CN106893259A - 一种热固性树脂组合物及其用途 - Google Patents
一种热固性树脂组合物及其用途 Download PDFInfo
- Publication number
- CN106893259A CN106893259A CN201510958047.3A CN201510958047A CN106893259A CN 106893259 A CN106893259 A CN 106893259A CN 201510958047 A CN201510958047 A CN 201510958047A CN 106893259 A CN106893259 A CN 106893259A
- Authority
- CN
- China
- Prior art keywords
- nano
- inorganic powder
- agent
- thermosetting resin
- nano inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种热固性树脂组合物以及含有它的预浸料、层压板以及印制电路板。所述热固性树脂组合物，其包括：热固性树脂和纳米无机粉末，且不包括其他固化剂。本发明在现有技术的基础上，将纳米无机粉末作为无机填充剂和固化剂使用，而省略了其他固化剂，不仅保持原有的固化功能，还可以显著提高复合材料的耐热性、韧性和阻燃性能，产生了本领域技术人员所不可预期的技术效果。
Description
技术领域
本发明属于覆铜板技术领域，涉及一种热固性树脂组合物及其用途，具体涉及一种热固性树脂组合物以及含有它的预浸料、层压板和印制电路板。
背景技术
近年来，随着电子信息技术的发展，电子设备安装的小型化、高密度化，信息的大容量化、传输信号的高频高速化，应用于高端的通讯网络硬件设备如路由器、交换机和服务器等所采用的电子电路板传输线路越来越长，要求电子电路基材具有优异的耐热性、韧性以及阻燃性。
CN 102040803A涉及一种环氧树脂组合物，包含固体环氧树脂、平均粒径为1nm～100nm的二氧化硅纳米粒子和平均粒径比前述二氧化硅纳米粒子的平均粒径大且为0.1μm～5.0μm的二氧化硅粒子。在该已有技术中，二氧化硅纳米粒子和平均粒径比前述二氧化硅纳米粒子的平均粒径大且为0.1μm～5.0μm的二氧化硅粒子均是作为环氧树脂组合物的填充剂，以提高产品的耐热性、阻燃性和粘结性。该发明的树脂组合物用于覆铜板领域时，还需要添加酚类等固化剂。
CN 102206399A公开了一种低介电常数的覆铜箔层压板用组合物，其包括：热固性树脂，1～30重量份的中空填料，1～50重量份的低吸水率填料，及0.5～5重量份的处理剂，该处理剂包括硅烷偶联剂、钛酸酯偶联剂或长链有机硅处理剂。在该已有技术中，中空填料以及低吸水率填料均是作为填充剂，以期降低吸水率。该发明的树脂组合物用于覆铜板领域时，还需要添加胺类等固化剂。
CN 102936397A公开了一种纳米填料改性环氧树脂，它由纳米填料和环氧树脂组成，其中纳米填料与环氧树脂的质量分数比为(0.5～20):100。该已有技术通过采用纳米填料对其进行表面处理，混合后改性环氧树脂，在环氧树脂固化后可以钝化裂纹，在提高环氧树脂韧性的同时，一定程度上提高固化后环氧树脂的玻璃化转变温度。该发明的纳米填料改性环氧树脂用于覆铜板领域时，还需要额外添加环氧树脂的固化剂。
CN 101837455A公开了一种壳核型纳米结构的制造方法，此方法是先提供纳米粒子，此纳米粒子中含有金属，其中纳米粒子适于将光能转换为热能。然后，将纳米粒子分布于第一热固性材料前驱物上。接着，在第一热固性材料前驱物上涂布第二热固性材料前驱物，以覆盖纳米粒子。而后，将光源照射纳米粒子以产生热能，使纳米粒子周围的第一热固性材料前驱物与第二热固性材料前驱物固化，以在纳米粒子上形成热固性材料层。之后，移除第一热固性材料前驱物的未固化部分与第二热固性材料前驱物的未固化部分。由于热固性材料前驱物固化需要一定的反应温度，该发明主要是利用纳米粒子的光热效应，使光能转化为热能，纳米粒子周围的热固性材料前驱物在吸收该热能之后固化，形成热固性材料层。在该发明中，纳米粒子的作用仅在于提供热能，热固性材料前驱物的固化主要依赖自交联。而且，在形成的最终产品中，所形成的热固性材料层均为热固性材料前驱物的自交联产物。
