CN110342878A - A kind of ventilative high-intensity inorganic quartz and preparation method thereof - Google Patents

A kind of ventilative high-intensity inorganic quartz and preparation method thereof Download PDF

Info

Publication number
CN110342878A
CN110342878A CN201910645284.2A CN201910645284A CN110342878A CN 110342878 A CN110342878 A CN 110342878A CN 201910645284 A CN201910645284 A CN 201910645284A CN 110342878 A CN110342878 A CN 110342878A
Authority
CN
China
Prior art keywords
parts
quartz
ventilative
template
inorganic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910645284.2A
Other languages
Chinese (zh)
Inventor
吴志超
陈炳林
林永山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan Huirui Import And Export Co Ltd
Original Assignee
Foshan Huirui Import And Export Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foshan Huirui Import And Export Co Ltd filed Critical Foshan Huirui Import And Export Co Ltd
Priority to CN201910645284.2A priority Critical patent/CN110342878A/en
Publication of CN110342878A publication Critical patent/CN110342878A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of ventilative high-intensity inorganic quartz and preparation method thereof, a kind of component of ventilative high-intensity inorganic quartz and the mass fraction of component are as follows: white portland cement: 20-30 parts;The quartz sand of 8-16 mesh: 3-9 parts;The quartz sand of 16-40 mesh: 35-50 parts;The quartz sand of 40-70 mesh: 8-15 parts;The quartz sand of 70-120 mesh: 8-15 parts;A material: 3-7 parts;B material: 0.3-1 parts;Water: 5-8 parts;0.1-0.5 parts of fiber;Inorganic pigment: 0.3-1 parts.The beneficial effects of the present invention are: avoiding poisonous and hazardous gaseous volatilization since formula uses pure inorganic binder and coming out and pollute environment, be detrimental to health;And the disadvantage and simple production process of traditional organic quartz and inorganic quartz performance difference are overcome, higher steam curing temperature is not needed, production cost is low, high efficiency.

Description

A kind of ventilative high-intensity inorganic quartz and preparation method thereof
Technical field
The present invention relates to artificial stone field, specially a kind of ventilative high-intensity inorganic quartz and preparation method thereof.
Background technique
Artificial organic quartzite slate that present architectural decoration uses mostly uses greatly unsaturated polyester resin for bonding Material.This unsaturated polyester resin quartzite slate, which exists, shrinks big, easily-deformable, easy to change, poor fire, and high temperature release has The shortcomings that poisonous gas, and the presence due to there are a large amount of organic solvents in production unsaturated polyester resin, there is certain VOCs to apply It releases, pollutes the environment, threaten human health.And traditional inorganic artificial stone, such as terrazzo, because of decorative and wearability It is poor, it has been unable to satisfy the Art Design requirement for the multiplicity that becomes increasingly abundant.In addition, organic quartz is compared, the inorganic quartz of tradition Plate toughness is poor, and flexural strength is low, when thickness be lower than 15mm when, processing and transportational process in be also easy to produce cracking, for guarantee compared with High yield rate, thickness often must be more than 18mm, to cause the increase of engineering cost and the waste of resource, this also becomes nothing Machine quartz critical issue to be solved in Ground Application.Therefore exploitation is environmentally protective, be unlikely to deform, good toughness, highly resistance are rolled over by force The pure inorganic quartzite slate problem to be solved of degree.
Summary of the invention
In order to reduce the pollution to environment, reduce the threat to human health, overcome traditional organic quartz with it is inorganic The disadvantage of quartz performance difference, the present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, this method Preparation inorganic quartz internal structure micro- stomata between formed it is netted be interconnected, permeability greatly improves, therefore high temperature Or be also unlikely to deform when frost, good toughness, high breaking strength, weatherability also greatly improve, to solve the above problem.
