CN104446145A - Double-color double-pattern artificial quartz stone plate and production process thereof - Google Patents

Double-color double-pattern artificial quartz stone plate and production process thereof Download PDF

Info

Publication number
CN104446145A
CN104446145A CN201410673899.3A CN201410673899A CN104446145A CN 104446145 A CN104446145 A CN 104446145A CN 201410673899 A CN201410673899 A CN 201410673899A CN 104446145 A CN104446145 A CN 104446145A
Authority
CN
China
Prior art keywords
look
double
colored
stone plate
decorative pattern
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410673899.3A
Other languages
Chinese (zh)
Inventor
周军
胡国强
张韡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG BANNER NEW MATERIAL TECHNOLOGY Co Ltd
Original Assignee
GUANGDONG BANNER NEW MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG BANNER NEW MATERIAL TECHNOLOGY Co Ltd filed Critical GUANGDONG BANNER NEW MATERIAL TECHNOLOGY Co Ltd
Priority to CN201410673899.3A priority Critical patent/CN104446145A/en
Publication of CN104446145A publication Critical patent/CN104446145A/en
Pending legal-status Critical Current

Abstract

The invention discloses a double-color double-pattern artificial quartz stone plate which comprises a main material color A, an auxiliary material color B, a pattern material color C and a pattern material color D, wherein the main material color A and the auxiliary material color B both comprise granular raw materials of 0.075-5 mm, quartz powder of 0.005-0.063 mm, colored pigment, a silane coupling agent, unsaturated polyester resin and a curing agent; the pattern material color C and the pattern material color D both comprise quartz granular raw materials of 0.075-0.5 mm, quartz powder of 0.005-0.063 mm, colored pigment and a silane coupling agent, wherein the granular raw materials are quartz granules, glass granules or a mixture of the two granules. The double-color double-pattern artificial quartz stone plate is high in production efficiency, the reject ratio of the product is effectively reduced, the colors can be separated from one another, and large-scale production can be achieved.

