CN105421118A - 一种新型环保无甲醛固色剂及其制备方法 - Google Patents
一种新型环保无甲醛固色剂及其制备方法 Download PDFInfo
- Publication number
- CN105421118A CN105421118A CN201610013958.3A CN201610013958A CN105421118A CN 105421118 A CN105421118 A CN 105421118A CN 201610013958 A CN201610013958 A CN 201610013958A CN 105421118 A CN105421118 A CN 105421118A
- Authority
- CN
- China
- Prior art keywords
- parts
- fixing agent
- novel environment
- formaldehyde
- color fixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型环保无甲醛固色剂,包括如下组分:丙烯酸;亚硫酸氢铵;环氧氯丙烷;苄基三乙基氯化铵;羟丙基三甲基氯化铵壳聚糖;多乙烯多胺树脂缩聚物;过硫酸盐;脂肪酸聚乙二醇酯;三乙烯三胺;甲基丙烯酸β-羟丁酯以及去离子水。本发明提供了一种环保无甲醛固色剂及其制备方法,用以提高织物对染料的固色效果,提高织物的色牢度,具有良好的耐水洗牢度。
Description
技术领域
本发明涉及一种印染助剂领域。更具体地说,本发明涉及一种新型环保无甲醛固色剂及其制备方法。
背景技术
纤维或织物染色后虽具有比较鲜艳的颜色,但是在洗涤时容易出现褪色和沾色现象,这是因为有些染料上的带有可溶性基团而使其牢度较差,织物一旦出现褪色不仅会使自身显得陈旧,退下来的颜色还会沾染其他织物,十分不便。
当前的织物染色主要以活性染料染色为主,由于活性染料分子结构中含有苯磺酸基、羧酸基等亲水性基团,染深色时往往会发生因浓度过高而其固着的染料量有限,使被染织物上存在大量的未固着染料,导致染色牢度不合格,湿处理牢度差,染料粒径大小也能影响染色的皂洗牢度。过去采用的固色剂大多含有甲醛或APEO,单因其固色性能优秀,且经济实惠深受众多厂家欢迎。单近年来人们的环保意识不断增强,随着一些国家或地区对甲醛含量的限制和对APEO的限量控制,使得含有甲醛或APEO的固色剂逐渐被淘汰,纺织印染助剂中甲醛、APEO的环保替代工作刻不容缓,印染厂家对环保固色剂的需求也与日俱增。
发明内容
本发明的目的是提供一种新型环保无甲醛固色剂及其制备方法,用以提高织物对染料的固色效果,提高织物的色牢度,具有良好的耐水洗牢度。
为了实现上述目的,本发明采用的技术方案如下:
一种新型环保无甲醛固色剂,包括如下重量份的组分:
丙烯酸:15~20份;亚硫酸氢铵:2~8份;环氧氯丙烷:1~5份;
苄基三乙基氯化铵:2~5份;
羟丙基三甲基氯化铵壳聚糖:8~20份;
多乙烯多胺树脂缩聚物:4~8份;过硫酸盐:0.3~4份;
脂肪酸聚乙二醇酯:1~3份;三乙烯三胺:0.5~5份;
甲基丙烯酸β-羟丁酯:2~8份;去离子水:20~60份。
优选的是,所述多乙烯多胺树脂缩聚物的缩聚率为40%。
优选的是,所述所述脂肪酸聚乙二醇酯选自月桂酸聚乙二醇酯、油酸聚乙二醇酯中的一种。
优选的是,所述过硫酸盐选自过硫酸铵、过硫酸钾或过硫酸钠中的一种。
本发明的另一个目的是提高一种环保无甲醛固色剂的制备方法,包括如下步骤:
步骤(1):按配比将丙烯酸、苄基三乙基氯化铵、亚硫酸氢铵、过硫酸盐、三乙烯三胺溶解在去离子水里,加热升温至40~60℃;滴加环氧氯丙烷,滴加时间为0.5~1小时,滴加保持温度不变继续反应0.5~1小时;
步骤(2):在步骤(1)得到的反应液中继续加入羟丙基三甲基氯化铵壳聚糖、多乙烯多胺树脂缩聚物、脂肪酸聚乙二醇酯、甲基丙烯酸β-羟丁酯、保持温度在40~60℃下2~3小时,然后加入冰醋酸条件pH为6~8,即得本发明的环保无甲醛固色剂。
本发明的有益效果:本发明固色剂不仅无甲醛,有利于环境保护,保证了人们的健康,而且固色效果好,即使容易褪色的红色,也能长时间保持其颜色的鲜艳。
具体实施方式
以下将结合具体实施例来详细说明本发明的实施方式,借此对本发明如何应用技术手段来解决技术问题,并达到技术效果的实现过程能充分理解并据以实施。
若未特别指明,实施例中所采用的技术手段为本领域技术人员所熟知的常规手段,所采用的原料也均为可商业获得的。未详细描述的各种过程和方法是本领域中公知的常规方法。
实施例1
