3 agitator tanks according to percentage by weight respectively, the constituent content of 3 agitator tanks 1 is 1：2：
3, and the color of the inorganic pigment in the component of 3 agitator tanks is light blue, white and grey, then passes through agitator tank bottom
The feed opening in portion, blanking velocity is controlled using the rotating speed of agitating paddle, material is delivered on conveyer belt, the rotating speed is 40rpm；
After S2, the material transmission to pair roller, it is resent to agitator disk and is stirred, the time of stirring is 45 seconds；
Material after S3, stirring carries out cloth as conveyer belt continues to be sent to distribution device and expects mould, and the distribution device is
Wolf's fang shape distribution device；
S4, the mould after cloth is delivered to vacuum press progress thin plate compacting, normal temperature maintenance area is delivered to after the material forming and is entered
The maintenance of 7 days behavior phases, finally carry out water mill polishing.
The three color Inorganic artificial stones and its manufacture method of the present invention, organic material is substituted with inorganic material, not only solved
The problem of environmental protection, moreover it is possible to make the pattern of artificial stone produced no longer dull, have it is deep have it is shallow, and three kinds of colors have it is mutual
The effect of infiltration, it can also produce the Inorganic artificial stone close to natural stone pattern.
The manufacturing process of the present invention is simple, and production efficiency is high, seldom produces waste material, waste water, and three colors that it is produced are inorganic
The physical and chemical performances such as the abrasion-proof corrosion-proof of artificial stone, resistance to compression, anti-folding, finish are reached natural granite level.
Embodiment 4
The present invention provides a kind of three color Inorganic artificial stones, and the component of the three colors Inorganic artificial stone and the mass fraction of component are such as
Under：White portland cement：17.5 parts；The quartz sand of 16-26 mesh：18.75 parts；The quartz sand of 26-50 mesh：12.5 parts；40-
The quartz sand of 120 mesh：12.5 parts；High-performance water reducing agent：6 parts；Water：6.5 part；901 glue：11.8 parts；Inorganic pigment：1.25 part.
The present invention also provides a kind of manufacture method of three colors Inorganic artificial stone, and methods described includes step：
S1, all components are weighed into 3 agitator tanks according to percentage by weight respectively, the constituent content of 3 agitator tanks 1 is 1：2：
3, and the color of the inorganic pigment in the component of 3 agitator tanks is black, gold and Dark grey, then passes through agitator tank bottom
The feed opening in portion, blanking velocity is controlled using the rotating speed of agitating paddle, material is delivered on conveyer belt, the rotating speed is 20rpm；
After S2, the material transmission to pair roller, it is resent to agitator disk and is stirred, the time of stirring is 38 seconds；
Material after S3, stirring carries out cloth as conveyer belt continues to be sent to distribution device and expects mould, and the distribution device is
Wolf's fang shape distribution device；
S4, the mould after cloth is delivered to vacuum press progress thin plate compacting, normal temperature maintenance area is delivered to after the material forming and is entered
The maintenance of 7 days behavior phases, finally carry out water mill polishing.
The three color Inorganic artificial stones and its manufacture method of the present invention, organic material is substituted with inorganic material, not only solved
The problem of environmental protection, moreover it is possible to make the pattern of artificial stone produced no longer dull, have it is deep have it is shallow, and three kinds of colors have it is mutual
The effect of infiltration, it can also produce the Inorganic artificial stone close to natural stone pattern.
The manufacturing process of the present invention is simple, and production efficiency is high, seldom produces waste material, waste water, and three colors that it is produced are inorganic
The physical and chemical performances such as the abrasion-proof corrosion-proof of artificial stone, resistance to compression, anti-folding, finish are reached natural granite level.
Embodiment 5
The present invention provides a kind of three color Inorganic artificial stones, and the component of the three colors Inorganic artificial stone and the mass fraction of component are such as
Under：White portland cement：20.5 parts；The quartz sand of 16-26 mesh：26.25 parts；The quartz sand of 26-50 mesh：17.5 parts；40-
The quartz sand of 120 mesh：22.5 parts；High-performance water reducing agent：6.5 part；Water：8.75 part；901 glue：14.25 parts；Inorganic pigment：1.85
Part.
