CN106698946A - Preparation technology of underglaze red glaze - Google Patents
Preparation technology of underglaze red glaze Download PDFInfo
- Publication number
- CN106698946A CN106698946A CN201611104274.0A CN201611104274A CN106698946A CN 106698946 A CN106698946 A CN 106698946A CN 201611104274 A CN201611104274 A CN 201611104274A CN 106698946 A CN106698946 A CN 106698946A
- Authority
- CN
- China
- Prior art keywords
- glaze
- preparation technology
- red
- stone
- underglaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation technology of underglaze red glaze. The underglaze red glaze comprises the following materials by mass percentage: 0.42% of copper flower, 74.97% of Chenwan glaze stone, 1.67% of tin frit, 1.19% of bryozoatum, 0.81% of ishiki, 0.26% of gypsum rubrum, 14.28% of glaze ash, 1.21% of flowery pumice and 0.40% of lump asteriated stone. The preparation technology comprises the steps of applying a layer of bluish-white glaze on a blank, decorating a pattern with a underglaze red pigment, covering a layer of bluish-white glaze, and then performing firing with a reduction flame. The preparation technology has the benefits that glaze allocation is fine and accurate; and the attractiveness and an artistic value of a ceramic firing product are improved and increased.
Description
Technical field
The present invention relates to a kind of preparation technology of glaze paint, a kind of preparation technology of under-glaze red glaze paint is specifically related to, belonged to
Ceramic sintering formula class field.
Background technology
At present, China has become Production of Ceramics state maximum in the world, and ceramic is also the master that China's export is earned foreign exchange
Want one of product.The Ceramic Export market of China is concentrated mainly on the U.S., Japan, South Korea, European Union etc..China is skill in the world
Art Production of Ceramics manufactures the first big country, but is not art pottery power, and most domestic enterprise is famous foreign ceramic brand
OEM the or ODM foundry vendors of enterprise, product is mainly based on outlet.At present the whole nation formed Jiangxi Jing Dezhen, Hunan Liling,
Several big art pottery producing regions such as Guangdong Chaozhou, Jiangsu, Tangshan and Handan, Shandong Zibo.Global art pottery in 2011
Porcelain yield is 7,000,000,000, and Chinese yield is 59.4 hundred million, and 47% art pottery is used to export, and is that generally acknowledged yield is maximum in the world
Big export country.Chinese light industry handicraft chamber of import and export trade ceramics branch in August, 2011 part announce " first half of the year in 2011 is complete
50 before outlet art pottery product enterprise of state " in ranking, several big producing region Jun You enterprises are on the list, and 23, Guangdong enterprise is shortlisted for, and is
Most active art pottery producing region is exported, wherein Chaozhou arrogates 10.In general, art pottery industry competitive situation is just gradually
Formed, industry concentration ratio is stepped up.
Under-glaze red is the founder of China's tradition in-glaze decoration.It is to coordinate certain raw material to be milled to superfine by copper compound and draw
The colour generation under glaze.Its decorative product is equally rare with other traditional rough flambe products, in process of production, it is necessary to connect formula
Weighing, alunite barreling is thin.
In order to more competitive in the industry, it is necessary to be devoted to innovation research and development.So, how potter is improved
Skill, is the purpose of present invention research.
The content of the invention
To overcome the shortcomings of the existing technology, the present invention provides a kind of preparation technology of under-glaze red glaze paint, U.S. of product is improve
The property seen and artistic value.
To solve prior art problem, the technical solution adopted in the present invention is：
A kind of preparation technology of under-glaze red glaze paint, includes in the material of every 100 mass component：Copper spends 0.42%, Chen Wan
74.97%, tin frit 1.67%, bryozoatum 1.19%, Shi Mu 0.81%, a gypsum rubrum 0.26%, glaze lime-ash
14.28%, flower float stone 1.21%, top star stone 0.40%；During glazing, bluish white glaze together is first applied on mold, then with glaze
Red stain decorative pattern, then the bluish white glaze of lid last layer again, uses firing with reductive flame.
Further, the technique firing temperature is maintained at 1280 DEG C.
The beneficial effects of the invention are as follows：Glaze configuration is fine, accurate；Improve the aesthetic property and artistic valency of ceramic sintering product
Value.
Specific embodiment
In order that those skilled in the art can more understand technical solution of the present invention, with reference to specific embodiment to this
Invention is further analyzed.
A kind of preparation technology of under-glaze red glaze paint, includes in the material of every 100 mass component：Copper spends 0.42%, Chen Wan
74.97%, tin frit 1.67%, bryozoatum 1.19%, Shi Mu 0.81%, a gypsum rubrum 0.26%, glaze lime-ash
14.28%, flower float stone 1.21%, top star stone 0.40%；During glazing, bluish white glaze together is first applied on mold, then with glaze
Red stain decorative pattern, then the bluish white glaze of lid last layer again, uses firing with reductive flame.Technique firing temperature is maintained at 1280 DEG C.
Technique of the present invention, glaze configuration is fine, accurate；Improve the aesthetic property and artistic value of ceramic sintering product.
Technical scheme provided herein is described in detail above, embodiment used herein is to the application
Principle and implementation method be set forth, the explanation of above example is only intended to help and understands the present processes and its core
Thought is thought；Simultaneously for those of ordinary skill in the art, according to the thought of the application, in specific embodiment and model is applied
Place and will change, in sum, this specification content should not be construed as the limitation to the application.
Claims (2)
1. a kind of preparation technology of under-glaze red glaze paint, it is characterised in that include in the material of every 100 mass component：Copper is spent
0.42%, old gulf 74.97%, tin frit 1.67%, bryozoatum 1.19%, Shi Mu 0.81%, a gypsum rubrum 0.26%, glaze lime-ash
14.28%, flower float stone 1.21%, top star stone 0.40%；During glazing, bluish white glaze together is first applied on mold, then use under-glaze red color
Material decorative pattern, then the bluish white glaze of lid last layer again, uses firing with reductive flame.
2. a kind of preparation technology of the red glaze glaze paint of an ancient unit of weight according to claim 1, it is characterised in that the technique firing temperature
It is maintained at 1280 DEG C.