环保无甲醛固色剂,包括如下重量份的组分:丙烯酸15份;亚硫酸氢铵2份;环氧氯丙烷1份;苄基三乙基氯化铵2份;羟丙基三甲基氯化铵壳聚糖8份;多乙烯多胺树脂缩聚物4份(缩聚率40%);过硫酸盐0.3份;脂肪酸聚乙二醇酯1份;三乙烯三胺0.5份;甲基丙烯酸β-羟丁酯2份;去离子水20份。
实施例2
环保无甲醛固色剂,包括如下重量份的组分:丙烯酸18份;亚硫酸氢铵6份;环氧氯丙烷4份;苄基三乙基氯化铵3份;羟丙基三甲基氯化铵壳聚糖10份;多乙烯多胺树脂缩聚物5份(缩聚率40%);过硫酸盐3份;脂肪酸聚乙二醇酯2份;三乙烯三胺4份;甲基丙烯酸β-羟丁酯5份;去离子水40份。
实施例3
环保无甲醛固色剂,包括如下重量份的组分:丙烯酸20份;亚硫酸氢铵8份;环氧氯丙烷5份;苄基三乙基氯化铵5份;羟丙基三甲基氯化铵壳聚糖20份;多乙烯多胺树脂缩聚物8份(缩聚率40%);过硫酸盐4份;脂肪酸聚乙二醇酯3份;三乙烯三胺5份;甲基丙烯酸β-羟丁酯8份;去离子水60份。
对比例1
环保无甲醛固色剂,包括如下重量份的组分:丙烯酸10份;亚硫酸氢铵1份;环氧氯丙烷1份;苄基三乙基氯化铵1份;羟丙基三甲基氯化铵壳聚糖4份;多乙烯多胺树脂缩聚物2份(缩聚率40%);过硫酸盐0.1份;脂肪酸聚乙二醇酯1份;三乙烯三胺0.1份;甲基丙烯酸β-羟丁酯1份;去离子水10份。
对比例2
环保无甲醛固色剂,包括如下重量份的组分:丙烯酸30份;亚硫酸氢铵10份;环氧氯丙烷6份;苄基三乙基氯化铵8份;羟丙基三甲基氯化铵壳聚糖22份;多乙烯多胺树脂缩聚物10份(缩聚率40%);过硫酸盐5份;脂肪酸聚乙二醇酯7份;三乙烯三胺8份;甲基丙烯酸β-羟丁酯9份;去离子水80份。
对比例3
环保无甲醛固色剂,包括如下重量份的组分:丙烯酸20份;亚硫酸氢铵8份;环氧氯丙烷5份;苄基三乙基氯化铵5份;羟丙基三甲基氯化铵壳聚糖20份;多乙烯多胺树脂缩聚物8份(缩聚率50%);过硫酸盐4份;脂肪酸聚乙二醇酯3份;三乙烯三胺5份;甲基丙烯酸β-羟丁酯8份;去离子水60份。
对比例4
环保无甲醛固色剂,包括如下重量份的组分:丙烯酸20份;亚硫酸氢铵8份;环氧氯丙烷5份;苄基三乙基氯化铵5份;羟丙基三甲基氯化铵壳聚糖20份;多乙烯多胺树脂缩聚物8份(缩聚率30%);过硫酸盐4份;脂肪酸聚乙二醇酯3份;三乙烯三胺5份;甲基丙烯酸β-羟丁酯8份;去离子水60份。
实施例1~3和对比例1~4的环保无甲醛固色剂的制备方法,包括如下步骤:
采用实施例1~3和对比例1~4的固色剂对织物固色,具体为:选用28tex×28tex、425×228根/10cm为织物材料,该织物用活性染料(K/S=26.4)染成黑色制品。用1.5%(owf)固色剂,在pH为3~9,温度为50℃下用浸渍法固色20min后烘干。将固色后的织物按GB/T3921-2008《纺织品色牢度试皂洗验:皂洗牢度》的方法对皂洗牢度测定;按照按GB/T3920-2008《纺织品色牢度试验:摩擦牢度》的方法对摩擦牢度测定。
表1测试结果
尽管本发明的实施方案已公开如上,但其并不仅仅限于说明书和实施方式中所列运用,它完全可以被适用于各种适合本发明的领域,对于熟悉本领域的人员而言,可容易地实现另外的修改,因此在不背离权利要求及等同范围所限定的一般概念下,本发明并不限于特定的细节。
Claims (5)
1.一种新型环保无甲醛固色剂,其特征在于,包括如下重量份的组分:
丙烯酸:15~20份;亚硫酸氢铵:2~8份;环氧氯丙烷:1~5份;
苄基三乙基氯化铵:2~5份;
羟丙基三甲基氯化铵壳聚糖:8~20份;
多乙烯多胺树脂缩聚物:4~8份;过硫酸盐:0.3~4份;
脂肪酸聚乙二醇酯:1~3份;三乙烯三胺:0.5~5份;
甲基丙烯酸β-羟丁酯:2~8份;去离子水:20~60份。
2.如权利要求1所述的新型环保无甲醛固色剂,其特征在于,所述多乙烯多胺树脂缩聚物的缩聚率为40%。
3.如权利要求1所述的新型环保无甲醛固色剂,其特征在于,所述所述脂肪酸聚乙二醇酯选自月桂酸聚乙二醇酯、油酸聚乙二醇酯中的一种。
4.如权利要求1所述的新型环保无甲醛固色剂,其特征在于,所述过硫酸盐选自过硫酸铵、过硫酸钾或过硫酸钠中的一种。
5.一种如权利要求1~%任一项所述的新型环保无甲醛固色剂的制备方法,其特征在于,包括如下步骤:
步骤(1):按配比将丙烯酸、苄基三乙基氯化铵、亚硫酸氢铵、过硫酸盐、三乙烯三胺溶解在去离子水里,加热升温至40~60℃;滴加环氧氯丙烷,滴加时间为0.5~1小时,滴加保持温度不变继续反应0.5~1小时;
步骤(2):在步骤(1)得到的反应液中继续加入羟丙基三甲基氯化铵壳聚糖、多乙烯多胺树脂缩聚物、脂肪酸聚乙二醇酯、甲基丙烯酸β-羟丁酯、保持温度在40~60℃下2~3小时,然后加入冰醋酸条件pH为6~8,即得本发明的环保无甲醛固色剂。