CN103043956A - 一种利用废弃泡沫玻璃制备节能型墙体材料的方法 - Google Patents

一种利用废弃泡沫玻璃制备节能型墙体材料的方法 Download PDF

Info

Publication number
CN103043956A
CN103043956A CN201210523073XA CN201210523073A CN103043956A CN 103043956 A CN103043956 A CN 103043956A CN 201210523073X A CN201210523073X A CN 201210523073XA CN 201210523073 A CN201210523073 A CN 201210523073A CN 103043956 A CN103043956 A CN 103043956A
Authority
CN
China
Prior art keywords
foam glass
waste foam
glass
glass filler
waste
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210523073XA
Other languages
English (en)
Inventor
朱惠英
卢凌寰
张渊
宾龙
梁凯
李贞�
陶尚儒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foam Glass Co Ltd Of Guangxi Institute Of Building Research & Design
Guangxi Institute Of Building Research & Design
Original Assignee
Foam Glass Co Ltd Of Guangxi Institute Of Building Research & Design
Guangxi Institute Of Building Research & Design
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foam Glass Co Ltd Of Guangxi Institute Of Building Research & Design, Guangxi Institute Of Building Research & Design filed Critical Foam Glass Co Ltd Of Guangxi Institute Of Building Research & Design
Priority to CN201210523073XA priority Critical patent/CN103043956A/zh
Publication of CN103043956A publication Critical patent/CN103043956A/zh
Pending legal-status Critical Current

Abstract

一种利用废弃泡沫玻璃制备节能型墙体材料的方法，具体步骤如下：对废弃泡沫玻璃进行破碎，筛分出粗泡沫玻璃填料和细泡沫玻璃填料。粗泡沫玻璃填料与水灰配比为0.35~0.47、砂率=0.45~0.50、细泡沫玻璃填料掺入20%~100%、粗泡沫玻璃填料掺入20%~40%，混合后制备出废弃泡沫玻璃再生混凝土空心砌块，再进行自然养护。采用本方法制备出来的废弃泡沫玻璃混凝土空心砌块强度等级达MU5.0~MU7.5，由该砌块砌筑的墙体构件的传热系数为K≤2.0W/m2?K。解决了泡沫玻璃生产过程中产生的边角料问题，有效利用固体废弃物，推广应用新型节能型墙体材料。

