CN104193417B - The celadon sintering technology method that brother's glaze combines with younger brother's glaze - Google Patents

The celadon sintering technology method that brother's glaze combines with younger brother's glaze Download PDF

Info

Publication number
CN104193417B
CN104193417B CN201410444480.0A CN201410444480A CN104193417B CN 104193417 B CN104193417 B CN 104193417B CN 201410444480 A CN201410444480 A CN 201410444480A CN 104193417 B CN104193417 B CN 104193417B
Authority
CN
China
Prior art keywords
glaze
brother
base substrate
temperature
younger
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410444480.0A
Other languages
Chinese (zh)
Other versions
CN104193417A (en
Inventor
许继武
Original Assignee
许继武
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 许继武 filed Critical 许继武
Priority to CN201410444480.0A priority Critical patent/CN104193417B/en
Publication of CN104193417A publication Critical patent/CN104193417A/en
Application granted granted Critical
Publication of CN104193417B publication Critical patent/CN104193417B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to celadon industrial art field, in particular disclose and a kind of traditional dragon's fountain brother glaze is combined the processing method and glaze formula thereof fired with younger brother's glaze.Because the coefficient of expansion difference of brother's glaze and younger brother's glaze is larger, brother's glaze cracking ultimate temperature is higher than the highest threshold temperature firing younger brother's glaze, when brother's glaze reaches capacity Cracking Temperature, the mobility of younger brother's glaze becomes large, cause traditional celadon artwork seldom to occur that brother's glaze is combined situation about firing with younger brother's glaze, especially vessel inside adopts brother glaze, outsidely adopts that younger brother's glaze or vessel inside adopt younger brother's glaze, the outside artwork of this inside and outside different glaze of brother's glaze that adopts also does not have technique great master to attempt.The present invention is by changing the glaze formula of brother's glaze and younger brother's glaze, reduce the lowest limit temperature that brother's glaze hacks, improve the highest threshold temperature that younger brother's glaze is fired, the firing temperature of the firing temperature of brother's glaze and younger brother's glaze is made to have had overlapping interval, while guarantee brother glaze hacks, the mobility of younger brother's glaze is relatively stable, lays the foundation for brother's glaze is combined to fire with younger brother's glaze.

Description

The celadon sintering technology method that brother's glaze combines with younger brother's glaze
Technical field
The present invention relates to celadon industrial art field, particularly relate to and a kind of traditional dragon's fountain brother glaze is combined with younger brother's glaze the processing method fired.
Background technology
Longquan celadon starts from Shanxi generation, begins to take shape during the Northern Song Dynasty, enters the period of great prosperity when Song Yuan, porcelain making scale is unique, skill reaches the peak of perfection, and the plum green in Di kiln, lavender grey glaze reach the tidemark of celadon glaze colours, and therefore dragon's fountain becomes famous Ci Ye center, the whole nation.Longquan celadon product has two kinds: one is white tire and cinnabar tire celadon, famous " Di kiln " or " Longqun Cave ", and another kind is the black tire celadon of crackle glaze, claims " brother's kiln ".
Di kiln celadon glaze layer is plump, and glaze colours green grass or young crops is green, and gloss is soft, sparkling and crystal-clear moist, surpasses emerald.There is the different glaze colours such as plum green, pale blue, bluish white, yellowish pea green glaze, light orchid, sallow." brother's kiln " celadon with magnificent, ancient line sheet of falling forward for decorative means, it is as broken in cracked ice pattern, crab claw line, ox hair line, flowing water line, roe line, meals blood line, hundred rubbish etc. that its glaze layer is full, shining and clean in addition, have the title of " purple mouth iron foot ", set each other off with glaze paint line sheet, more aobvious Gu is fallen forward, elegance, treasure in profound title porcelain.
