CN104972036A - 一种工件锻造工艺 - Google Patents

一种工件锻造工艺 Download PDF

Info

Publication number
CN104972036A
CN104972036A CN201510352038.XA CN201510352038A CN104972036A CN 104972036 A CN104972036 A CN 104972036A CN 201510352038 A CN201510352038 A CN 201510352038A CN 104972036 A CN104972036 A CN 104972036A
Authority
CN
China
Prior art keywords
workpiece
forging process
workpiece forging
forging
moulds
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510352038.XA
Other languages
English (en)
Inventor
陈文建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510352038.XA priority Critical patent/CN104972036A/zh
Publication of CN104972036A publication Critical patent/CN104972036A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种工件锻造工艺，包括以下步骤：步骤一：将毛坯料放于模具之间；步骤二：将模具放入锻造炉加热，加热温度1000-1200℃，加热时间为1小时；步骤三：冷却3小时；步骤四：对工件进行检查。本发明所公开的一种工件锻造工艺，工艺路线设计合理，简单易行，极大提高了生产效率，同时也提高了工件的表面质量。

Description

一种工件锻造工艺
技术领域
本发明涉及锻造技术领域，具体涉及一种工件锻造工艺。
背景技术
锻造是一种利用锻压机械对金属坯料施加压力，使其产生塑性变形以获得具有一定机械性能、一定形状和尺寸锻件的加工方法，锻压（锻造与冲压）的两大组成部分之一。在机械领域，锻造被广泛的应用于诸多方面，如很多金属工件的制造就是主要通过锻造完成。但是，在现有的工件锻造工艺中，由于工艺设计存在的各种问题，工艺周期较长，耗时耗力，生产效率低下。
发明内容
为解决现有技术中存在的上述问题，本发明提供了一种工件锻造工艺。
本发明的技术效果通过以下技术方案实现：
一种工件锻造工艺，包括以下步骤：
步骤一：将毛坯料放于模具之间；
步骤二：将模具放入锻造炉加热，加热温度1000-1200℃，加热时间为1小时；
步骤三：冷却3小时；
步骤四：对工件进行检查。
本发明的有益效果是：
本发明所公开的一种工件锻造工艺，工艺路线设计合理，简单易行，极大提高了生产效率，同时也提高了工件的表面质量。
具体实施方式
本发明通过以下具体实施方式实现：
一种工件锻造工艺，包括以下步骤：
步骤一：将毛坯料放于模具之间；
步骤二：将模具放入锻造炉加热，加热温度1000-1200℃，加热时间为1小时；
步骤三：冷却3小时；
步骤四：对工件进行检查。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (1)

1.一种工件锻造工艺，其特征在于：包括以下步骤：
步骤一：将毛坯料放于模具之间；
步骤二：将模具放入锻造炉加热，加热温度1000-1200℃，加热时间为1小时；
步骤三：冷却3小时；
步骤四：对工件进行检查。
CN201510352038.XA 2015-06-24 2015-06-24 一种工件锻造工艺 Pending CN104972036A (zh)