CN110028282A - The self-dense type terrazzo of terrazzo slurry and its curing molding - Google Patents

The self-dense type terrazzo of terrazzo slurry and its curing molding Download PDF

Info

Publication number
CN110028282A
CN110028282A CN201910317328.9A CN201910317328A CN110028282A CN 110028282 A CN110028282 A CN 110028282A CN 201910317328 A CN201910317328 A CN 201910317328A CN 110028282 A CN110028282 A CN 110028282A
Authority
CN
China
Prior art keywords
terrazzo
slurry
parts
cement
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910317328.9A
Other languages
Chinese (zh)
Inventor
刘辉
王海如
丁旺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuo Hun New Material Technology (shanghai) Co Ltd
Original Assignee
Zhuo Hun New Material Technology (shanghai) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhuo Hun New Material Technology (shanghai) Co Ltd filed Critical Zhuo Hun New Material Technology (shanghai) Co Ltd
Priority to CN201910317328.9A priority Critical patent/CN110028282A/en
Publication of CN110028282A publication Critical patent/CN110028282A/en
Pending legal-status Critical Current

Abstract

It include the component of following parts by weight the invention proposes a kind of terrazzo slurry and its self-dense type terrazzo of curing molding, slurry；30-80 parts of cement, 20-40 parts of 2-3mm color pebble, 30-60 parts of 3-5mm color pebble, 20-40 parts of 40-80 mesh quartz sand, 2-8 parts of hone sand；And melamine resin analog high efficiency water reducing agent, defoaming agent, the third cream and water.The mobility of terrazzo slurry of the invention is strong, and self-dense type is high, the direction discharge that the bubble in the slurry can be self-possessed opposite towards slurry.One-pass molding can be poured in grinding tool using slurry of the invention, the exterior decoration of moulding complexity can be made, the application field of terrazzo is widened, especially compensate for the blank in European Architecture field.

