CN101380870A - Production method of artificial rockery - Google Patents

Production method of artificial rockery Download PDF

Info

Publication number
CN101380870A
CN101380870A CNA2008101431894A CN200810143189A CN101380870A CN 101380870 A CN101380870 A CN 101380870A CN A2008101431894 A CNA2008101431894 A CN A2008101431894A CN 200810143189 A CN200810143189 A CN 200810143189A CN 101380870 A CN101380870 A CN 101380870A
Authority
CN
China
Prior art keywords
artificial
lime stone
rockery
artificial hillock
fine sand
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008101431894A
Other languages
Chinese (zh)
Other versions
CN101380870B (en
Inventor
李顺炳
Original Assignee
李顺炳
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 李顺炳 filed Critical 李顺炳
Priority to CN2008101431894A priority Critical patent/CN101380870B/en
Publication of CN101380870A publication Critical patent/CN101380870A/en
Application granted granted Critical
Publication of CN101380870B publication Critical patent/CN101380870B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a method for making an artificial rockwork which is manufactured by the procedures of welding by using framework of steel reinforcement, filling stuffing, wet masonry, superficial treatment, maintaining rockwork body, etc. The artificial rockwork made by the method has the advantages of high intensity, strong toughness, multiple shapes, excellent verisimilitude, convenient production, easy transportation, etc.

Description

The preparation method of artificial rockery
Technical field
The present invention relates to a kind of preparation method of artificial rockery.
Background technology
What busy work allowed people pursue the nature a home from home requires growingly, and the hope that the restriction of city condition makes people get close to the Nature is difficult to realize.So artificial hillock in different poses and with different expressions has occurred, brought beautiful enjoyment for people's work and living environment.But natural artificial hillock quantity is few, and type is more fixing, and moulding also is difficult to change, and does not catch up with the changeable demand of people gradually.The appearance of artificial rockery has remedied the weak point of natural artificial hillock again.It can simulate stalactitic form, allows collection lime stone water quality elite in 1,100 among the Shen Zang cave and the stalactite that forms is come into everybody visual field on ordinary days.Satisfied the artistic connotation that has also enriched artificial hillock when numerous fans and audience require.
Summary of the invention
The present invention aims to provide a kind of preparation method of artificial rockery.
The preparation method of artificial rockery of the present invention is earlier according to the designing requirement weldering system framework of steel reinforcement identical with the artificial hillock shape, the lime stone plates that adopt different size, different size and different geometries again are as filler, grout out the artificial hillock body with the cement of certain proportion allotment and the mortar of lime stone fine sand, with cement mortar the reinforcing bar that exposes outside the artificial hillock body surface is whitewashed again, and then artificial hillock body body surface is done painted processing with the thin pulp that yellow clay powder, lime stone fine sand and water are deployed into, carry out maintenance with clear water at last.
The concrete preparation method of artificial rockery of the present invention is the framework of steel reinforcement of the artificial hillock homomorphosis at first being welded into and being designed by reinforcing bar; Again with the lime stone plates of different size, different size and different geometries as filler, be made into cement mortar in cement than the ratio of fine sand 1:1 with 800 label cement and fine sand after lime stone is pulverized and grout into the artificial hillock body; With cement mortar the reinforcing bar that exposes outside the artificial hillock body surface is whitewashed once, it whitewashes thickness is the 2-5 millimeter again; Adopt siliceous, the more rich natural yellow clay of calcium again, clay diameter after crushed is about the 0.02-0.2 millimeter, be made into thin pulp with lime stone fine sand (granularity is identical with the clay powder) and water, on the artificial hillock surface, its thickness is the 3-5 millimeter to thin pulp through three titration; After treating the slurry surface dewatering, used the clear water maintenance again 10-15 days.
The inventive method is made artificial rockery, has following advantage: 1, artificial rockery can design and produce the position of various green plantss of cultivation and flowers, and the whole layout of artificial hillock is beautified more.2, the intensity of artificial rockery, hardness are all greater than natural stalactite.Particularly impact flexibility be the nature artificial hillock 3-5 doubly.3, all identical with the natural artificial hillock rate of artificial rockery color and form reaches more than 90%.Color has particularly adopted occurring in nature is siliceous, calcium is heavier yellow or red clay to do the pigment preparation, through experiment repeatedly, no matter the sun is exposed to the sun, exposes to wind and rain, and does not fade, and is basic identical with the stalactite in the karst cave.4, artificial rockery can design and make differing heights, and different sizes, and different shape in different poses and with different expressions are to satisfy all kinds of personages' esthetic requirement.No matter 5, artificial rockery is how high much, all is an integral body, need not bonding for the second time or make up overlapping.Can in factory building, make, also can make at the scene.

Claims (1)

1, a kind of preparation method of artificial rockery the invention is characterized in earlier according to the designing requirement weldering system framework of steel reinforcement identical with the artificial hillock shape; Adopt different size, size and difform lime stone plates as the skeleton filler again, the mortar of allocating with the 1:1 ratio with 800 label cement and lime stone fine sand grouts out the artificial hillock body; Cement mortar with the 2-5 millimeters thick covers the body surface reinforcing bar again, then with contain thin pulp that the natural yellow clay powder that enriches silicon, calcium and lime stone fine sand (diameter is the 0.02-0.2 millimeter) and water is made into through three titration on the massif surface, thickness is the 3-5 millimeter; Treat at last to use clear water maintenance 10-15 days after the dehydration of slurry table.
CN2008101431894A 2008-09-09 2008-09-09 Production method of artificial rockery Expired - Fee Related CN101380870B (en)