CN106673433A - Yuezhou kiln celadon fine ice crack glaze product and manufacturing process thereof - Google Patents
Yuezhou kiln celadon fine ice crack glaze product and manufacturing process thereof Download PDFInfo
- Publication number
- CN106673433A CN106673433A CN201710008871.1A CN201710008871A CN106673433A CN 106673433 A CN106673433 A CN 106673433A CN 201710008871 A CN201710008871 A CN 201710008871A CN 106673433 A CN106673433 A CN 106673433A
- Authority
- CN
- China
- Prior art keywords
- kiln
- celadon
- weight
- glaze
- yuezhou
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a Yuezhou kiln celadon fine ice crack glaze product which comprises a celadon body and glaze. The glaze comprises 60%-75% of albite, 15%-26% of limestone, 3%-8% of Zijin clay, 2%-10% of quartz, 0.8%-1% of ferric oxide and 3%-6% of feldspar ends. The invention further discloses a manufacturing process of the Yuezhou kiln celadon fine ice crack glaze product. Fine ice cracks on the product are quite fine, the product is attractive, glittering, translucent, glossy and as beautiful as a fine jade, and overall stereoscopic effects of the finished product can be expressed.
Description
Technical field
The present application relates to chinaware article, more particularly to a kind of Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits and its system
Make technique.
Background technology
China is the country of earliest porcelain making in the world.Up in the development process of thousands of years, ceramics not only act as storage
The effect of vessel, also acts as the effect of decorator.
With expanding economy and the improvement of people's living standards, people have higher wanting to the decoration technology of porcelain
Ask.At present, piece line on the ceramics of in the market is too thick, unsightly, the overall stereoeffect of finished product, not sparkling and crystal-clear enough can not be given expression to
It is moist.
The content of the invention
The purpose of the present invention is directed to shortcoming present in background technology and problem is improved and innovated, there is provided a kind of piece
Line is very thin, attractive in appearance, sparkling and crystal-clear moist Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits and its manufacture craft.
A kind of Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits, including celadon base and glaze, the glaze include following weight hundred
Divide the raw mineral materials of ratio:
Receive feldspar 60%~75%
Lime stone 15%~26%
Zijin soil 3%~8%
Quartz 2%~10%
Iron oxide 0.8%~1%
Feldspar 3%~6%.
Wherein in one embodiment, the percentage by weight for receiving feldspar is 70%.The weight percent of the lime stone
Than being 16%.The percentage by weight of the Zijin soil is 5%.The percentage by weight of the quartz is 5%.The weight of the iron oxide
Amount percentage is 0.9%.The percentage by weight of the feldspar is 3.1%.
The manufacture craft of above Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits, comprises the following steps:
(1)Receive feldspar, lime stone, Zijin soil, quartz, iron oxide, the feldspar for taking out corresponding weight by above-mentioned formula are added to the water,
Raw mineral materials, the weight ratio of water are 1:1.5, ball milling is carried out after mixing, Ball-milling Time is 20~26 hours, obtains glaze slip, glaze slip
Fineness crosses 250 mesh sieves.
(2)Celadon base is entered into kiln carries out 800 DEG C~900 DEG C biscuitings, kiln is taken out after cooling, then will cross the glaze of 250 mesh sieves
Slurry is imposed on the celadon base after taking out kiln, is then repaired and is dried.
(3)Enter kiln again after finishing, drying, burn till under reducing atmosphere, firing temperature is 1240 DEG C~1280 DEG C, i.e.,
Can obtain the ice crack in small, broken bits on Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits, and Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits
The width of piece line is 0.5mm~2mm.
The present invention has advantages below and beneficial effect:
1st, the ice crack piece line in small, broken bits in the present invention is very thin.
2nd, attractive in appearance, the sparkling and crystal-clear moist, Mei Ruoqiong of the present invention is beautiful.
3rd, the present invention can give expression to the overall stereoeffect of finished product.
Specific embodiment
For the ease of understanding the present invention, the present invention will be described more fully below.The present invention can be with many not
With form realize, however it is not limited to embodiment described herein.On the contrary, the purpose for providing these embodiments is made to this
Disclosure of the invention content is more thorough comprehensive.
Unless otherwise defined, the skill of all of technology used herein and scientific terminology and technical field of the invention
The implication that art personnel are generally understood that is identical.Term used in the description is intended merely to describe specifically to implement purpose, is not
It is intended to the limitation present invention.
Embodiment 1
A kind of Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits, including celadon base and glaze, ore deposit of the glaze comprising following percentage by weight
Raw material:
Receive feldspar percentage by weight be 70%.The percentage by weight of lime stone is 16%.Zijin soil percentage by weight be
5%.The percentage by weight of quartz is 5%.The percentage by weight of iron oxide is 0.9%.The percentage by weight of feldspar is 3.1%.