在上述已有技术中，纳米粒子均是作为填充剂或者提供热能，关于纳米粒子的其他用途，已有技术并未有披露。
发明内容
基于此，第一方面，本发明的目的之一在于提供一种热固性树脂组合物，在该热固性树脂组合物中，纳米无机粉末同时作为固化剂和无机填充剂。
为了实现上述目的，本发明采用了如下技术方案：
一种热固性树脂组合物，其包括：热固性树脂和纳米无机粉末，且不包括其他固化剂。
在本发明中，纳米无机粉末同时作为无机填充剂和固化剂使用，本发明的热固性树脂组合物中不再添加其他固化剂。
在已有技术中，热固性树脂组合物均包括纳米无机粉末以及固化剂，而本发明在现有技术的基础上，将纳米无机粉末作为无机填充剂和固化剂使用，而省略了其他固化剂，本发明相对于现有技术(如102040803A和CN 102206399A)为要素省略的发明。
此外，在本发明中，所述纳米无机粉末不需要进行表面处理，而已有技术如CN 102936397A所示，其纳米填料需要进行表面处理，本发明相对于该已有技术，省略了“表面处理”要素，并实现其所不能实现的作为固化剂的作用。
在本发明中，所述“不包括其他固化剂”中的“其他固化剂”是指，除本发明的纳米无机粉末以外的能和环氧树脂等热固性树脂发生固化反应的树脂，所有能与环氧树脂等热固性树脂发生固化反应的树脂均属于本发明的“其他固化剂”。例如当热固性树脂为环氧树脂时，酚醛树脂和苯并噁嗪树脂即是本发明的“其他固化剂”。
本发明的发明人虽然不知晓纳米无机粉末在作为无机填充剂的基础上，还可以同时作为固化剂的机理，但是这并不影响本发明的实施和纳米无机粉末作为无机填充剂和固化剂的使用。本发明的发明人推测纳米无机粉末可以作为固化剂使用的机理为：
纳米无机粉末表面的基团尤其是羟基易与热固性树脂的活性基团反应，在纳米粒子表面形成一层排斥力较强的保护层，减弱了纳米粒子之间的作用力，即增强了纳米粒子与热固性树脂之间的作用力，减少了分子链间的空间位阻，降低了热固性树脂固化反应的能垒，并最终促使热固性树脂的固化反应。此外，纳米无机粉末的尺寸为小于100nm，此时纳米无机粉末表现出强烈的纳米效应，其表面具有很高的活性，并且纳米粒子比表面积大，单位面积所具有的活性基团更多，更易与树脂的活性基团进行反应。
本发明在现有技术的基础上，采用纳米无机粉末固化热固性树脂，省略了其他固化剂的使用。而且，如前所述，由于纳米无机粉末作为固化剂可以降低热固性树脂固化反应的能垒，从而达到固化的作用，并且可以显著提高复合材料的耐热性。同时，由于纳米无机粉末是增韧剂，作为固化剂固化树脂，在提高复合材料的固化程度和板材刚性的同时，也提高了复合材料的韧性。另外，纳米无机粉末由于具有强烈的表面效应与吸附能力，能有效捕获燃烧反应放出的自由基，增强材料的阻燃性能。
据此可以得出，本发明在现有技术的基础上，将纳米无机粉末作为无机填充剂和固化剂使用，而省略了其他固化剂，不仅保持原有的固化功能，还可以提高复合材料的耐热性、韧性和阻燃性能，产生了本领域技术人员所不可预期的技术效果。本发明相对于现有技术，属于要素省略的发明。
优选地，在本发明中，一种热固性树脂组合物，其由热固性树脂和纳米无机粉末组成。在该优选技术方案中，所述热固性树脂组合物仅由热固性树脂和纳米无机粉末组成，其中，纳米无机粉末作为无机填充剂和固化剂使用。相对于现有技术，本发明省略了其他固化剂的使用，不仅保持原有的固化功能，还可以提高耐热性、韧性和阻燃性能，产生了本领域技术人员所不可预期的技术效果。本发明相对于现有技术，属于要素省略的发明。
优选地，在本发明中，所述纳米无机粉末为表面带有羟基的纳米无机粉末。在本发明中，纳米无机粉末表面带有羟基，例如纳米二氧化硅，其表面的硅醇更易与树脂的活性基团反应，在纳米粒子表面形成一层排斥力较强的保护层，减弱了粒子之间的作用力，即增强了纳米粒子与树脂之间的作用力，减少分子链间的空间位阻，降低热固性树脂固化反应的能垒，并最终使热固性树脂的固化反应。
