CN104472370A - Iron ore powder micro-hole cat litter and preparation method thereof - Google Patents
Iron ore powder micro-hole cat litter and preparation method thereof Download PDFInfo
- Publication number
- CN104472370A CN104472370A CN201410653636.6A CN201410653636A CN104472370A CN 104472370 A CN104472370 A CN 104472370A CN 201410653636 A CN201410653636 A CN 201410653636A CN 104472370 A CN104472370 A CN 104472370A
- Authority
- CN
- China
- Prior art keywords
- cat litter
- iron ore
- parts
- ore powder
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an iron ore powder micro-hole cat litter which is prepared from raw materials including, by weight, 6-8 parts of saw powder, 10-12 parts of iron ore powder, 35-40 parts of kaolin, 10-15 parts of waste newspaper, 2-3 parts of sodium hydroxide, 5-7 parts of calcium oxide, 2-4 parts of carrageenan, 10-12 parts of ammonium sulfate, 4-5 parts of adhesives and an appropriate amount of water. The iron ore powder is added, the water absorption effect of the cat litter is enhanced, the iron ore powder has a certain magnetism and easily forms loose multi-hole structures, space structures of the cat litter are larger, the water absorption capacity of the cat litter is higher, the specially-made strong adhesives are added and have excellent adhesion effects, a user does not worry about that the cat litter is broken and difficultly treated due to loose structures after the cat litter absorbs water, the carrageenan and plant fibers of the smashed saw powder have the same effects, and the materials have first-class adsorption effects and are pollution-free and fine in toughness.
Description
Technical field
The present invention is a kind of Iron Ore Powder micropore cat litter and preparation method thereof, belongs to the technology field of cat litter.
Background technology
Cat litter is the very large pet supplies of a kind of consumption abroad, and be the conventional necessary article of most pet feeding cat family, in addition in pet shop, pet cat breeding farm etc. all will use cat litter, manufactures in industry occupy very important status at pet supplies.
In cat culture, of paramount importance progress is exactly the use of cat litter, early stage cat litter is mainly based on incoagulable cat litter, everybody master is to receive cat just, but along with the continuous progress of cat litter technology, it is simple like this that people are not limited only to storage, so constantly there is again present condensation sand, wooden sand, and chalazie, bentonite bonded sand etc.
General cat litter uses paper pulp to break into fine granularity to simulate sandy soil and to provide water imbibition, also has the particle using the physical dryness agent such as silica gel.Generally can add the chemical products such as deodorant/preservative, cat litter runs into water can condense into block, although be convenient to cleaning but suggestion collocation by special leakage shovel, to be stained with after most of cat litter cat steps on pin and to take that other is local to, therefore please noting frequent cleaning.
During use, cat litter is poured into cat litter box (a kind of container filling cat litter belongs to pet supplies), auxiliary 7 ~ 10cm is thick, just can use to cat, during clean cat litter box, with cat litter shovel (specific purpose tool belongs to pet supplies), those cakey blocks are shoveled out from cat litter, lose into dustbin, just reach and remove the ight soil of cat and the object of urine, and remaining cat litter in cat litter box, be still clean, can continue to use, after consumption reduces, can continue to add new cat litter and supplement.
Summary of the invention
A kind of Iron Ore Powder micropore cat litter, it is characterized in that, be made up of the raw material of following weight portion: sawdust powder 6 ~ 8, iron ore powder 10 ~ 12, kaolin 35 ~ 40, old newsprint 10 ~ 15, sodium hydroxide 2 ~ 3, calcium oxide 5 ~ 7, carragheen 2 ~ 4, ammonium sulfate 10 ~ 12, binding agent 4 ~ 5 and appropriate water;
Described binding agent is made up of the raw material of following weight portion: dextrin 12 ~ 16, sodium alginate 2 ~ 3, active carbon 1.5 ~ 2, calcium oxide 3 ~ 4, glycerine 4 ~ 6, polybutene 2 ~ 3, ethanol 15 ~ 20, lauryl sodium sulfate 1 ~ 2 and appropriate water; Preparation method is: water dilution ethanol being added 3 times, then glycerine, polybutene and lauryl sodium sulfate is added, heating stirring and dissolving, is finally blended into the dextrin of powdery, sodium alginate, active carbon and calcium oxide mixture, adds thermal agitation 20 ~ 30min and becomes homogenate shape and get final product.
A preparation method for Iron Ore Powder micropore cat litter, is characterized in that, comprises following step:
(1) by the sodium hydrate aqueous solution degraded 60 ~ 80min of old newsprint with 4 times of dilutions, then add sawdust powder, iron ore powder, kaolin and calcium oxide, be blended into a certain amount of water furnishing and stick with paste, tax-inclusive amount about 40%;
(2) mix ammonium sulfate and carragheen, add appropriate water just stirring and dissolving, again drying crystalline be ground into the pulvis of 40 order sizes;
(3) pulvis of (2), binding agent and other residual components are added in the thickener of (1), knead and pulvis is fully mixed, finally make the cat litter blank of diameter 5 ~ 8mm;
(4) 30 ~ 40min is toasted, after completing under (3) cat litter being put in more than 200 DEG C high temperature.
