CN105944621B - 松香乳液专用乳化剂的制备方法 - Google Patents
松香乳液专用乳化剂的制备方法 Download PDFInfo
- Publication number
- CN105944621B CN105944621B CN201610313825.8A CN201610313825A CN105944621B CN 105944621 B CN105944621 B CN 105944621B CN 201610313825 A CN201610313825 A CN 201610313825A CN 105944621 B CN105944621 B CN 105944621B
- Authority
- CN
- China
- Prior art keywords
- parts
- trisiloxanes
- deionized water
- ethyl alcohol
- lignosulfonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种松香乳液专用乳化剂的制备方法,属于松香深加工技术领域。本发明采用以下重量份的原料:腰果酚5份~8份、聚乙醚改三硅氧烷1份~2份、乙醇6份~10份、磺化木质素0.1份~0.2份、十二烷基硫酸钠15份~25份以及电导率小于5μS/cm的去离子水10份~15份;其中,包括先将上述去离子水放入反应器中,然后调节其pH值至9,然后加入腰果酚、聚乙醚改三硅氧烷、乙醇、磺化木质素、十二烷基硫酸钠,然后先加热至80℃~95℃反应0.5小时,然后降温至55℃~65℃1小时,接着再升温至80℃~95℃反应0.5小时。本发明用于制备松香乳液,具有乳化活性高、稳定性强的优点。
Description
技术领域
本发明属于松香深加工技术领域,尤其涉及一种松香乳液专用乳化剂的制备方法。
背景技术
松香,指以松树松脂为原料,通过不同的加工方式得到的非挥发性天然树脂,它是重要的化工原料,广泛应用于肥皂、造纸、油漆、橡胶等行业。此外,松香还可以通过改性、或进行乳化制成乳液,使松香的某一方面性能得到显著的提高,从而扩大松香的应用价值。
其中,松香经过乳化制成乳液后,可用于造纸工业,填充在纤维之间,达到“上胶”或“施胶”的目的,从而增加纸张的抗水性能,防止墨水渗透、改善强度和平滑度,减少伸缩度。
松香乳液通常是通过外加乳化剂法制备而成。然而,由于现有乳化剂的乳化性能较差,导致制得的松香乳液的稳定性能有待提高。
发明内容
本发明所要解决的技术问题是提供一种松香乳液专用乳化剂的制备方法,将松香乳液专用乳化剂的制备方法应用于制备松香乳液,可解决现有松香乳液性能差的问题。
为了解决上述技术问题,本发明所采用的技术方案是:
它采用以下重量份的原料:
腰果酚5份~8份、聚乙醚改三硅氧烷1份~2份、乙醇6份~10份、磺化木质素0.1份~0.2份、十二烷基硫酸钠15份~25份以及电导率小于5μS/cm的去离子水10份~15份;
包括以下步骤:
将上述电导率小于5μS/cm的去离子水放入反应器中,然后调节其pH值至9,然后加入腰果酚、聚乙醚改三硅氧烷、乙醇、磺化木质素、十二烷基硫酸钠,并加热进行反应,制得;其中,所述加热的具体过程为:先加热至80℃~95℃反应0.5小时,然后降温至55℃~65℃1小时,接着再升温至80℃~95℃反应0.5小时。
上述技术方案中,更具体的技术方案是:腰果酚5份、聚乙醚改三硅氧烷2份、乙醇8份、磺化木质素0.15份、十二烷基硫酸钠20份以及电导率小于5μS/cm的去离子水15份;
更进一步的,腰果酚8份、聚乙醚改三硅氧烷1份、乙醇10份、磺化木质素0.1份、十二烷基硫酸钠15份以及电导率小于5μS/cm的去离子水12份;
