CN104761175A - 硅酸盐水泥发泡轻质隔墙板用防水增韧剂及其制备方法 - Google Patents
硅酸盐水泥发泡轻质隔墙板用防水增韧剂及其制备方法 Download PDFInfo
- Publication number
- CN104761175A CN104761175A CN201510125650.3A CN201510125650A CN104761175A CN 104761175 A CN104761175 A CN 104761175A CN 201510125650 A CN201510125650 A CN 201510125650A CN 104761175 A CN104761175 A CN 104761175A
- Authority
- CN
- China
- Prior art keywords
- unsaturated solution
- waterproof
- water
- polyvinyl alcohol
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明是一种硅酸盐水泥发泡轻质隔墙板用防水增韧剂，其特点是，包括原料重量组份的组成为：硅酸钠不饱和溶液1～5份、聚乙烯醇不饱和溶液1～5份、荷叶素不饱和溶液5～10份；并提供其制备方法。本产品具有粘着力强：用于硅酸盐水泥发泡轻质隔墙板时，对瓷砖及各种混凝土等材料均具有很强的粘合力和耐久性能及耐磨性，不吸潮、不泛霜、不返卤，绝缘、防水增韧和抗折性能好。其制备方法科学合理，易控制，成品率高，质量好。
Description
技术领域
本发明涉及建筑用墙体材料领域，具体地说，是一种硅酸盐水泥发泡轻质隔墙板用防水增韧剂及其制备方法。
背景技术
现有的各类防水剂不能用于发泡硅酸盐水泥制品。迄今未见有关防水剂用于发泡硅酸盐水泥制品的文献报道和实际应用。
发明内容
本发明的目的是，提供一种适用于硅酸盐水泥发泡轻质隔墙板用防水增韧剂；并提供科学合理，易控制，成品率高，质量好的硅酸盐水泥发泡轻质隔墙板用防水增韧剂的制备方法。
实现本发明目的之一采用的技术方案是，一种硅酸盐水泥发泡轻质隔墙板用防水增韧剂，其特征是，它包括原料重量组份的组成为：硅酸钠不饱和溶液1～5份、聚乙烯醇不饱和溶液1～5份、荷叶素不饱和溶液5～10份。
所述的硅酸钠不饱和溶液的原料重量组份的组成为：硅酸钠1份和水1份。
所述的聚乙烯醇不饱和溶液原料重量组份的组成为：聚乙烯醇1份和水32份。
所述的荷叶素不饱和溶液原料重量组份的组成为：荷叶素1份和水12份。
实现本发明目的之二采用的技术方案是，一种硅酸盐水泥发泡轻质隔墙板用防水增韧剂的制备方法，其特征是，它包括的内容有；将重量份的硅酸钠1份和水1份置于盛具内，加温60～90℃溶解，制成硅酸钠不饱和溶液待用；将重量份的聚乙烯醇1份和水32份置于盛具内，加温60～90℃溶解制成聚乙烯醇不饱和溶液待用；将重量份的荷叶素1份和水12份置于盛具内，加温60～90℃溶解制成荷叶素不饱和溶液待用；开启温控电热搅拌罐机，温控电热搅拌罐机的温度达到40℃时，将重量份的硅酸钠不饱和溶液1～5份和聚乙烯醇不饱和溶液1～5份放入温控电热搅拌罐机内，温控电热搅拌罐机的温度达到60℃时，将重量份的荷叶素不饱和溶液加入温控电热搅拌罐机内，继续加热至90℃，在连续加热的同时，搅拌30～50min，充分溶解后降温净化至常温，在温控电热搅拌罐机保持2～3h，将料从温控电热搅拌罐机放出，且通过200目过滤器进行过滤制得防水增韧剂成品。
本发明的硅酸盐水泥发泡轻质隔墙板用防水增韧剂具有的优点体现在：
1.粘着力强：硅酸盐水泥发泡轻质隔墙板对瓷砖及各种混凝土等材料均具有很强的粘合力和耐久性能及耐磨性；不吸潮、不泛霜、不返卤、不导电绝缘；碱含量低。
2.能够通过本发明的乳液其结构相似纳米级颗粒微分子与发泡水泥之间强劲的物理化学作用，抑制或减少水泥砂浆中的空隙，阻止了水分的渗透，具有很强的韧性和抗折性能；
3.在硅酸盐水泥发泡轻质隔墙板中能够形成刚韧性的防水层，具有优异抗冲击和耐磨性能，还可长期在水上漂浮不下沉；
4.具有耐酸碱性，耐腐蚀性，无毒，无氯离子、可减少混凝土的自然裂缝，能够防止由于气候等因素而造成的损伤现象；
