CN104828830A - 一种提高白炭黑bet的方法 - Google Patents

一种提高白炭黑bet的方法 Download PDF

Info

Publication number
CN104828830A
CN104828830A CN201510302140.9A CN201510302140A CN104828830A CN 104828830 A CN104828830 A CN 104828830A CN 201510302140 A CN201510302140 A CN 201510302140A CN 104828830 A CN104828830 A CN 104828830A
Authority
CN
China
Prior art keywords
carbon black
white carbon
concentration
bet
mixed solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510302140.9A
Other languages
English (en)
Other versions
CN104828830B (zh
Inventor
王永庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Quechen Silicon Chemical Co Ltd
Original Assignee
Quechen Silicon Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Quechen Silicon Chemical Co Ltd filed Critical Quechen Silicon Chemical Co Ltd
Priority to CN201510302140.9A priority Critical patent/CN104828830B/zh
Publication of CN104828830A publication Critical patent/CN104828830A/zh
Application granted granted Critical
Publication of CN104828830B publication Critical patent/CN104828830B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种提高白炭黑BET的方法，该方法包括如下步骤：（1）向水玻璃溶液中加入尿素和聚乙二醇，混匀，所得混合液中尿素的浓度为3-8g/L，聚乙二醇的浓度为1-2g/L；（2）将步骤（1）所得的混合液加热至70-80℃，加入硫酸，酸化至pH为5-6，老化20-30min；（3）老化后，过滤、干燥得到白炭黑。与传统硫酸沉淀法制备的白炭黑相比，本发明方法可显著提高白炭黑的比表面积。

Description

一种提高白炭黑BET的方法
技术领域
本发明涉及一种提高白炭黑比表面积（BET）的方法。
背景技术
白炭黑的生产方法可以分为干法和湿法两种。干法主要是指气相法，湿法可以分为沉淀法和凝胶法。气相法的优点是产品纯度高，分散性好，颗粒细且呈球形，表面羟基少，因而具有优异的补强性能，但原料昂贵，能耗高，技术复杂，限制了该方法的应用。凝胶法制得的产品特性类似于干法产品，但工艺较沉淀法复杂，成本也高。沉淀法是通过对硅酸盐酸化获得疏松分散的、以絮状结构沉淀出的SiO2，大多采用硫酸或盐酸与硅酸钠溶液进行反应，该法原料易得，生产流程简单，能耗低，投资少，与干法相比，颗粒较大，比表面积更低。
发明内容
本发明要解决的技术问题是克服现有的缺陷，提供了一种提高白炭黑BET的方法。
为了解决上述技术问题，本发明提供了如下的技术方案：
一种提高白炭黑BET的方法，包括如下步骤：
（1）向水玻璃溶液中加入尿素和聚乙二醇，混匀，所得混合液中尿素的浓度为3-8g/L，聚乙二醇的浓度为1-2g/L；
（2）将步骤（1）所得的混合液加热至70-80℃，加入硫酸，酸化至pH为5-6，老化20-30min；
（3）老化后，过滤、干燥得到白炭黑。
进一步，所述聚乙二醇的平均分子量为300-1200。
进一步，所述水玻璃溶液的SiO2浓度为10-20wt%，SiO2/Na2O的摩尔比为3.2-3.4。
采用本发明方法所得的白炭黑比表面积可达370-400m2/g。
附图说明
附图用来提供对本发明的进一步理解，并且构成说明书的一部分，与本发明的实施例一起用于解释本发明，并不构成对本发明的限制。在附图中：
图1是本发明的工艺流程图。
具体实施方式
以下结合附图对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例1
一种提高白炭黑BET的方法，工艺流程如图1所示，包括如下步骤：
（1）向水玻璃溶液（模数：3.3，SiO2（wt%）：15）中加入尿素和聚乙二醇，混匀，混合液中尿素的浓度为3g/L，聚乙二醇（PEG1000）的浓度为1g/L；
（2）将步骤（1）所得的混合液加热至70℃，缓慢加入硫酸（浓度72wt%），酸化至pH为5，然后老化30min；
（3）老化后，经过滤、烘干干燥，即得到白炭黑，比表面积（BET）：382m2/g，孔容：1.6cm3/g。
实施例2
一种提高白炭黑BET的方法，包括如下步骤：
（1）向水玻璃溶液（模数：3.4，SiO2（wt%）：18）中加入尿素和聚乙二醇，混匀，混合液中尿素的浓度为5g/L，聚乙二醇（PEG600）的浓度为2g/L；
（2）将步骤（1）所得的混合液加热至75℃，缓慢加入硫酸（浓度72wt%），酸化至pH为5.5，然后老化30min；
（3）老化后，经过滤、烘干干燥，即得到白炭黑，比表面积（BET）：374m2/g，孔容：1.7cm3/g。
实施例3
一种提高白炭黑BET的方法，包括如下步骤：
（1）向水玻璃溶液（模数：3.2，SiO2（wt%）：12）中加入尿素和聚乙二醇，混匀，混合液中尿素的浓度为8g/L，聚乙二醇（PEG400）的浓度为1.5g/L；
（2）将步骤（1）所得的混合液加热至80℃，缓慢加入硫酸（浓度72wt%），酸化至pH为6，然后老化20min；
（3）老化后，经过滤、烘干干燥，即得到白炭黑，比表面积（BET）：390m2/g，孔容：1.65cm3/g。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (3)

1.一种提高白炭黑BET的方法，包括如下步骤：
（1）向水玻璃溶液中加入尿素和聚乙二醇，混匀，所得混合液中尿素的浓度为3-8g/L，聚乙二醇的浓度为1-2g/L；
（2）将步骤（1）所得的混合液加热至70-80℃，加入硫酸，酸化至pH为5-6，老化20-30min；
（3）老化后，过滤、干燥得到白炭黑。
2.根据权利要求1所述提高白炭黑BET的方法，其特征在于，所述聚乙二醇的平均分子量为300-1200。
3.根据权利要求1所述提高白炭黑BET的方法，其特征在于，所述水玻璃溶液的SiO2浓度为10-20wt%，SiO2/Na2O的摩尔比为3.2-3.4。
CN201510302140.9A 2015-06-05 2015-06-05 一种提高白炭黑bet的方法 Active CN104828830B (zh)