优选地，所述表面带有羟基的纳米无机粉末为纳米SiO2、纳米高岭土、纳米TiO2、纳米粘土、纳米勃姆石、纳米滑石、纳米云母、纳米氢氧化铝、纳米氢氧化镁、纳米硼酸锌、纳米锡酸锌、纳米玻璃微粉、凹凸棒、埃洛石或纳米炭黑中的任意一种或者至少两种的混合物。所述混合物例如：纳米SiO2和纳米高岭土的混合物，纳米TiO2和纳米氢氧化铝的混合物，纳米粘土和纳米氢氧化镁的混合物，纳米勃姆石和纳米氧化铝的混合物，纳米滑石、纳米云母和纳米氢氧化铝的混合物，纳米氢氧化镁、纳米硼酸锌和纳米锡酸锌的混合物，纳米玻璃微粉、凹凸棒、埃洛石和纳米炭黑的混合物，纳米SiO2、纳米高岭土和纳米TiO2的混合物，纳米勃姆石、纳米氢氧化铝和纳米滑石的混合物，纳米云母、纳米氢氧化铝、纳米氢氧化镁和纳米硼酸锌的混合物。
优选地，所述的纳米无机粉末为表面带有两种以上的基团，如纳米炭黑。所述表面带有两种以上的基团，意指，除羟基以外，表面还带有至少一种其它基团。
优选地，所述纳米无机粉末的平均粒径为100nm以下，优选50nm以下。
优选地，所述纳米无机粉末为实心、多孔或中空形式的纳米无机粉末，优选为多孔形式的纳米无机粉末。多孔形式的纳米无机粉末具有巨大的比表面积和丰富的表面基团，有利于纳米无机粉末对树脂的附着并且提供二者反应的场所，有利于促进固化反应的进行。
优选地，所述纳米无机粉末为球形、纤维状或具有两个面以上的形状，优选为球形。
优选地，所述纳米无机粉末占热固性树脂组合物总质量的21～80％，例如25％、30％、35％、40％、45％、50％、55％、60％、65％、70％或75％，优选21～50％。当用量低于21％时，无法起到其固化的作用，当用量高于80％时，体系粘度较高，且填料较难分散，无法正常使用。
当所述热固性树脂组合物仅由热固性树脂和纳米无机粉末组成时，此时，即纳米无机粉末和热固性树脂的质量比为1:4～4:1，优选3:10～3:5。
在本发明中，也可以选择经过表面处理的纳米无机粉末，即纳米无机粉末也可以经过表面处理，所使用的表面处理剂包括硅烷偶联剂、钛酸酯类处理剂、铝酸盐、锆酸盐、阳离子型表面活性剂、阴离子型表面活性剂、两性表面活性剂、非离子型表面活性剂、硬脂酸、油酸、月桂酸、硬脂酸金属盐、油酸金属盐、月桂酸金属盐、酚醛树脂、有机硅油或分子量在300-1000长链处理剂中的任意一种或者至少两种的组合。
优选地，所述纳米无机粉末经过表面处理，所使用的表面处理剂包括：
表面处理剂A：分子链两端各具有2-3个可水解的硅官能基有机硅硅烷偶联剂，其结构式如式1所示；和，
表面处理剂B；表面处理剂B包括分子链一端具有2-3个可水解的硅官能基有机硅硅烷偶联剂、钛酸酯类处理剂、铝酸盐、锆酸盐、阳离子型表面活性剂、阴离子型表面活性剂、两性表面活性剂、非离子型表面活性剂、硬脂酸、油酸、月桂酸、硬脂酸金属盐、油酸金属盐、月桂酸金属盐、酚醛树脂、有机硅油或分子量在300-1000长链处理剂中的任意一种或者至少两种的组合。
分子链两端各具有2-3个可水解的硅官能基有机硅硅烷偶联剂与一般的偶联剂相比，具有更多的反应点，可以更有效的附着和连接无机物-无机物，以及无机物-有机物，促使反应更容易进行，并且可以增强复合材料的强度。另外实验发现，表面处理剂A与表面处理剂B配合使用，其效果更为显著，可能是因为表面处理剂A与表面处理剂B配合使用后，增加了处理剂链段以及增加了处理剂的反应点，使表面处理剂、纳米无机粉末、热固性树脂有更好的接触，促使固化反应的进行。
其中，R为非反应性/可反应性基团，优选为芳基、硫基、烃基或氨基；X为可水解的硅官能基；Y为可水解的硅官能基或不可水解的硅官能基，n为1～18的整数，例如2、3、4、5、6、7、8、9、10、11、12、13、14、15、16或17。
优选地，所述表面处理剂A和表面处理剂B的质量比为3:7。
所述的纳米无机粉末采用搅拌、球磨、砂磨和高压均质等物理方式进行混合均匀。
优选地，所述热固性树脂包括环氧树脂、有机硅树脂、酚醛树脂、氰酸酯树脂、苯并噁嗪树脂或不饱和聚酯中的任意一种或者至少两种的混合物，优选环氧树脂。在本发明中，选择热固性树脂的依据在于，可以选择上述热固性树脂中的任意一种，也可以选择上述热固性树脂中的至少两种的混合物。当选择上述热固性树脂中的至少两种的混合物时，所选择的热固性树脂相互之间不能发生化学反应。例如，当热固性树脂为环氧树脂时，则所述热固性树脂组合物中还可以包括其他热固性树脂，但是不能包括与环氧树脂可以发生反应，使环氧树脂固化的酚醛树脂和苯并噁嗪树脂，此时酚醛树脂和苯并噁嗪树脂即是本发明前述提到的“其他固化剂”。