Description

A kind of double-colored honeysuckle line artificial quartz stone plate and production technique thereof
Technical field
The present invention relates to a kind of artificial quartz stone plate, specifically, relate to a kind of double-colored honeysuckle line artificial quartz stone plate and production technique thereof.
Background technology
Artificial quartz in lump is main stuffing by quartz sand powder, using unsaturated polyester resin as tackiness agent, the Novel stone formalized vibrate press forming, middle temperature state under vacuum condition under, it is a kind of no radioactivity pollute, the environmental protection that can reuse, green building material and finishing material.
At first, quartzite is only applied on the higher cabinet table surface of effects on surface requirement, furniture table-board, laboratory operation platform.Along with Economic development and market are ripe further, the every field such as domestic and international more ground, metope, furniture bring into use quartzite, such as various large hotel, mansion, landmark, and quartzite just progressively becomes the substitute products of lithotome.
Conventional quartz stone product is at first based on monochrome, and along with the development in market, plain quarz stone can not meet the esthetic requirement of the continuous renewal in market, the secondary color plate of nearly 2 years existing imitated natural granites and diamond plate, but color is relatively stiff, and texture is nature not.Meanwhile, secondary color and pattern type quartzite slate are due to complex process, and production efficiency is low, and sheet material color in pressing process easily interpenetrates, and fraction defective is high, thus cause the supply of material few, and price is high.
Therefore be necessary to carry out upgrading or technological transformation to existing production technique.
Summary of the invention
Instant invention overcomes shortcoming of the prior art, provide a kind of one double-colored honeysuckle line artificial quartz stone plate and the production technique thereof with natural stone texture and rich colors, good product performance, production efficiency is high, and qualification rate is high.
In order to solve the problems of the technologies described above, the present invention is achieved by the following technical solutions:
A kind of double-colored honeysuckle line artificial quartz stone plate, comprises major ingredient A look, auxiliary material B look, decorative pattern material C look and decorative pattern material D look,
The raw material of described major ingredient A look and auxiliary material B look includes 0.075 ~ 5mm particulate material, 0.005 ~ 0.063mm silica powder; Colored pigment; Silane coupling agent; Unsaturated polyester resin and solidifying agent;
The raw material of described decorative pattern material C look and decorative pattern material D look includes: 0.075 ~ 0.5mm quartz particles, 0.005 ~ 0.063mm silica powder, colored pigment and silane coupling agent;
Wherein, particulate material is quartz particles or glass particle, or the mixture of two kinds.
Further, by total amount 100 parts, described major ingredient A look is 58-80 part, auxiliary material B look is 18-40 part, and decorative pattern material C look is 0.1-1 part, and decorative pattern material D look is 0.1-1 part.
Further, component and the proportioning of described major ingredient A look and auxiliary material B look are: according to weight percent, 0.075 ~ 5mm particulate material 55% ~ 65%, 0.005 ~ 0.063mm silica powder 20%-30%; Colored pigment 0.01%-10%; Silane coupling agent 0.1%-1%; Unsaturated polyester resin 8%-12%; Solidifying agent 0.8%-1.2%.
Further, according to weight percent, component and the proportioning of described decorative pattern material C look and decorative pattern material D look are: 0.075 ~ 0.5mm quartz particles 75% ~ 90%, 0.005 ~ 0.063mm silica powder 5%-20%; Colored pigment 0.01%-15%; Silane coupling agent 0.1%-1%.
Further, described colored pigment is one or more of mineral dye or pigment dyestuff.
Further, described mineral dye is titanium white, medium chrome yellow medium yellow, iron oxide yellow, iron oxide red or red lead.
Further, described pigment dyestuff is red, phthalein viridescent or phthalocyanine blue.
