CN101618943A - Transparent crack glaze and method for processing transparent crack product - Google Patents
Transparent crack glaze and method for processing transparent crack product Download PDFInfo
- Publication number
- CN101618943A CN101618943A CN200910012808A CN200910012808A CN101618943A CN 101618943 A CN101618943 A CN 101618943A CN 200910012808 A CN200910012808 A CN 200910012808A CN 200910012808 A CN200910012808 A CN 200910012808A CN 101618943 A CN101618943 A CN 101618943A
- Authority
- CN
- China
- Prior art keywords
- glaze
- transparent crack
- transparent
- color
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to ceramic glaze preparation and ceramic product production. The transparent crack glaze mainly uses the following raw materials by weight percent for preparing basic glaze: 40% of sodium feldspar and potassium feldspar, 5% of kaolin, 23% of quartz and 32% of limestone. The formula of the transparent crack glaze is reasonable, the content of the sodium feldspar can directly affect the expansion coefficient of the glaze, so that the content can be appropriately increased or decreased for controlling the density of cracks after burning under the premise of not changing the proportion of the feldspars. The prepared basic glaze is applicable to preparing the color glaze with a variety of colors, as the color development of the glaze relies on metal ions after high-temperature burning in the glaze, the preparation of the transparent color glaze only needs to add an appropriate amount of metal compounds which can lead the glaze to develop color after burning in the raw materials before ball milling. The product burned by using the transparent crack glaze has great mechanical strength, and the product can not only be used as a furnishing, but also be used as a daily product.
Description
One, technical field:
The present invention relates to the preparation of pottery art glaze, and use the working method of this glaze potting.
Two, background technology:
China is the country of invention fire porcelain the earliest, and just can fire original celadon late period in the Shang Dynasty, all with truly porcelain a certain distance is arranged owing to make the glaze of raw material, preparation of carcass and firing temperature, so be referred to as original celadon.To Eastern Han Dynasty last years of a dynasty or reign southern kiln porcelain stone more be the carcass raw material, improved glaze formulation, improved firing temperature, can burn out real celadon.The carcass and the glaze coefficient of expansion are inconsistent in the ceramic making, and the glaze coefficient of expansion is greater than the carcass coefficient of expansion, and it is big and the drawing crack glaze forms crackle to burn till back kiln discharge carcass contraction ratio glaze, otherwise the glaze surface expansion is peeled off.These all are some disadvantages during ceramic making is burnt till.When ceramics is developed to the Song dynasty, craftsman make full use of glaze and shrink the characteristics that form the crackle skin texture, infiltrate in the crackle with prepared Chinese ink and some mineral colors, make it fully to display with physical method, government porcelain kiln and brother's kiln in five your name's kilns of the Song dynasty are exactly typical example.And have the present age ceramist that crackle is handled, infiltrate glaze in cracks, carry out resintering again, the firing temperature of seeing works with regard to apparent present situation is lower, physical strength is little, substantially can only be as stuff and inapplicable, its crackle skin texture forms on the basis that big solid hacks at opaque glaze substantially and manifests, and the prescription of its parent glaze is still indeterminate.
Three, summary of the invention:
The objective of the invention is to overcome above-mentioned not enough problem, a kind of transparent crack glaze is provided, prescription rationally can be mixed with multiple color, can control the density that burns till the back crackle, and product strength is good and attractive in appearance.The present invention also provides the working method of transparent crack glaze goods in addition, and method is simple, easy handling.
The technical scheme that the present invention is adopted for achieving the above object is: transparent crack glaze mainly is mixed with parent glaze by following weight percentages: albite and potassium felspar sand mixture 40%, kaolin 5%, quartz 23%, Wingdale 32%.
The per-cent that described albite and potassium felspar sand account for gross weight is respectively: potassium felspar sand 20-39%, albite 1-20%.
Described transparent crack glaze mainly is mixed with parent glaze by following weight percentages: potassium felspar sand 35%, albite 5%, kaolin 5%, quartz 23%, Wingdale 32%.
Also be added with chromogenic reagent in the described transparent crack glaze, the glaze chromogenic reagent adopts metallic compound, and the metal in the metallic compound is the metal of its metal ion state energy color development of energy after high temperature burns till.As the oxide compound of copper, the oxide compound of iron or the oxide compound of cobalt etc.
The amount that described metallic compound adds is decided according to metal ion color development ability, is generally the 0.5-10% of parent glaze gross weight.
The method for making of transparent crack glaze of the present invention is, parent glaze raw material (dose color glaze also comprise chromogenic reagent) is mixed according to quantity, adds an amount of water and inserts in the ball mill, and ball milling 18-20 hour formulated.