Description

一种利用废弃泡沫玻璃制备节能型墙体材料的方法
 
一、技术领域
本发明涉及一种利用废弃泡沫玻璃制备节能型墙体材料的方法，具体涉及以废弃泡沫玻璃为部分骨料制备再生混凝土空心砌块的制备工艺。
二、背景技术
随着国家对建筑围护结构保温隔热材料使用性能，特别是防火性能要求的不断提高，作为无机材料的泡沫玻璃保温隔热体系的市场需求将会大幅上升，发展前景极为广阔。目前泡沫玻璃保温隔热体系在生产及加工成成品的过程中会产生大量的边角料，成为固体废弃物。这些废弃泡沫玻璃造成了极大的资源能源浪费并占用大量的堆放空间。这些废弃物如果可以进行资源化综合利用，制备成节能型的新型墙体材料，既可解决泡沫玻璃在生产过程中产生的边角料浪费问题，同时又能达到节约成本、节约资源、有效利用固体废弃物并减少固体废弃物排放，生产并推广应用新型节能型墙体材料的目的。
目前市场上普遍使用的免烧型新型节能型墙体材料主要有加气混凝土砌块、孔内插入保温板材的自隔热混凝土砌块和陶粒混凝土砌块，它们均能够满足国家、行业及广西地方建筑节能标准对建筑外墙的热工性能要求。但是加气混凝土砌块强度较低，且具有较大的吸水率，一旦墙体产生裂缝，湿气将由裂缝处进入加气混凝土砌块墙内，必将大大降低加气混凝土砌块墙体的保温隔热性能。另外加气混凝土砌块的生产成本偏高，建厂投资大，砌块强度低，使其在外墙的大面积推广使用受到影响。加气混凝土砌块、自隔热砌块和陶粒砌块目前普遍存在价格偏高的问题。
三、发明内容
本发明的目的是提供一种利用废弃泡沫玻璃制备节能型新型墙材的工艺，采用该方法能够制备出以废弃泡沫玻璃为部分骨料的再生混凝土空心砌块。
本发明通过以下技术方案达到上述目的，一种利用废弃泡沫玻璃制备节能型墙体材料的方法，具体步骤如下：
（1）采用单轴撕碎机对废弃泡沫玻璃进行破碎，筛分，得到粒径为5~20mm的粗泡沫玻璃填料和粒径为≤5mm细泡沫玻璃填料，
（2）利用水、水泥、废弃泡沫玻璃、河砂、石子、减水剂，配合比选取水灰比=0.35~0.47、砂率=0.45~0.50、细泡沫玻璃填料掺入20~100%、粗泡沫玻璃填料掺入25~40%，混合后制备出废弃泡沫玻璃再生混凝土空心砌块，
（3）对废弃泡沫玻璃再生混凝土空心砌块进行自然养护。就可以直接应用在实际工程项目中。
所述墙体材料强度等级达MU5.0~MU7.5，传热系数为K≤2.0W/m2?K。
本发明的突出优点在于：
首次提出了利用废弃泡沫玻璃制备节能型新型墙材的方法，利用废弃泡沫玻璃制备得到的节能型新型墙体材料，既具备了泡沫玻璃的保温、隔热等优点，又利用了泡沫玻璃特有的轻质特性降低墙体材料的密度。实现了废弃泡沫玻璃材料的资源化再利用，有效减少固体废弃物的排放。制备得的废弃泡沫玻璃再生混凝土空心砌块规格分别为390×240×190mm以及390×190×190mm，其强度等级可达到MU5.0~MU7.5，传热系数为K≤2.0W/m2?K。与强度等级相同的其他隔热型砌块相比，价格低廉，具有极大的市场竞争优势。
四、附图说明
图1是本发明所述的利用废弃泡沫玻璃制备节能型墙体材料的方法的工艺流程图。
五、具体实施方式
以下通过具体实施例对本发明的技术方案作进一步描述。
本发明所述的利用废弃泡沫玻璃制备节能型新型墙体材料的方法，包括以下步骤：
（1）采用单轴撕碎机对废弃泡沫玻璃进行破碎，筛分，得到粒径为5~20mm的粗泡沫玻璃填料和粒径为≤5mm细泡沫玻璃填料。
（2）利用水、水泥、泡沫玻璃、河砂、石子、减水剂，根据配合比为水灰比=0.35~0.47、砂率=0.45~0.50、细泡沫玻璃填料掺入20~40%、粗泡沫玻璃填料掺入25~100%，混合后制备出废弃泡沫玻璃再生混凝土空心砌块。
（3）对废弃泡沫玻璃再生混凝土空心砌块进行自然养护。
实施例1
（1）采用单轴撕碎机对废弃泡沫玻璃进行破碎，筛分，得到粒径为5~20mm的粗泡沫玻璃填料和粒径为≤5mm细泡沫玻璃填料。
（2）利用水、水泥、废弃泡沫玻璃、河砂、石子、减水剂，根据配合比为水灰比=0.41、砂率=0.35、细泡沫玻璃填料掺入20%、粗泡沫玻璃填料掺入25%，混合后制备出规格为390×240×190mm的废弃泡沫玻璃再生混凝土空心砌块。
（3）对废弃泡沫玻璃再生混凝土空心砌块进行自然养护。
（4）经检测，砌块的抗压强度为7.6MPa，砌体的传热系数为2.0W/m2?K。
实施例2
（1）采用单轴撕碎机对废弃泡沫玻璃进行破碎，筛分，得到粒径为5~20mm的粗泡沫玻璃填料和粒径为≤5mm细泡沫玻璃填料。
（2）利用水、水泥、废弃泡沫玻璃、河砂、石子、减水剂，根据配合比为水灰比=0.47、砂率=0.40、细泡沫玻璃填料掺入40%、粗泡沫玻璃填料掺25%，混合后制备出规格为390×190×190mm的废弃泡沫玻璃再生混凝土空心砌块。
（3）对废弃泡沫玻璃再生混凝土空心砌块进行自然养护。
（4）经检测，砌块的抗压强度为5.4MPa，砌体的传热系数为2.0W/m2?K。

Claims (2)

1.一种利用废弃泡沫玻璃制备节能型墙体材料的方法，其特征在于，该方法具体步骤如下：
（1）采用单轴撕碎机对废弃泡沫玻璃进行破碎，筛分，得到粒径为5~20mm的粗泡沫玻璃填料和粒径为≤5mm细泡沫玻璃填料，
（2）利用水、水泥、废弃泡沫玻璃、河砂、石子、减水剂，配合比选取水灰比=0.35~0.47、砂率=0.45~0.50、细泡沫玻璃填料掺入20~100%、粗泡沫玻璃填料掺入25~40%，混合后制备出废弃泡沫玻璃再生混凝土空心砌块，
（3）对废弃泡沫玻璃再生混凝土空心砌块进行自然养护。
2.如权利要求1所述的利用废弃泡沫玻璃制备节能型墙体材料的方法，其特征在于，所述墙体材料强度等级达MU5.0~MU7.5，传热系数为K≤2.0W/m2?K。
CN201210523073XA 2012-12-09 2012-12-09 一种利用废弃泡沫玻璃制备节能型墙体材料的方法 Pending CN103043956A (zh)