The technical solution adopted by the present invention is that: a kind of ventilative high-intensity inorganic quartz and preparation method thereof, institute are provided A kind of component for the ventilative high-intensity inorganic quartz stated and the mass fraction of component are as follows:
White portland cement: 20-30 parts;The quartz sand of 8-16 mesh: 3-9 parts;The quartz sand of 16-40 mesh: 35-50 parts;40-70 Purpose quartz sand: 8-15 parts;The quartz sand of 70-120 mesh: 8-15 parts;A material: 3-7 parts;B material: 0.3-1 parts;Water: 5-8 parts;Fiber 0.1-0.5 parts;Inorganic pigment: 0.3-1 parts.
Further, A material by: silica, calcium carbonate, calcium formate, calcium oxide, ca aluminosilicate, carboxylic acid polyalcohol, One or more compositions of catalyst.
Further, B material is by: silica, calcium carbonate, calcium oxide, fibre-forming polymer, one kind of catalyst or more Kind composition.
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, and the method includes walking as follows It is rapid:
S1, according to weight percent all raw materials are weighed up respectively, and installed respectively spare;
S2.1, the white portland cement weighed up, the quartz sand of various specifications and A are expected to be sent in blender to be stirred, is stirred Mix uniform mixture;
S2.2, the B weighed up material, fiber, inorganic pigment are sent in batch mixer carry out it is uniformly mixed;
S3, it will be stirred evenly in mixture that the water weighed up is added in step S2.1;
S4, it will be stirred evenly in mixture that the material of step S2.2 is added in step S3;
S5, according to plate specification, install corresponding silica gel strip in template surrounding, then template bottom spread layer of plastic film, modeling Material film covers template bottom and silica gel strip;
S6, the material transmission for stirring evenly step S4 to laying device carry out in stone to the template of step S5;
S7, one layer of Silicone Rubber is spread on template material, then template is sent to being suppressed in vacuum vibration press, material pressure Open Silicone Rubber after type is made, then template is sent together with material to solidification room in solidify, the period be 3 days;
S8, plate are demoulded after solidifying 3 days, and the plate after demoulding conserves 4 days under normal temperature conditions, are then delivered to fixed thick polishing Line carries out fixed thick polishing treatment, then obtains finished product.
Further, the laying device in the step S6 is waterfall type distribution device.
Further, the step S7 solidification room temperature is (20~35 DEG C), and humidity is (70~80%)
Compared with prior art, a kind of ventilative high-intensity inorganic quartz of the present invention and preparation method thereof, with inorganic material The problem of material replaces organic material as adhesive, not only solves environmental protection, moreover it is possible to produce performance and more be superior to pass The inorganic artificial quartz of system.
Manufacturing process of the invention is simple, high production efficiency, and seldom generation waste material, waste water, the one kind produced are ventilative High-intensity inorganic quartz is wear-resisting, corrosion-resistant, resistance to compression, anti-folding, indeformable, non-discolouring, good weatherability, highly polished, fire-retardant Property the characteristics such as good.
Compared with existing organic quartz, inorganic quartz and natural stone, the ventilative high-intensity inorganic quartz Can be more preferable, the service life is longer, and application range is more extensive.
Specific embodiment
For the ease of the understanding of those skilled in the art, the present invention provides following specific embodiments to technical side of the invention Case is described in further detail.
Embodiment 1
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, a kind of ventilative high-intensity inorganic The component of quartz and the mass fraction of component are as follows: white portland cement: 21.5 parts;The quartz sand of 8-16 mesh: 7.5 parts; The quartz sand of 16-40 mesh: 43.5 parts;The quartz sand of 40-70 mesh: 9.8 parts;The quartz sand of 70-120 mesh: 10.3 parts;A material: 6 parts; B material: 0.6 part;Water: 5.5 parts;0.35 part of fiber;Inorganic pigment: 0.45 part;Wherein A material by: silica, calcium carbonate, Calcium formate, calcium oxide, ca aluminosilicate, carboxylic acid polyalcohol, catalyst one or more compositions;B material by: silica, Calcium carbonate, calcium oxide, fibre-forming polymer, catalyst one or more compositions.