The manufacture craft of above Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits:
(1)Receive feldspar, lime stone, Zijin soil, quartz, iron oxide, the feldspar for taking out corresponding weight by above-mentioned formula are added to the water,
Raw mineral materials, the weight ratio of water are 1:1.5, ball milling is carried out after mixing, Ball-milling Time is 24 hours, obtains glaze slip, glaze slip fineness
Cross 250 mesh sieves.
(2)Celadon base is entered into kiln carries out 850 DEG C of biscuitings, takes out kiln after cooling, then the glaze slip for crossing 250 mesh sieves is imposed on takes
On celadon base after kiln discharge, then repaired and dried.
(3)Enter kiln again after finishing, drying, burn till under reducing atmosphere, firing temperature is 1260 DEG C, you can obtain high mountain
The width of the ice crack piece line in small, broken bits on state kiln celadon ice crack piece line glaze product in small, broken bits, and Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits
It is 0.5mm~2mm to spend.
Embodiment 2
A kind of Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits, including kiln celadon base and glaze, glaze include following percentage by weight
Raw mineral materials:
Receive feldspar percentage by weight be 60%.The percentage by weight of lime stone is 21%.Zijin soil percentage by weight be
6%.The percentage by weight of quartz is 6%.The percentage by weight of iron oxide is 1%.The percentage by weight of feldspar is 6%.
The manufacture craft of above Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits:
(1)Receive feldspar, lime stone, Zijin soil, quartz, iron oxide, the feldspar for taking out corresponding weight by above-mentioned formula are added to the water,
Raw mineral materials, the weight ratio of water are 1:1.5, ball milling is carried out after mixing, Ball-milling Time is 26 hours, obtains glaze slip, glaze slip fineness
Cross 250 mesh sieves.
(2)Celadon base is entered into kiln carries out 900 DEG C of biscuitings, takes out kiln after cooling, then the glaze slip for crossing 250 mesh sieves is imposed on takes
On celadon base after kiln discharge, then repaired and dried.
(3)Enter kiln again after finishing, drying, burn till under reducing atmosphere, firing temperature is 1240 DEG C, you can obtain high mountain
The width of the ice crack piece line in small, broken bits on state kiln celadon ice crack piece line glaze product in small, broken bits, and Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits
It is 0.5mm~2mm to spend.
The present invention has advantages below and beneficial effect:
1st, the ice crack piece line in small, broken bits in the present invention is very thin.
2nd, attractive in appearance, the sparkling and crystal-clear moist, Mei Ruoqiong of the present invention is beautiful.
3rd, the present invention can give expression to the overall stereoeffect of finished product.
Embodiment of the present invention is only the description carried out to the preferred embodiment of the present invention, not to the present invention
Spirit and scope are defined, and on the premise of design philosophy of the present invention is not departed from, engineers and technicians are to this hair in this area
The all variations and modifications that bright technical scheme is made, all should fall into protection scope of the present invention, claimed skill of the invention
Art content, has all recorded in detail in the claims.
Claims (3)
1. a kind of Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits, including celadon base and glaze, it is characterised in that the glaze include with
The raw mineral materials of lower percentage by weight:
Receive feldspar 60%~75%
Lime stone 15%~26%
Zijin soil 3%~8%
Quartz 2%~10%
Iron oxide 0.8%~1%
Feldspar 3%~6%.
2. kiln celadon in Yuezhou according to claim 1 ice crack piece line glaze product in small, broken bits, it is characterised in that the feldspar of receiving
Percentage by weight is 70%, and the percentage by weight of the lime stone is 16%, and the percentage by weight of the Zijin soil is 5%, institute
It is 5% to state the percentage by weight of quartz, and the percentage by weight of the iron oxide is 0.9%, and the percentage by weight of the feldspar is
3.1%.
3. a kind of manufacture craft of Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits described in claim 1, it is characterised in that bag
Include following steps:
(1)Receive feldspar, lime stone, Zijin soil, quartz, iron oxide, the feldspar for taking out corresponding weight by above-mentioned formula are added to the water,
Raw mineral materials, the weight ratio of water are 1:1.5, ball milling is carried out after mixing, Ball-milling Time is 20~26 hours, obtains glaze slip, glaze slip
Fineness crosses 250 mesh sieves;
(2)Celadon base is entered into kiln carries out 800 DEG C~900 DEG C biscuitings, kiln is taken out after cooling, then the glaze slip for crossing 250 mesh sieves is applied
On celadon base after kiln is taken out, then repaired and dried;
(3)Enter kiln again after finishing, drying, burn till under reducing atmosphere, firing temperature is 1240 DEG C~1280 DEG C, you can
Ice crack piece line in small, broken bits onto Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits, and Yuezhou kiln celadon ice crack piece line glaze product in small, broken bits
Width be 0.5mm~2mm.