Geware glaze matter is purely dense, very not lustrous and transparent, has bubble in glaze more, as pearl is dimly visible, therefore common name " poly-foam collects together pearl ".Accumulate in the precious light of glaze colours, moist as crisp.Line sheet is varied, be referred to as with track yellow eel line, black blue line, brother's vitreous enamel key character be crackle glaze, this is a kind of natural cracking phenomenon occurred in glaze paint.Cracking is the defect during porcelain is fired originally, and people had grasped the rule of cracking afterwards, allowed it produce consciously and hacked, thus create a kind of aesthetic feeling of uniqueness.Song dynasty brother vitreous enamel enamel jade-like stone profit, entire body glaze paint is interweaved by two kinds of slightly dark or carefully shallow streaklines and cuts, and term is called " cracked ice pattern ", is commonly called as " spun gold iron wire ".Brother's kiln china clay weak pulse is purple, and matter is thin, has glaze grey, cream-coloured, pale blue look three kinds of enamel coloured silks, the full crackle in surface.Because soil property iron-holder is higher, reduce when burning embryo, porcelain embryo is purple black iron look, and the bottom that porcelain is not coated with glaze manifests the original iron look of porcelain embryo, cries " iron foot ", and the thinner oral area of muffle painting is purple, cries " purple mouth ", is commonly called as " purple mouth iron foot ".In general, not hack greatly person rather precious for the little person of hacking of large device and little device.Because brother's vitreous enamel is careful, exquisite, there is imitation in each generation to it later.Particularly arrive the Qing Dynasty, have also appeared the climax of imitative brother's vitreous enamel.Arrived Qing Dynasty's later stage, brother's glaze is significantly not as clear early stage, and color is more and more darker, and hack more and more in small, broken bits, rough uneven glaze even appears in glaze paint, and tire matter also becomes loose.Pale yellow line, roe line; Guiding principle shape line, plum blossom line, line in small, broken bits, size check, cracked ice pattern etc. have been referred to as with line shape, total by name hundred extremely broken.
Brother's kiln and the maximum difference of Di kiln are that brother's kiln hacks porcelain, and namely there is the lines of picture slight crack on celadon surface, this line is because the carcass coefficient of expansion is greater than the coefficient of expansion of glaze, occurring when firing cools, is originally a kind of defect, but produces the special decorative effect of " spun gold iron wire ".Di kiln is then do not hack porcelain.
Because the coefficient of expansion difference of brother's glaze and younger brother's glaze is larger, brother's glaze cracking ultimate temperature is higher than the highest threshold temperature firing younger brother's glaze, when brother's glaze reaches capacity Cracking Temperature, the mobility of younger brother's glaze becomes large, cause, traditional celadon artwork seldom occurs that brother's glaze is combined situation about firing with younger brother's glaze, and especially vessel inside adopts brother's glaze, outside adopts younger brother's glaze or vessel inside adopts younger brother's glaze, the artwork of this inside and outside different glaze of outside employing brother glaze does not also have technique great master to attempt.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of sintering technology method firing the inner glaze different from outside of vessel.
In order to solve the problems of the technologies described above, the technical solution used in the present invention is as follows: a kind of celadon sintering technology method that brother's glaze combines with younger brother's glaze, comprises following processing step:
(1) base: the base substrate making vessel according to demand;
(2) brushing stopper line: at the vessel base substrate opening part brushing stopper line of drying, the main component of its stopper line is Zijin soil;
(3) biscuiting: by brushing stopper line and dried base substrate is placed in kiln biscuiting, biscuiting temperature is 780 ~ 820 DEG C, and the biscuiting time is 5 ~ 8h, naturally cools to room temperature after biscuiting completes;
(4) glazing: first, carries out glazing operation to the inside of vessel base substrate, carries out drying after glazing completes; Secondly, carry out glazing operation to the outside of vessel base substrate, carry out drying after glazing completes, its base substrate outside uses the glaze inner different from base substrate, and when base substrate inside uses brother's glaze, base substrate outside uses younger brother's glaze; When base substrate inside uses younger brother's glaze, base substrate outside uses brother's glaze; Again, carry out glaze spraying inside and outside the base substrate also dry to overall glazing, its glaze spraying pass is 2 ~ 3 times simultaneously; Finally, glaze is picked to the blocked up place of base substrate glazing.
