CN104725875A - 高抗撕裂高耐寒硅橡胶及其制备方法 - Google Patents

高抗撕裂高耐寒硅橡胶及其制备方法 Download PDF

Info

Publication number
CN104725875A
CN104725875A CN201410787224.1A CN201410787224A CN104725875A CN 104725875 A CN104725875 A CN 104725875A CN 201410787224 A CN201410787224 A CN 201410787224A CN 104725875 A CN104725875 A CN 104725875A
Authority
CN
China
Prior art keywords
parts
minutes
cold
silicone rubber
sulfuration
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410787224.1A
Other languages
English (en)
Inventor
张国青
孙政良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU JIN TENG ELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
SUZHOU JIN TENG ELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU JIN TENG ELECTRONIC TECHNOLOGY Co Ltd filed Critical SUZHOU JIN TENG ELECTRONIC TECHNOLOGY Co Ltd
Priority to CN201410787224.1A priority Critical patent/CN104725875A/zh
Publication of CN104725875A publication Critical patent/CN104725875A/zh
Pending legal-status Critical Current

Abstract

本发明揭示了一种高抗撕裂高耐寒硅橡胶，其特征在于：按重量份计，其包括如下成份，甲基乙烯基硅橡胶100～160份；气相法白炭黑20～35份；炭黑40～65份；活性碳酸钙12～22份；硅藻土11～21份；环烷油4～9份；羟基硅油7～15份；2-硫醇基苯并咪唑10～25份；乙烯基硅烷20～25份；硬脂酸甘油单酯3～10份；癸二酸二辛脂4～6份；双二五硫化剂3～8份。本发明的硅橡胶具有价格低廉，品相良好，抗撕裂强度高，耐寒性能好，并且制备方法简便等优点。

Description

高抗撕裂高耐寒硅橡胶及其制备方法
技术领域
本发明涉及一种橡胶产品及其制备方法，尤其涉及一种高抗撕裂高耐寒硅橡胶及其制备方法。
背景技术
硅橡胶是一种特殊的合成橡胶，其具有优良的耐高、低温性，电绝缘性，防潮性，化学稳定性以及耐臭氧，耐紫外线，防火、无毒等特点，在国防工业及国民经济各部门具有十分重要的用途，可广泛应用于航空、宇宙航行、电器、医疗器械等方面。
发明内容
本发明的目的在于针对现有技术中的上述缺陷，提供一种价格低廉，品相良好，抗撕裂强度高，耐寒性能好，并且制备方法简便的高抗撕裂高耐寒硅橡胶及其制备方法。
为实现上述发明目的，本发明采用了如下技术方案：一种高抗撕裂高耐寒硅橡胶，按重量份计，其包括如下成份，
此外，本发明还提供如下附属技术方案：
按重量份计，所述高抗撕裂高耐寒硅橡胶包括如下成份，
一种高抗撕裂高耐寒硅橡胶的制备方法，其包括如下步骤：
1)按重量份计，称取定量的甲基乙烯基硅橡胶、气相法白炭黑、炭黑、活性碳酸钙、硅藻土、环烷油、羟基硅油、2-硫醇基苯并咪唑、乙烯基硅烷、硬脂酸甘油单酯、癸二酸二辛脂和双二五硫化剂放入混炼机内，并且将混炼机温度调节为50～80℃，真空度为-0.01～-0.1MPa，然后开始搅拌，搅拌速度为40～70r/min，搅拌时间为20～45分钟，得到混合胶料；
2)将所得的混合胶料静置冷却25～30分钟；
3)冷却后的混料放入平流压片机上进行一段硫化，硫化温度为50～120℃，气压为10～20MPa，时间为30～50分钟；
4)一段硫化后的物料放入烘箱内进行二段硫化，硫化温度为30～250℃，气压为常压，时间至少6小时；
5)包装出品。
其中所述步骤4)包括：
a.温度30℃时，硫化15分钟；
b.温度100℃时，硫化60分钟；
c.温度180℃时，硫化120分钟；
d.温度250℃时，硫化220分钟。
相比于现有技术，本发明的优势在于：本发明所揭示的高抗撕裂高耐寒硅橡胶包括：甲基乙烯基硅橡胶、气相法白炭黑、炭黑、活性碳酸钙、硅藻土、环烷油、羟基硅油、2硫醇基苯并咪唑、乙烯基硅烷、硬脂酸甘油单酯、癸二酸二辛脂和双二五硫化剂，体现了本发明的硅橡胶具有价格低廉，品相良好，抗撕裂强度高，耐寒性能好，并且制备方法简便等优点。
具体实施方式
以下结合较佳实施例对本发明技术方案作进一步非限制性的详细说明。
一种高抗撕裂高耐寒硅橡胶，按重量份计，其包括如下成份，
该高抗撕裂高耐寒硅橡胶的制备方法包括如下步骤：
1)按重量份计，称取上述量的甲基乙烯基硅橡胶、气相法白炭黑、炭黑、活性碳酸钙、硅藻土、环烷油、羟基硅油、2-硫醇基苯并咪唑、乙烯基硅烷、硬脂酸甘油单酯、癸二酸二辛脂和双二五硫化剂放入混炼机内，并且将混炼机温度调节为70℃，真空度为0.05MPa，然后开始搅拌，搅拌速度为55r/min，搅拌时间为35分钟，得到混合胶料；
2)将所得的混合胶料静置冷却28分钟；
3)冷却后的混料放入平流压片机上进行一段硫化，硫化温度为80℃，气压为15MPa，时间为40分钟；
4)一段硫化后的物料放入烘箱内进行二段硫化，硫化温度为30～250℃，气压为常压，时间至少6小时；
5)包装出品。
其中步骤4)包括：
a.温度30℃时，硫化15分钟；
b.温度100℃时，硫化60分钟；
c.温度180℃时，硫化120分钟；
d.温度250℃时，硫化220分钟。
本发明的硅橡胶具有价格低廉，品相良好，抗撕裂强度高，耐寒性能好，并且制备方法简便等优点。
需要指出的是，上述较佳实施例仅为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。