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, and the method includes walking as follows It is rapid:
S1, according to weight percent all raw materials are weighed up respectively, and installed respectively spare;
S2.1, the white portland cement weighed up, the quartz sand of various specifications and A are expected to be sent in blender to be stirred, is stirred Mix uniform mixture;
S2.2, the B weighed up material, fiber, inorganic pigment are sent in batch mixer carry out it is uniformly mixed;
S3, it will be stirred evenly in mixture that the water weighed up is added in step S2.1;
S4, it will be stirred evenly in mixture that the material of step S2.2 is added in step S3;
S5, according to plate specification, install corresponding silica gel strip in template surrounding, then template bottom spread layer of plastic film, modeling Material film covers template bottom and silica gel strip;
S6, the material transmission for stirring evenly step S4 to laying device carry out in stone to the template of step S5, the stone Device is waterfall type distribution device;
S7, one layer of Silicone Rubber is spread on template material, then template is sent to being suppressed in vacuum vibration press, material pressure Open Silicone Rubber after type is made, then template is sent together with material to solidification room in solidify, the period be 3 days, the solidification room Temperature is (20~35 DEG C), and humidity is (70~80%);
S8, plate are demoulded after solidifying 3 days, and the plate after demoulding conserves 4 days under normal temperature conditions, are then delivered to fixed thick polishing Line carries out fixed thick polishing treatment, then obtains finished product.
A kind of ventilative high-intensity inorganic quartz of the present invention and preparation method thereof replaces organic material to make with inorganic material For adhesive, the problem of not only solving environmental protection, moreover it is possible to produce performance and more be superior to traditional inorganic artificial quartz Stone.
Manufacturing process of the invention is simple, high production efficiency, and seldom generation waste material, waste water, the one kind produced are ventilative High-intensity inorganic quartz is wear-resisting, corrosion-resistant, resistance to compression, anti-folding, indeformable, non-discolouring, good weatherability, highly polished, fire-retardant Property the characteristics such as good.
Embodiment 2
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, a kind of ventilative high-intensity inorganic The component of quartz and the mass fraction of component are as follows: white portland cement: 25.5 parts;The quartz sand of 8-16 mesh: 5.5 parts; The quartz sand of 16-40 mesh: 40.5 parts;The quartz sand of 40-70 mesh: 12 parts;The quartz sand of 70-120 mesh: 11..5 parts;A material: 4 parts; B material: 0.45 part;Water: 6.5 parts;0.15 part of fiber;Inorganic pigment: 0.4 part;Wherein A material by: silica, calcium carbonate, Calcium formate, calcium oxide, ca aluminosilicate, carboxylic acid polyalcohol, catalyst one or more compositions;B material by: silica, Calcium carbonate, calcium oxide, fibre-forming polymer, catalyst one or more compositions.
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, and the method includes walking as follows It is rapid:
S1, according to weight percent all raw materials are weighed up respectively, and installed respectively spare;
S2.1, the white portland cement weighed up, the quartz sand of various specifications and A are expected to be sent in blender to be stirred, is stirred Mix uniform mixture;
S2.2, the B weighed up material, fiber, inorganic pigment are sent in batch mixer carry out it is uniformly mixed;
S3, it will be stirred evenly in mixture that the water weighed up is added in step S2.1;
S4, it will be stirred evenly in mixture that the material of step S2.2 is added in step S3;
S5, according to plate specification, install corresponding silica gel strip in template surrounding, then template bottom spread layer of plastic film, modeling Material film covers template bottom and silica gel strip;
S6, the material transmission for stirring evenly step S4 to laying device carry out in stone to the template of step S5, the stone Device is waterfall type distribution device;
S7, one layer of Silicone Rubber is spread on template material, then template is sent to being suppressed in vacuum vibration press, material pressure Open Silicone Rubber after type is made, then template is sent together with material to solidification room in solidify, the period be 3 days, the solidification room Temperature is (20~35 DEG C), and humidity is (70~80%);
S8, plate are demoulded after solidifying 3 days, and the plate after demoulding conserves 4 days under normal temperature conditions, are then delivered to fixed thick polishing Line carries out fixed thick polishing treatment, then obtains finished product.
A kind of ventilative high-intensity inorganic quartz of the present invention and preparation method thereof replaces organic material to make with inorganic material For adhesive, the problem of not only solving environmental protection, moreover it is possible to produce performance and more be superior to traditional inorganic artificial quartz Stone.
