CN106190001A - 一种防虫鼠啃咬的聚氨酯密封用发泡胶 - Google Patents
一种防虫鼠啃咬的聚氨酯密封用发泡胶 Download PDFInfo
- Publication number
- CN106190001A CN106190001A CN201610604973.5A CN201610604973A CN106190001A CN 106190001 A CN106190001 A CN 106190001A CN 201610604973 A CN201610604973 A CN 201610604973A CN 106190001 A CN106190001 A CN 106190001A
- Authority
- CN
- China
- Prior art keywords
- foamed glue
- mus
- bites
- heated
- insect protected
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种防虫鼠啃咬的聚氨酯密封用发泡胶,由下列重量份的原料制成:二苯基甲烷二异氰酸酯150‑160、三羟基聚氧化丙烯醚100‑105、蓖麻油100‑110、丙三醇5‑6、磷酸二乙酯40‑43、1mol/L的氢氧化钠溶液适量、硅藻土13‑15、蒸馏水5‑6、三乙醇胺2‑3、二月桂酸二丁基锡3‑4、鲸蜡醇3‑4、硅油5‑6、樟脑粉2‑3、辣椒碱1‑1.2、氯氟氰菊酯杀虫剂0.5‑0.6、去离子水适量、瓜尔胶2‑3、海泡石粉4‑5。本发明产品可现场发泡,工艺简单,可用于开关柜的密封,尤其适合室外开关柜的密封,防虫防蚁,延长密封胶的使用寿命,维护机柜安全。
Description
技术领域
本发明涉及发泡胶技术领域,尤其涉及一种防虫鼠啃咬的聚氨酯密封用发泡胶。
背景技术
双组分聚氨酯胶黏剂是聚氨酯胶黏剂中最重要的一类,通常由A组分(主剂)和B组分(固化剂)组成,其中A组分为羟基组分,B组分为含游离异氰酸酯基组分,二者分开包装,可按一定比例配制使用。在我国,发泡型双组分聚氨酯胶黏剂的研究始于1995年,20世纪90年代后期逐渐投入使用。发泡型双组分聚氨酯胶黏剂具有多孔性、相对密度较低、比强度较高等特点,按照原料和配方的不同可制成普通软泡、硬泡、高回弹泡沫以及慢回弹泡沫等,现已被广泛应用于汽车、电子、机柜、过滤器、三防灯具、防爆壳体、家用电器等多个应用领域。因此,发泡型双组分聚氨酯胶黏剂的推广前景非常乐观。本发明针对其在开关柜、机柜密封等方面的应用进行研究。开关柜或者机柜等外壳的作用是避免内部设备受外界因素的干扰,但仅有外壳不足以阻挡外部风沙或电磁辐射,这时,需要密封条来增加产品整体密封性能。传统密封工艺是采用物理粘接方法将标准密封件粘接在密封位置,该方法存在生产效率低、可靠性差、不美观等诸多缺陷。
《发泡型双组分聚氨酯胶黏剂的制备》一文中以三羟基聚氧化丙烯醚、蓖麻油和二苯基甲烷二异氰酸酯为主要原料,丙三醇为扩链剂,水为发泡剂,通过合适的配比,采用预聚法合成了一种发泡型双组分聚氨酯胶黏剂,制成的发泡胶黏剂泡沫均匀细腻,拉伸剪切强度较高,综合性能较优,但其耐热性能较差,容易燃烧,用做开关柜或者机柜的密封时,不能满足使用的安全性,这就需要对其热稳定性进行加强改性,提高阻燃性能。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种防虫鼠啃咬的聚氨酯密封用发泡胶。
