CN104788863A - 一种新型生物降解塑料膜 - Google Patents
一种新型生物降解塑料膜 Download PDFInfo
- Publication number
- CN104788863A CN104788863A CN201510146665.8A CN201510146665A CN104788863A CN 104788863 A CN104788863 A CN 104788863A CN 201510146665 A CN201510146665 A CN 201510146665A CN 104788863 A CN104788863 A CN 104788863A
- Authority
- CN
- China
- Prior art keywords
- starch
- new type
- biodegradable plastics
- plastics film
- type biodegradable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型生物降解塑料膜,由下列材料组成:聚乙烯醇、淀粉、次氯酸钠、环氧植物油、抗氧剂、热稳定剂、丙三纯、甲醛及尿素,其中各成份的重量份数比例为: 聚乙烯醇85%~95%、淀粉3.5%~5%、次氯酸钠5%~10%、环氧植物油4.5%~6.5%、抗氧剂1.5%~2.5%、热稳定剂0.8%~1.5%、丙三纯5%~8%、甲醛0.05%~0.15%、尿素2.5%~4.5%,本发明也介绍了制备新型生物降解塑料膜的方法。通过上述方式,本发明一种新型生物降解塑料膜,属于完全可降解塑料,对自然环境没有造成污染危害,同时具有耐高温的特点,在实际生活中有着广泛的应用。
Description
技术领域
本发明涉及塑料膜,特别是涉及一种新型生物降解塑料膜。
背景技术
塑料垃圾是公认的人为生产出来的非常污染环境的物质。然而,塑料的用途却特别广泛,比如塑料玩具,塑料瓶,塑料包装,塑料袋等,我们生活根本离不开塑料。
在以绿色环保为主题的当今世界,对于环保型塑料的应用也越来越多,从根本上解决白色污染的问题。
发明内容
本发明主要解决的技术问题是提供一种新型生物降解塑料膜,属于完全可降解塑料,对自然环境没有造成污染危害,同时具有耐高温的特点,在实际生活中有着广泛的应用。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种新型生物降解塑料膜,由下列材料组成:聚乙烯醇、淀粉、次氯酸钠、环氧植物油、抗氧剂、热稳定剂、丙三纯、甲醛及尿素,其中各成份的重量份数比例为: 聚乙烯醇85%~95%、淀粉3.5%~5%、次氯酸钠5%~10%、环氧植物油4.5%~6.5%、抗氧剂1.5%~2.5%、热稳定剂0.8%~1.5%、丙三纯5%~8%、甲醛0.05%~0.15%、尿素2.5%~4.5%。
在本发明一个较佳实例中,各成份的重量份数比例为: 聚乙烯醇90%~95%、淀粉4%~5%、次氯酸钠8%~10%、环氧植物油5%~6.5%、抗氧剂2%~2.5%、热稳定剂1%~1.5%、丙三纯6.5%~8%、甲醛0.08%~0.15%、尿素3%~4.5%。
在本发明一个较佳实例中,所述淀粉为马铃薯淀粉或玉米淀粉。
在本发明一个较佳实例中,所述抗氧剂为偏重亚硫酸钠。
在本发明一个较佳实例中,所述热稳定剂为羧甲基纤维素。
一种新型生物降解塑料膜的制备方法,其特征在于,包括以下步骤;
步骤一、将淀粉与水按1:2.5在45℃水浴下搅拌成混合液体,加热浓度为3.5%的氢氧化钠溶液将PH值调至8±2,间隔35~45min钟后,加入浓度为0.5%的次氯酸钠溶液进行反应,待反应结束后加入浓度为1.5%的盐酸将PH调整至6.5,加入8.5%偏重亚硫酸钠进行反应,在温度为85~90℃的烘干炉中烘干,制成改性淀粉,研磨待用;
步骤二、在100ml的水中,加入改性淀粉,然后加热至105~110℃糊化;
步骤三、待糊化25min钟后,加入质量百分比为90%的聚乙烯醇、6.5%环氧植物油、1.2%羧甲基纤维素及3.5%的尿素混合搅拌均匀;
步骤四、搅拌均匀后依次加入质量百分比为7%丙三纯,0.15%甲醛后保温45~90min钟进行反应,然后反应后的液体倒入预热的玻璃板上低温烘干。
在本发明一个较佳实例中,所述步骤一中的淀粉采用马铃薯淀粉。