Beneficial effect of the present invention: cat litter of the present invention utilizes strengthen its soaking effect adding of Iron Ore Powder, Iron Ore Powder possesses certain magnetic, it is caused more easily to form loose porous structure, the space structure of cat litter is larger, the ability of its water suction is also stronger, here the special strength adhesive of the present invention is added, possesses fabulous adhesion effect, so because the loosely organized cat litter that causes is broken after water suction need not be worried, be difficult to process, effect same also have carragheen and sawdust to pulverize after vegetable fiber, these materials not only adsorption effect are first-class, pollution-free, its toughness is also better.
Embodiment
Embodiment 1:
A kind of Iron Ore Powder micropore cat litter, is characterized in that, be made up of the raw material of following weight portion: sawdust powder 8, iron ore powder 10, kaolin 35, old newsprint 10, sodium hydroxide 3, calcium oxide 7, carragheen 3, ammonium sulfate 10, binding agent 4 and appropriate water;
Described binding agent is made up of the raw material of following weight portion: dextrin 16, sodium alginate 2, active carbon 2, calcium oxide 3, glycerine 4, polybutene 2, ethanol 16, lauryl sodium sulfate 1 and appropriate water; Preparation method is: water dilution ethanol being added 3 times, then glycerine, polybutene and lauryl sodium sulfate is added, heating stirring and dissolving, is finally blended into the dextrin of powdery, sodium alginate, active carbon and calcium oxide mixture, adds thermal agitation 20 ~ 30min and becomes homogenate shape and get final product.
A preparation method for Iron Ore Powder micropore cat litter, is characterized in that, comprises following step:
(1) by the sodium hydrate aqueous solution degraded 60 ~ 80min of old newsprint with 4 times of dilutions, then add sawdust powder, iron ore powder, kaolin and calcium oxide, be blended into a certain amount of water furnishing and stick with paste, tax-inclusive amount about 40%;
(2) mix ammonium sulfate and carragheen, add appropriate water just stirring and dissolving, again drying crystalline be ground into the pulvis of 40 order sizes;
(3) pulvis of (2), binding agent and other residual components are added in the thickener of (1), knead and pulvis is fully mixed, finally make the cat litter blank of diameter 5 ~ 8mm;
(4) 30 ~ 40min is toasted, after completing under (3) cat litter being put in more than 200 DEG C high temperature.
The common cat litter that Iron Ore Powder micropore cat litter of the present invention and market are sold is contrasted result of use, get a certain amount of fresh cat ight soil and the common cat litter of cat urine effect, the time of its absorption urine is about 55s, it makes the time of ight soil dehydration sclerosis be about 400s, and same urine and ight soil effect Iron Ore Powder micropore of the present invention cat litter, the time of its absorption urine approximately only has 18 ~ 22s, the time of ight soil dehydration sclerosis is made approximately to only have 220s, substantially reduce action time, reduce distributing of peculiar smell.
Claims (2)
1. an Iron Ore Powder micropore cat litter, it is characterized in that, be made up of the raw material of following weight portion: sawdust powder 6 ~ 8, iron ore powder 10 ~ 12, kaolin 35 ~ 40, old newsprint 10 ~ 15, sodium hydroxide 2 ~ 3, calcium oxide 5 ~ 7, carragheen 2 ~ 4, ammonium sulfate 10 ~ 12, binding agent 4 ~ 5 and appropriate water;
Described binding agent is made up of the raw material of following weight portion: dextrin 12 ~ 16, sodium alginate 2 ~ 3, active carbon 1.5 ~ 2, calcium oxide 3 ~ 4, glycerine 4 ~ 6, polybutene 2 ~ 3, ethanol 15 ~ 20, lauryl sodium sulfate 1 ~ 2 and appropriate water; Preparation method is: water dilution ethanol being added 3 times, then glycerine, polybutene and lauryl sodium sulfate is added, heating stirring and dissolving, is finally blended into the dextrin of powdery, sodium alginate, active carbon and calcium oxide mixture, adds thermal agitation 20 ~ 30min and becomes homogenate shape and get final product.
2. the preparation method of a kind of Iron Ore Powder micropore cat litter according to claim 1, is characterized in that, comprise following step:
(1) by the sodium hydrate aqueous solution degraded 60 ~ 80min of old newsprint with 4 times of dilutions, then add sawdust powder, iron ore powder, kaolin and calcium oxide, be blended into a certain amount of water furnishing and stick with paste, tax-inclusive amount about 40%;
(2) mix ammonium sulfate and carragheen, add appropriate water just stirring and dissolving, again drying crystalline be ground into the pulvis of 40 order sizes;
(3) pulvis of (2), binding agent and other residual components are added in the thickener of (1), knead and pulvis is fully mixed, finally make the cat litter blank of diameter 5 ~ 8mm;
(4) 30 ~ 40min is toasted, after completing under (3) cat litter being put in more than 200 DEG C high temperature.