本发明所述的“包括”，意指其除所述组份外，还可以包括其他组份，但除本发明前述提到的“其他固化剂”外。除此之外，本发明所述的“包括”，还可以替换为封闭式的“为”或“由……组成”。
例如，所述热固性树脂组合物还可以含有各种添加剂，作为具体例，可以举出偶联剂、抗氧剂、热稳定剂、抗静电剂、紫外线吸收剂、颜料、着色剂或润滑剂等。这些各种添加剂可以单独使用，也可以两种或者两种以上混合使用。
本发明的另一目的在于提供一种用热固性树脂组合物制成的预浸料，其包括增强材料及通过含浸干燥后附着其上的如上所述的热固性树脂组合物。
本发明的另一目的在于提供一种层压板，其包括至少一张如上所述的预浸料。
本发明的另一目的在于提供一种印制电路板，其包括至少一张如上所述的预浸料。
本发明的又一目的在于提供一种覆铜箔层压板，其含有至少一张如上所述的预浸料以及覆于叠合后的预浸料一侧或两侧的金属箔。
第二方面，本发明还提供一种纳米无机粉末同时作为无机填充剂和固化剂在热固性树脂组合物中的应用，所述热固性树脂组合物包括热固性树脂和纳米无机粉末，且不包括其他固化剂。
在已有技术中，在热固性树脂组合物中，纳米无机粉末均是作为填充剂使用，本发明在现有技术的基础上，发现了纳米无机粉末除可以作为无机填充剂外，还可以作为热固性树脂的固化剂来使用。
在本发明中，所述“不包括其他固化剂”中的“其他固化剂”是指，除本发明的纳米无机粉末以外的能和环氧树脂等热固性树脂发生反固化反应的树脂，所有能与环氧树脂等热固性树脂发生固化反应的树脂均属于本发明的“其他固化剂”。例如当热固性树脂为环氧树脂时，酚醛树脂和苯并噁嗪树脂即是本发明的“其他固化剂”。
本发明的发明人虽然不知晓纳米无机粉末在作为无机填充剂的基础上，还可以同时作为固化剂的机理，但是这并不影响本发明的实施和纳米无机粉末作为无机填充剂和固化剂的使用。本发明的发明人推测纳米无机粉末可以作为固化剂使用的机理为：
纳米无机粉末表面的基团易与热固性树脂的活性基团反应，在纳米粒子表面形成一层排斥力较强的保护层，减弱了纳米粒子之间的作用力，即增强了纳米粒子与热固性树脂之间的作用力，减少了分子链间的空间位阻，降低了热固性树脂固化反应的能垒，并最终促使热固性树脂的固化反应。此外，纳米无机粉末的尺寸为小于100nm，此时纳米无机粉末表现出强烈的纳米效应，其表面具有很高的活性，并且纳米粒子比表面积大，单位面积所具有的活性基团更多，更易与树脂的活性基团进行反应。
本发明在现有技术的基础上，采用纳米无机粉末固化热固性树脂，省略了其他固化剂的使用。而且，如前所述，由于纳米无机粉末作为固化剂可以降低热固性树脂固化反应的能垒，因此，使用纳米无机粉末固化热固性树脂，可以显著提高复合材料的耐热性。同时，由于纳米无机粉末是增韧剂，作为固化剂固化树脂，在提高复合材料的固化程度和板材刚性的同时，也提高了复合材料的韧性。另外，纳米无机粉末由于具有强烈的表面效应与吸附能力，能有效捕获燃烧反应放出的自由基，增强材料的阻燃性能。
优选地，在本发明中，一种热固性树脂组合物，其由热固性树脂和纳米无机粉末组成。在该优选技术方案中，所述热固性树脂组合物仅由热固性树脂和纳米无机粉末组成，其中，纳米无机粉末作为无机填充剂和固化剂使用。
优选地，在本发明中，所述纳米无机粉末为表面带有羟基的纳米无机粉末。在本发明中，纳米无机粉末表面带有羟基，例如纳米二氧化硅，其表面的硅醇更易与树脂的活性基团反应，在纳米粒子表面形成一层排斥力较强的保护层，减弱了粒子之间的作用力，即增强了纳米粒子与树脂之间的作用力，减少分子链间的空间位阻，降低热固性树脂固化反应的能垒，并最终使热固性树脂的固化反应。
