CN106436345B - 一种用于软质气垫粉扑的剥离革的制作方法 - Google Patents

一种用于软质气垫粉扑的剥离革的制作方法 Download PDF

Info

Publication number
CN106436345B
CN106436345B CN201611042556.2A CN201611042556A CN106436345B CN 106436345 B CN106436345 B CN 106436345B CN 201611042556 A CN201611042556 A CN 201611042556A CN 106436345 B CN106436345 B CN 106436345B
Authority
CN
China
Prior art keywords
leather
parts
powder puff
bass
air cushion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201611042556.2A
Other languages
English (en)
Other versions
CN106436345A (zh
Inventor
陈勋森
陈勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Youxi Fujian Yikang Leather Making Co Ltd
Original Assignee
Youxi Fujian Yikang Leather Making Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Youxi Fujian Yikang Leather Making Co Ltd filed Critical Youxi Fujian Yikang Leather Making Co Ltd
Priority to CN201611042556.2A priority Critical patent/CN106436345B/zh
Publication of CN106436345A publication Critical patent/CN106436345A/zh
Application granted granted Critical
Publication of CN106436345B publication Critical patent/CN106436345B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及面料生产技术领域，具体涉及一种用于软质气垫粉扑的剥离革的制作方法，其包括如下步骤：将如下质量份比的聚氨酯树脂、木质粉、白色浆、DMF、气孔调节剂及分散剂进行混合并搅拌均匀得混合物；选好合适的革基布涂刮上步骤一中得到的混合物，得湿法贝斯；涂覆离型纸后，离型纸的纹路面与湿法贝斯的涂覆面贴合，将离型纸与贝斯分离后，所得贝斯中的膜层与革基布分离得用于软质气垫粉扑的剥离革。本发明一种用于软质气垫粉扑的剥离革的制作方法所得剥离革为柔韧性好、手感柔软、厚度较薄的无基布人造革，所得剥离革用于粉扑表层，位于海绵层上，使得粉扑柔软舒适，为使用者提供更安全的化妆体验。