本发明的有益效果是:本发明一种新型生物降解塑料膜,属于完全可降解塑料,对自然环境没有造成污染危害,同时具有耐高温的特点,在实际生活中有着广泛的应用。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
在本发明一个较佳实例中,一种新型生物降解塑料膜,由下列材料组成:聚乙烯醇、淀粉、次氯酸钠、环氧植物油、抗氧剂、热稳定剂、丙三纯、甲醛及尿素,其中各成份的重量份数比例为: 聚乙烯醇85%~95%、淀粉3.5%~5%、次氯酸钠5%~10%、环氧植物油4.5%~6.5%、抗氧剂1.5%~2.5%、热稳定剂0.8%~1.5%、丙三纯5%~8%、甲醛0.05%~0.15%、尿素2.5%~4.5%。
进一步,各成份的重量份数比例为: 聚乙烯醇90%~95%、淀粉4%~5%、次氯酸钠8%~10%、环氧植物油5%~6.5%、抗氧剂2%~2.5%、热稳定剂1%~1.5%、丙三纯6.5%~8%、甲醛0.08%~0.15%、尿素3%~4.5%。
进一步,所述淀粉为马铃薯淀粉或玉米淀粉。
进一步,所述抗氧剂为偏重亚硫酸钠。
进一步,所述热稳定剂为羧甲基纤维素。
一种新型生物降解塑料膜的制备方法,其特征在于,包括以下步骤;
步骤一、将淀粉与水按1:2.5在45℃水浴下搅拌成混合液体,加热浓度为3.5%的氢氧化钠溶液将PH值调至8±2,间隔35~45min钟后,加入浓度为0.5%的次氯酸钠溶液进行反应,待反应结束后加入浓度为1.5%的盐酸将PH调整至6.5,加入8.5%偏重亚硫酸钠进行反应,在温度为85~90℃的烘干炉中烘干,制成改性淀粉,研磨待用;
步骤二、在100ml的水中,加入改性淀粉,然后加热至105~110℃糊化;
步骤三、待糊化25min钟后,加入质量百分比为90%的聚乙烯醇、6.5%环氧植物油、1.2%羧甲基纤维素及3.5%的尿素混合搅拌均匀;
步骤四、搅拌均匀后依次加入质量百分比为7%丙三纯,0.15%甲醛后保温45~90min钟进行反应,然后反应后的液体倒入预热的玻璃板上低温烘干。
进一步,所述步骤一中的淀粉采用马铃薯淀粉。
本发明的有益效果是:本发明一种新型生物降解塑料膜,属于完全可降解塑料,对自然环境没有造成污染危害,同时具有耐高温的特点,在实际生活中有着广泛的应用。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其它相关的技术领域,均同理包括在本发明的专利保护范围。
Claims (7)
1.一种新型生物降解塑料膜,其特征在于,由下列材料组成:聚乙烯醇、淀粉、次氯酸钠、环氧植物油、抗氧剂、热稳定剂、丙三纯、甲醛及尿素,其中各成份的重量份数比例为: 聚乙烯醇85%~95%、淀粉3.5%~5%、次氯酸钠5%~10%、环氧植物油4.5%~6.5%、抗氧剂1.5%~2.5%、热稳定剂0.8%~1.5%、丙三纯5%~8%、甲醛0.05%~0.15%、尿素2.5%~4.5%。
2.根据权利要求1所述的新型生物降解塑料膜,其特征在于,各成份的重量份数比例为: 聚乙烯醇90%~95%、淀粉4%~5%、次氯酸钠8%~10%、环氧植物油5%~6.5%、抗氧剂2%~2.5%、热稳定剂1%~1.5%、丙三纯6.5%~8%、甲醛0.08%~0.15%、尿素3%~4.5%。
3.根据权利要求1所述的新型生物降解塑料膜,其特征在于,所述淀粉为马铃薯淀粉或玉米淀粉。
4.根据权利要求1所述的新型生物降解塑料膜,其特征在于,所述抗氧剂为偏重亚硫酸钠。
5.根据权利要求1所述的新型生物降解塑料膜,其特征在于,所述热稳定剂为羧甲基纤维素。
6.一种新型生物降解塑料膜的制备方法,其特征在于,包括以下步骤;
步骤一、将淀粉与水按1:2.5在45℃水浴下搅拌成混合液体,加热浓度为3.5%的氢氧化钠溶液将PH值调至8±2,间隔35~45min钟后,加入浓度为0.5%的次氯酸钠溶液进行反应,待反应结束后加入浓度为1.5%的盐酸将PH调整至6.5,加入8.5%偏重亚硫酸钠进行反应,在温度为85~90℃的烘干炉中烘干,制成改性淀粉,研磨待用;
步骤二、在100ml的水中,加入改性淀粉,然后加热至105~110℃糊化;
步骤三、待糊化25min钟后,加入质量百分比为90%的聚乙烯醇、6.5%环氧植物油、1.2%羧甲基纤维素及3.5%的尿素混合搅拌均匀;
步骤四、搅拌均匀后依次加入质量百分比为7%丙三纯,0.15%甲醛后保温45~90min钟进行反应,然后反应后的液体倒入预热的玻璃板上低温烘干。
7.根据权利要求6所述的新型生物降解塑料膜制备方法,其特征在于,所述步骤一中的淀粉采用马铃薯淀粉。