优选地，所述表面带有羟基的纳米无机粉末为纳米SiO2、纳米高岭土、纳米TiO2、纳米粘土、纳米勃姆石、纳米滑石、纳米云母、纳米氢氧化铝、纳米氢氧化镁、纳米硼酸锌、纳米锡酸锌、纳米玻璃微粉、凹凸棒、埃洛石或纳米炭黑中的任意一种或者至少两种的混合物。所述混合物例如：纳米SiO2和纳米高岭土的混合物，纳米TiO2和纳米氢氧化铝的混合物，纳米粘土和纳米氢氧化镁的混合物，纳米勃姆石和纳米氧化铝的混合物，纳米滑石、纳米云母和纳米氢氧化铝的混合物，纳米氢氧化镁、纳米硼酸锌和纳米锡酸锌的混合物，纳米玻璃微粉、凹凸棒、埃洛石和纳米炭黑的混合物，纳米SiO2、纳米高岭土和纳米TiO2的混合物，纳米勃姆石、纳米氢氧化铝和纳米滑石的混合物，纳米云母、纳米氢氧化铝、纳米氢氧化镁和纳米硼酸锌的混合物。
优选地，所述的纳米无机粉末为表面带有两种以上的基团，如纳米炭黑。所述表面带有两种以上的基团，意指，除羟基以外，表面还带有至少一种其它基团。
优选地，所述纳米无机粉末的平均粒径为100nm以下，优选50nm以下。
优选地，所述纳米无机粉末为实心、多孔或中空形式的纳米无机粉末，优选为多孔形式的纳米无机粉末。多孔形式的纳米无机粉末具有巨大的比表面积和丰富的表面基团，有利于纳米无机粉末对树脂的附着并且提供二者反应的场所，有利于促进固化反应的进行。
优选地，所述纳米无机粉末为球形、纤维状或具有两个面以上的形状，优选为球形。
优选地，所述纳米无机粉末占热固性树脂组合物总质量的21～80％，例如25％、30％、35％、40％、45％、50％、55％、60％、65％、70％或75％，优选21～50％。当用量低于21％时，无法起到其固化的作用，当用量高于80％时，体系粘度较高，且填料较难分散，无法正常使用。
当所述热固性树脂组合物仅由热固性树脂和纳米无机粉末组成时，此时，即纳米无机粉末和热固性树脂的质量比为1:4～4:1，优选3：10～3：5。
在本发明中，也可以选择经过表面处理的纳米无机粉末，即纳米无机粉末也可以经过表面处理，所使用的表面处理剂包括硅烷偶联剂、钛酸酯类处理剂、铝酸盐、锆酸盐、阳离子型表面活性剂、阴离子型表面活性剂、两性表面活性剂、非离子型表面活性剂、硬脂酸、油酸、月桂酸、硬脂酸金属盐、油酸金属盐、月桂酸金属盐、酚醛树脂、有机硅油或分子量在300-1000长链处理剂中的任意一种或者至少两种的组合。
优选地，所述纳米无机粉末经过表面处理，所使用的表面处理剂包括：
表面处理剂A：分子链两端各具有2-3个可水解的硅官能基有机硅硅烷偶联剂，其结构式如式1所示；和，
表面处理剂B；表面处理剂B包括分子链一端具有2-3个可水解的硅官能基有机硅硅烷偶联剂、钛酸酯类处理剂、铝酸盐、锆酸盐、阳离子型表面活性剂、阴离子型表面活性剂、两性表面活性剂、非离子型表面活性剂、硬脂酸、油酸、月桂酸、硬脂酸金属盐、油酸金属盐、月桂酸金属盐、酚醛树脂、有机硅油或分子量在300-1000长链处理剂中的任意一种或者至少两种的组合。
分子链两端各具有2-3个可水解的硅官能基有机硅硅烷偶联剂与一般的偶联剂相比，具有更多的反应点，可以更有效的附着和连接无机物-无机物，以及无机物-有机物，促使反应更容易进行，并且可以增强复合材料的强度。另外实验发现，表面处理剂A与表面处理剂B配合使用，其效果更为显著，可能是因为表面处理剂A与表面处理剂B配合使用后，增加了处理剂链段以及增加了处理剂的反应点，使表面处理剂、纳米无机粉末、热固性树脂有更好的接触，促使固化反应的进行。
其中，R为非反应性/可反应性基团，优选为芳基、硫基、烃基或氨基；X为可水解的硅官能基；Y为可水解的硅官能基或不可水解的硅官能基，n为1～18的整数，例如2、3、4、5、6、7、8、9、10、11、12、13、14、15、16或17。
优选地，所述表面处理剂A和表面处理剂B的质量比为3:7。
所述的纳米无机粉末采用搅拌、球磨、砂磨、高压均质等物理方式进行混合均匀。
优选地，所述热固性树脂包括环氧树脂、有机硅树脂、酚醛树脂、氰酸酯树脂、苯并噁嗪树脂或不饱和聚酯中的任意一种或者至少两种的混合物，优选环氧树脂。在本发明中，选择热固性树脂的依据在于，可以选择上述热固性树脂中的任意一种，也可以选择上述热固性树脂中的至少两种的混合物。当选择上述热固性树脂中的至少两种的混合物时，所选择的热固性树脂相互之间不能发生化学反应。例如，当热固性树脂为环氧树脂时，则所述热固性树脂组合物中还可以包括其他热固性树脂，但是不能包括与环氧树脂可以发生反应，使环氧树脂固化的酚醛树脂和苯并噁嗪树脂，此时酚醛树脂和苯并噁嗪树脂即是本发明前述提到的“其他固化剂”。