本发明是通过以下技术方案实现的:
一种防虫鼠啃咬的聚氨酯密封用发泡胶,由下列重量份的原料制成:二苯基甲烷二异氰酸酯150-160、三羟基聚氧化丙烯醚100-105、蓖麻油100-110、丙三醇5-6、磷酸二乙酯40-43、1mol/L的氢氧化钠溶液适量、硅藻土13-15、蒸馏水5-6、三乙醇胺2-3、二月桂酸二丁基锡3-4、鲸蜡醇3-4、硅油5-6、樟脑粉2-3、辣椒碱1-1.2、氯氟氰菊酯杀虫剂0.5-0.6、去离子水适量、瓜尔胶2-3、海泡石粉4-5。
所述一种防虫鼠啃咬的聚氨酯密封用发泡胶,由以下具体步骤制成:
(1)将三羟基聚氧化丙烯醚、蓖麻油和丙三醇倒入反应釜中,恒温水浴加热至85-90℃,以150-200转/分的速度搅拌反应60-90分钟,然后降温至40-50℃,缓慢滴加磷酸二乙酯,在30分钟内加完,滴加完毕,升温至70-75℃,反应2-3小时,待反应完毕用1mol/L的氢氧化钠溶液中和至pH为7,在55-60℃减压脱水;
(2)将海泡石粉粉碎,过300目筛,然后与瓜尔胶混合,加入去离子水,加热至50-60℃,搅拌分散30-40分钟后加入樟脑粉、辣椒碱、氯氟氰菊酯杀虫剂,继续以300-400转/分的速度搅拌10-15分钟,最后喷雾干燥,得到杀虫填料;
(3)将硅藻土烘干粉碎,过300目筛,然后与步骤(1)得到的反应产物、步骤(2)得到的杀虫填料混合,依次加入三乙醇胺、二月桂酸二丁基锡、蒸馏水以及除二苯基甲烷二异氰酸酯之外的其余剩余成分,以800-1000转/分的速度搅拌2-3分钟,得到混合料A;
(4)在发泡胶使用现场将混合料A加热至恒温30℃,然后加入二苯基甲烷二异氰酸酯,快速混合,用电动搅拌器以300-400转/分的速度进行搅拌15-20秒后,将混合料涂到工件表面,加热至25-30℃,使其自行发泡,然后表面干燥,实现现场发泡成型,得到发泡胶。
本发明的优点是:本发明通过三羟基聚氧化丙烯醚、蓖麻油与丙三醇复配,通过搅拌混合可以与B组分中游离的异氰酸酯基发生交联反应,生成稳定的体型结构;在反应体系中添加磷酸二乙酯,可以提高体系的氧指数,配合硅藻土的添加,进一步提高体系的阻燃性能,而且随着硅藻土的添加,发泡胶的泡孔变得更加紧密,降低了其导热系数,使其具有良好的隔热效果;本发明还在反应过程中添加一定量的三乙醇胺和二月桂酸二丁基锡,使其形成复合催化体系,对体系中各个反应进行催化作用从而达到平衡的发泡状态;本发明利用蒸馏水作为发泡剂,不使用有机溶剂,安全环保,可以形成外观优良,泡沫均匀细腻,黏度适中,阻燃效果优异,使用时易于涂覆,并且固化后的拉伸剪切强度较高的发泡胶。
本发明通过一定的工艺手段将樟脑酚、辣椒碱、氯氟氰菊酯杀虫剂等成分有效的吸附在海泡石粉体中,然后添加到发泡体系中,能够在体系中分散均匀,有效的提高了防虫、防蚁效果,而且增强发泡体的韧性、强度;本发明产品可现场发泡,工艺简单,可用于开关柜的密封,尤其适合室外开关柜的密封,防虫防蚁,延长密封胶的使用寿命,维护机柜安全。
具体实施方式
一种防虫鼠啃咬的聚氨酯密封用发泡胶,由下列重量份(公斤)的原料制成:二苯基甲烷二异氰酸酯150、三羟基聚氧化丙烯醚100、蓖麻油100、丙三醇5、磷酸二乙酯40、1mol/L的氢氧化钠溶液适量、硅藻土13、蒸馏水5、三乙醇胺2、二月桂酸二丁基锡3、鲸蜡醇3、硅油5、樟脑粉2、辣椒碱1、氯氟氰菊酯杀虫剂0.5、去离子水适量、瓜尔胶2、海泡石粉4。
