CN105055365A - 一种普鲁兰多糖空心胶囊的制作工艺 - Google Patents

一种普鲁兰多糖空心胶囊的制作工艺 Download PDF

Info

Publication number
CN105055365A
CN105055365A CN201510466717.XA CN201510466717A CN105055365A CN 105055365 A CN105055365 A CN 105055365A CN 201510466717 A CN201510466717 A CN 201510466717A CN 105055365 A CN105055365 A CN 105055365A
Authority
CN
China
Prior art keywords
pullulan
pulullan polysaccharide
liquor
celsius
glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510466717.XA
Other languages
English (en)
Other versions
CN105055365B (zh
Inventor
刘百平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi Jiayuan Bioengineering Co Ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510466717.XA priority Critical patent/CN105055365B/zh
Publication of CN105055365A publication Critical patent/CN105055365A/zh
Application granted granted Critical
Publication of CN105055365B publication Critical patent/CN105055365B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种普鲁兰多糖空心胶囊的制作工艺,其特征是:工艺步骤为:1)选择粘度为3~15厘泊的普鲁兰多糖,加入温度为40~80摄氏度的热水配置成按重量比浓度计20~25%的普鲁兰多糖溶液,搅拌均匀、保温、静置除去气泡;2)将配置的普鲁兰多糖溶液放到空心胶囊生产线胶槽中,模具温度控制在零下40~0摄氏度之间进行蘸胶;3)摄氏零下40度至0度区间内调节定型风的温度,使普鲁兰多糖溶液形成的膜不会在模具上流淌,直至形状固定;4)干燥、切割、套合、成品入库。其优点是:生产过程中不加凝胶剂、安全性高、干燥速度快、生产效率高。

