CN106746654A - A kind of preparation technology of celeste glaze glaze paint - Google Patents
A kind of preparation technology of celeste glaze glaze paint Download PDFInfo
- Publication number
- CN106746654A CN106746654A CN201611102958.7A CN201611102958A CN106746654A CN 106746654 A CN106746654 A CN 106746654A CN 201611102958 A CN201611102958 A CN 201611102958A CN 106746654 A CN106746654 A CN 106746654A
- Authority
- CN
- China
- Prior art keywords
- glaze
- pearl
- oxide
- bright material
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation technology of celeste glaze glaze paint, include in the material of every 100 mass component：Two is most of：The bright material proportioning of pearl and color glaze formula, the bright material of pearl match and are：Quartz 24.70%, cupric oxide 0.98%, barium carbonate 0.10%, manganese oxide 29.65%, magnesia 0.10%, lime stone 0.30%, aluminum oxide 34.58%, sodium carbonate 0.20%, ferroso-ferric oxide 2.47%, cobaltosic oxide 6.92%；Color glaze formula is：Dolomite 2.21%, oxidation brill 0.06%, the bright material 0.33% of pearl, feldspar glaze 97.40%；The bright material of pearl is prepared, it is necessary to which, by formula weighing, wet-milling 00h, in 1000~1100 DEG C of scope calcinings, then finely ground, rewetting mill l00h is dried stand-by；When preparing color glaze, also should strictly weighing according to quantity, first that dolomite, cobalt oxide and the bright material of pearl is finely ground, then dissolved with feldspar glaze, glazing can be carried out with various methods, and glazed thickness is with 1~1.5mm.The beneficial effects of the invention are as follows：Glaze configuration is fine, accurate；Improve the aesthetic property and artistic value of ceramic sintering product.
Description
Technical field
The present invention relates to a kind of preparation technology of glaze paint, a kind of preparation technology of celeste glaze glaze paint is specifically related to, belonged to
Ceramic sintering formula class field.
Background technology
At present, China has become Production of Ceramics state maximum in the world, and ceramic is also the master that China's export is earned foreign exchange
Want one of product.The Ceramic Export market of China is concentrated mainly on the U.S., Japan, South Korea, European Union etc..China is skill in the world
Art Production of Ceramics manufactures the first big country, but is not art pottery power, and most domestic enterprise is famous foreign ceramic brand
OEM the or ODM foundry vendors of enterprise, product is mainly based on outlet.At present the whole nation formed Jiangxi Jing Dezhen, Hunan Liling,
Several big art pottery producing regions such as Guangdong Chaozhou, Jiangsu, Tangshan and Handan, Shandong Zibo.Global art pottery in 2011
Porcelain yield is 7,000,000,000, and Chinese yield is 59.4 hundred million, and 47% art pottery is used to export, and is that generally acknowledged yield is maximum in the world
Big export country.Chinese light industry handicraft chamber of import and export trade ceramics branch in August, 2011 part announce " first half of the year in 2011 is complete
50 before outlet art pottery product enterprise of state " in ranking, several big producing region Jun You enterprises are on the list, and 23, Guangdong enterprise is shortlisted for, and is
Most active art pottery producing region is exported, wherein Chaozhou arrogates 10.In general, art pottery industry competitive situation is just gradually
Formed, industry concentration ratio is stepped up.
Celeste glaze is the effect of imitative Jing Dezhen tradition celeste glaze, belongs to a kind of plain color glaze.
In order to more competitive in the industry, it is necessary to be devoted to innovation research and development.So, how potter is improved
Skill, is the purpose of present invention research.
The content of the invention
To overcome the shortcomings of the existing technology, the present invention provides a kind of preparation technology of celeste glaze glaze paint, U.S. of product is improve
The property seen and artistic value.