与已有技术相比，本发明具有如下有益效果：
本发明在现有技术的基础上，将纳米无机粉末作为无机填充剂和固化剂使用，而省略了其他固化剂，不仅保持原有的固化功能，还可以提高复合材料的耐热性、韧性和阻燃性能。其中，采用该热固性树脂组合物的层压板的CTE％可达到2.7以下，Td(5％)为325～375℃，阻燃性可达到V-0级别，韧性可达到176～306mm2，固化峰温为202～265℃，产生了本领域技术人员所不可预期的技术效果。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。
实施例1-8
将溴化双酚A型环氧树脂(陶氏化学，环氧当量435，溴含量19％，产品名DER530)，纳米无机粉末混合于有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。
实施例9
将苯并噁嗪树脂(东材科技，产品名D125)，纳米无机粉末混合于有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。
实施例10
将氰酸酯树脂(扬州天启，产品名CE01PS)，纳米无机粉末混合于有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。
实施例11
将酚醛树脂(迈图化学，产品名2812)，纳米无机粉末有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。
实施例12
将溴化双酚A型环氧树脂(陶氏化学，环氧当量435，溴含量19％，产品名DER530)，纳米无机粉末以及1wt％(以填料重量计)的混合处理剂(六官能偶联剂:环氧偶联剂＝3:7)混合于有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。
实施例13
将溴化双酚A型环氧树脂(陶氏化学，环氧当量435，溴含量19％，产品名DER530)，纳米无机粉末以及1wt％(以填料重量计)的混合处理剂(四官能偶联剂:钛酸酯偶联剂＝3:7)混合于有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。
实施例14
将溴化双酚A型环氧树脂(陶氏化学，环氧当量435，溴含量19％，产品名DER530)，纳米无机粉末以及1％(以填料重量计)的环氧硅烷偶联剂混合于有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。
实施例15
将溴化双酚A型环氧树脂(陶氏化学，环氧当量435，溴含量19％，产品名DER530)，纳米无机粉末以及1wt％(以填料重量计)的六官能偶联剂混合于有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。
使用得到的覆铜板，用以下所示的方法，对凝胶点、热膨胀系数、耐热性、阻燃性、韧性效果进行测定和评价，结果见表1。
纳米无机粉末：
1)纳米二氧化硅，YA010(10nm)，YA050(50nm)，日本admatechs；
2)纳米二氧化硅，sciqas 0.1(100nm)，日本堺化学；
3)纳米炭黑，COLOUR BLACK FW200(13nm)德固赛碳黑；
4)纳米氧化镁，VK-Mg30(30nm)，宣城晶瑞新材料有限公司。
处理剂：
1)z-6040，环氧基硅烷偶联剂，美国道康宁公司；
2)SIB1620，四官能硅烷偶联剂，美国Gelest公司；
3)SIB1817，六官能硅烷偶联剂，美国Gelest公司；
4)PN-130，钛酸酯偶联剂，南京品宁偶联剂优选公司。
比较例1
除了使用二氧化硅(SFP30，0.5μm，日本电气化学)替代纳米无机粉末外，用与实施例2同样的方法，得到使用树脂组合物的覆铜板。测定、评价结果示于表2。
比较例2
除了使用二氧化硅(DQ1040，4μm，东海联瑞)替代纳米无机粉末外，用与实施例2同样的方法，得到使用树脂组合物的覆铜板。测定、评价结果示于表2。
比较例3