Further, described solidifying agent is one or more in peroxidation (2 ethyl hexanoic acid) tert-butyl ester, methylethyl ketone peroxide, peroxidized t-butyl perbenzoate, dibenzoyl peroxide and fat polyamine.
Further, described silane coupling agent is one or more in γ-methacryloxypropyl trimethoxy silane, γ-(2,3-epoxy third oxygen) propyl trimethoxy silicane, N-β (aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane, N-(β-aminoethyl)-γ-aminopropyl triethoxysilane, N-β (aminoethyl)-γ-aminopropyltrimethoxysilane, anilinomethyl triethoxysilane, γ-aminopropyl triethoxysilane, vinyltriethoxysilane, vinyltrimethoxy silane and γ-chloropropyl triethoxysilane.
A production technique for double-colored honeysuckle line artificial quartz stone plate, comprises the following steps:
(1) each material each component is taken according to formula;
(2) stir:
The quartz particles of the major ingredient A look 1. step 1 taken, glass particle, silane coupling agent, the pre-mixing in No. 1 double planetary agitation vat of 0.005 ~ 0.063mm silica powder; The unsaturated polyester resin being mixed with solidifying agent and colored pigment is reentered in No. 1 double planetary agitation vat and mix, stirring frequency 15-55Hz, churning time 180-600s;
2. mixed accessories B colorant in No. 2 double planetary agitation vats, stirring operation technique is identical with mixing A colorant;
3. decorative pattern material C colorant, decorative pattern material D colorant batch mixing is even;
4. put into by the B colorant be stirred and stirred in A colorant, low frequency is uniformly mixed, and forms AB colorant, stirring frequency 10-25Hz, churning time 5-60S;
5. spread by color patterned for C material in the AB colorant mixed, low frequency is uniformly mixed; Sprinkled by color patterned for D material, low frequency is uniformly mixed again, and obtains final compound, stirring frequency 5-15Hz, churning time 5-60S;
(3) cloth: batch mixing is sent in charge car by distributing belt, then by charge car batch mixing is evenly arranged framed with cloth in;
(4) suppress: after cloth completes, repressed vibration equipment compression moulding under the vacuum condition of-0.1Mpa, pressure 50-100t, vibrational frequency 30-55Hz, time 180-600s;
(5) thermofixation: after vibration compacting, enter curing apparatus, solidify at the temperature of 80-120 DEG C, set time is for being 60 ~ 90 minutes;
(6) after having solidified, normal temperature place to be cooled completely after to enter sheet material thicknessing machine fixed thick, then carry out polishing through 20 water mill polissoirs.
Compared with prior art, the invention has the beneficial effects as follows:
One of the present invention double-colored honeysuckle line artificial quartz stone plate and production technique thereof, production efficiency is high, and effectively reduce the fraction defective of product, color is separated from each other simultaneously, can mass production.
Embodiment
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
Embodiment 1:
A kind of double-colored honeysuckle line artificial quartz stone plate described in the present embodiment, comprises major ingredient A look, auxiliary material B look, decorative pattern material C look and decorative pattern material D look,
By total amount 100 parts, major ingredient A look is 75 parts, auxiliary material B look is 24 parts, and decorative pattern material C look is 0.5 part, and decorative pattern material D look is 0.5 part.
Component and the proportioning of major ingredient A look and auxiliary material B look are: according to weight percent, 0.075 ~ 5mm particulate material 60%, 0.005 ~ 0.063mm silica powder 25%; Colored pigment 5%; Silane coupling agent 0.5%; Unsaturated polyester resin 8.5%; Solidifying agent 1%.
Particulate material can be quartz particles or glass particle, or the mixture of two kinds.
Further, according to weight percent, component and the proportioning of decorative pattern material C look and decorative pattern material D look are: 0.075 ~ 0.5mm quartz particles 80%, 0.005 ~ 0.063mm silica powder 15%; Colored pigment 4.5%; Silane coupling agent 0.5%.
Colored pigment is mineral dye, and mineral dye is titanium white.
Solidifying agent is peroxidation (2 ethyl hexanoic acid) tert-butyl ester and methylethyl ketone peroxide.