The present invention also provides a kind of manufacture method of three colors Inorganic artificial stone, and methods described includes step：
S1, all components are weighed into 3 agitator tanks according to percentage by weight respectively, the constituent content of 3 agitator tanks 1 is 1：2：
3, and the color of the inorganic pigment in the component of 3 agitator tanks is light yellow, bronzing and canescence, then passes through stirring
The feed opening of pot bottom, blanking velocity is controlled using the rotating speed of agitating paddle, material is delivered on conveyer belt, the rotating speed is
60rpm；
After S2, the material transmission to pair roller, it is resent to agitator disk and is stirred, the time of stirring is 53 seconds；
Material after S3, stirring carries out cloth as conveyer belt continues to be sent to distribution device and expects mould, and the distribution device is
Wolf's fang shape distribution device；
S4, the mould after cloth is delivered to vacuum press progress thin plate compacting, normal temperature maintenance area is delivered to after the material forming and is entered
The maintenance of 7 days behavior phases, finally carry out water mill polishing.
The three color Inorganic artificial stones and its manufacture method of the present invention, organic material is substituted with inorganic material, not only solved
The problem of environmental protection, moreover it is possible to make the pattern of artificial stone produced no longer dull, have it is deep have it is shallow, and three kinds of colors have it is mutual
The effect of infiltration, it can also produce the Inorganic artificial stone close to natural stone pattern.
The manufacturing process of the present invention is simple, and production efficiency is high, seldom produces waste material, waste water, and three colors that it is produced are inorganic
The physical and chemical performances such as the abrasion-proof corrosion-proof of artificial stone, resistance to compression, anti-folding, finish are reached natural granite level.
Above-described embodiment 1-5 is the preferable implementation of the present invention, is not limited to the present invention, and is not departing from this
It is any obviously to replace within protection scope of the present invention on the premise of the inventive concept of invention.
Claims (7)
- A kind of 1. three color Inorganic artificial stones, it is characterised in that：The component of the three colors Inorganic artificial stone and the mass fraction of component It is as follows：White portland cement：15-25 parts；The quartz sand of 16-26 mesh：15-30 parts；The quartz sand of 26-50 mesh：10-20 parts； The quartz sand of 40-120 mesh：10-30 parts；High-performance water reducing agent：5-7 parts；Water：5-8 parts；901 glue：8-15 parts；Inorganic pigment：1- 2 parts.
- 2. the manufacture method of three colors Inorganic artificial stone according to claim 1, it is characterised in that：Methods described includes step Suddenly：S1, all components are weighed into 3 agitator tanks according to percentage by weight respectively, by stirring the feed opening of pot bottom thing Material is delivered on conveyer belt；After S2, the material transmission to pair roller, it is resent to agitator disk and is stirred；Material after S3, stirring carries out cloth as conveyer belt continues to be sent to distribution device and expects mould；S4, the mould after cloth is delivered to vacuum press progress thin plate compacting, deliver to maintenance area after the material forming and supported Shield, finally carry out water mill polishing.
- 3. the manufacture method of three colors Inorganic artificial stone according to claim 2, it is characterised in that：3 are stirred in the step 1 The constituent content for mixing tank is 1：2：3.
- 4. the manufacture method of three colors Inorganic artificial stone according to claim 3, it is characterised in that：Utilized in the step S1 The rotating speed control blanking velocity of agitating paddle, the rotating speed is 0-80rpm.
- 5. the manufacture method of three colors Inorganic artificial stone according to claim 4, it is characterised in that：In the step S2, stir The time for mixing disk stirring is the 30-60 seconds.
- 6. the manufacture method of three colors Inorganic artificial stone according to claim 5, it is characterised in that：Cloth in the step S3 Material device is wolf's fang shape distribution device.
- 7. according to the manufacture method of three color Inorganic artificial stones described in claim any one of 2-6, it is characterised in that：The step Maintenance area in rapid S4 conserves area for normal temperature, and curing time is 7 days.