更进一步的,腰果酚6份、聚乙醚改三硅氧烷1.5份、乙醇6份、磺化木质素0.2份、十二烷基硫酸钠25份以及电导率小于5μS/cm的去离子水10份。
由于采用上述技术方案,本发明具有如下有益效果:
本发明是通过采用腰果酚、聚乙醚改三硅氧烷、乙醇、磺化木质素、十二烷基硫酸钠以及电导率小于5μS/cm的去离子水为原料制得的,经特定的加热反应方式制得;本发明用于制备松香乳液,具有乳化活性高、稳定性强的优点。
具体实施方式
以下结合具体实例对本发明作进一步详述:
实施例1
本松香乳液专用乳化剂的制备方法包括以下步骤:
将15kg电导率小于5μS/cm的去离子水放入反应器中,然后调节其pH值至9,然后加入5kg腰果酚、2kg聚乙醚改三硅氧烷、8kg乙醇、0.15kg磺化木质素、20kg十二烷基硫酸钠,并加热进行反应,制得;其中,所述加热的具体过程为:先加热至90℃反应0.5小时,然后降温至60℃1小时,接着再升温至90℃反应0.5小时。
将本实施例制得的乳化剂用于制备松香乳液时,其用量仅为松香质量的1%,且其得到的松香乳液稳定性好,在40℃时可贮存2年。
实施例2
本松香乳液专用乳化剂的制备方法包括以下步骤:
将12kg电导率小于5μS/cm的去离子水放入反应器中,然后调节其pH值至9,然后加入8kg腰果酚、1kg聚乙醚改三硅氧烷、10kg乙醇、0.1kg磺化木质素、15kg十二烷基硫酸钠,并加热进行反应,制得;其中,所述加热的具体过程为:先加热至95℃反应0.5小时,然后降温至55℃1小时,接着再升温至95℃反应0.5小时。
将本实施例制得的乳化剂用于制备松香乳液时,其用量仅为松香质量的2%,且其得到的松香乳液稳定性好,在40℃时可贮存2年。
实施例3
本松香乳液专用乳化剂的制备方法包括以下步骤:
将10kg电导率小于5μS/cm的去离子水放入反应器中,然后调节其pH值至9,然后加入6kg腰果酚、1.5kg聚乙醚改三硅氧烷、6kg乙醇、0.2kg磺化木质素、25kg十二烷基硫酸钠,并加热进行反应,制得;其中,所述加热的具体过程为:先加热至80℃反应0.5小时,然后降温至65℃1小时,接着再升温至80℃反应0.5小时。
将本实施例制得的乳化剂用于制备松香乳液时,其用量仅为松香质量的1%,且其得到的松香乳液稳定性好,在40℃时可贮存2年。
Claims (4)
1.一种松香乳液专用乳化剂的制备方法,其特征在于:
采用以下重量份的原料:
腰果酚5份~8份、聚乙醚改三硅氧烷1份~2份、乙醇6份~10份、磺化木质素0.1份~0.2份、十二烷基硫酸钠15份~25份以及电导率小于5μS/cm的去离子水10份~15份;
包括以下步骤:
将上述电导率小于5μS/cm的去离子水放入反应器中,然后调节其pH值至9,然后加入腰果酚、聚乙醚改三硅氧烷、乙醇、磺化木质素、十二烷基硫酸钠,并加热进行反应,制得;其中,所述加热的具体过程为:先加热至80℃~95℃反应0.5小时,然后降温至55℃~65℃1小时,接着再升温至80℃~95℃反应0.5小时。
2.根据权利要求1所述的松香乳液专用乳化剂的制备方法,其特征在于:腰果酚5份、聚乙醚改三硅氧烷2份、乙醇8份、磺化木质素0.15份、十二烷基硫酸钠20份以及电导率小于5μS/cm的去离子水15份。
3.根据权利要求1所述的松香乳液专用乳化剂的制备方法,其特征在于:腰果酚8份、聚乙醚改三硅氧烷1份、乙醇10份、磺化木质素0.1份、十二烷基硫酸钠15份以及电导率小于5μS/cm的去离子水12份。
4.根据权利要求1所述的松香乳液专用乳化剂的制备方法,其特征在于:腰果酚6份、聚乙醚改三硅氧烷1.5份、乙醇6份、磺化木质素0.2份、十二烷基硫酸钠25份以及电导率小于5μS/cm的去离子水10份。