Description

一种用于软质气垫粉扑的剥离革的制作方法
技术领域
本发明涉及面料生产技术领域，具体涉及一种用于软质气垫粉扑的剥离革的制作方法。
背景技术
人们对开始对环境保护的逐渐重视，绿色是环境保护的代名词，意味着发展和可持续生存，也是未来社会的代名词，是希望，也是目标。正因如此，在提倡环保节能的今天，人们也开始开发出PU(聚氨酯)面料来取代动物皮革，以避免对野生动物的伤害和对自然环境的破坏。
基布层在人造革后道处理工序如揉纹过程中，可以起到定型的作用，防止人造革因外力发生变形或撕裂。但由于基布层的存在，制得的人造革柔韧性较差，手感偏硬，而且不易与其他材料复合制成人造革复合产品，容易相互剥离，因此也限制了人造革在其他领域的应用和发展。开发无基布人造革，可以有效解决上述问题，大大拓宽人造革的应用领域和产品性能。
好的妆容要用好的化妆工具来完成，而粉扑作为一种常用的化妆用具，是为化妆时的基底及定妆而服务的，常用于底妆、定妆和补妆中，目前，市面上已有的化妆用粉扑品种繁多，造型各式各样，海绵粉扑是化妆必不可少的，传统的海绵粉扑为一块海绵体，使用时，水性化妆粉底会进入海绵中间层，使粉扑一直处于湿态，容易滋生细菌，造成粉扑污染，对人体皮肤有很大的伤害；另外，多余粉底进入海绵中间层，造成粉底大量的浪费，极大的缩短了粉底的使用时间。
发明内容
本发明所要解决的技术问题是：本发明的目的在于提供一种柔韧性好、手感柔软、厚度较薄的用于软质气垫粉扑的剥离革的制作方法。
为了解决上述技术问题，本发明采用的技术方案为：一种用于软质气垫粉扑的剥离革的制作方法，其特征在于，包括如下步骤：
步骤一：将如下质量份比的聚氨酯树脂100-150份、木质粉8-10份、白色浆2-5份、DMF30-60份、气孔调节剂1-3份及分散剂2-3份进行混合并搅拌均匀得混合物；
步骤二：将革基布在质量百分数为12-25％的二甲基甲酰胺水溶液当中含浸，再经过60-120℃的热烫辊进行烫平、烘干后再涂刮上步骤一中得到的混合物，再进入质量百分数为15-30％的二甲基甲酰胺水溶液当中进行凝固，反复水洗、挤压上述革基布后，烘干、水冷却，得湿法贝斯，其中烘干温度为120℃～140℃；
步骤三：将如下质量份比的聚氯乙烯树脂100-150份、邻苯二甲酸二辛酯50-60份和热稳定剂1-2份搅拌均匀，搅拌均匀后涂覆在离型纸有纹路的一面，并烘半干，剩余含水量为50％；
步骤四：将步骤三所得离型纸的纹路面与湿法贝斯的涂覆面贴合，以130℃进行烘干，冷却；
步骤五：将离型纸与贝斯分离后，所得贝斯中的膜层与革基布分离得用于软质气垫粉扑的剥离革。
本发明有益效果如下：本发明一种用于软质气垫粉扑的剥离革的制作方法所得剥离革为柔韧性好、手感柔软、厚度较薄的无基布革，所得剥离革可用于粉扑海绵层上的表层，使得粉扑柔软舒适便于使用的同时，树脂薄膜层能有效的阻挡水性化妆粉底进入中间海绵层，从而减少细菌滋生，为使用者提供更安全的化妆体验。
具体实施方式
为详细说明本发明的技术内容、所实现目的及效果，以下结合实施方式予以说明。
本发明最关键的构思在于：本发明各原料的配比可增强所得无基布皮革的力学性能，聚氯乙烯原料可以和其他原料发生不同程度的聚合，使得结合力变强，从而提高获得的剥离革的整体的撕裂强度。
实施例1
一种用于软质气垫粉扑的剥离革的制作方法，包括如下步骤：
步骤一：将如下质量份比的聚氨酯树脂100份、木质粉10份、白色浆2份、DMF60份、气孔调节剂3份及分散剂2份进行混合并搅拌均匀得混合物；
步骤二：选好合适的革基布，然后将选好的革基布在质量百分数为12-25％的二甲基甲酰胺水溶液当中含浸，再经过60-120℃的热烫辊进行烫平、烘干后再涂刮上步骤一中得到的混合物，再进入质量百分数为15-30％的二甲基甲酰胺水溶液当中进行凝固，反复水洗、挤压上述革基布后，烘干、水冷却，得湿法贝斯，其中烘干温度为120℃～140℃；
步骤三：将如下质量份比的聚氯乙烯树脂100-150份、邻苯二甲酸二辛酯50-60份和热稳定剂1-2份搅拌均匀，搅拌均匀后涂覆在离型纸有纹路的一面，并烘半干，剩余含水量为50％；
步骤四：将步骤三所得离型纸的纹路面与湿法贝斯的涂覆面贴合，以130℃进行烘干，冷却；
步骤五：将离型纸与贝斯分离后，收卷过程中所得贝斯中的膜层与革基布分离得用于软质气垫粉扑的剥离革。
上述的用于软质气垫粉扑的剥离革的制作方法中，所述分散剂为阴离子界面活性剂，该阴离子界面活性剂为聚丙烯酰胺。所述气孔调节剂为纳米二氧化硅改性环氧树脂。所述热稳定剂为BaZn。所述革基布选用波水性能是4级、分离性面是0.15kg/cm的底布。
实施例2
一种用于软质气垫粉扑的剥离革的制作方法，包括如下步骤：
步骤一：将如下质量份比的聚氨酯树脂150份、木质粉8、白色浆5份、DMF30份、气孔调节剂1份及分散剂3份进行混合并搅拌均匀得混合物；
步骤二：选好合适的革基布，然后将选好的革基布在质量百分数为12-25％的二甲基甲酰胺水溶液当中含浸，再经过60-120℃的热烫辊进行烫平、烘干后再涂刮上步骤一中得到的混合物，再进入质量百分数为15-30％的二甲基甲酰胺水溶液当中进行凝固，反复水洗、挤压上述革基布后，烘干、水冷却，得湿法贝斯，其中烘干温度为120℃～140℃；
步骤三：将如下质量份比的聚氯乙烯树脂100-150份、邻苯二甲酸二辛酯50-60份和热稳定剂1-2份搅拌均匀，搅拌均匀后涂覆在离型纸有纹路的一面，并烘半干，剩余含水量为50％；
步骤四：将步骤三所得离型纸的纹路面与湿法贝斯的涂覆面贴合，以130℃进行烘干，冷却；
步骤五：将离型纸与贝斯分离后，收卷过程中所得贝斯中的膜层与革基布分离得用于软质气垫粉扑的剥离革。
上述的用于软质气垫粉扑的剥离革的制作方法中，所述分散剂为阴离子界面活性剂，该阴离子界面活性剂为聚丙烯酰胺。所述气孔调节剂为纳米二氧化硅改性环氧树脂。所述热稳定剂为BaZn。
上述的用于软质气垫粉扑的剥离革的制作方法中，所述分散剂为阴离子界面活性剂，该阴离子界面活性剂为聚丙烯酰胺。所述气孔调节剂为纳米二氧化硅改性环氧树脂。所述热稳定剂为BaZn。所述革基布选用波水性能是4级、分离性面是0.15kg/cm的底布。
实施例3
一种用于软质气垫粉扑的剥离革的制作方法，包括如下步骤：
步骤一：将如下质量份比的聚氨酯树脂130份、木质粉9份、白色浆3份、DMF50份、气孔调节剂2份及分散剂2份进行混合并搅拌均匀得混合物；
步骤二：选好合适的革基布，然后将选好的革基布在质量百分数为12-25％的二甲基甲酰胺水溶液当中含浸，再经过60-120℃的热烫辊进行烫平、烘干后再涂刮上步骤一中得到的混合物，再进入质量百分数为15-30％的二甲基甲酰胺水溶液当中进行凝固，反复水洗、挤压上述革基布后，烘干、水冷却，得湿法贝斯，其中烘干温度为120℃～140℃；
步骤三：将如下质量份比的聚氯乙烯树脂100-150份、邻苯二甲酸二辛酯50-60份和热稳定剂1-2份搅拌均匀，搅拌均匀后涂覆在离型纸有纹路的一面，并烘半干，剩余含水量为50％；
步骤四：将步骤三所得离型纸的纹路面与湿法贝斯的涂覆面贴合，以130℃进行烘干，冷却；
步骤五：将离型纸与贝斯分离后，收卷过程中所得贝斯中的膜层与革基布分离得用于软质气垫粉扑的剥离革。
上述的用于软质气垫粉扑的剥离革的制作方法中，所述分散剂为阴离子界面活性剂，该阴离子界面活性剂为聚丙烯酰胺。所述气孔调节剂为纳米二氧化硅改性环氧树脂。所述热稳定剂为BaZn。
综上所述本发明的用于软质气垫粉扑的剥离革的制作方法有益效果如下：本发明一种用于软质气垫粉扑的剥离革的制作方法所得剥离革为柔韧性好、手感柔软、厚度较薄的无基布人造革，所得剥离革用于粉扑表层，可按需要加工成圆形、方形、椭圆形、菱形、三角形、鹅卵形或锥形的一种使用胶水黏贴在海绵层上，使得粉扑柔软舒适，便于使用的同时，树脂薄膜层能有效的阻挡水性化妆粉底进入中间海绵层，从而减少细菌滋生，为使用者提供更安全的化妆体验。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等同变换，或直接或间接运用在相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (1)