To solve prior art problem, the technical solution adopted in the present invention is：
A kind of preparation technology of celeste glaze glaze paint, includes in the material of every 100 mass component：Two is most of：The bright material proportioning of pearl
With color glaze formula, pearl bright material proportioning is：Quartz 24.70%, cupric oxide 0.98%, barium carbonate 0.10%, manganese oxide
29.65%, magnesia 0.10%, lime stone 0.30%, aluminum oxide 34.58%, sodium carbonate 0.20%, ferroso-ferric oxide
2.47%, cobaltosic oxide 6.92%；Color glaze formula is：Dolomite 2.21%, oxidation brill 0.06%, the bright material of pearl
0.33%, feldspar glaze 97.40%；The bright material of pearl is prepared, it is necessary to which, by formula weighing, wet-milling 00h is forged in 1000~1100 DEG C of scopes
Burn, then finely ground, rewetting mill l00h is dried stand-by；Prepare color glaze when, also should strictly weighing according to quantity, first by dolomite, cobalt oxide
It is finely ground with the bright material of pearl, then dissolved with feldspar glaze, glazing can be carried out with various methods, and glazed thickness is with 1~1.5mm.
Further, the firing temperature of the technique is not limited with 1320~1350 DEG C by flame.
The beneficial effects of the invention are as follows：Glaze configuration is fine, accurate；Improve the aesthetic property and art of ceramic sintering product
Value.
Specific embodiment
In order that those skilled in the art can more understand technical solution of the present invention, with reference to specific embodiment to this
Invention is further analyzed.
A kind of preparation technology of celeste glaze glaze paint, includes in the material of every 100 mass component：Two is most of：The bright material of pearl
Proportioning and color glaze formula, the bright material of pearl match and are：Quartz 24.70%, cupric oxide 0.98%, barium carbonate 0.10%, manganese oxide
29.65%, magnesia 0.10%, lime stone 0.30%, aluminum oxide 34.58%, sodium carbonate 0.20%, ferroso-ferric oxide
2.47%, cobaltosic oxide 6.92%；Color glaze formula is：Dolomite 2.21%, oxidation brill 0.06%, the bright material of pearl
0.33%, feldspar glaze 97.40%；The bright material of pearl is prepared, it is necessary to which, by formula weighing, wet-milling 00h is forged in 1000~1100 DEG C of scopes
Burn, then finely ground, rewetting mill l00h is dried stand-by；Prepare color glaze when, also should strictly weighing according to quantity, first by dolomite, cobalt oxide
It is finely ground with the bright material of pearl, then dissolved with feldspar glaze, glazing can be carried out with various methods, and glazed thickness is with 1~1.5mm.It is described
The firing temperature of technique is not limited with 1320~1350 DEG C by flame.
Technique of the present invention, glaze configuration is fine, accurate；Improve the aesthetic property and artistic valency of ceramic sintering product
Value.
Technical scheme provided herein is described in detail above, embodiment used herein is to the application
Principle and implementation method be set forth, the explanation of above example is only intended to help and understands the present processes and its core
Thought is thought；Simultaneously for those of ordinary skill in the art, according to the thought of the application, in specific embodiment and model is applied
Place and will change, in sum, this specification content should not be construed as the limitation to the application.
Claims (2)
1. a kind of preparation technology of celeste glaze glaze paint, it is characterised in that include in the material of every 100 mass component：Two big portions
Point：The bright material proportioning of pearl and color glaze formula, the bright material of pearl match and are：Quartz 24.70%, cupric oxide 0.98%, barium carbonate 0.10%, oxygen
Change manganese 29.65%, magnesia 0.10%, lime stone 0.30%, aluminum oxide 34.58%, sodium carbonate 0.20%, ferroso-ferric oxide
2.47%, cobaltosic oxide 6.92%；Color glaze formula is：Dolomite 2.21%, oxidation brill 0.06%, the bright material 0.33% of pearl is long
Stone glaze 97.40%；The bright material of pearl is prepared, it is necessary to by formula weighing, wet-milling 00h, in 1000~1100 DEG C of scope calcinings, Ran Houyan
Carefully, rewetting mill l00h, dries stand-by；Prepare color glaze when, also should strictly weighing according to quantity, first by dolomite, cobalt oxide and the bright material of pearl
It is finely ground, then dissolved with feldspar glaze, glazing can be carried out with various methods, and glazed thickness is with 1~1.5mm.
2. a kind of preparation technology of celeste glaze glaze paint, it is characterised in that the firing temperature of the technique with 1320~1350 DEG C, no
Limited by flame.