除了纳米无机粉末的用量为11.1份外，用与实施例1同样的方法，得到使用树脂组合物的覆铜板。测定、评价结果示于表2。
比较例4
除了纳米无机粉末的用量为900份外，用与实施例1同样的方法，得到使用树脂组合物的覆铜板。测定、评价结果示于表2。
比较例5
将溴化双酚A型环氧树脂(陶氏化学，环氧当量435，溴含量19％，产品名DER530)，双氰胺混合于有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。测定、评价结果示于表2。
比较例6
将溴化双酚A型环氧树脂(陶氏化学，环氧当量435，溴含量19％，产品名DER530)，双氰胺以及二氧化硅(DQ1040，4μm，东海联瑞)混合于有机溶剂中，机械搅拌、乳化配制成65wt％的胶水，然后含浸玻璃纤维布，经过加热干燥后形成预浸体(prepreg)，两面放置铜箔，加压加热制成覆铜板。测定、评价结果示于表2。
1、热膨胀率的测定
利用蚀刻液去除覆铜层叠板的铜箔后，切成5mm×5mm见方的大小制作试验片。使用TMA试验装置以升温速度10℃/min，测定该试验片在30℃～260℃下的Z轴方向(玻璃布垂直方向)的平均线热膨胀率。热膨胀率越小，效果越好。
2、冲击韧性测试：
将50×50mm的板材置于底座中央，然后将一定重量的实心锤在一定的高度以一定的速度对板材进行冲击，观察并测量裂纹的面积，面积越小，韧性越好。
3、燃烧性测试
采用垂直燃烧法，按照ANSI/UL-94-1985标准进行测试。
4、耐热性测试
采用热重分析仪进行测试。测试条件：氮气氛围，升温速率为10℃/min，测试失重5％时的温度，测试温度范围为25-550℃，失重5％的温度越高，说明耐热性越好。
5、固化温度测试
采用差式扫描量热仪测试。测试条件：升温速率为5℃/min。测试范围为25-300℃，测量外推起始固化温度及峰值温度。起始固化温度及峰值温度越低，说明树脂的固化温度越低。
表1
表2
备注：“/”表示无法测试。
从表1和表2可以看出，使用纳米无机粉末固化的环氧树脂复合物的耐热性、韧性和阻燃性等均比使用常规DICY固化的复合物要好，而且粒径越小，其性能越好。当粒子的粒径超过100nm后，对环氧树脂没有固化作用，其耐热性和阻燃性等性能均较差。另外，我们也可以看出，纳米无机粉末的用量越多，材料的CTE越小，阻燃性越好，Td越高，韧性越好，但同时这些指标均存在最佳添加量。另外，当用量少于21％或少于80％时，复合物的性能也明显下降，CTE明显增大，耐热性、阻燃性和韧性也明显变差。另外，从实施例2、7和8可以看出，使用表面带有两种官能团的炭黑固化的复合材料的性能稍胜于表面只带羟基的二氧化硅，且明显优于表面无官能基团的氧化镁。另外，从实施例2、12、13和实施例14、15可以看出，使用4/6官能硅烷偶联剂与其它类型偶联剂复配添加到体系中可促进固化反应的进行，同时对性能也有所提升，而单独添加这两种处理剂性能虽有提升，但不明显。
申请人声明，本发明通过上述实施例来说明本发明的详细方法，但本发明并不局限于上述详细方法，即不意味着本发明必须依赖上述详细方法才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。
Claims (10)
1.一种热固性树脂组合物，其包括：热固性树脂和纳米无机粉末，且不包括其他固化剂。
2.如权利要求1所述的热固性树脂组合物，其特征在于，一种热固性树脂组合物，其由热固性树脂和纳米无机粉末组成。
3.如权利要求1或2所述的热固性树脂组合物，其特征在于，所述纳米无机粉末为表面带有羟基的纳米无机粉末；
优选地，所述表面带有羟基的纳米无机粉末为纳米SiO2、纳米高岭土、纳米TiO2、纳米粘土、纳米勃姆石、纳米滑石、纳米云母、纳米氢氧化铝、纳米氢氧化镁、纳米硼酸锌、纳米锡酸锌、纳米玻璃微粉、凹凸棒、埃洛石或纳米炭黑中的任意一种或者至少两种的混合物；
优选地，所述的纳米无机粉末为表面带有两种以上的基团；
优选地，所述纳米无机粉末的平均粒径为100nm以下，优选50nm以下；
优选地，所述纳米无机粉末为实心、多孔或中空形式的纳米无机粉末，优选多孔形式的纳米无机粉末；
优选地，所述纳米无机粉末为球形、纤维状或具有两个面以上的形状；
