CN104828831A - 一种连续生产白炭黑的方法 - Google Patents

一种连续生产白炭黑的方法 Download PDF

Info

Publication number
CN104828831A
CN104828831A CN201510302180.3A CN201510302180A CN104828831A CN 104828831 A CN104828831 A CN 104828831A CN 201510302180 A CN201510302180 A CN 201510302180A CN 104828831 A CN104828831 A CN 104828831A
Authority
CN
China
Prior art keywords
white carbon
carbon black
sodium silicate
hydrochloric acid
concentration
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510302180.3A
Other languages
English (en)
Other versions
CN104828831B (zh
Inventor
王永庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Quechen Silicon Chemical Co Ltd
Original Assignee
Quechen Silicon Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Quechen Silicon Chemical Co Ltd filed Critical Quechen Silicon Chemical Co Ltd
Priority to CN201510302180.3A priority Critical patent/CN104828831B/zh
Publication of CN104828831A publication Critical patent/CN104828831A/zh
Application granted granted Critical
Publication of CN104828831B publication Critical patent/CN104828831B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种连续生产白炭黑的方法，包括如下步骤：（1）向浓度为0.1～1mol/L的硅酸钠溶液中加入聚丙烯酰胺，聚丙烯酰胺的用量为硅酸钠的0.1～0.3wt%；（2）将步骤（1）得到的硅酸钠溶液、碳酸氢钠溶液和盐酸混合反应，其中，碳酸氢钠：盐酸：硅酸钠的摩尔比为（0.1～0.15）：（1～1.1）：1；（3）步骤（2）的反应液经板框过滤机过滤后，干燥得到白炭黑。与现有沉淀法相比，本发明方法无需老化，可实现连续生产。

Description

一种连续生产白炭黑的方法
技术领域
本发明涉及一种连续生产白炭黑的方法。
背景技术
白炭黑的生产方法可以分为干法和湿法两种。干法主要是指气相法，湿法可以分为沉淀法和凝胶法。气相法的优点是产品纯度高，分散性好，颗粒细且呈球形，表面羟基少，因而具有优异的补强性能，但原料昂贵，能耗高，技术复杂，限制了该方法的应用。凝胶法制得的产品特性类似于干法产品，但工艺较沉淀法复杂，成本也高。沉淀法是通过对硅酸盐酸化获得疏松分散的、以絮状结构沉淀出的SiO2，大多采用硫酸或盐酸与硅酸钠溶液进行反应，该法原料易得，生产流程简单，能耗低，投资少，但酸化后需要老化，大多为间歇式生产。
发明内容
本发明要解决的技术问题是克服现有的缺陷，提供了一种连续生产白炭黑的方法。
为了解决上述技术问题，本发明提供了如下的技术方案：
一种利用低浓度硅酸钠连续生产白炭黑的方法，包括如下步骤：
（1）向浓度为0.1～1mol/L的硅酸钠溶液中加入聚丙烯酰胺，聚丙烯酰胺的用量为硅酸钠的0.1～0.3wt%；
（2）将步骤（1）得到的硅酸钠溶液、碳酸氢钠溶液和盐酸混合反应，其中，碳酸氢钠：盐酸：硅酸钠的摩尔比为（0.1～0.15）：（1～1.1）：1；
（3）步骤（2）的反应液经板框过滤机过滤后，干燥得到白炭黑。
与现有方法相比，本发明酸化后无需老化，从而可实现白炭黑的连续生产。
附图说明
附图用来提供对本发明的进一步理解，并且构成说明书的一部分，与本发明的实施例一起用于解释本发明，并不构成对本发明的限制。在附图中：
图1是本发明的工艺流程示意图。
具体实施方式
以下结合附图对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例1
如图1所示，本发明连续生产白炭黑的方法，包括如下步骤：
（1）向浓度为0.1mol/L的硅酸钠溶液中加入聚丙烯酰胺（R200），聚丙烯酰胺的用量为硅酸钠的0.1wt%；
（2）将步骤（1）得到的硅酸钠溶液与浓度为0.2mol/L的碳酸氢钠溶液和浓度为1mol/L的盐酸连续混合反应，混合时控制碳酸氢钠、盐酸和硅酸钠的摩尔比为0.1：1：1；
（3）步骤（2）的混合反应液无需老化，直接用板框过滤机过滤，再经干燥得到白炭黑，比表面积（BET）：306m2/g。
实施例2
一种连续生产白炭黑的方法，步骤如下：
（1）向浓度为0.4mol/L的硅酸钠溶液中加入聚丙烯酰胺（Zetag 8125），聚丙烯酰胺的用量为硅酸钠的0.2wt%；
（2）将步骤（1）得到的硅酸钠溶液与浓度为0.4mol/L的碳酸氢钠溶液和浓度为1.5mol/L的盐酸连续混合反应，混合时控制碳酸氢钠、盐酸和硅酸钠的摩尔比为0.12：1.05：1；
（3）步骤（2）的混合反应液无需老化，直接用板框过滤机过滤，再经干燥得到白炭黑，比表面积（BET）：298m2/g。
实施例3
一种连续生产白炭黑的方法，包括如下步骤：
（1）向浓度为1mol/L的硅酸钠溶液中加入聚丙烯酰胺（ZETAG 7652），聚丙烯酰胺的用量为硅酸钠的0.3wt%；
（2）将步骤（1）得到的硅酸钠溶液与浓度为0.2mol/L的碳酸氢钠溶液和浓度为1mol/L的盐酸连续混合反应，混合时控制碳酸氢钠、盐酸和硅酸钠的摩尔比为0.15：1.1：1；
（3）步骤（2）的混合反应液无需老化，直接用板框过滤机过滤，再经干燥得到白炭黑，比表面积（BET）：310m2/g。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (3)

1.一种连续生产白炭黑的方法，包括如下步骤：
（1）向浓度为0.1～1mol/L的硅酸钠溶液中加入聚丙烯酰胺，聚丙烯酰胺的用量为硅酸钠的0.1～0.3wt%；
（2）将步骤（1）得到的硅酸钠溶液、碳酸氢钠溶液和盐酸混合反应，其中，碳酸氢钠：盐酸：硅酸钠的摩尔比为（0.1～0.15）：（1～1.1）：1；
（3）步骤（2）的反应液经板框过滤机过滤后，干燥得到白炭黑。
2.根据权利要求1所述的方法，其特征在于，步骤（2）所述碳酸氢钠溶液的浓度为0.1～0.5mol/L。
3.根据权利要求1所述的方法，其特征在于，步骤（2）所述盐酸的浓度为1～2mol/L。
CN201510302180.3A 2015-06-05 2015-06-05 一种连续生产白炭黑的方法 Active CN104828831B (zh)