(5) glaze firing: base substrate loading of kiln glazing completed, carries out glaze firing; Its glaze firing comprises drying, oxidation, reduction, one-tenth porcelain, insulation double teacher successively, and at its drying stage, kiln temperature slowly rises, wicket offers the gap for moisture evaporation effusion in base substrate, through 2 ~ 3 hours, close wicket when temperature reaches 300 ~ 400 DEG C, continue heat temperature raising;
At its oxidation stage, with 4 ~ 5 hours, kiln temperature is promoted to 950 DEG C, makes base substrate obtain fully being oxidized, then using about 1 hours slowly, make kiln temperature rise to 980 DEG C and carry out transition insulation;
At its reduction phase, from 980 DEG C, carry out strong firing with reductive flame, heat-up rate controls at 1 DEG C ~ 1.5 DEG C/min, and kiln temperature rises to 1250 DEG C from 980 DEG C, and gaseous-pressure is enlarged to 0.02 ~ 0.05Mpa, carries out the strong reduction reaction of 3 ~ 4 hours;
Become the porcelain stage at it, turn gaseous-pressure to 0.005 ~ 0.02Mpa down, reduce reducing atmosphere, within 2 hours, cellar for storing things temperature is raised to 1280 DEG C from 1250 DEG C;
At its holding stage, keep kiln temperature flame-out after 20 ~ 30 minutes between 1280 DEG C ~ 1290 DEG C;
(6) cool: after glaze firing completes, naturally cool to after room temperature until kiln temperature and open kiln, take out finished product.
Further, adopt taxi driver brother's glaze in described step (4), calculate by mass percentage, be made up of following component and content:
Ridge root china clay: 52% ~ 57%;
Wingdale: 9.2% ~ 10%;
Wood Mount Tai mouth Zijin soil: 1.5% ~ 2.5%;
Eight all fluorites: 4% ~ 4.5%;
Grain ash: 17% ~ 19%;
Quartz: 5% ~ 6%;
Feldspar: 6% ~ 7%;
The younger brother's glaze adopted in described step (4) is lavender grey glaze or plum green, and described lavender grey glaze is calculated by mass percentage, is made up of following component and content:
Dayao china clay: 25% ~ 30%;
Ridge root china clay: 23% ~ 26%;
Wingdale: 15.5% ~ 16.5%;
High border sand Zijin soil: 8.5% ~ 9.5%;
Grain ash: 22% ~ 24%;
Described plum green is calculated by mass percentage, is made up of following component and content:
Dayao china clay: 19% ~ 21%;
Ridge root china clay: 25% ~ 28%;
Wingdale: 15.5% ~ 16.5%;
High border sand Zijin soil: 14.5% ~ 15.5%;
Grain ash: 22% ~ 24%.
Further, the dust of surfaces externally and internally before glazing takes place, is first processed by air pump and wet sponge by its vessel base substrate.
Further, before the outside glazing of its vessel base substrate, near the position of bottom, even swabbing process is carried out to its base substrate outside surface.
Further, before the outside glazing of its vessel base substrate, near the position of bottom, even swabbing process is carried out to its base substrate outside surface.
The glaze formula of brother's glaze of the present invention and younger brother's glaze, which reduce the lowest limit temperature that brother's glaze hacks, improve the highest threshold temperature that younger brother's glaze is fired, the firing temperature of the firing temperature of brother's glaze and younger brother's glaze is made to have had overlapping interval, while guarantee brother glaze hacks, the mobility of younger brother's glaze is relatively stable, lays the foundation for brother's glaze is combined to fire with younger brother's glaze.Brother's glaze of the present invention is used to be combined with younger brother's glaze the celadon product fired, overturned the tradition that traditional celadon product same glaze is fired, the glaze that especially brother's glaze is different from this limit of younger brother's glaze firing temperature combines, in celadon field, start the beginning, there is great historic significance.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.It should be noted that, each raw material in the glaze formula related in the present invention, the place of production is Zhejiang Province's Longquan City, and its title and composition, for its those skilled in the relevant art, are all clear and definite.
In Jiangxi Science technology press publishes, and " pottery 300 is asked " that Pan Zhaohong writes has included the glaze formula of Zhejiang Province's Longquan City, and its Geware glaze by mass percentage, comprises following component:
Ridge root china clay: 64.15%;
Wingdale: 8.95%;
Wood Mount Tai mouth Zijin soil: 1.88%;
Eight all fluorites: 4.95%;
Grain ash: 20.07%.
Its lavender grey glaze by mass percentage, comprises following component:
Dayao china clay: 26.3%;
Ridge root china clay: 24.9%;
Wingdale: 18.7%;
High border sand Zijin soil: 8.9%;
Grain ash: 21.2%.
Its plum green by mass percentage, comprises following component:
Dayao china clay: 18.3%;
Ridge root china clay: 26.5%;
Wingdale: 18.8%;
High border sand Zijin soil: 14.9%;
Grain ash: 21.6%.