Description

The self-dense type terrazzo of terrazzo slurry and its curing molding
Technical field
The present invention relates to artificial stone field, the self-dense type water mill of a kind of terrazzo slurry and its curing molding is particularly related to Stone.
Background technique
1. terrazzo is widely used in ground, there is great market at home.Existing decorative kind terrazzo mainly uses resin Addition aggregate pours polishing and is formed.
2. being secondly applied to kitchen, the interior decorations such as toilet more.Resin pours type terrazzo, because of the uvioresistant of resin Line ability is poor, and outdoor poor for applicability, outdoor utility is substantially zeroed.
3. other existing terrazzo technique, which mostly uses, pours rear lash method raising terrazzo product compactness, and shakes and need A large amount of manpowers and working hour.
4. existing terrazzo technique can only make planar products, as some angled, the special-shaped product of curved surface then bad system Make.
5. will appear terrazzo stone aggregate deposit buildup phenomenon if using the abnormity components such as traditional handicraft production curved surface, out The problem of existing stone is all deposited on bottom, and top is then cement slurry entirely.
To sum up, cement base terrazzo is mainly applied and ground, for decoration of exterior wall using less, and complex model application base It originally is zero.
Summary of the invention
The present invention proposes the self-dense type terrazzo of a kind of terrazzo slurry and its curing molding, solves water in the prior art Mud base terrazzo applies the restricted problem on ground.
The technical scheme of the present invention is realized as follows:
A kind of terrazzo slurry, including, the component of following parts by weight；
30-80 parts of cement, 20-40 parts of 2-3mm color pebble, 30-60 parts of 3-5mm color pebble, 40-80 mesh quartz sand 20-40 parts, 2-8 parts of hone sand,
And melamine resin analog high efficiency water reducing agent, defoaming agent, the third cream and water；
Wherein the weight ratio of melamine resin analog high efficiency water reducing agent and cement amount is 0.2%-0.4%, defoaming agent and cement Weight ratio is 0.04%-0.06%, and the weight ratio of the third cream and cement is 3%-5%, and the weight ratio of water and cement is 15-26%.
The terrazzo slurry further includes additive as a preferred technical solution, and the additive is selected from plasticiser, delays Solidifying agent (such as summer temperature is properly added when higher can delay to solidify), (such as winter temperature is properly added when lower can for early strength agent To accelerate to solidify), the combination of one or more of antifreezing agent (such as winter temperature is properly added when lower can be with anti-freezing anti-cracking).
The terrazzo slurry further includes one or more of silicon ash, white carbon black, mountain flour as a preferred technical solution, Combination.
The terrazzo slurry further includes toner as a preferred technical solution,；The toner is titanium dioxide, iron oxide yellow The combination of one or more of powder, iron oxide black powder, iron oxide brown powder, ferric oxide red powder.
The cement is 52.5 white cement of A Erbo as a preferred technical solution,.
The quartz sand is the quartz sand of 99% silicon content or more as a preferred technical solution,.
The defoaming agent is western card defoaming agent as a preferred technical solution,.
Above-mentioned melamine resin analog high efficiency water reducing agent can make the appropriate adjustments according to weather, as can be appropriate in the higher situation of temperature Increase, winter temperature is suitably reduced when low.
It is a kind of by above-mentioned mold cured of terrazzo slurry self-dense type terrazzo after molding.
The mode of the curing molding is to pour as a preferred technical solution, described to pour without vibration.
Beneficial effect
(1) mobility of terrazzo slurry of the invention is strong, and self-dense type is high, and the bubble in the slurry can be towards slurry from heavy phase Anti- direction discharge.
(2) terrazzo formula of the present invention and manufacture craft can be unevenly distributed phenomenon to avoid terrazzo stone aggregate.
(3) one-pass molding can be poured in grinding tool using slurry of the invention, the outdoor dress of moulding complexity can be made Decorations, widen the application field of terrazzo, especially compensate for the blank in European Architecture field.
(4) finished product made of slurry of the invention, thickness can be adjusted arbitrarily, and minimum to accomplish 0.5cm, finished product is certainly Important place.And existing terrazzo all applies ground indoors, thickness is generally 5cm, and screed-coat is with a thickness of 3.5cm, surface layer 1.5cm。
(5) terrazzo of the invention can be mixed colours using toner, and the product of color multiplicity can be made.
(6) material of the invention is environmentally protective, low in cost, is convenient for factory scale production.
(7) formula water-cement ratio of the invention is 15-26%, so product strength obtained is higher.
Detailed description of the invention
It, below will be to embodiment in order to illustrate more clearly of embodiment of the present invention or technical solution in the prior art Or attached drawing needed to be used in the description of the prior art is briefly described, it should be apparent that, the accompanying drawings in the following description is only It is some embodiments of the invention, for those of ordinary skill in the art, in the premise of not making the creative labor property Under, it is also possible to obtain other drawings based on these drawings.
Fig. 1 is terrazzo product figure made from embodiment 1.
Fig. 2 is terrazzo grouting schematic diagram of the invention.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects It encloses.
The invention discloses the formulas of terrazzo slurry.Those skilled in the art can make according to formula disclosure Terrazzo is obtained, technical solution of the present invention can be achieved in following disclosed components.
The component and parts by weight that terrazzo slurry includes are as follows:
30-80 parts of cement, 20-40 parts of 2-3mm color pebble, 30-60 parts of 3-5mm color pebble, 40-80 mesh quartz sand 20-40 parts, 2-8 parts of hone sand,
And melamine resin analog high efficiency water reducing agent, defoaming agent, the third cream and water；
Wherein the weight ratio of melamine resin analog high efficiency water reducing agent and cement amount is 0.2%-0.4%, defoaming agent and cement Weight ratio is 0.04%-0.06%, and the weight ratio of the third cream and cement is 3%-5%, and the weight ratio of water and cement is 15-26%.
In addition, those skilled in the art can according to need the following substance of addition:
Additive is selected from the combination of one or more of plasticiser, retarder, early strength agent, antifreezing agent.
The combination of one or more of silicon ash, white carbon black, mountain flour.
Toner；The toner is titanium dioxide, in iron oxide bloom, iron oxide black powder, iron oxide brown powder, ferric oxide red powder One or more of combinations.
Self-dense type terrazzo is made in above-mentioned terrazzo slurry method according to disclosed in embodiment 1.
Embodiment 1
The formula of terrazzo slurry is as follows:
The process for preparing terrazzo using above-mentioned terrazzo slurry is as follows:
(1) it stirs: the raw material of above-mentioned formula, in addition to water and defoaming agent, being put into stirring in blender, dry powder stirring Uniformly, mixing time about 3-5 minutes.Load weighted water is added in the powder stirred evenly to continue to stir, about 7 points of mixing time Clock is eventually adding defoaming agent, continues stir about 1 minute.
(2) it pours: being poured in preprepared mold, poured using one-pass molding, avoid repeatedly pouring.Because pouring It does not need to shake after the completion of building, so preventing the product layering for repeatedly pouring generation, (traditional terrazzo way needs to shake can Bubble is discharged, reduction porosity or product need to repair the product that few porosity could be made after polishing；This product due to Material mixture ratio reason, when production, do not need to shake this link, and also not needing repairing can be prepared by the densification product of few porosity, It has saved and has manually reduced costs in this way).
(3) it maintenance in mold: about 1 hour or so after the completion of pouring, is integrally covered using plastic film.Prevent moisture from evaporating A series of mixed mud FAQs (such as crackle, color difference caused by dehydration is too fast etc.) of too fast generation.
(4) demoulding: maintenance about 24 hours in mold under normal temperature condition.If temperature is too low, steam curing can be used, when maintenance Between about 12 hours or so demouldings.
(5) it polishes: continuing maintenance about one week or so after demoulding in the case of room temperature, start to polish, polishing uses different meshes Water mill piece is polished for a plurality of times.
It dries after the completion of polishing, is protected in product surface brushing.Equal protection parch to get.
The product testing data of the terrazzo of above-mentioned preparation are shown in Table 1.
Table 1 (result detected according to national detection project)
The water-cement ratio of product of the invention is 15-26%, and the water-cement ratio in the present embodiment is 22%.And existing product Water-cement ratio is 30-40%.
Below table content is two kinds of water-cement ratio test comparison data
Detection project Water-cement ratio is 30%-40% Water-cement ratio is 15%-26%
Physics anti-bending strength ≥14 ≥20
Physics compressive property ≥40 ≥60
Physics tensile property ≥4 ≥8
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.