Manufacturing process of the invention is simple, high production efficiency, and seldom generation waste material, waste water, the one kind produced are ventilative High-intensity inorganic quartz is wear-resisting, corrosion-resistant, resistance to compression, anti-folding, indeformable, non-discolouring, good weatherability, highly polished, fire-retardant Property the characteristics such as good.
Embodiment 3
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, a kind of ventilative high-intensity inorganic The component of quartz and the mass fraction of component are as follows: white portland cement: 28.5 parts;The quartz sand of 8-16 mesh: 4.5 parts; The quartz sand of 16-40 mesh: 44.8 parts;The quartz sand of 40-70 mesh: 9 parts;The quartz sand of 70-120 mesh: 8.5 parts;A material: 3.5 parts;B Material: 0.35 part;Water: 5.2 parts;0.25 part of fiber;Inorganic pigment: 0.6 part;Wherein A material is by silica, calcium carbonate, first Sour calcium, calcium oxide, ca aluminosilicate, carboxylic acid polyalcohol, catalyst one or more compositions;B material is by silica, carbon Sour calcium, calcium oxide, fibre-forming polymer, catalyst one or more compositions.
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, and the method includes walking as follows It is rapid:
S1, according to weight percent all raw materials are weighed up respectively, and installed respectively spare;
S2.1, the white portland cement weighed up, the quartz sand of various specifications and A are expected to be sent in blender to be stirred, is stirred Mix uniform mixture;
S2.2, the B weighed up material, fiber, inorganic pigment are sent in batch mixer carry out it is uniformly mixed;
S3, it will be stirred evenly in mixture that the water weighed up is added in step S2.1;
S4, it will be stirred evenly in mixture that the material of step S2.2 is added in step S3;
S5, according to plate specification, install corresponding silica gel strip in template surrounding, then template bottom spread layer of plastic film, modeling Material film covers template bottom and silica gel strip;
S6, the material transmission for stirring evenly step S4 to laying device carry out in stone to the template of step S5, the stone Device is waterfall type distribution device;
S7, one layer of Silicone Rubber is spread on template material, then template is sent to being suppressed in vacuum vibration press, material pressure Open Silicone Rubber after type is made, then template is sent together with material to solidification room in solidify, the period be 3 days, the solidification room Temperature is (20~35 DEG C), and humidity is (70~80%);
S8, plate are demoulded after solidifying 3 days, and the plate after demoulding conserves 4 days under normal temperature conditions, are then delivered to fixed thick polishing Line carries out fixed thick polishing treatment, then obtains finished product.
A kind of ventilative high-intensity inorganic quartz of the present invention and preparation method thereof replaces organic material to make with inorganic material For adhesive, the problem of not only solving environmental protection, moreover it is possible to produce performance and more be superior to traditional inorganic artificial quartz Stone.
Manufacturing process of the invention is simple, high production efficiency, and seldom generation waste material, waste water, the one kind produced are ventilative High-intensity inorganic quartz is wear-resisting, corrosion-resistant, resistance to compression, anti-folding, indeformable, non-discolouring, good weatherability, highly polished, fire-retardant Property the characteristics such as good.
Embodiment 4
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, a kind of ventilative high-intensity inorganic The component of quartz and the mass fraction of component are as follows:
White portland cement: 23.5 parts;The quartz sand of 8-16 mesh: 8.5 parts;The quartz sand of 16-40 mesh: 39.3 parts;40-70 mesh Quartz sand: 11.5 parts;The quartz sand of 70-120 mesh: 11 parts;A material: 5 parts;B material: 0.5 part;Water: 6.2 parts;0.2 part of fiber;Nothing Machine pigment: 0.5 part;Wherein A material by: silica, calcium carbonate, calcium formate, calcium oxide, ca aluminosilicate, carboxylic acid polyalcohol, One or more compositions of catalyst;B material by: silica, calcium carbonate, calcium oxide, fibre-forming polymer, catalyst one Kind or a variety of compositions.
