CN103058597B - Material for manufacturing wood color self-compacting concrete - Google Patents

Material for manufacturing wood color self-compacting concrete Download PDF

Info

Publication number
CN103058597B
CN103058597B CN201310017440.3A CN201310017440A CN103058597B CN 103058597 B CN103058597 B CN 103058597B CN 201310017440 A CN201310017440 A CN 201310017440A CN 103058597 B CN103058597 B CN 103058597B
Authority
CN
China
Prior art keywords
kilograms
concrete
water
formula
compacting concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310017440.3A
Other languages
Chinese (zh)
Other versions
CN103058597A (en
Inventor
黄清林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIAXING DINGYE NEW BUILDING MATERIALS CO., LTD.
Original Assignee
JIAXING DINGYE NEW BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIAXING DINGYE NEW BUILDING MATERIALS Co Ltd filed Critical JIAXING DINGYE NEW BUILDING MATERIALS Co Ltd
Priority to CN201310017440.3A priority Critical patent/CN103058597B/en
Publication of CN103058597A publication Critical patent/CN103058597A/en
Application granted granted Critical
Publication of CN103058597B publication Critical patent/CN103058597B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a material for manufacturing a wood color self-compacting concrete. Each cubic meter of concrete comprises a basic formula and a developing formula, wherein the basic formula comprises 246-252 kg of cement, 98.4-100.8 kg of superfine slag powder, 752.8-771.1 kg of yellow sand, 1031.2-1056.4 kg of macadam and 162.4-166.3 kg of water. The material disclosed by the invention is convenient for construction, and can be used for pouring a structure with complex structure, thin wall and dense reinforcement without vibrating, and improves the surface quality of the concrete. The color concrete can be obtained by adding the developing formula.

