CN104160050B - 热冲压用钢板及其制造方法和热冲压钢材 - Google Patents

热冲压用钢板及其制造方法和热冲压钢材 Download PDF

Info

Publication number
CN104160050B
CN104160050B CN201380012499.1A CN201380012499A CN104160050B CN 104160050 B CN104160050 B CN 104160050B CN 201380012499 A CN201380012499 A CN 201380012499A CN 104160050 B CN104160050 B CN 104160050B
Authority
CN
China
Prior art keywords
steel plate
hot
steel
drop stamping
inclusions
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201380012499.1A
Other languages
English (en)
Chinese (zh)
Other versions
CN104160050A (zh
Inventor
棚桥浩之
友清寿雅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of CN104160050A publication Critical patent/CN104160050A/zh
Application granted granted Critical
Publication of CN104160050B publication Critical patent/CN104160050B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B1/00—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations
    • B21B1/22—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length
    • B21B1/24—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length in a continuous or semi-continuous process
    • B21B1/26—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length in a continuous or semi-continuous process by hot-rolling, e.g. Steckel hot mill
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0421—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the working steps
    • C21D8/0436—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0447—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment
    • C21D8/0463—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y10T428/1275—Next to Group VIII or IB metal-base component
    • Y10T428/12757—Fe
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Heat Treatment Of Steel (AREA)
CN201380012499.1A 2012-03-07 2013-03-05 热冲压用钢板及其制造方法和热冲压钢材 Active CN104160050B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2012050935 2012-03-07
JP2012-050935 2012-03-07
PCT/JP2013/055992 WO2013133270A1 (ja) 2012-03-07 2013-03-05 ホットスタンプ用鋼板及びその製造方法並びにホットスタンプ鋼材

Publications (2)

Publication Number Publication Date
CN104160050A CN104160050A (zh) 2014-11-19
CN104160050B true CN104160050B (zh) 2016-05-18

Family

ID=49116745

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201380012499.1A Active CN104160050B (zh) 2012-03-07 2013-03-05 热冲压用钢板及其制造方法和热冲压钢材

Country Status (12)

Country Link
US (2) US10161023B2 (https=)
EP (1) EP2824207A4 (https=)
JP (1) JP5541421B2 (https=)
KR (1) KR101629594B1 (https=)
CN (1) CN104160050B (https=)
BR (1) BR112014021801B1 (https=)
CA (1) CA2865910C (https=)
IN (1) IN2014DN08225A (https=)
MX (1) MX366958B (https=)
RU (1) RU2587106C2 (https=)
WO (1) WO2013133270A1 (https=)
ZA (1) ZA201406644B (https=)