Claims (4)

1.一种高抗撕裂高耐寒硅橡胶，其特征在于：按重量份计，其包括如下成份，
2.根据权利要求1所述的高抗撕裂高耐寒硅橡胶，其特征在于：按重量份计，其包括如下成份，
3.根据权利要求1或2所述的高抗撕裂高耐寒硅橡胶的制备方法，其特征在于其包括如下步骤：
1)按重量份计，称取定量的甲基乙烯基硅橡胶、气相法白炭黑、炭黑、活性碳酸钙、硅藻土、环烷油、羟基硅油、2-硫醇基苯并咪唑、乙烯基硅烷、硬脂酸甘油单酯、癸二酸二辛脂和双二五硫化剂放入混炼机内，并且将混炼机温度调节为50～80℃，真空度为-0.01～-0.1MPa，然后开始搅拌，搅拌速度为40～70r/min，搅拌时间为20～45分钟，得到混合胶料；
2)将所得的混合胶料静置冷却25～30分钟；
3)冷却后的混料放入平流压片机上进行一段硫化，硫化温度为50～120℃，气压为10～20MPa，时间为30～50分钟；
4)一段硫化后的物料放入烘箱内进行二段硫化，硫化温度为30～250℃，气压为常压，时间至少6小时；
5)包装出品。
4.根据权利要求3所述的高抗撕裂高耐寒硅橡胶的制备方法，其特征在于：所述步骤4)包括：
a.温度30℃时，硫化15分钟；
b.温度100℃时，硫化60分钟；
c.温度180℃时，硫化120分钟；
d.温度250℃时，硫化220分钟。
CN201410787224.1A 2014-12-17 2014-12-17 高抗撕裂高耐寒硅橡胶及其制备方法 Pending CN104725875A (zh)