Above-mentioned lavender grey glaze and plum green are traditional Di kiln glaze.Collect taxi driver brother's glaze in this book and younger brother's glaze is traditional glaze formula, its firing temperature is generally, brother's glaze: 1290 DEG C ~ 1320 DEG C, younger brother's glaze: 1270 DEG C ~ 1280 DEG C.As mentioned above, the minimum of its brother's glaze hacks the highest threshold temperature of temperature higher than younger brother's glaze, when reach brother's glaze hack temperature time, the mobility of younger brother's glaze is excessive, and therefore, traditional taxi driver brother's glaze and younger brother's glaze cannot be fired simultaneously.
In order to solve the problem that above-mentioned brother's glaze and younger brother's glaze cannot be fired simultaneously, the formula of the present invention to brother's glaze and younger brother's glaze adjusts.
Its brother's glaze, calculates by mass percentage, is made up of following component and content:
Ridge root china clay: 52% ~ 57%;
Wingdale: 9.2% ~ 10%;
Wood Mount Tai mouth Zijin soil: 1.5% ~ 2.5%;
Eight all fluorites: 4% ~ 4.5%;
Grain ash: 17% ~ 19%;
Quartz: 5% ~ 6%;
Feldspar: 6% ~ 7%.
Compared with above-mentioned brother's glaze formula includes taxi driver brother's glaze formula with " pottery 300 is asked ", the content of Wingdale increases to some extent, and add quartz and feldspar, for the technician in celadon field, Wingdale, feldspar and quartz, in glaze and blank batching, play the effect of solvent, the increase of its content, the effect played adds mobility, reduces the ultimate temperature that brother's glaze hacks.Improveing taxi driver brother's glaze firing temperature through the applicant is 1280 DEG C ~ 1310 DEG C.
Its younger brother's glaze comprises lavender grey glaze and plum green, and its lavender grey glaze is calculated by mass percentage, is made up of following component and content:
Dayao china clay: 25% ~ 30%;
Ridge root china clay: 23% ~ 26%;
Wingdale: 15.5% ~ 16.5%;
High border sand Zijin soil: 8.5% ~ 9.5%;
Grain ash: 22% ~ 24%;
Its plum green is calculated by mass percentage, is made up of following component and content:
Dayao china clay: 19% ~ 21%;
Ridge root china clay: 25% ~ 28%;
Wingdale: 15.5% ~ 16.5%;
High border sand Zijin soil: 14.5% ~ 15.5%;
Grain ash: 22% ~ 24%.
Compared with younger brother's glaze formula that the formula of above-mentioned younger brother's glaze and " pottery 300 is asked " are included, mainly reduce the limestone content as solvent, the stability of glaze is increased, mobility reduces, corresponding firing temperature rising.Improved younger brother's glaze, its firing temperature is: 1280 DEG C ~ 1290 DEG C.
After to improvement, to fire temperature analysis known for taxi driver brother's glaze and younger brother's glaze, and it has an overlapping temperature range, and 1280 DEG C ~ 1290 DEG C.Therefore, as long as temperature controlled enough accurate, its improve after taxi driver brother's glaze and younger brother's glaze have can with the basis of klining, also with regard to for use different glaze to lay the foundation inside and outside same vessel.
In the present embodiment, the celadon sintering technology method that its brother's glaze combines with younger brother's glaze, comprises following processing step:
(1) base: the base substrate making vessel according to demand.
(2) brushing stopper line: at the vessel base substrate opening part brushing stopper line of drying, for brother's glaze and younger brother's glaze being separated, prevents mixing, and the main component of its stopper line is Zijin soil.
(3) biscuiting: by brushing stopper line and dried base substrate is placed in kiln biscuiting, biscuiting temperature is 780 ~ 820 DEG C, the biscuiting time is 5 ~ 8h, naturally cools to room temperature after biscuiting completes, to the base substrate air pump of its biscuiting and wet sponge by clean for the dust process of surfaces externally and internally.
(4) glazing: first, carries out glazing operation to the inside of vessel base substrate, carries out drying after glazing completes; Secondly, glazing operation is carried out to the outside of vessel base substrate, after glazing completes, carries out drying, it should be noted that, on its outer before glaze, near the position of bottom, even swabbing process is carried out to its base substrate outside surface, after preventing glaze, toward current downflow in sintering procedure.