所述一种防虫鼠啃咬的聚氨酯密封用发泡胶,由以下具体步骤制成:
(1)将三羟基聚氧化丙烯醚、蓖麻油和丙三醇倒入反应釜中,恒温水浴加热至85℃,以150转/分的速度搅拌反应60分钟,然后降温至40℃,缓慢滴加磷酸二乙酯,在30分钟内加完,滴加完毕,升温至70℃,反应2小时,待反应完毕用1mol/L的氢氧化钠溶液中和至pH为7,在55℃减压脱水;
(2)将海泡石粉粉碎,过300目筛,然后与瓜尔胶混合,加入去离子水,加热至50℃,搅拌分散30分钟后加入樟脑粉、辣椒碱、氯氟氰菊酯杀虫剂,继续以300转/分的速度搅拌10分钟,最后喷雾干燥,得到杀虫填料;
(3)将硅藻土烘干粉碎,过300目筛,然后与步骤(1)得到的反应产物、步骤(2)得到的杀虫填料混合,依次加入三乙醇胺、二月桂酸二丁基锡、蒸馏水以及除二苯基甲烷二异氰酸酯之外的其余剩余成分,以800转/分的速度搅拌2分钟,得到混合料A;
(4)在发泡胶使用现场将混合料A加热至恒温30℃,然后加入二苯基甲烷二异氰酸酯,快速混合,用电动搅拌器以300转/分的速度进行搅拌15秒后,将混合料涂到工件表面,加热至25℃,使其自行发泡,然后表面干燥,实现现场发泡成型,得到发泡胶。
本发明将混合料A与二苯基甲烷二异氰酸酯通过合适的配比通过混合搅拌,再涂到开关柜或机柜的沟槽中,经化学反应发泡、表面结皮,实现现场发泡成型;通过测试,得到表干时间27分钟,完全固化时间小于12小时;进行专项的压缩试验,测试回弹损失率符合产品要求。
Claims (2)
1.一种防虫鼠啃咬的聚氨酯密封用发泡胶,其特征在于,由下列重量份的原料制成:二苯基甲烷二异氰酸酯150-160、三羟基聚氧化丙烯醚100-105、蓖麻油100-110、丙三醇5-6、磷酸二乙酯40-43、1mol/L的氢氧化钠溶液适量、硅藻土13-15、蒸馏水5-6、三乙醇胺2-3、二月桂酸二丁基锡3-4、鲸蜡醇3-4、硅油5-6、樟脑粉2-3、辣椒碱1-1.2、氯氟氰菊酯杀虫剂0.5-0.6、去离子水适量、瓜尔胶2-3、海泡石粉4-5。
2.根据权利要求1所述一种防虫鼠啃咬的聚氨酯密封用发泡胶,其特征在于,由以下具体步骤制成:
(1)将三羟基聚氧化丙烯醚、蓖麻油和丙三醇倒入反应釜中,恒温水浴加热至85-90℃,以150-200转/分的速度搅拌反应60-90分钟,然后降温至40-50℃,缓慢滴加磷酸二乙酯,在30分钟内加完,滴加完毕,升温至70-75℃,反应2-3小时,待反应完毕用1mol/L的氢氧化钠溶液中和至pH为7,在55-60℃减压脱水;
(2)将海泡石粉粉碎,过300目筛,然后与瓜尔胶混合,加入去离子水,加热至50-60℃,搅拌分散30-40分钟后加入樟脑粉、辣椒碱、氯氟氰菊酯杀虫剂,继续以300-400转/分的速度搅拌10-15分钟,最后喷雾干燥,得到杀虫填料;
(3)将硅藻土烘干粉碎,过300目筛,然后与步骤(1)得到的反应产物、步骤(2)得到的杀虫填料混合,依次加入三乙醇胺、二月桂酸二丁基锡、蒸馏水以及除二苯基甲烷二异氰酸酯之外的其余剩余成分,以800-1000转/分的速度搅拌2-3分钟,得到混合料A;
(4)在发泡胶使用现场将混合料A加热至恒温30℃,然后加入二苯基甲烷二异氰酸酯,快速混合,用电动搅拌器以300-400转/分的速度进行搅拌15-20秒后,将混合料涂到工件表面,加热至25-30℃,使其自行发泡,然后表面干燥,实现现场发泡成型,得到发泡胶。