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, and the method includes walking as follows It is rapid:
S1, according to weight percent all raw materials are weighed up respectively, and installed respectively spare;
S2.1, the white portland cement weighed up, the quartz sand of various specifications and A are expected to be sent in blender to be stirred, is stirred Mix uniform mixture;
S2.2, the B weighed up material, fiber, inorganic pigment are sent in batch mixer carry out it is uniformly mixed;
S3, it will be stirred evenly in mixture that the water weighed up is added in step S2.1;
S4, it will be stirred evenly in mixture that the material of step S2.2 is added in step S3;
S5, according to plate specification, install corresponding silica gel strip in template surrounding, then template bottom spread layer of plastic film, modeling Material film covers template bottom and silica gel strip;
S6, the material transmission for stirring evenly step S4 to laying device carry out in stone to the template of step S5, the stone Device is waterfall type distribution device;
S7, one layer of Silicone Rubber is spread on template material, then template is sent to being suppressed in vacuum vibration press, material pressure Open Silicone Rubber after type is made, then template is sent together with material to solidification room in solidify, the period be 3 days, the solidification room Temperature is (20~35 DEG C), and humidity is (70~80%);
S8, plate are demoulded after solidifying 3 days, and the plate after demoulding conserves 4 days under normal temperature conditions, are then delivered to fixed thick polishing Line carries out fixed thick polishing treatment, then obtains finished product.
A kind of ventilative high-intensity inorganic quartz of the present invention and preparation method thereof replaces organic material to make with inorganic material For adhesive, the problem of not only solving environmental protection, moreover it is possible to produce performance and more be superior to traditional inorganic artificial quartz Stone.
Manufacturing process of the invention is simple, high production efficiency, and seldom generation waste material, waste water, the one kind produced are ventilative High-intensity inorganic quartz is wear-resisting, corrosion-resistant, resistance to compression, anti-folding, indeformable, non-discolouring, good weatherability, highly polished, fire-retardant Property the characteristics such as good.
Embodiment 5
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, a kind of ventilative high-intensity inorganic The component of quartz and the mass fraction of component are as follows: white portland cement: 26.5 parts;The quartz sand of 8-16 mesh: 5.4 parts; The quartz sand of 16-40 mesh: 42 parts;The quartz sand of 40-70 mesh: 10.5 parts;The quartz sand of 70-120 mesh: 10 parts;A material: 4.5 parts;B Material: 0.45 part;Water: 5.8 parts;0.3 part of fiber;Inorganic pigment: 0.35 part;Wherein A material is by silica, calcium carbonate, first Sour calcium, calcium oxide, ca aluminosilicate, carboxylic acid polyalcohol, catalyst one or more compositions;B material is by silica, carbon Sour calcium, calcium oxide, fibre-forming polymer, catalyst one or more compositions.
The present invention provides a kind of ventilative high-intensity inorganic quartz and preparation method thereof, and the method includes walking as follows It is rapid:
S1, according to weight percent all raw materials are weighed up respectively, and installed respectively spare;
S2.1, the white portland cement weighed up, the quartz sand of various specifications and A are expected to be sent in blender to be stirred, is stirred Mix uniform mixture;
S2.2, the B weighed up material, fiber, inorganic pigment are sent in batch mixer carry out it is uniformly mixed;
S3, it will be stirred evenly in mixture that the water weighed up is added in step S2.1;
S4, it will be stirred evenly in mixture that the material of step S2.2 is added in step S3;
S5, according to plate specification, install corresponding silica gel strip in template surrounding, then template bottom spread layer of plastic film, modeling Material film covers template bottom and silica gel strip;
S6, the material transmission for stirring evenly step S4 to laying device carry out in stone to the template of step S5, the stone Device is waterfall type distribution device;
S7, one layer of Silicone Rubber is spread on template material, then template is sent to being suppressed in vacuum vibration press, material pressure Open Silicone Rubber after type is made, then template is sent together with material to solidification room in solidify, the period be 3 days, the solidification room Temperature is (20~35 DEG C), and humidity is (70~80%);
S8, plate are demoulded after solidifying 3 days, and the plate after demoulding conserves 4 days under normal temperature conditions, are then delivered to fixed thick polishing Line carries out fixed thick polishing treatment, then obtains finished product.