Silane coupling agent is γ-methacryloxypropyl trimethoxy silane and γ-(2,3-epoxy third oxygen) propyl trimethoxy silicane.
A production technique for double-colored honeysuckle line artificial quartz stone plate, comprises the following steps:
(1) each material each component is taken according to formula;
(2) stir:
The quartz particles of the major ingredient A look 1. step 1 taken, glass particle, silane coupling agent, the pre-mixing in No. 1 double planetary agitation vat of 0.005 ~ 0.063mm silica powder; The unsaturated polyester resin being mixed with solidifying agent and colored pigment is reentered in No. 1 double planetary agitation vat and mix, stirring frequency 15-55Hz, churning time 180-600s;
2. mixed accessories B colorant in No. 2 double planetary agitation vats, stirring operation technique is identical with mixing A colorant;
3. decorative pattern material C colorant, decorative pattern material D colorant batch mixing is even;
4. put into by the B colorant be stirred and stirred in A colorant, low frequency is uniformly mixed, and forms AB colorant, stirring frequency 10-25Hz, churning time 5-60S;
5. spread by color patterned for C material in the AB colorant mixed, low frequency is uniformly mixed; Sprinkled by color patterned for D material, low frequency is uniformly mixed again, and obtains final compound, stirring frequency 5-15Hz, churning time 5-60S;
(3) cloth: batch mixing is sent in charge car by distributing belt, then by charge car batch mixing is evenly arranged framed with cloth in;
(4) suppress: after cloth completes, repressed vibration equipment compression moulding under the vacuum condition of-0.1Mpa, pressure 50-100t, vibrational frequency 30-55Hz, time 180-600s;
(5) thermofixation: after vibration compacting, enter curing apparatus, solidify at the temperature of 80-120 DEG C, set time is for being 60 ~ 90 minutes;
(6) after having solidified, normal temperature place to be cooled completely after to enter sheet material thicknessing machine fixed thick, then carry out polishing through 20 water mill polissoirs.
Embodiment 2:
A kind of double-colored honeysuckle line artificial quartz stone plate described in the present embodiment, comprise major ingredient A look, auxiliary material B look, decorative pattern material C look and decorative pattern material D look, by total amount 100 parts, major ingredient A look is 58-80 part, auxiliary material B look is 18-40 part, decorative pattern material C look is 0.2 part, and decorative pattern material D look is 0.8 part.
The raw material of major ingredient A look and auxiliary material B look includes 0.075 ~ 5mm particulate material, 0.005 ~ 0.063mm silica powder; Colored pigment; Silane coupling agent; Unsaturated polyester resin and solidifying agent;
The raw material of decorative pattern material C look and decorative pattern material D look includes: 0.075 ~ 0.5mm quartz particles, 0.005 ~ 0.063mm silica powder, colored pigment and silane coupling agent;
Particulate material can be quartz particles or glass particle, or the mixture of two kinds.
Component and the proportioning of major ingredient A look and auxiliary material B look are: according to weight percent, 0.075 ~ 5mm particulate material 58%, 0.005 ~ 0.063mm silica powder 28%; Colored pigment 2.8%; Silane coupling agent 0.3%; Unsaturated polyester resin 10%; Solidifying agent 0.9%.
Further, according to weight percent, component and the proportioning of described decorative pattern material C look and decorative pattern material D look are: 0.075 ~ 0.5mm quartz particles 85%, 0.005 ~ 0.063mm silica powder 7%; Colored pigment 7.2%; Silane coupling agent 0.8%.
Colored pigment is pigment dyestuff, selects phthalein dark green.
Solidifying agent is peroxidized t-butyl perbenzoate, dibenzoyl peroxide and fat polyamine.
Silane coupling agent is vinyltriethoxysilane.
Last it is noted that these are only the preferred embodiments of the present invention; be not limited to the present invention; although with reference to embodiment to invention has been detailed description; for a person skilled in the art; it still can be modified to the technical scheme described in foregoing embodiments; or equivalent replacement is carried out to wherein portion of techniques feature; but it is within the spirit and principles in the present invention all; any amendment of doing, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.