Claims (9)

1. a kind of terrazzo slurry, which is characterized in that including the component of following parts by weight；
30-80 parts of cement, 20-40 parts of 2-3mm color pebble, 30-60 parts of 3-5mm color pebble, 40-80 mesh quartz sand 20-40 Part, 2-8 parts of hone sand,
And melamine resin analog high efficiency water reducing agent, defoaming agent, the third cream and water；
Wherein the weight ratio of melamine resin analog high efficiency water reducing agent and cement amount is 0.2%-0.4%, the weight of defoaming agent and cement Than for 0.04%-0.06%, the weight ratio of the third cream and cement is 3%-5%, and the weight ratio of water and cement is 15-26%.
2. a kind of terrazzo slurry according to claim 1, which is characterized in that the terrazzo slurry further includes additional Agent, the additive are selected from the combination of one or more of plasticiser, retarder, early strength agent, antifreezing agent.
3. a kind of terrazzo slurry according to claim 1, which is characterized in that the terrazzo slurry further include silicon ash, The combination of one or more of white carbon black, mountain flour.
4. a kind of terrazzo slurry according to claim 1, which is characterized in that the terrazzo slurry further includes toner； The toner is one or more of titanium dioxide, iron oxide bloom, iron oxide black powder, iron oxide brown powder, ferric oxide red powder Combination.
5. a kind of terrazzo slurry according to claim 1, which is characterized in that the cement is 52.5 plain boiled water of A Erbo Mud.
6. a kind of terrazzo slurry according to claim 1, which is characterized in that the quartz sand is 99% silicon content or more Quartz sand.
7. a kind of terrazzo slurry according to claim 1, which is characterized in that the defoaming agent is western card defoaming agent.
8. one kind is by mold cured self-dense type after molding of terrazzo slurry as claimed in any one of claims 1 to 7 Terrazzo.
9. terrazzo according to claim 8, which is characterized in that the mode of the curing molding is to pour, described to pour Without vibration.
CN201910317328.9A 2019-04-19 2019-04-19 The self-dense type terrazzo of terrazzo slurry and its curing molding Pending CN110028282A (en)