A kind of ventilative high-intensity inorganic quartz of the present invention and preparation method thereof replaces organic material to make with inorganic material For adhesive, the problem of not only solving environmental protection, moreover it is possible to produce performance and more be superior to traditional inorganic artificial quartz Stone.
Manufacturing process of the invention is simple, high production efficiency, and seldom generation waste material, waste water, the one kind produced are ventilative High-intensity inorganic quartz is wear-resisting, corrosion-resistant, resistance to compression, anti-folding, indeformable, non-discolouring, good weatherability, highly polished, fire-retardant Property the characteristics such as good.
Above-described embodiment 1-5 is preferable implementation of the invention, is not limited to the present invention, all in the present invention Spirit and principle within, any modification, equivalent replacement, improvement and so on, should be included in protection scope of the present invention it It is interior.

Claims (6)

1. a kind of ventilative high-intensity inorganic quartz and preparation method thereof, it is characterised in that: described a kind of ventilative high-strength The mass fraction of the component and component of spending inorganic quartz is as follows:
White portland cement: 20-30 parts;The quartz sand of 8-16 mesh: 3-9 parts;The quartz sand of 16-40 mesh: 35-50 parts;40-70 Purpose quartz sand: 8-15 parts;The quartz sand of 70-120 mesh: 8-15 parts;A material: 3-7 parts;B material: 0.3-1 parts;Water: 5-8 parts;Fiber 0.1-0.5 parts;Inorganic pigment: 0.3-1 parts.
2. a kind of ventilative high-intensity inorganic quartz according to claim 1 and preparation method thereof, it is characterised in that: institute The A material stated is by: silica, calcium carbonate, calcium formate, calcium oxide, ca aluminosilicate, carboxylic acid polyalcohol, one kind of catalyst or more Kind composition.
3. a kind of ventilative high-intensity inorganic quartz according to claim 1 and preparation method thereof, it is characterised in that: institute State B material by: silica, calcium carbonate, calcium oxide, fibre-forming polymer, the one or more of catalyst form.
4. a kind of ventilative high-intensity inorganic quartz according to claim 1 and preparation method thereof, it is characterised in that: institute The method of stating includes the following steps:
S1, according to weight percent all raw materials are weighed up respectively, and installed respectively spare;
S2.1, the white portland cement weighed up, the quartz sand of various specifications and A are expected to be sent in blender to be stirred, is stirred Mix uniform mixture;
S2.2, the B weighed up material, fiber, inorganic pigment are sent in batch mixer carry out it is uniformly mixed;
S3, it will be stirred evenly in mixture that the water weighed up is added in step S2.1;
S4, it will be stirred evenly in mixture that the material of step S2.2 is added in step S3;
S5, according to plate specification, install corresponding silica gel strip in template surrounding, then template bottom spread layer of plastic film, modeling Material film covers template bottom and silica gel strip;
S6, the material transmission for stirring evenly step S4 to laying device carry out in stone to the template of step S5;
S7, one layer of Silicone Rubber is spread on template material, then template is sent to being suppressed in vacuum vibration press, material pressure Open Silicone Rubber after type is made, then template is sent together with material to solidification room in solidify, the period be 3 days;
S8, plate are demoulded after solidifying 3 days, and the plate after demoulding conserves 4 days under normal temperature conditions, are then delivered to fixed thick polishing Line carries out fixed thick polishing treatment, then obtains finished product.
5. a kind of ventilative high-intensity inorganic quartz described in -4 and preparation method thereof according to claim 1, it is characterised in that: Laying device in the step S6 is waterfall type distribution device.
6. a kind of ventilative high-intensity inorganic quartz described in -5 and preparation method thereof according to claim 1, it is characterised in that: The step S7 solidification room temperature is (20~35 DEG C), and humidity is (70~80%).
CN201910645284.2A 2019-07-17 2019-07-17 A kind of ventilative high-intensity inorganic quartz and preparation method thereof Pending CN110342878A (en)