CN101190550A - Artificialness sandstone product made by white cement - Google Patents
Artificialness sandstone product made by white cement Download PDFInfo
- Publication number
- CN101190550A CN101190550A CNA2006101297612A CN200610129761A CN101190550A CN 101190550 A CN101190550 A CN 101190550A CN A2006101297612 A CNA2006101297612 A CN A2006101297612A CN 200610129761 A CN200610129761 A CN 200610129761A CN 101190550 A CN101190550 A CN 101190550A
- Authority
- CN
- China
- Prior art keywords
- grams
- white
- product
- gram
- artificial sandstone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The main materials of an artificial sandstone product which is made of white cement are 108 glue, quartz sand and part of fine sand used in buildings. Because most of the artificial sandstone products are light yellow, the color adjustability of the white cement just adapts to the color of the artificial sandstone. The price of the artificial sandstone product made by the material is one third of that of the existing artificial sandstone product. The artificial sandstone product can be industrially produced, which is not only suitable for all kinds of high-grade hotels, bath center, real estate guilds, and clubs and homes but also has no odor and is a novel environment friendly product.
Description
Technical field:
The invention belongs to building and ornament materials, specially refer to a kind of artificial sandstone product of making of white cement.
Background technology:
In the various high-grade decorated articles at home, as in large-scale star hotel, the bath center, building guild hall etc. has located all design and installations artificial sandstone product of various styles, openwork carving is arranged, card-cut, there is the garden to carve, these have the artificial sandstone product of original creation artistic design theory, mostly having adopted with saturated polyester not is coagulating agent, quartz sand with various particles is the technical formula of main stuffing, this is that the shortcoming of the artificial sandstone product of coagulating agent is with saturated polyester not, because the rise in price of oil, this resin 30 percent the price that also risen, from original 8～9 yuan one kilogram, increase to present 12～13 1 kilograms, this has just strengthened the cost of making artificial sandstone product, make and original manyly want to adopt the construction unit of this way of art not using this material, closing mylar with insatiable hunger is that the artificial sandstone product of coagulating agent also has a shortcoming to be, because this resin has added styrene and has done diluted material, the smell of goods is difficult to hear, and environmental pollution is in various degree arranged when interior decoration.The present invention makes artificial sandstone product with No. 500 white portland cements, main material adopts 108 glue, quartz sand and part fine sand for building, because artificial sandstone product mostly is light yellow, and the color tunable positive adaptation of white cement the color of this artificial sandstone, artificial sandstone product with this material making, it is 1/3rd of existing artificial sandstone product price, can suitability for industrialized production, be suitable for various high-grade hotels, bath center, real estate guild hall, club, family and, belong to the new product of environment-friendly type without any smell.
Technology contents:
Main coagulated material of the present invention has been selected No. 500 silicate white cement for use, makees bond with 108 glue, and packing material is a 60-120 quartz sand, and part is watered brown color sand.We know that artificial sandstone product adopts insatiable hunger to close mylar as coagulated material, the batch mixing process is the mode of dry blend, it is not the humidity as the cement mortar of being mixed out, but it is very approximate with the batch mixing in the lathe emery wheel grinding tool manufacture process, the particle that is each quartz sand is stained with bond on every side, and it is wet not need too much bond that quartz sand particle is all done, and blendes together half-dried material with above material, pour in the various moulds of making artificial sandstone, can finish after the material sclerosis in 24 hours.
Specific embodiments:
It is as follows to fill a prescription: that at first prepares 1000 grams makes the dry blend of artificial sandstone product with white cement:
No. 500 white portland cements of fine sand 50 grams for building 300 grams
No. 60 200 grams of the white quartz sand of 108 building glue, 100 grams
White quartz sand 80-100 number 220 grams of light brown color matching quartz sand 50 grams
Brown mill base 5 grams of yellow mill base 10 grams
Early strength agent 5 gram water 50 grams
1. at first 100 gram 108 glue and 50 gram water, 5 gram early strength agent, the yellow slurry of 10 grams, the brown slurry allotment of 5 grams evenly, this is a kind of bond.
2. No. 60 crystobalite sand of 200 grams, 80～No. 100 quartz sands of 220 grams, 50 gram building fine sands are poured on and are mixed together evenly, pour the first kind of bond that is mixed then into, above material is dried to be mixed evenly, allows the surface of each quartz sand all soak into bond.
3. above two kinds of materials are mixed evenly that the back is mixed evenly once more pouring 300 gram white silicates into, make each quartz sand particle surface all be stained with white cement, and this batch mixing and to paste the block marble slab the same on ground now also is the dry mixing material mode of cement and sand.
4. after above material all is mixed evenly, pour in the mould of artificial sandstone product and firmly make real, after solidifying in 24 hours, throwing off die products promptly finishes, more than prescription is the sandstone product of making below 1 square metre, strengthen as size, add braiding iron net in the time of can in manufacturing process, pouring the mould half of materials into, make product increase structural capacity.If the client has requirement to the color of sandstone surface, in mixed ingredients, can add required mill base.
Claims (1)
1. artificial sandstone product of making of white cement is characterized in that:
It is as follows to fill a prescription: that at first prepares 1000 grams makes the dry blend of artificial sandstone product with white cement:
No. 500 white portland cements of fine sand 50 grams for building 300 grams
No. 60 200 grams of the white quartz sand of 108 building glue, 100 grams
White quartz sand 80-100 number 220 grams of light brown color matching quartz sand 50 grams
Brown mill base 5 grams of yellow mill base 10 grams
Early strength agent 5 gram water 50 grams
(1) at first 100 gram 108 glue and 50 gram water, 5 gram early strength agent, the yellow slurry of 10 grams, the brown slurry allotment of 5 grams evenly, this is a kind of bond.
(2) No. 60 crystobalite sand of 200 grams, 80～No. 100 quartz sands of 220 grams, 50 gram building fine sands are poured on and are mixed together evenly, pour the first kind of bond that is mixed then into, above material is dried to be mixed evenly, allows the surface of each quartz sand all soak into bond.
(3) above two kinds of materials are mixed evenly that the back is mixed evenly once more pouring 300 gram white silicates into, make each quartz sand particle surface all be stained with white cement, and this batch mixing and to paste the block marble slab the same on ground now also is the dry mixing material mode of cement and sand.
(4) after above material all is mixed evenly, pour in the mould of artificial sandstone product and firmly make real, after solidifying in 24 hours, throwing off die products promptly finishes, more than prescription is the sandstone product of making below 1 square metre, strengthen as size, add braiding iron net in the time of can in manufacturing process, pouring the mould half of materials into, make product increase structural capacity.If the client has requirement to the color of sandstone surface, in mixed ingredients, can add required mill base.