Description

For the manufacture of the material of wood grain look self-compacting concrete
Technical field
The present invention relates to a kind of material of construction, particularly relate to a kind of material for the manufacture of wood grain look self-compacting concrete.
Background technology
Concrete is configured by suitable proportion by gelling material, aggregate and water, then through certain hour sclerosis artificial stone material.Concrete hardness is high, sturdy and durable, raw material sources are extensive, making method is simple, with low cost, plasticity-strong, be applicable to various physical environment, be culture's material that usage quantity is maximum in the world, be widely used in the structures such as house, bridge, highway, runway, retaining wall, bank protection, culvert, dam, water tank, water tower, oil groove, channel, ditch, harbour, seawall, military fortification, nuclear plant.
CN201110316681.9 provides a kind of high-strength high-performance concrete, it is characterized in that: comprise following component, cement 270-430kg, flyash 30-100kg, breeze 30-100kg, sand 650-750kg, stone 1050-1200kg, water 110-160kg, admixture is prepared from.The present invention utilizes popular material, by various mixing proportion design method and a large amount of concrete test, show that strength grade is the high-strength high-performance concrete of C60, C70, C80, C90, C100, intensity is high, good endurance, can be used for the various engineerings under high level, large span and mal-condition environment.
CN200810163848.0 provides a kind of concrete, particularly relate to a kind of debris concrete, comprise cement, water, stone, flyash, breeze, river sand and admixture, it is characterized in that: also comprise chip, this chip is the tailing screened in the process of mechanical workout ore, the particle diameter of described chip is between 0.1-5MM, and the particle diameter of described stone is between 5-25MM; Wherein cement is 200-292KG, and water is 185-190KG, and stone is 1043-1088KG, flyash is 56-75KG, and breeze is 44-85KG, and river sand is 152-257KG, admixture is 5.1-7.7KG, and chip is 534-599KG, and above each component all by weight percentage.Production cost of the present invention is low, concrete density and anti-permeability performance good.
At present, a kind of available self-compacting concrete is not still had.
Summary of the invention
The object of this invention is to provide a kind of material for the manufacture of wood grain look self-compacting concrete, obtain the self-compacting color concrete of constructability, Concrete Structure appearance colour.
For the manufacture of a material for wood grain look self-compacting concrete, every cube of concrete comprises basic components and colour developing formula.
Basic components is: cement 246 ~ 252 kilograms, slag micropowder 98.4 ~ 100.8 kilograms, yellow ground 752.8 ~ 771.1 kilograms, rubble 1031.2 ~ 1056.4 kilograms and 162.4 ~ 166.3 kilograms, water.
Colour developing formula is: titanium dioxide 49.2 ~ 50.4 kilograms, iron oxide yellow 0.98 ~ 1.01 kilogram, iron oxide red 0.49 ~ 0.50 kilogram and special polycarboxylate water-reducer 4.13 ~ 4.23 kilograms.
Slag micropowder is by ore through ore dressing or the obtained micro mist of the resistates after smelting, its raw material that commonly use to by this area.The slag micropowder more than preferred S95 level of the present invention.
Rubble is not particularly limited, the raw material commonly used by this area.Continuous grading or 2 and the collocation of above one-stone grading should be adopted to form, and nominal maximum aggregate size is no more than 20mm.
Material for the manufacture of wood grain look self-compacting concrete provided by the invention, does not need to vibrate, and just may be used for the structure of building forming shape complexity, thin-walled and intensive arrangement of reinforcement, improves concrete surface quality.It is C35 that the self-compacting concrete made realizes strength grade of concrete, and apparent color presents wood grain look, there will not be open bubble or honeycomb and scale, does not need to carry out skin patching, true to naturely can present texture or the moulding of template surface.
After adding colour developing formula, obtain color concrete.Therefore the face of building can be made for good and all to present various color and luster, pattern, texture, the material of simulating nature and texture, indiscriminately ad. as one wishes all kinds of pattern of cropping realistically, and it is new, make people realize buildings and humanistic environment like a cork, physical environment is got along amiably and peacefully, the ideal combined together.According to owner's needs, the creating conception of Designers develops uniqueness and applicable color artistic concrete product and embossment, instead of existing decoration of exterior wall.
Embodiment
Below describe technical scheme of the present invention in detail.
Embodiment 1
Consist of basic components with cement 246 kilograms, slag micropowder 98.4 kilograms, yellow ground 752.8 kilograms, rubble 1031.2 kilograms and 162.4 kilograms, water etc., and coordinate with titanium dioxide 49.2 kilograms, iron oxide yellow 0.98 kilogram, iron oxide red 0.49 kilogram and special polycarboxylate water-reducer 4.13 kilograms for colour developing formula makes concrete.Strength grade of concrete is C35 after testing, apparently presents wood grain look.
Embodiment 2
Consist of basic components with cement 252 kilograms, slag micropowder 100.8 kilograms, yellow ground 771.1 kilograms, rubble 1056.4 kilograms and 166.3 kilograms, water etc., and coordinate with titanium dioxide 49.2 kilograms, iron oxide yellow 0.98 kilogram, iron oxide red 0.49 kilogram and special polycarboxylate water-reducer 4.13 kilograms for colour developing formula makes concrete.Strength grade of concrete is C35 after testing, apparently presents wood grain look.
Embodiment 3
Consist of basic components with cement 246 kilograms, slag micropowder 98.4 kilograms, yellow ground 752.8 kilograms, rubble 1031.2 kilograms and 162.4 kilograms, water etc., and coordinate with titanium dioxide 49.2 kilograms, iron oxide yellow 0.98 kilogram, iron oxide red 0.49 kilogram and special polycarboxylate water-reducer 4.13 kilograms for colour developing formula makes concrete.After testing
Test one: Control Measures for Concrete Slump divergence 578mm, through flowing the time T=4.2s of 50cm;
Test two: Control Measures for Concrete Slump divergence 566mm, through flowing the time T=4.5s of 50cm;
Test three: Control Measures for Concrete Slump divergence 562mm, through flowing the time T=4.5s of 50cm.

Claims (1)

1. the material for the manufacture of wood grain look self-compacting concrete, every cube of concrete comprises basic components and colour developing formula, basic components: cement 246 ~ 252 kilograms, slag micropowder 98.4 ~ 100.8 kilograms, yellow ground 752.8 ~ 771.1 kilograms, rubble 1031.2 ~ 1056.4 kilograms and 162.4 ~ 166.3 kilograms, water;
Colour developing formula: titanium dioxide 49.2 ~ 50.4 kilograms, iron oxide yellow 0.98 ~ 1.01 kilogram, iron oxide red 0.49 ~ 0.50 kilogram and special polycarboxylate water-reducer 4.13 ~ 4.23 kilograms.
CN201310017440.3A 2013-01-08 2013-01-08 Material for manufacturing wood color self-compacting concrete Active CN103058597B (en)