Its base substrate outside uses the glaze inner different from base substrate, and when base substrate inside uses brother's glaze, base substrate outside uses younger brother's glaze; When base substrate inside uses younger brother's glaze, base substrate outside uses brother's glaze; Again, carry out glaze spraying inside and outside the base substrate also dry to overall glazing, its glaze spraying pass is 2 ~ 3 times simultaneously; Finally, glaze is picked to the blocked up place of base substrate glazing.
In the present embodiment, its brother's glaze is calculated by mass percentage, is made up of following component and content:
Ridge root china clay: 55%;
Wingdale: 9.6%;
Wood Mount Tai mouth Zijin soil: 1.9%;
Eight all fluorites: 4.2%;
Grain ash: 17.6%;
Quartz: 5.4%;
Feldspar: 6.3%.
During its younger brother's glaze selection lavender grey glaze, calculate by mass percentage, be made up of following component and content:
Dayao china clay: 27.7%;
Ridge root china clay: 24.9%;
Wingdale: 15.9%;
High border sand Zijin soil: 8.9%;
Grain ash: 22.6%.
During its younger brother's glaze selection plum green, calculate by mass percentage, be made up of following component and content:
Dayao china clay: 19.8%;
Ridge root china clay: 26.5%;
Wingdale: 16%;
High border sand Zijin soil: 14.9%;
Grain ash: 22.8.
(5) glaze firing: base substrate loading of kiln glazing completed, carries out glaze firing; Its glaze firing comprises drying, oxidation, reduction, one-tenth porcelain, insulation double teacher successively, and at its drying stage, kiln temperature slowly rises, wicket offers the gap for moisture evaporation effusion in base substrate, through 2 ~ 3 hours, close wicket when temperature reaches 300 ~ 400 DEG C, continue heat temperature raising;
At its oxidation stage, with 4 ~ 5 hours, kiln temperature is promoted to 950 DEG C, makes base substrate obtain fully being oxidized, then using about 1 hours slowly, make kiln temperature rise to 980 DEG C and carry out transition insulation;
At its reduction phase, from 980 DEG C, carry out strong firing with reductive flame, heat-up rate controls at 1 DEG C ~ 1.5 DEG C/min, and kiln temperature rises to 1250 DEG C from 980 DEG C, and gaseous-pressure is enlarged to 0.02 ~ 0.05Mpa, carries out the strong reduction reaction of 3 ~ 4 hours;
Become the porcelain stage at it, turn gaseous-pressure to 0.005 ~ 0.02Mpa down, reduce reducing atmosphere, within 2 hours, cellar for storing things temperature is raised to 1280 DEG C from 1250 DEG C;
At its holding stage, keep kiln temperature flame-out after 20 ~ 30 minutes between 1280 DEG C ~ 1290 DEG C.
(6) cool: after glaze firing completes, naturally cool to after room temperature until kiln temperature and open kiln, take out finished product.
The glaze formula of brother's glaze of the present invention and younger brother's glaze, which reduce the lowest limit temperature that brother's glaze hacks, improve the highest threshold temperature that younger brother's glaze is fired, the firing temperature of the firing temperature of brother's glaze and younger brother's glaze is made to have had overlapping interval, while guarantee brother glaze hacks, the mobility of younger brother's glaze is relatively stable, lays the foundation for brother's glaze is combined to fire with younger brother's glaze.Brother's glaze of the present invention is used to be combined with younger brother's glaze the celadon product fired, overturned the tradition that traditional celadon product same glaze is fired, the glaze that especially brother's glaze is different from this limit of younger brother's glaze firing temperature combines, in celadon field, start the beginning, there is great historic significance.