1.一种用于软质气垫粉扑的剥离革的制作方法，其特征在于，包括如下步骤：
步骤一：将如下质量份比的聚氨酯树脂100-150份、木质粉8-10份、白色浆2-5份、DMF30-60份、气孔调节剂1-3份及分散剂2-3份进行混合并搅拌均匀得混合物；所述分散剂为为聚丙烯酰胺；所述气孔调节剂为纳米二氧化硅改性环氧树脂；
步骤二：将革基布在质量百分数为12-25％的二甲基甲酰胺水溶液当中含浸，再经过60-120℃的热烫辊进行烫平、烘干后再涂刮上步骤一中得到的混合物，再进入质量百分数为15-30％的二甲基甲酰胺水溶液当中进行凝固，反复水洗、挤压上述革基布后，烘干、水冷却，得湿法贝斯，其中烘干温度为120℃～140℃；所述革基布选用波水性能是4级、分离性面是0.15kg/cm的底布；
步骤三：将如下质量份比的聚氯乙烯树脂100-150份、邻苯二甲酸二辛酯50-60份和热稳定剂1-2份搅拌均匀，搅拌均匀后涂覆在离型纸有纹路的一面，并烘半干，剩余含水量为50％；所述热稳定剂为BaZn；
步骤四：将步骤三所得离型纸的纹路面与湿法贝斯的涂覆面贴合，以130℃进行烘干，冷却；
步骤五：将离型纸与贝斯分离后，所得贝斯中的膜层与革基布分离得用于软质气垫粉扑的剥离革。
CN201611042556.2A 2016-11-24 2016-11-24 一种用于软质气垫粉扑的剥离革的制作方法 Active CN106436345B (zh)