5.在硅酸盐水泥发泡轻质隔墙板中、能在冲击荷载作用时，横跨载裂隙上的聚合物纤维，能阻止微小裂缝的产生，具有抵抗冲击力的功效。
其制备方法具有科学合理，易控制，成品率高，质量好等优点。
具体实施方式
下面利用实施例对本发明作进一步描述。
本发明的硅酸盐水泥发泡轻质隔墙板用防水增韧剂，包括原料重量组份的组成为：硅酸钠不饱和溶液1～5份、聚乙烯醇不饱和溶液1～5份、荷叶素不饱和溶液5～10份。
所述的硅酸钠不饱和溶液的原料重量组份的组成为：硅酸钠1份和水1份。
所述的聚乙烯醇不饱和溶液原料重量组份的组成为：聚乙烯醇1份和水32份。
所述的荷叶素不饱和溶液原料重量组份的组成为：荷叶素1份和水12份。
分别制备硅酸盐水泥发泡轻质隔墙板用防水增韧剂的硅酸钠不饱和溶液、聚乙烯醇不饱和溶液和荷叶素不饱和溶液。将重量份的硅酸钠1份和水1份置于盛具内，加温60～90℃溶解，制成硅酸钠不饱和溶液；将重量份的聚乙烯醇1份和水32份置于盛具内，加温60～90℃溶解制成聚乙烯醇不饱和溶液；将重量份的荷叶素1份和水12份置于盛具内，加温60～90℃溶解制成荷叶素不饱和溶液。
制备硅酸盐水泥发泡轻质隔墙板用防水增韧剂的实施例1-5各原料的重量配比见下表。重量单位：kg
| 例号 | 硅酸钠不饱和溶液 | 聚乙烯醇不饱和溶液 | 荷叶素不饱和溶液 |
| 1 | 1 | 1 | 5 |
| 2 | 2 | 2 | 6.25 |
| 3 | 3 | 3 | 7.5 |
| 4 | 4 | 4 | 8.75 |
| 5 | 5 | 5 | 10 |
以实施例3为例：制备硅酸盐水泥发泡轻质隔墙板用防水增韧剂，开启温控电热搅拌罐机，温控电热搅拌罐机的温度达到40℃时，将硅酸钠不饱和溶液3kg和聚乙烯醇不饱和溶液kg放入温控电热搅拌罐机内，温控电热搅拌罐机的温度达到60℃时，将荷叶素不饱和溶液7.5kg加入温控电热搅拌罐机内，继续加热至90℃，在连续加热的同时，搅拌30～50min，充分溶解后降温净化至常温，在温控电热搅拌罐机保持2～3h，将料从温控电热搅拌罐机放出，且通过200目过滤器进行过滤制得防水增韧剂成品。其它实施例按各自原料用量进行制备，其制备方法相同。
本发明所用的原料易得，均为市售产品。其中，硅酸钠：在制作硅酸盐水泥发泡轻质隔墙板时，用作水溶性胶黏剂，可增加韧性，可作为增黏剂或pH值调节剂；提高发泡混凝土的耐酸、耐温、密实抗渗和增加韧性；聚乙烯醇；作用为硅酸盐水泥发泡轻质隔墙板混合材料溶合、粘合、改性和防水；荷叶素是由天然植物水莲的茎、叶(荷叶),采用现代高科技生物提取术，分离出纳米生物活性功能粉体与超细旦纤维呼吸界面防水生物素，科学浓缩而成具有荷叶疏水效应的荷叶嵌合体，同时保留了催化、渗透、防腐、透气、憎水、抗紫外线等特性。
Claims (5)
1.一种硅酸盐水泥发泡轻质隔墙板用防水增韧剂，其特征是，它包括原料重量组份的组成为：硅酸钠不饱和溶液1～5份、聚乙烯醇不饱和溶液1～5份、荷叶素不饱和溶液5～10份。
2.根据权利要求1所述的硅酸盐水泥发泡轻质隔墙板用防水增韧剂，其特征是，所述的硅酸钠不饱和溶液的原料重量组份的组成为：硅酸钠1份和水1份。
3.根据权利要求1所述的硅酸盐水泥发泡轻质隔墙板用防水增韧剂，其特征是，所述的聚乙烯醇不饱和溶液原料重量组份的组成为：聚乙烯醇1份和水32份。
4.根据权利要求1所述的硅酸盐水泥发泡轻质隔墙板用防水增韧剂，其特征是，所述的荷叶素不饱和溶液原料重量组份的组成为：荷叶素1份和水12份。
5.一种硅酸盐水泥发泡轻质隔墙板用防水增韧剂的制备方法，其特征是，它包括的内容有；将重量份的硅酸钠1份和水1份置于盛具内，加温60～90℃溶解，制成硅酸钠不饱和溶液待用；将重量份的聚乙烯醇1份和水32份置于盛具内，加温60～90℃溶解制成聚乙烯醇不饱和溶液待用；将重量份的荷叶素1份和水12份置于盛具内，加温60～90℃溶解制成荷叶素不饱和溶液待用；开启温控电热搅拌罐机，温控电热搅拌罐机的温度达到40℃时，将重量份的硅酸钠不饱和溶液1～5份和聚乙烯醇不饱和溶液1～5份放入温控电热搅拌罐机内，温控电热搅拌罐机的温度达到60℃时，将重量份的荷叶素不饱和溶液加入温控电热搅拌罐机内，继续加热至90℃，在连续加热的同时，搅拌30～50min，充分溶解后降温净化至常温，在温控电热搅拌罐机保持2～3h，将料从温控电热搅拌罐机放出，且通过200目过滤器进行过滤制得防水增韧剂成品。