Claims (5)

1. the celadon sintering technology method that combines with younger brother's glaze of brother's glaze, is characterized in that, comprise following processing step:
(1) base: the base substrate making vessel according to demand;
(2) brushing stopper line: at the vessel base substrate opening part brushing stopper line of drying, the main component of its stopper line is Zijin soil;
(3) biscuiting: by brushing stopper line and dried base substrate is placed in kiln biscuiting, biscuiting temperature is 780 ~ 820 DEG C, and the biscuiting time is 5 ~ 8h, naturally cools to room temperature after biscuiting completes;
(4) glazing: first, carries out glazing operation to the inside of vessel base substrate, carries out drying after glazing completes; Secondly, carry out glazing operation to the outside of vessel base substrate, carry out drying after glazing completes, its base substrate outside uses the glaze inner different from base substrate, and when base substrate inside uses brother's glaze, base substrate outside uses younger brother's glaze; When base substrate inside uses younger brother's glaze, base substrate outside uses brother's glaze; Again, carry out glaze spraying inside and outside the base substrate also dry to overall glazing, its glaze spraying pass is 2 ~ 3 times simultaneously; Finally, glaze is picked to the blocked up place of base substrate glazing;
The firing temperature of described brother's glaze is 1280 DEG C ~ 1310 DEG C, and the firing temperature of described younger brother's glaze is 1280 DEG C ~ 1290 DEG C;
(5) glaze firing: base substrate loading of kiln glazing completed, carries out glaze firing; Its glaze firing comprises drying, oxidation, reduction, one-tenth porcelain, insulation double teacher successively, and at its drying stage, kiln temperature slowly rises, wicket offers the gap for moisture evaporation effusion in base substrate, through 2 ~ 3 hours, close wicket when temperature reaches 300 ~ 400 DEG C, continue heat temperature raising;
At its oxidation stage, with 4 ~ 5 hours, kiln temperature is promoted to 950 DEG C, makes base substrate obtain fully being oxidized, then using about 1 hours slowly, make kiln temperature rise to 980 DEG C and carry out transition insulation;
At its reduction phase, from 980 DEG C, carry out strong firing with reductive flame, heat-up rate controls at 1 DEG C ~ 1.5 DEG C/min, and kiln temperature rises to 1250 DEG C from 980 DEG C, and gaseous-pressure is enlarged to 0.02 ~ 0.05MPa, carries out the strong reduction reaction of 3 ~ 4 hours;
Become the porcelain stage at it, turn gaseous-pressure to 0.005 ~ 0.02MPa down, reduce reducing atmosphere, within 2 hours, kiln temperature is raised to 1280 DEG C from 1250 DEG C;
At its holding stage, keep kiln temperature flame-out after 20 ~ 30 minutes between 1280 DEG C ~ 1290 DEG C;
(6) cool: after glaze firing completes, naturally cool to after room temperature until kiln temperature and open kiln, take out finished product.
2. according to processing method according to claim 1, it is characterized in that, adopt taxi driver brother's glaze in described step (4), calculate by mass percentage, be made up of following component and content:
Ridge root china clay: 52% ~ 57%;
Wingdale: 9.2% ~ 10%;
Wood Mount Tai mouth Zijin soil: 1.5% ~ 2.5%;
Eight all fluorites: 4% ~ 4.5%;
Grain ash: 17% ~ 19%;
Quartz: 5% ~ 6%;
Feldspar: 6% ~ 7%;
The younger brother's glaze adopted in described step (4) is lavender grey glaze or plum green, and described lavender grey glaze is calculated by mass percentage, is made up of following component and content:
Dayao china clay: 25% ~ 30%;
Ridge root china clay: 23% ~ 26%;
Wingdale: 15.5% ~ 16.5%;
High border sand Zijin soil: 8.5% ~ 9.5%;
Grain ash: 22% ~ 24%;
Described plum green is calculated by mass percentage, is made up of following component and content:
Dayao china clay: 19% ~ 21%;
Ridge root china clay: 25% ~ 28%;
Wingdale: 15.5% ~ 16.5%;
High border sand Zijin soil: 14.5% ~ 15.5%;
Grain ash: 22% ~ 24%.
3. according to the processing method described in claim 1 or 2, it is characterized in that, the dust of surfaces externally and internally before glazing takes place, is first processed by air pump and wet sponge by its vessel base substrate.
4. according to the processing method described in claim 1 or 2, it is characterized in that, before the outside glazing of its vessel base substrate, near the position of bottom, even swabbing process is carried out to its base substrate outside surface.
5. according to processing method according to claim 3, it is characterized in that, before the outside glazing of its vessel base substrate, near the position of bottom, even swabbing process is carried out to its base substrate outside surface.
CN201410444480.0A 2014-09-03 2014-09-03 The celadon sintering technology method that brother's glaze combines with younger brother's glaze Active CN104193417B (en)