Description

一种普鲁兰多糖空心胶囊的制作工艺
技术领域
本发明涉及一种普鲁兰多糖空心胶囊的制作工艺,属于药用空心胶囊制作技术领域。
背景技术
明胶空心胶囊(Emptycapsule):由药用明胶加辅料制作而成的帽、体两节胶囊壳组成。主要用于盛装固体药物。如自制散剂、保健品、药剂等,为服用者解决了难入口、口感差的问题,真正实现了良药不再苦口。空心胶囊越来越受欢迎,首先胶囊的形状细长,易于吞服,是最受消费者欢迎的剂型;此外,胶囊能够很有效地掩盖内容物的令人不舒服的味道和气味。胶囊的尺寸有多种多样,包括00号加长、00号、0号、1号、2号、3号、4号和5号胶囊。胶囊上还可印上文字、商标和图案,呈现出独特的定制外观。
普鲁兰多糖(Pullulan)是一种由出芽短梗霉发酵所产生的类似葡聚糖、黄原胶的胞外水溶性粘质多糖。该多糖是由α—1,4糖苷键连接的麦芽三糖重复单位经α—1,6糖苷键聚合而成的直链状多糖,分子量2万~200万,聚合度100~5000。(一般商品分子量在20万左右.大约由480个麦芽三糖组成)。该多糖有两个重要的特性:结构上富有弹性,溶解度比较大。普鲁兰多糖的成膜性、阻气性、可塑性、粘性均较强,并且具有易溶于水、无毒无害、无色无味等优良特性,已广泛应用于医药、食品、轻工、化工和石油等领域。2006年5月19日.国家卫生部发布了第8号公告,普鲁兰多糖为新增四种食品添加剂产品之一,可在糖果、巧克力包衣、膜片、复合调味科和果蔬汁饮料中用作被膜剂和增稠剂。
普鲁兰多糖空心胶囊:是指使用普鲁兰多糖为主要原料生产的空心胶囊,是目前主要的植物空心胶囊之一。
现有普鲁兰多糖空心胶囊生产工艺:现有的空心胶囊的生产过程,是利用模具在胶液中蘸胶、定型、干燥、切割、套合后形成的,由于模具是桶状结构,如果胶液在模具上面不能快速定型,胶液就会流淌,导致生产失败。
传统的明胶空心胶囊使用的明胶本身具有凝胶的特性。也就是说明胶胶液在40摄氏度以下的时候,明胶的分子链从无序状态相互缠绕,形成网状结构,从而形成有弹性不流动的类似果冻状称为凝胶,明胶胶囊就是利用明胶的这种特性生产。
普鲁兰多糖空心胶囊是目前国际上用量最大的植物来源的空心胶囊之一。普鲁兰多糖因为本身不具有凝胶型,所以在配置普鲁兰多糖胶液的时候,需要加入凝胶剂或者凝胶剂复配料。其生产流程如附图1。因为凝胶剂一般为高粘度胶体,严重影响了胶液的浓度,造成生产效率下降。凝胶剂种类众多,胶囊内容物种类更加庞大,胶凝剂和胶囊内容物可能发生反应,造成安全性的潜在风险。
名词解释:
1.蘸胶:是指将空心胶囊模具浸入胶液中,使胶液粘附在模具上成型的过程。
2.凝胶剂或者胶凝剂:是指一类在高温下为液体,在冷却后结冻成为不流动的类似果冻状的物质,在制药和食品行业主要包括明胶(Gelatin)、琼脂(Agar-Agar)、卡拉胶(Carrageenan)、结冷胶(GellanGum)等。
发明内容
本发明的目的是提供一种生产过程中不加凝胶剂、安全性高、干燥速度快、生产效率高的普鲁兰多糖空心胶囊的制作工艺。
本发明的工艺步骤如下:
1)选择粘度为50-180mm2/s的普鲁兰多糖,加入温度为40~80摄氏度的热水配置成按重量比浓度计20~25%的普鲁兰多糖溶液,搅拌均匀、保温、静置除去气泡;
2)将配置的普鲁兰多糖溶液放到空心胶囊生产线胶槽中,模具温度控制在零下40~0摄氏度之间进行蘸胶;
3)摄氏零下40度至0度区间内调节定型风的温度,使普鲁兰多糖溶液形成的膜不会在模具上流淌,直至形状固定;
4)干燥、切割、套合、成品入库。
步骤1中所述的保温温度不低于20摄氏度。
步骤2中不使用凝胶剂,利用胶液中水在0摄氏度以下结冻的原理定型。
步骤3利用水在0摄氏度以下可以直接升华的原理干燥。
本发明的优点如下:
本发明放弃了传统的生产工艺中必须利用凝胶剂使胶体凝胶的特性,而是利用水在0摄氏度以下结冻的特性,生产过程中不需要加入凝胶剂,定型的过程中利用水的升华作用,在0摄氏度以下定型,具有以下优点:
1、本发明在生产植物空心胶囊时消除了加入凝胶剂或凝胶剂复配可能造成的不安全因素。在胶囊装填内容物时,只要实验普鲁兰多糖和内容物之间配伍安全性,不需要实验所加入的凝胶剂和内容物的配伍安全性,增加了使用的便捷性,提高了安全性。
2、因传统的普鲁兰多糖空心胶囊在生产的过程中加入的凝胶剂粘度都比较高,严重的影响了胶液的浓度,造成干燥困难,本发明不加入凝胶剂,可以增加胶液的浓度,提高了干燥速度,从而提高了生产效率。
附图说明
图1是现有普鲁兰多糖空心胶囊生产工艺图;
图2是本发明的生产工艺图。
具体实施方式
实施例1:
称重20公斤粘度为50mm2/s普鲁兰多糖,加入60公斤温度为60摄氏度的去离子水,搅拌静置成为均匀的重量比浓度为25%的胶液,用温度为摄氏零下14度的模具蘸胶,使用零下10摄氏度的温度进行干燥。得到的样品为例1。
经过实际测定,普鲁兰多糖胶囊厚度符合普鲁兰多糖胶囊的厚度,因中国目前没有普鲁兰多糖的标准,按照《中国药典》明胶空心胶囊的标准进行测试,均达到要求。
实施例2:
称重20公斤粘度为180mm2/s的普鲁兰多糖,加入80公斤温度为60摄氏度的去例子水,搅拌静置,配置成重量比浓度为20%普鲁兰多糖溶液。
设定零下35摄氏度的模具蘸胶,在控制空心胶囊厚度时根据空心胶囊的厚度要求在摄氏零下30度至40度之间调节,使用摄氏零下20度温度进行干燥,得到的样品为例2,按照标准测试,均达到要求。
实施例3:
称重20公斤称重20公斤粘度为100mm2/s的普鲁兰多糖,加入60公斤温度为40摄氏度的去离子水,搅拌静置,成为均匀的重量比浓度为25%的胶液,用温度为摄氏零下5度的模具蘸胶,使用设定零下30摄氏度的温度进行干燥。根据胶囊的要求厚度在摄氏零下20度到零下40度之间调节,得到的样品为实施例3,按照标准测试,达到要求。
分析和实施例1相比,溶液浓度完全相同,虽然模具温度增高,但是干燥温度较低,成功的抵消了普鲁兰多糖溶液对模具的加热作用,同样可以生产出符合标准的普鲁兰多糖空心胶囊产品。
同时,我们得出结论,使用40摄氏度的去离子水溶解普鲁兰多糖,同样可以得到均匀的普鲁兰多糖溶液,但去除气泡所需要的时间比较长。
实施例4:
称重20公斤粘度为180mm2/s的普鲁兰多糖,加入80公斤温度为60摄氏度的去例子水,搅拌静置,配置成重量比浓度为20%普鲁兰多糖溶液。
设定零摄氏度的模具蘸胶,在控制空心胶囊厚度时根据空心胶囊的厚度要求在摄氏零下40至45度之间调节,因普鲁兰多糖溶液在模具上流淌,不能定型,实验失败。
结论:按照实施例1、例2、例3,均可以生产出符合《中华人民共和国药典》标准,并符合客户使用要求厚度的普鲁兰多糖空心胶囊。

Claims (4)

1.一种普鲁兰多糖空心胶囊的制作工艺,其特征是:工艺步骤如下:
1)选择粘度为50-180mm2/s的普鲁兰多糖,加入温度为40~80摄氏度的热水配置成按重量比浓度计20~25%的普鲁兰多糖溶液,搅拌均匀、保温、静置除去气泡;
2)将配置的普鲁兰多糖溶液放到空心胶囊生产线胶槽中,模具温度控制在零下40~0摄氏度之间进行蘸胶;
3)摄氏零下40度至0度区间内调节定型风的温度,使普鲁兰多糖溶液形成的膜不会在模具上流淌,直至形状固定;
4)干燥、切割、套合、成品入库。
2.根据权利要求1所述的普鲁兰多糖空心胶囊的制作工艺,其特征是:步骤1中所述的保温温度不低于20摄氏度。
3.根据权利要求1所述的普鲁兰多糖空心胶囊的制作工艺,其特征是:步骤2中不使用凝胶剂,利用胶液中水在0摄氏度以下结冻的原理定型。
4.根据权利要求1所述的普鲁兰多糖空心胶囊的制作工艺,其特征是:步骤3利用水在0摄氏度以下可以直接升华的原理干燥。
CN201510466717.XA 2015-07-31 2015-07-31 一种普鲁兰多糖空心胶囊的制作工艺 Active CN105055365B (zh)