CN104556680A - 不锈钢真空保温容器无尾封口用玻璃及其制备方法 - Google Patents
不锈钢真空保温容器无尾封口用玻璃及其制备方法 Download PDFInfo
- Publication number
- CN104556680A CN104556680A CN201410848262.3A CN201410848262A CN104556680A CN 104556680 A CN104556680 A CN 104556680A CN 201410848262 A CN201410848262 A CN 201410848262A CN 104556680 A CN104556680 A CN 104556680A
- Authority
- CN
- China
- Prior art keywords
- glass
- sealing
- preparation
- steel vacuum
- stainless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种锈钢真空保温容器无尾封口用玻璃及其制备方法,将原料PbO75%-85%、B2O35%-15%、ZnO?0-5%、SiO2?1%-5%、Al2O3?0.5%-5%、CuO?0-5%,在混料机内混合;再到铂金锅内熔制,熔制温度1100℃,用对辊轧机轧成薄片,用刚玉罐球磨,过200目筛;然后加入0.1%~1.0%有机造粒剂聚氧化乙烯进行造粒,用压机成型,在箱式高温电阻炉内烧结成玻坯。本发明封口时不会产生气泡、不易脱落、抗酸性好。
Description
技术领域
本发明属于化工技术领域,具体涉及到一种不锈钢真空保温容器无尾封口用玻璃,同时还涉及该不锈钢真空保温容器无尾封口用玻璃的制备方法。
背景技术
不锈钢真空保温容器的封口一般在真空炉内进行,先将真空炉抽到要求的真空状态,在升温到玻璃组成的熔化温度进行封接。一般的焊料玻璃在封接时易产生气泡,易脱落,抗酸性差。本发明的玻璃组成封接的器件气泡少,不宜脱落,抗酸性好。
目前市场上应用的不锈钢无尾焊料主要为PbO- B2O3-SiO2体系,该体系玻璃主要为非结晶型玻璃,其主要成分为PbO 85%、B2O3 12.5%、SiO21.0%、Al2O31.5%。该类玻璃虽然流动性好,但在真空下烧结时气泡消除缓慢,甚至残留少数气泡无法消除,当未消除的气泡破裂时,会导致真空度下降。另一方面,抗酸性差也是这类玻璃存在的主要问题之一,由于抗酸性差,当不锈钢制品在后续电解工艺加工时易发生玻璃脱落。也有研究人员试图利用结晶型玻璃强度高的特点来克服玻璃脱落这一问题,由于结晶型玻璃的流动性差,从而导致这一问题未能克服。
发明内容
本发明的目的在于克服上述缺点而提供的一种不会产生气泡、不易脱落、抗酸性好的不锈钢真空保温容器无尾封口用玻璃。
本发明的另一目的在于提供该不锈钢真空保温容器无尾封口用玻璃的制备方法。
本发明的一种不锈钢真空保温容器无尾封口用玻璃,由下述重量比的原料制得:
PbO 75%-85% B2O3 5%-15% ZnO 0-5% SiO2 1%-5% Al2O3 0.5%-5% CuO 0-5%。
本发明的一种不锈钢真空保温容器无尾封口用玻璃,包括以下步骤:
(1)混料:将原料在混料机内混合;
(2)熔制:再到铂金锅内熔制,熔制温度1100℃,用对辊轧机轧成薄片,用刚玉罐球磨,过200目筛;
(3)球磨:然后加入0.1%~1.0%有机造粒剂聚氧化乙烯进行造粒,用压机成型,在箱式高温电阻炉内烧结成玻坯。
本发明与现有技术相比,具有明显的有益效果,从以上技术方案可知:本发明原料中PbO主要形成玻璃,降低温度;B2O3降低组成温度,改善流动性;SiO2改善玻璃组成和抗酸性;ZnO降低组成的温度,提高抗水性;Al2O3用于改善玻璃的抗酸性并调整组成的结晶性;CuO可改善玻璃组成的表面张力,提高玻璃的浸润性。本发明在真空焊接条件下消除气泡快、流动性好、焊接强度好等特点。技术参数:Tg(转变温度):310℃,Tf(软化温度):380℃,烧结流动温度:440℃,膨胀系数(20~250℃):120×10-7/℃。本发明在玻璃组成的流动点具有一定的结晶性,当高于流动点以后结晶消失。该性能的主要特点:既可使封口时充分流动和浸润,焊接完成后,又能通过二次结晶提高强度。本发明的玻璃,既具有非结晶型玻璃流动性好的特点,也完善了玻璃抗酸性和焊接强度额的不足,也确保了不锈钢无尾焊料焊接制品的质量。
以下通过具体实施方式,进一步说明本发明的有益效果。
具体实施方式
实施例1
一种不锈钢真空保温容器无尾封口用玻璃的制备方法,包括:
PbO 4050g,B2O3 500g,ZnO 250g,SiO2 100g,Al2O3 100g。
原料在混料机内混合,再到铂金锅内熔制,熔制温度1100℃,用对辊轧机轧成薄片,用刚玉罐球磨,过200目筛,然后加入0.1%~1.0%有机造粒剂聚氧化乙烯进行造粒,用压机成型,在箱式高温电阻炉内烧结成玻坯。
使用时,放入不锈钢容器封口处焊接,该样转变点315℃,软化温度380℃,膨胀系数115×10-7/℃。
实施例2
一种不锈钢真空保温容器无尾封口用玻璃的制备方法,包括:
PbO 4175g,B2O3 600g,ZnO 50g,SiO2 110g,Al2O3 90g。
其余与实施例1相同。
使用时,放入不锈钢容器封口处焊接,该样转变点310℃,软化点375℃,膨胀系数120×10-7/℃。
实施例3
一种不锈钢真空保温容器无尾封口用玻璃的制备方法,包括:
PbO 3750g,B2O3 250g,ZnO 0g,SiO2 50g,Al2O3 250g。
其余与实施例1相同。
使用时,放入不锈钢容器封口处焊接,该样转变点315℃,软化点382℃,膨胀系数110×10-7/℃。
实施例4
一种不锈钢真空保温容器无尾封口用玻璃的制备方法,包括:
PbO 4250g,B2O3 750g,ZnO 250g,SiO2 150g,Al2O3 25g,CuO 250g,
其余与实施例1相同。
使用时,放入不锈钢容器封口处焊接,该样转变点308℃,软化点370℃,膨胀系数118×10-7/℃。
以上所述,仅是本发明的较佳实施例而已,并非对本发明做任何形式上的限制,任何未脱离本发明技术方案内容,依据本发明的技术实质对以上实施例所作的任何简单修改等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (2)
1.一种不锈钢真空保温容器无尾封口用玻璃,由下述重量比的原料制得:
PbO 75%-85% B2O3 5%-15% ZnO 0-5% SiO2 1%-5% Al2O3 0.5%-5% CuO 0-5%。
2.如权利要求1所述的一种不锈钢真空保温容器无尾封口用玻璃,包括以下步骤:
(1)混料:将原料在混料机内混合;
(2)熔制:再到铂金锅内熔制,熔制温度1100℃,用对辊轧机轧成薄片,用刚玉罐球磨,过200目筛;
(3)球磨:然后加入0.1%~1.0%有机造粒剂聚氧化乙烯进行造粒,用压机成型,在箱式高温电阻炉内烧结成玻坯。