CN104609886A - 一种抗震加气砌块及其制备方法 - Google Patents
一种抗震加气砌块及其制备方法 Download PDFInfo
- Publication number
- CN104609886A CN104609886A CN201410792184.XA CN201410792184A CN104609886A CN 104609886 A CN104609886 A CN 104609886A CN 201410792184 A CN201410792184 A CN 201410792184A CN 104609886 A CN104609886 A CN 104609886A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminium powder
- powder
- modified aluminium
- building block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种抗震加气砌块及其制备方法,其由以下重量份的原料制成:建筑垃圾56-68、刚玉粉14-21、磷酸盐水泥23-29、硅微粉32-48、植物秸秆粉20-30、活性白土11-17、方解石24-32、草酸亚铁2-3、碳化锆3-6、聚酰胺环氧氯丙烷树脂1.5-2.5、碳酸锂3-4、纳米硼纤维4-7、改性铝粉1.5-2、聚乙烯吡咯烷酮3-5、月桂醇醚磷酸酯钾1-2。本发明加气砌块强度高,抗震性好,抗震能力达到九级以上,同时具有耐热性好,保温隔热性好,耐老化,防渗,耐水,防潮,耐腐蚀性等优点,应用前景广阔。
Description
技术领域
本发明涉及一种抗震加气砌块及其制备方法,属于建筑材料领域。
背景技术
加气砌块是以硅质材料(砂、粉煤灰及含硅尾矿等)和钙质材料(石灰、水泥等)为主要原料,掺加发气剂(铝粉),经加水搅拌,由化学反应形成孔隙,通过浇注成型、预养切割、蒸压养护等工艺过程制成的多孔硅酸盐制品。
加气砌块具有质轻、保温隔热、可加工性好、原料来源广、生产效率高、生产能耗低等特点,广泛应用于工业和民用建筑的承重或围护、填充等,受到世界各国的普遍重视,成为许多国家大力推广和发展的优选建筑材料。
随着我国建筑行业的快速发展,对加气砌块的性能要求越来越高,然而传统加气砌块存在着抗震性差的缺点,无法满足特殊场合的使用要求。
因此,急需开发一种抗震加气砌块。
发明内容
本发明的目的在于提供一种抗震加气砌块及其制备方法。
为实现上述目的,本发明采用如下技术方案:
一种抗震加气砌块,由以下重量份的原料制成:建筑垃圾56-68、刚玉粉14-21、磷酸盐水泥23-29、硅微粉32-48、植物秸秆粉20-30、活性白土11-17、方解石24-32、草酸亚铁2-3、碳化锆3-6、聚酰胺环氧氯丙烷树脂1.5-2.5、碳酸锂3-4、纳米硼纤维4-7、改性铝粉1.5-2、聚乙烯吡咯烷酮3-5、月桂醇醚磷酸酯钾1-2;
所述改性铝粉的制备方法如下:(a)、取以下重量份的原料:活性铝粉60-80、亚甲基二萘磺酸钠3-6、椰油酰胺丙基甜菜碱2-4、十四烷基二甲基氧化胺1.5-2.5、十二烷基苯磺酸钠4.5-6.5、月桂酰二乙醇胺4-7、松香酸钠5-8、鲸蜡硬脂基葡糖苷2-4、茶皂素1-3;(b)、取铝粉加适量的水,搅拌制成浓度为50-60%的浆液,然后加入亚甲基二萘磺酸钠、椰油酰胺丙基甜菜碱、十四烷基二甲基氧化胺和十二烷基苯磺酸钠,在50-80r/min的转速下搅拌1-2h,抽滤,烘干;(c)、取1/3-1/2量的上述烘干的铝粉与月桂酰二乙醇胺、茶皂素混合,在40-60r/min的转速下搅拌2-3h,得改性铝粉A;(d)、取余下的铝粉与松香酸钠、鲸蜡硬脂基葡糖苷混合,在30-50r/min的转速下搅拌3-4h,得改性铝粉B;(e)、将改性铝粉A和改性铝粉B混合均匀,即得所需的改性铝粉。
上述改性铝粉采用传统铝粉与月桂酰二乙醇胺、松香酸钠、鲸蜡硬脂基葡糖苷、茶皂素等多种原料复合,能显著增加料浆稠度,大幅度提高铝粉的发气效率,有效解决了传统铝粉发气剂发气效率低的缺点。
一种抗震加气砌块的制备方法,由下列步骤组成:
(1)取建筑垃圾、方解石混合均匀,粉碎,过150-250目筛,加水使得混合料的含水量控制在65-75%,然后加入活性白土、草酸亚铁、碳化锆,600-1200rpm研磨15-20min后加入刚玉粉、磷酸盐水泥、硅微粉、植物秸秆粉、聚酰胺环氧氯丙烷树脂、纳米硼纤维、聚乙烯吡咯烷酮,搅拌均匀后再调整混合料的含水量至80-85%,500-1000rpm搅拌3-5min;
(2)将改性铝粉、碳酸锂、月桂醇醚磷酸酯钾加入步骤(1)制得的浆料中,搅拌均匀后在70-75℃温度下发泡25-30min;
(3)将步骤(2)得到的发泡浆料注入成型模具中,自然养护35-45h,拆模,得生坯;