优选地，所述纳米无机粉末占热固性树脂组合物总质量的21～80％，优选30～60％；
优选地，所述纳米无机粉末经过表面处理，所使用的表面处理剂包括硅烷偶联剂、钛酸酯类处理剂、铝酸盐、锆酸盐、阳离子型表面活性剂、阴离子型表面活性剂、两性表面活性剂、非离子型表面活性剂、硬脂酸、油酸、月桂酸、硬脂酸金属盐、油酸金属盐、月桂酸金属盐、酚醛树脂、有机硅油或分子量在300-1000长链处理剂中的任意一种或者至少两种的组合；
优选地，所述表面处理剂包括：
表面处理剂A：分子链两端各具有2-3个可水解的硅官能基有机硅硅烷偶联剂，其结构式如式1所示；和，
表面处理剂B：分子链一端具有2-3个可水解的硅官能基有机硅硅烷偶联剂、钛酸酯类处理剂、铝酸盐、锆酸盐、阳离子型表面活性剂、阴离子型表面活性剂、两性表面活性剂、非离子型表面活性剂、硬脂酸、油酸、月桂酸、硬脂酸金属盐、油酸金属盐、月桂酸金属盐、酚醛树脂、有机硅油或分子量在300-1000长链处理剂中的任意一种或者至少两种的组合；
其中，R为非反应性/可反应性基团，优选为芳基、硫基、烃基、氨基；X为可水解的硅官能基；Y为可水解的硅官能基或不可水解的硅官能基；n为1-18的整数；
优选地，所述表面处理剂A和表面处理剂B的质量比为3:7；
优选地，所述热固性树脂包括环氧树脂、有机硅树脂、酚醛树脂、氰酸酯树脂、苯并噁嗪树脂或不饱和聚酯中的任意一种或者至少两种的混合物，优选环氧树脂。
4.一种预浸料，其包括增强材料及通过含浸干燥后附着其上的如权利要求1-3之一所述的热固性树脂组合物。
5.一种层压板，其包括至少一张如权利要求4所述的预浸料。
6.一种印制电路板，其包括至少一张如权利要求4所述的预浸料。
7.一种纳米无机粉末同时作为无机填充剂和固化剂在热固性树脂组合物中的应用，所述热固性树脂组合物包括热固性树脂和纳米无机粉末，且不包括其他固化剂。
8.如权利要求7所述的应用，其特征在于，所述热固性树脂组合物，其由热固性树脂和纳米无机粉末组成。
9.如权利要求7或8所述的应用，其特征在于，所述纳米无机粉末为表面带有羟基的纳米无机粉末；
优选地，所述表面带有羟基的纳米无机粉末为纳米SiO2、纳米高岭土、纳米TiO2、纳米粘土、纳米勃姆石、纳米滑石、纳米云母、纳米氢氧化铝、纳米氢氧化镁、纳米硼酸锌、纳米锡酸锌、纳米玻璃微粉、凹凸棒、埃洛石或纳米炭黑中的任意一种或者至少两种的混合物。
10.如权利要求7-9之一所述的应用，其特征在于，所述纳米无机粉末的平均粒径为100nm以下，优选50nm以下；
优选地，所述纳米无机粉末为实心、多孔或中空形式的纳米无机粉末，优选多孔形式的纳米无机粉末；
优选地，所述纳米无机粉末为球形、纤维状或具有两个面以上的形状，优选为球形；
优选地，所述纳米无机粉末占热固性树脂组合物总质量的21～80％，优选30-60％；
优选地，所述纳米无机粉末经过表面处理，所使用的表面处理剂包括硅烷偶联剂、钛酸酯类处理剂、铝酸盐、锆酸盐、阳离子型表面活性剂、阴离子型表面活性剂、两性表面活性剂、非离子型表面活性剂、硬脂酸、油酸、月桂酸、硬脂酸金属盐、油酸金属盐、月桂酸金属盐、酚醛树脂、有机硅油或分子量在300-1000长链处理剂中的任意一种或者至少两种的组合；
优选地，所述表面处理剂包括：
表面处理剂A：分子链两端各具有2-3个可水解的硅官能基有机硅硅烷偶联剂，其结构式如式1所示；和，
表面处理剂B：分子链一端具有2-3个可水解的硅官能基有机硅硅烷偶联剂、钛酸酯类处理剂、铝酸盐、锆酸盐、阳离子型表面活性剂、阴离子型表面活性剂、两性表面活性剂、非离子型表面活性剂、硬脂酸、油酸、月桂酸、硬脂酸金属盐、油酸金属盐、月桂酸金属盐、酚醛树脂、有机硅油或分子量在300-1000长链处理剂中的任意一种或者至少两种的组合；
其中，R为非反应性/可反应性基团，优选为芳基、硫基、烃基、氨基；X为可水解的硅官能基；Y为可水解的硅官能基或不可水解的硅官能基；n为1-18的整数；
优选地，所述表面处理剂A和表面处理剂B的质量比为3:7；
优选地，所述热固性树脂包括环氧树脂、有机硅树脂、酚醛树脂、氰酸酯树脂、苯并噁嗪树脂或不饱和聚酯中的任意一种或者至少两种的混合物，优选环氧树脂。