The working method of transparent crack glaze product of the present invention:
The first step carcass is made: use less than the pug of the glaze coefficient of expansion and make tire, drying and moulding is for increasing carcass strength 780 ℃ of-800 ℃ of low temperature biscuitings earlier once;
The second step glazing: the transparent crack color glaze glaze that ball milling is good, adopt glaze spraying, soak glaze, drench glaze, swing method such as glaze and give carcass glazing, glaze thickness 0.8-1 millimeter;
The 3rd step burnt till: adopt electrical kiln or gas klining to become, kiln temperature is controlled at 1180 ℃-1200 ℃;
The 4th cooled processing of step: to be cooled during to 60 ℃, in kiln, works are taken out the transparent crack color glaze glaze of putting into 60 ℃ of another kind of colors and soak, take out after soaking half a minute, the glaze that the flush away surface is useless, the glaze that keeps cracks dries;
The 5th step burnt till once more: adopt electrical kiln or gas klining to become, kiln temperature is controlled at 1180 ℃-1200 ℃;
The 6th walks out of kiln: treat to take out when temperature thoroughly is cooled to room temperature, promptly make the transparent crack glaze product.
Described the 4th cooled processing of step: glaze dries the back 80 ℃ of-100 ℃ of taking-ups, washes away the part with cold water, again carcass is carried out the crackle glazing; Make the transparent crack glaze product of hacking the part.
Transparent crack glaze formula of the present invention is reasonable, the content of albite can directly influence the coefficient of expansion of glaze, therefore increasing or reduce its content under the prerequisite that does not change the feldspar ratio in right amount can control and burn till afterwards the density of crackle (the albite amount can be allocated from 1%-20%, and it is 40% constant that albite and potassium felspar sand total content keep).The parent glaze that makes is applicable to versicolor color glaze preparation, because the glaze color development is to burn till back metal ion color development in glaze by high temperature, as preparing transparency enamel, only need before ball milling, in raw material, to add the metallic compound that can make the glaze color development after burning till in right amount, make the glaze green-emitting after burning till as the oxide compound oxidation of copper, after burning till, the oxide compound oxidation of iron make glaze send out brown, after burning till, the oxide compound oxidation of cobalt makes glaze Fa Lanse, glaze colours deep or light can add-on how much regulate (general be 1%-10%, extremely strong material of color development such as cobalt oxide add-on are generally 0.5%-5%).
Adopt transparent crack glaze of the present invention to fire goods, burn till the back form crackle be since the coefficient of expansion of glaze greater than the carcass coefficient, glaze contraction ratio carcass is wanted big and is formed crackle when burning till postcooling, thus the glaze of this prescription can only use with the coefficient of expansion than its little carcass.
The inventive method can be recycled and reused for same carcass, repeatedly burn till, can obtain the effect of levels are rich, (firing temperature is at 1180 ℃-1200 ℃) works characteristics that high temperature burns till be crackle simple and elegant, fine and smooth, do not make widely known, combine together fully with glaze, scrutinize just as filament and be suspended in the glaze laminar surface, the works physical strength is big after burning till, can can also use as articles for daily use as stuff.
Four, embodiment:
The invention will be further described below in conjunction with specific embodiment, but the present invention is not limited to specific embodiment.
Embodiment 1
Transparent crack glaze, it is mainly by the formulated parent glaze of following weight percentages: potassium felspar sand 35%, albite 5%, kaolin 5%, quartz 23%, Wingdale 32%, raw material is mixed according to quantity, add an amount of water and insert in the ball mill, be mixed with the water white transparency parent glaze in ball milling 18-20 hour.
Transparent crack glaze, it is mainly by the formulated blue glaze of following weight percentages: potassium felspar sand 32%, albite 8%, kaolin 5%, quartz 23%, Wingdale 32%, the cobalt oxide add-on is 0.5% of an aforementioned parent glaze raw material gross weight.After above-mentioned each raw material mixing, add an amount of water and insert in the ball mill, be mixed with transparent blue crackle glaze in ball milling 18-20 hour, standby.
Transparent crack glaze, it is mainly by the formulated green glaze of following weight percentages: potassium felspar sand 37%, albite 3%, kaolin 5%, quartz 23%, Wingdale 32%, the cupric oxide add-on is 5% of a parent glaze gross weight, after above-mentioned each raw material mixing, adding an amount of water inserts in the ball mill, be mixed with transparent green crackle glaze in ball milling 18-20 hour, standby.
Transparent crack glaze, it is mainly by the formulated red glaze of following weight percentages: potassium felspar sand 25%, albite 15%, kaolin 5%, quartz 23%, Wingdale 32%, the add-on of ferric oxide is 7% of aforementioned each raw material gross weight, after above-mentioned each raw material mixing, adding an amount of water inserts in the ball mill, be mixed with transparent red crackle glaze in ball milling 18-20 hour, standby.
