CN106746663A - A kind of preparation technology of ox-blood glaze glaze paint - Google Patents
A kind of preparation technology of ox-blood glaze glaze paint Download PDFInfo
- Publication number
- CN106746663A CN106746663A CN201611104304.8A CN201611104304A CN106746663A CN 106746663 A CN106746663 A CN 106746663A CN 201611104304 A CN201611104304 A CN 201611104304A CN 106746663 A CN106746663 A CN 106746663A
- Authority
- CN
- China
- Prior art keywords
- glaze
- glass
- blood
- preparation technology
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation technology of ox-blood glaze glaze paint, include in the material of every 100 mass component:Imitation frosted glass 1.6%, gypsum rubrum 0.4%, white glass 1.2%, old gulf 67.6% makes pearl 0.4%, crystalline substance expect 0.4%, and kaolin 0.4%, two ashes 22.5%, copper spends 0.4%, green glass 3.2%, glass 0.8%;During glazing, glaze slip moisture content is 50%, and mold is imposed on to press down glaze method, and glazed thickness is 1.5~2.0mm;When burning till, 2~4 tunnels of town kiln position are placed on, with firing with reductive flame.The beneficial effects of the invention are as follows:Glaze configuration is fine, accurate;Improve the aesthetic property and artistic value of ceramic sintering product.
Description
Technical field
The present invention relates to a kind of preparation technology of glaze paint, the preparation technology that a kind of ox-blood glaze is formulated glaze paint is specifically related to,
Belong to ceramic sintering formula class field.
Background technology
At present, China has become Production of Ceramics state maximum in the world, and ceramic is also the master that China's export is earned foreign exchange
Want one of product.The Ceramic Export market of China is concentrated mainly on the U.S., Japan, South Korea, European Union etc..China is skill in the world
Art Production of Ceramics manufactures the first big country, but is not art pottery power, and most domestic enterprise is famous foreign ceramic brand
OEM the or ODM foundry vendors of enterprise, product is mainly based on outlet.At present the whole nation formed Jiangxi Jing Dezhen, Hunan Liling,
Several big art pottery producing regions such as Guangdong Chaozhou, Jiangsu, Tangshan and Handan, Shandong Zibo.Global art pottery in 2011
Porcelain yield is 7,000,000,000, and Chinese yield is 59.4 hundred million, and 47% art pottery is used to export, and is that generally acknowledged yield is maximum in the world
Big export country.Chinese light industry handicraft chamber of import and export trade ceramics branch in August, 2011 part announce " first half of the year in 2011 is complete
50 before outlet art pottery product enterprise of state " in ranking, several big producing region Jun You enterprises are on the list, and 23, Guangdong enterprise is shortlisted for, and is
Most active art pottery producing region is exported, wherein Chaozhou arrogates 10.In general, art pottery industry competitive situation is just gradually
Formed, industry concentration ratio is stepped up.
Ox-blood glaze is one of famous traditional rough flambe of China, referred to as " Lang Hong ", also there is person " ruby red ", Sai Geer
It is 18th century to superintend and direct to send and form in the kiln official youth front yard pole of superintending and directing in Jing Dezhen at that time that (8eger) be referred to as " ox blood is red " to pass on from one to another it, therefore claims youth
It is red.The extremely bright-coloured smoothness of colour generation, glaze paint has micro-crack.
In order to more competitive in the industry, it is necessary to be devoted to innovation research and development.So, how potter is improved
Skill, is the purpose of present invention research.
The content of the invention
To overcome the shortcomings of the existing technology, the present invention provides a kind of preparation technology of ox-blood glaze glaze paint, U.S. of product is improve
The property seen and artistic value.
To solve prior art problem, the technical solution adopted in the present invention is:
A kind of preparation technology of ox-blood glaze glaze paint, includes in the material of every 100 mass component:Imitation frosted glass 1.6%, Han Shui
Stone 0.4%, white glass 1.2%, pearl 0.4%, crystalline substance material 0.4%, kaolin are in old gulf 67.6%
0.4%, two ashes 22.5%, copper spends 0.4%, green glass 3.2%, glass 0.8%;During glazing, glaze slip moisture content
It is 50%, mold is imposed on to press down glaze method, glazed thickness is 1.5~2.0mm;When burning till, 2~4 tunnels of town kiln position are placed on, with also
Former flame burns till.
Further, the formula firing temperature control is at 1300 DEG C.
The beneficial effects of the invention are as follows:Glaze configuration is fine, accurate;Improve the aesthetic property and art of ceramic sintering product
Value.
Specific embodiment
In order that those skilled in the art can more understand technical solution of the present invention, with reference to specific embodiment to this
Invention is further analyzed.
A kind of preparation technology of ox-blood glaze glaze paint, includes in the material of every 100 mass component:Imitation frosted glass 1.6%,
Gypsum rubrum 0.4%, white glass 1.2%, pearl 0.4%, crystalline substance material 0.4%, kaolinite are in old gulf 67.6%
Soil 0.4%, two ashes 22.5%, copper spends 0.4%, green glass 3.2%, glass 0.8%;During glazing, glaze slip contains
Water rate is 50%, and mold is imposed on to press down glaze method, and glazed thickness is 1.5~2.0mm;When burning till, 2~4 tunnels of town kiln position are placed on,
With firing with reductive flame.The formula firing temperature control is at 1300 DEG C.
Technique of the present invention, glaze configuration is fine, accurate;Improve the aesthetic property and artistic valency of ceramic sintering product
Value.
Technical scheme provided herein is described in detail above, embodiment used herein is to the application
Principle and implementation method be set forth, the explanation of above example is only intended to help and understands the present processes and its core
Thought is thought;Simultaneously for those of ordinary skill in the art, according to the thought of the application, in specific embodiment and model is applied
Place and will change, in sum, this specification content should not be construed as the limitation to the application.
Claims (2)
1. a kind of preparation technology of ox-blood glaze glaze paint, it is characterised in that:Include in the material of every 100 mass component:Imitation frosted glass
1.6%, gypsum rubrum 0.4%, white glass 1.2%, pearl 0.4%, crystalline substance material 0.4%, kaolin 0.4%, two are in old gulf 67.6%
Ash 22.5%, copper spends 0.4%, green glass 3.2%, glass 0.8%;During glazing, glaze slip moisture content is 50%, is imposed on pressing down glaze method
Mold, glazed thickness is 1.5~2.0mm;When burning till, 2~4 tunnels of town kiln position are placed on, with firing with reductive flame.
2. the preparation technology of a kind of ox-blood glaze glaze paint according to claim 1, it is characterised in that:The formula firing temperature
Control is at 1300 DEG C.