CN105733344A - 塑料脱漆方法 - Google Patents

塑料脱漆方法 Download PDF

Info

Publication number
CN105733344A
CN105733344A CN201610231434.1A CN201610231434A CN105733344A CN 105733344 A CN105733344 A CN 105733344A CN 201610231434 A CN201610231434 A CN 201610231434A CN 105733344 A CN105733344 A CN 105733344A
Authority
CN
China
Prior art keywords
plastics
working
plastic
depainting
steam
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610231434.1A
Other languages
English (en)
Inventor
吴春刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI LIUZHOU ZHONGJIA INTELLECTUAL PROPERTY RIGHTS SERVICE CO Ltd
Original Assignee
GUANGXI LIUZHOU ZHONGJIA INTELLECTUAL PROPERTY RIGHTS SERVICE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGXI LIUZHOU ZHONGJIA INTELLECTUAL PROPERTY RIGHTS SERVICE CO Ltd filed Critical GUANGXI LIUZHOU ZHONGJIA INTELLECTUAL PROPERTY RIGHTS SERVICE CO Ltd
Priority to CN201610231434.1A priority Critical patent/CN105733344A/zh
Publication of CN105733344A publication Critical patent/CN105733344A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种塑料脱漆方法，涉及塑料制品技术领域，该方法包括以下步骤：将待脱漆的塑料件用60～65℃的蒸汽熏蒸20～30min；在2min内将塑料件涂刷上脱漆剂，保持3～5min，再用60～65℃的蒸汽熏蒸5～8min；然后把塑料件放入水槽内，用棕刷来回刷塑料件的表面，去除漆层；高压冲洗塑料件，烘干即可。本发明解决了现有塑料脱漆方法存在脱漆效率低和对塑料本身会造成损伤的问题。

Description

塑料脱漆方法
技术领域
本发明涉及塑料制品技术领域，尤其是一种塑料脱漆方法。
背景技术
塑料因其质量轻、不会锈蚀、绝缘性好、导热性低等特点被广泛应用于生产或生活用品上。为了保护塑料件的表面，增强其表面性能，延长其使用寿命，通常会在塑料件的表面涂覆涂料，对于喷漆出现缺陷需要返工的塑料件或者回收利用的塑料制品，均需要进行脱漆处理，以进行重新涂覆或者再利用。目前的脱漆方法是依靠化学药剂来清洗去除塑料件的涂层，但是现有的塑料脱漆方法存在脱漆效率低，化学药剂使用量大，有毒有害物质多，会对塑料本身造成损伤，缩短其使用寿命的问题。
发明内容
本发明的目的是提供一种塑料脱漆方法，这种方法可以解决现有塑料脱漆方法存在脱漆效率低和对塑料本身会造成损伤的问题。
为了解决上述问题，本发明采用的技术方案是：这种塑料脱漆方法包括以下步骤：
A、将待脱漆的塑料件用60～65℃的蒸汽熏蒸20～30min；
B、在2min内将塑料件涂刷上脱漆剂，保持3～5min，再用60～65℃的蒸汽熏蒸5～8min；
C、然后把塑料件放入水槽内，用棕刷来回刷塑料件的表面，去除漆层；
D、高压冲洗塑料件，烘干即可。
上述塑料脱漆方法的技术方案中，更具体的技术方案还可以是：在步骤C中，完成步骤B的2min内将塑料件放入水温为40～55℃的水槽内。
进一步的，步骤D的水压为0.5～0.6MPa，持续3～5min。
由于采用了上述技术方案，本发明与现有技术相比具有如下有益效果：塑料件不用长时间浸泡在脱漆剂内，脱漆效率高，使用的脱漆剂用量少，不会对塑料本身造成任何损伤。
具体实施方式
下面结合实施例对本发明作进一步详述：
实施例1
本实施例的塑料脱漆方法包括以下步骤：
A、将待脱漆的塑料件用60℃的蒸汽熏蒸30min；
B、在2min内将塑料件涂刷上脱漆剂，保持3min，再用60℃的蒸汽熏蒸8min；
C、在2min内将塑料件放入水温为40℃的水槽内，用棕刷来回刷塑料件的表面，去除漆层；
D、高压冲洗塑料件，水压为0.5MPa，持续5min，烘干即可。
定时将水槽内的漆皮捞出，根据水槽内的水质，隔一段时间就换另一个干净的水槽内刷洗。
实施例2
本实施例的塑料脱漆方法包括以下步骤：
A、将待脱漆的塑料件用65℃的蒸汽熏蒸20min；
B、在2min内将塑料件涂刷上脱漆剂，保持5min，再用65℃的蒸汽熏蒸5min；
C、在2min内将塑料件放入水温为55℃的水槽内，用棕刷来回刷塑料件的表面，去除漆层；
D、高压冲洗塑料件，水压为0.6MPa，持续3min，烘干即可。
定时将水槽内的漆皮捞出，根据水槽内的水质，隔一段时间就换另一个干净的水槽内刷洗。
实施例3
本实施例的塑料脱漆方法包括以下步骤：
A、将待脱漆的塑料件用62℃的蒸汽熏蒸25min；
B、在2min内将塑料件涂刷上脱漆剂，保持4min，再用62℃的蒸汽熏蒸6min；
C、在2min内将塑料件放入水温为50℃的水槽内，用棕刷来回刷塑料件的表面，去除漆层；
D、高压冲洗塑料件，水压为0.6MPa，持续4min，烘干即可。
定时将水槽内的漆皮捞出，根据水槽内的水质，隔一段时间就换另一个干净的水槽内刷洗。

Claims (3)

1.一种塑料脱漆方法，其特征在于包括以下步骤：
A、将待脱漆的塑料件用60～65℃的蒸汽熏蒸20～30min；
B、在2min内将塑料件涂刷上脱漆剂，保持3～5min，再用60～65℃的蒸汽熏蒸5～8min；
C、然后把塑料件放入水槽内，用棕刷来回刷塑料件的表面，去除漆层；
D、高压冲洗塑料件，烘干即可。
2.根据权利要求1所述的塑料脱漆方法，其特征在于：在步骤C中，完成步骤B的2min内将塑料件放入水温为40～55℃的水槽内。
3.根据权利要求1所述的塑料脱漆方法，其特征在于：步骤D的水压为0.5～0.6MPa，持续3～5min。
CN201610231434.1A 2016-04-14 2016-04-14 塑料脱漆方法 Pending CN105733344A (zh)