(4)将步骤(3)得到的生坯在温度为55-65℃、压力为0.5-1.0MPa的条件下蒸汽养护15-25h,即得加气砌块成品。
本发明的有益效果:
本发明加气砌块强度高,抗震性好,抗震能力达到九级以上,同时具有耐热性好,保温隔热性好,耐老化,防渗,耐水,防潮,耐腐蚀性等优点,应用前景广阔。
具体实施方式
一种抗震加气砌块,由以下重量(kg)的原料制成:建筑垃圾62、刚玉粉19、磷酸盐水泥27、硅微粉42、植物秸秆粉25、活性白土15、方解石28、草酸亚铁2.5、碳化锆4.5、聚酰胺环氧氯丙烷树脂2、碳酸锂3.5、纳米硼纤维6、改性铝粉1.7、聚乙烯吡咯烷酮4、月桂醇醚磷酸酯钾1.5;
所述改性铝粉的制备方法如下:(a)、取以下重量(kg)的原料:活性铝粉70、亚甲基二萘磺酸钠4、椰油酰胺丙基甜菜碱3、十四烷基二甲基氧化胺2、十二烷基苯磺酸钠5.5、月桂酰二乙醇胺5、松香酸钠7、鲸蜡硬脂基葡糖苷3、茶皂素2;(b)、取铝粉加适量的水,搅拌制成浓度为55%的浆液,然后加入亚甲基二萘磺酸钠、椰油酰胺丙基甜菜碱、十四烷基二甲基氧化胺和十二烷基苯磺酸钠,在60r/min的转速下搅拌1.5h,抽滤,烘干;(c)、取1/2量的上述烘干的铝粉与月桂酰二乙醇胺、茶皂素混合,在50r/min的转速下搅拌2.5h,得改性铝粉A;(d)、取余下的铝粉与松香酸钠、鲸蜡硬脂基葡糖苷混合,在40r/min的转速下搅拌3.5h,得改性铝粉B;(e)、将改性铝粉A和改性铝粉B混合均匀,即得所需的改性铝粉。
一种抗震加气砌块的制备方法,由下列步骤组成:
(1)取建筑垃圾、方解石混合均匀,粉碎,过200目筛,加水使得混合料的含水量控制在70%,然后加入活性白土、草酸亚铁、碳化锆,800rpm研磨18min后加入刚玉粉、磷酸盐水泥、硅微粉、植物秸秆粉、聚酰胺环氧氯丙烷树脂、纳米硼纤维、聚乙烯吡咯烷酮,搅拌均匀后再调整混合料的含水量至82%,600rpm搅拌4min;
(2)将改性铝粉、碳酸锂、月桂醇醚磷酸酯钾加入步骤(1)制得的浆料中,搅拌均匀后在75℃温度下发泡25min;
(3)将步骤(2)得到的发泡浆料注入成型模具中,自然养护40h,拆模,得生坯;
(4)将步骤(3)得到的生坯在温度为60℃、压力为0.8MPa的条件下蒸汽养护20h,即得加气砌块成品。
上述实施例制得的加气砌块的的主要性能检测见下表:
项目 | 单位 | 检测结果 |
常温耐压强度 | Mpa | 5.0 |
干燥收缩值 | mm/m | 0.6 |
导热系数 | W/m.K | 0.16 |
抗震等级 | 级 | 10 |
吸水率 | % | 1.8 |
Claims (2)
1.一种抗震加气砌块,其特征在于,由以下重量份的原料制成:建筑垃圾56-68、刚玉粉14-21、磷酸盐水泥23-29、硅微粉32-48、植物秸秆粉20-30、活性白土11-17、方解石24-32、草酸亚铁2-3、碳化锆3-6、聚酰胺环氧氯丙烷树脂1.5-2.5、碳酸锂3-4、纳米硼纤维4-7、改性铝粉1.5-2、聚乙烯吡咯烷酮3-5、月桂醇醚磷酸酯钾1-2;
所述改性铝粉的制备方法如下:(a)、取以下重量份的原料:活性铝粉60-80、亚甲基二萘磺酸钠3-6、椰油酰胺丙基甜菜碱2-4、十四烷基二甲基氧化胺1.5-2.5、十二烷基苯磺酸钠4.5-6.5、月桂酰二乙醇胺4-7、松香酸钠5-8、鲸蜡硬脂基葡糖苷2-4、茶皂素1-3;(b)、取铝粉加适量的水,搅拌制成浓度为50-60%的浆液,然后加入亚甲基二萘磺酸钠、椰油酰胺丙基甜菜碱、十四烷基二甲基氧化胺和十二烷基苯磺酸钠,在50-80r/min的转速下搅拌1-2h,抽滤,烘干;(c)、取1/3-1/2量的上述烘干的铝粉与月桂酰二乙醇胺、茶皂素混合,在40-60r/min的转速下搅拌2-3h,得改性铝粉A;(d)、取余下的铝粉与松香酸钠、鲸蜡硬脂基葡糖苷混合,在30-50r/min的转速下搅拌3-4h,得改性铝粉B;(e)、将改性铝粉A和改性铝粉B混合均匀,即得所需的改性铝粉。
2.根据权利要求1所述的抗震加气砌块的制备方法,其特征在于,由下列步骤组成:
(1)取建筑垃圾、方解石混合均匀,粉碎,过150-250目筛,加水使得混合料的含水量控制在65-75%,然后加入活性白土、草酸亚铁、碳化锆,600-1200rpm研磨15-20min后加入刚玉粉、磷酸盐水泥、硅微粉、植物秸秆粉、聚酰胺环氧氯丙烷树脂、纳米硼纤维、聚乙烯吡咯烷酮,搅拌均匀后再调整混合料的含水量至80-85%,500-1000rpm搅拌3-5min;
(2)将改性铝粉、碳酸锂、月桂醇醚磷酸酯钾加入步骤(1)制得的浆料中,搅拌均匀后在70-75℃温度下发泡25-30min;
(3)将步骤(2)得到的发泡浆料注入成型模具中,自然养护35-45h,拆模,得生坯;
(4)将步骤(3)得到的生坯在温度为55-65℃、压力为0.5-1.0MPa的条件下蒸汽养护15-25h,即得加气砌块成品。