Embodiment 2
Adopt the working method of above-mentioned transparent crack color glaze bowl:
The first step carcass is made: use less than the pug of the glaze coefficient of expansion and make tire, be dried to a bowl type, for increasing carcass strength 780 ℃ of-800 ℃ of low temperature biscuitings earlier once;
The second step glazing: adopt the blue transparent glaze that splits, by glaze spraying, soak glaze, drench glaze, swing method such as glaze and carry out glazing, the about 0.8-1 mm thick of glaze;
The 3rd step burnt till: the carcass after the glazing is inserted electrical kiln, the gas klining becomes, and kiln temperature is at 1180 ℃-1200 ℃;
The 4th cooled processing of step: when treating that kiln temperature is cooled to about 60 ℃, in kiln 60 ℃ of green transparent crackle color glaze being put in the taking-up of bowl goods soaks, soak in the time of warm and help cracks absorption glaze, take out after half a minute approximately, the glaze that the flush away surface is useless, the glaze that keeps cracks dries.
The 5th step burnt till once more: electrical kiln, gas klining Cheng Junke, and temperature is at 1180 ℃-1200 ℃;
The 6th walks out of kiln: treat to take out when temperature thoroughly is cooled to room temperature.
Embodiment 3
By the local dish that hacks of method for making preparation of embodiment 2,
Three steps of the first step to the are identical with embodiment 2,
The 4th cooled processing of step: when treating that kiln temperature is cooled to about 60 ℃, in kiln 60 ℃ of red transparent crack color glaze being put in the taking-up of dish goods soaks, soak in the time of warm and help cracks absorption glaze, take out after half a minute approximately, the glaze on flush away surface, the glaze that keeps cracks dries, and pursues local special-effect of hacking as need and can wash away the part again to its crackle glazing with cold water 80 ℃ of-100 ℃ of taking-ups;
The 6th step of the 5th step is identical with embodiment 2.
Claims (9)
1, transparent crack glaze is characterized in that: it mainly is mixed with parent glaze by following weight percentages: albite and potassium felspar sand mixture 40%, kaolin 5%, quartz 23%, Wingdale 32%.
2, the described transparent crack glaze of claim 1, it is characterized in that: the per-cent that albite and potassium felspar sand account for gross weight is respectively: potassium felspar sand 20-39%, albite 1-20%.
3, the described transparent crack glaze of claim 1, it is characterized in that: it mainly is mixed with parent glaze by following weight percentages: potassium felspar sand 35%, albite 5%, kaolin 5%, quartz 23%, Wingdale 32%.
4, the arbitrary described transparent crack glaze of claim 1-3 is characterized in that: also be added with chromogenic reagent in the transparent crack glaze, chromogenic reagent adopts metallic compound, and the metal in the metallic compound is the metal of its metal ion state energy color development of energy after high temperature burns till.
5, the described transparent crack glaze of claim 4 is characterized in that: chromogenic reagent adopts oxide compound, the oxide compound of iron or the oxide compound of cobalt of copper.
6, the described transparent crack glaze of claim 4 is characterized in that: the amount that metallic compound adds is decided according to metal ion color development ability, is generally the 0.5-10% of parent glaze gross weight.
7, the method for making of transparent crack glaze is characterized in that: parent glaze raw material (dose color glaze also comprise chromogenic reagent) is mixed according to quantity, add an amount of water and insert in the ball mill, ball milling 18-20 hour formulated.
8, the working method of transparent crack glaze product is characterized in that:
The first step carcass is made: use less than the pug of the glaze coefficient of expansion and make tire, drying and moulding is for increasing carcass strength 780 ℃ of-800 ℃ of low temperature biscuitings earlier once;
The second step glazing: the transparent crack color glaze glaze that ball milling is good, adopt glaze spraying, soak glaze, drench glaze, swing method such as glaze and give carcass glazing, glaze thickness 0.8-1 millimeter;
The 3rd step burnt till: adopt electrical kiln or gas klining to become, kiln temperature is controlled at 1180 ℃-1200 ℃;
The 4th cooled processing of step: to be cooled during to 60 ℃, in kiln, works are taken out the transparent crack color glaze glaze of putting into 60 ℃ of another kind of colors and soak, take out after soaking half a minute, the glaze that the flush away surface is useless, the glaze that keeps cracks dries;
The 5th step burnt till once more: adopt electrical kiln or gas klining to become, kiln temperature is controlled at 1180 ℃-1200 ℃;
The 6th walks out of kiln: treat to take out when temperature thoroughly is cooled to room temperature, promptly make the transparent crack glaze product.
9, the working method of transparent crack glaze product according to claim 7 is characterized in that: the 4th cooled processing of step: glaze dries the back 80 ℃ of-100 ℃ of taking-ups, washes away the part with cold water, again carcass is carried out the crackle glazing; Make the transparent crack glaze product of hacking the part.