Claims (10)

1. a double-colored honeysuckle line artificial quartz stone plate, is characterized in that: comprise major ingredient A look, auxiliary material B look, decorative pattern material C look and decorative pattern material D look,
The raw material of described major ingredient A look and auxiliary material B look includes 0.075 ~ 5mm particulate material, 0.005 ~ 0.063mm silica powder; Colored pigment; Silane coupling agent; Unsaturated polyester resin and solidifying agent;
The raw material of described decorative pattern material C look and decorative pattern material D look includes: 0.075 ~ 0.5mm quartz particles, 0.005 ~ 0.063mm silica powder, colored pigment and silane coupling agent;
Wherein, particulate material is quartz particles or glass particle, or the mixture of two kinds.
2. a kind of double-colored honeysuckle line artificial quartz stone plate according to claim 1, it is characterized in that: by total amount 100 parts, described major ingredient A look is 58-80 part, auxiliary material B look is 18-40 part, decorative pattern material C look is 0.1-1 part, and decorative pattern material D look is 0.1-1 part.
3. one according to claim 2 double-colored honeysuckle line artificial quartz stone plate, it is characterized in that: component and the proportioning of described major ingredient A look and auxiliary material B look are: according to weight percent, 0.075 ~ 5mm particulate material 55% ~ 65%, 0.005 ~ 0.063mm silica powder 20%-30%; Colored pigment 0.01%-10%; Silane coupling agent 0.1%-1%; Unsaturated polyester resin 8%-12%; Solidifying agent 0.8%-1.2%.
4. one according to claim 2 double-colored honeysuckle line artificial quartz stone plate, it is characterized in that: according to weight percent, component and the proportioning of described decorative pattern material C look and decorative pattern material D look are: 0.075 ~ 0.5mm quartz particles 75% ~ 90%, 0.005 ~ 0.063mm silica powder 5%-20%; Colored pigment 0.01%-15%; Silane coupling agent 0.1%-1%.
5. a kind of double-colored honeysuckle line artificial quartz stone plate according to claim 1, is characterized in that: described colored pigment is one or more of mineral dye or pigment dyestuff.
6. a kind of double-colored honeysuckle line artificial quartz stone plate according to claim 5, is characterized in that: described mineral dye is titanium white, medium chrome yellow medium yellow, iron oxide yellow, iron oxide red or red lead.
7. a kind of double-colored honeysuckle line artificial quartz stone plate according to claim 5, is characterized in that: described pigment dyestuff is red, the dark green or phthalocyanine blue of phthalein.
8. a kind of double-colored honeysuckle line artificial quartz stone plate according to claim 1, is characterized in that: described solidifying agent is one or more in peroxidation (2 ethyl hexanoic acid) tert-butyl ester, methylethyl ketone peroxide, peroxidized t-butyl perbenzoate, dibenzoyl peroxide and fat polyamine.
9. a kind of double-colored honeysuckle line artificial quartz stone plate according to claim 1, it is characterized in that: described silane coupling agent is γ-methacryloxypropyl trimethoxy silane, γ-(2, 3-epoxy third oxygen) propyl trimethoxy silicane, N-β (aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane, N-(β-aminoethyl)-γ-aminopropyl triethoxysilane, N-β (aminoethyl)-γ-aminopropyltrimethoxysilane, anilinomethyl triethoxysilane, γ-aminopropyl triethoxysilane, vinyltriethoxysilane, one or more in vinyltrimethoxy silane and γ-chloropropyl triethoxysilane.
10. the production technique of a kind of double-colored honeysuckle line artificial quartz stone plate according to claim 1, is characterized in that: comprise the following steps:
(1) each material each component is taken according to formula;
(2) stir:
The quartz particles of the major ingredient A look 1. step 1 taken, glass particle, silane coupling agent, the pre-mixing in No. 1 double planetary agitation vat of 0.005 ~ 0.063mm silica powder; The unsaturated polyester resin being mixed with solidifying agent and colored pigment is reentered in No. 1 double planetary agitation vat and mix, stirring frequency 15-55Hz, churning time 180-600s;
2. mixed accessories B colorant in No. 2 double planetary agitation vats, stirring operation technique is identical with mixing A colorant;
3. decorative pattern material C colorant, decorative pattern material D colorant batch mixing is even;
4. put into by the B colorant be stirred and stirred in A colorant, low frequency is uniformly mixed, and forms AB colorant, stirring frequency 10-25Hz, churning time 5-60S;
5. spread by color patterned for C material in the AB colorant mixed, low frequency is uniformly mixed; Sprinkled by color patterned for D material, low frequency is uniformly mixed again, and obtains final compound, stirring frequency 5-15Hz, churning time 5-60S;
(3) cloth: batch mixing is sent in charge car by distributing belt, then by charge car batch mixing is evenly arranged framed with cloth in;
(4) suppress: after cloth completes, repressed vibration equipment compression moulding under the vacuum condition of-0.1Mpa, pressure 50-100t, vibrational frequency 30-55Hz, time 180-600s;
(5) thermofixation: after vibration compacting, enter curing apparatus, solidify at the temperature of 80-120 DEG C, set time is for being 60 ~ 90 minutes;
(6) after having solidified, normal temperature place to be cooled completely after to enter sheet material thicknessing machine fixed thick, then carry out polishing through 20 water mill polissoirs.
CN201410673899.3A 2014-11-21 2014-11-21 Double-color double-pattern artificial quartz stone plate and production process thereof Pending CN104446145A (en)