Families Citing this family (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
MX374823B (es) * 2013-03-14 2025-03-06 Nippon Steel Corp Star Placa de acero de alta firmeza con excelentes caracteristicas de resistencia a la destruccion retardada y tenacidad a temperaturas bajas y elemento de alta firmeza manufacturado que usa la misma.
US20160145731A1 (en) * 2014-11-26 2016-05-26 GM Global Technology Operations LLC Controlling Liquid Metal Embrittlement In Galvanized Press-Hardened Components
CN104846274B (zh) * 2015-02-16 2017-07-28 重庆哈工易成形钢铁科技有限公司 热冲压成形用钢板、热冲压成形工艺及热冲压成形构件
EP3278895B1 (en) * 2015-03-31 2020-03-11 Nippon Steel Corporation Steel sheet for hot stamping, method for manufacturing same, and hot stamp molded article
CN105420598A (zh) * 2015-12-14 2016-03-23 浙江海洋学院 一种船锚用低碳合金钢及其热处理工艺
CN105546228A (zh) * 2016-01-20 2016-05-04 浙江海洋学院 一种船舶用无缝钢管及其制备方法
US10619223B2 (en) 2016-04-28 2020-04-14 GM Global Technology Operations LLC Zinc-coated hot formed steel component with tailored property
US10385415B2 (en) 2016-04-28 2019-08-20 GM Global Technology Operations LLC Zinc-coated hot formed high strength steel part with through-thickness gradient microstructure
MX2019001760A (es) * 2016-08-16 2019-06-17 Nippon Steel & Sumitomo Metal Corp Pieza conformada por prensado en caliente.
CN106086683B (zh) * 2016-08-24 2018-05-01 武汉钢铁有限公司 用薄板坯直接轧制的抗拉强度≥1700MPa薄热成形钢及生产方法
CN106086632B (zh) * 2016-08-24 2018-01-12 武汉钢铁有限公司 用薄板坯直接轧制的抗拉强度≥1100MPa薄热成形钢及生产方法
CN106119692B (zh) * 2016-08-24 2018-03-20 武汉钢铁有限公司 用中薄板坯直接轧制的抗拉强度≥1500MPa热成形钢及生产方法
CN106119695B (zh) * 2016-08-24 2018-03-20 武汉钢铁有限公司 用中薄板坯直接轧制的抗拉强度≥1100MPa热成形钢及生产方法
CN106086685B (zh) * 2016-08-24 2018-01-12 武汉钢铁有限公司 用薄板坯直接轧制的抗拉强度≥1500MPa薄热成形钢及生产方法
CN106222555B (zh) * 2016-08-24 2018-03-20 武汉钢铁有限公司 用薄板坯直接轧制的抗拉强度≥1300MPa薄热成形钢及生产方法
CN106222556B (zh) * 2016-08-24 2018-03-16 武汉钢铁有限公司 用中薄板坯直接轧制的抗拉强度≥1300MPa热成形钢及生产方法
JP6572864B2 (ja) * 2016-10-18 2019-09-11 Ｊｆｅスチール株式会社 電磁鋼板製造用の熱延鋼板およびその製造方法
CN106636890B (zh) * 2016-11-11 2018-09-14 武汉钢铁有限公司 直接热成形用薄规格热轧钢板及其制造方法
WO2018096387A1 (en) * 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
JP6271067B1 (ja) * 2017-06-01 2018-01-31 日新製鋼株式会社 高強度Ｚｎ−Ａｌ−Ｍｇ系表面被覆鋼板およびその製造方法
WO2018220412A1 (fr) * 2017-06-01 2018-12-06 Arcelormittal Procede de fabrication de pieces d'acier a haute resistance mecanique et ductilite amelioree, et pieces obtenues par ce procede
DE102017218704A1 (de) * 2017-10-19 2019-04-25 Thyssenkrupp Ag Verfahren zur Herstellung eines mit einem metallischen, vor Korrosion schützenden Überzug versehenen Stahlbauteils
TWI682066B (zh) 2018-02-15 2020-01-11 日商日本製鐵股份有限公司 Fe-Al系鍍敷熱壓印構件及Fe-Al系鍍敷熱壓印構件的製造方法
MX2020009562A (es) * 2018-03-20 2020-10-05 Nippon Steel Corp Cuerpo estampado en caliente.
US11338550B2 (en) * 2018-03-20 2022-05-24 Nippon Steel Corporation Hot-stamped body
WO2019188622A1 (ja) * 2018-03-27 2019-10-03 株式会社神戸製鋼所 ホットスタンプ用鋼板
JP7353768B2 (ja) * 2018-03-27 2023-10-02 株式会社神戸製鋼所 ホットスタンプ用鋼板
CN112513310A (zh) 2018-05-24 2021-03-16 通用汽车环球科技运作有限责任公司 改善压制硬化钢的强度和延性的方法
CN112534078A (zh) 2018-06-19 2021-03-19 通用汽车环球科技运作有限责任公司 具有增强的机械性质的低密度压制硬化钢
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
MY210557A (en) 2020-09-01 2025-09-30 Hyundai Steel Co Material for hot stamping and method of manufacturing the same
CN112326551B (zh) * 2020-11-13 2023-07-18 江苏省沙钢钢铁研究院有限公司 一种复合钢板性能的测试方法
CN114807739A (zh) * 2021-01-28 2022-07-29 宝山钢铁股份有限公司 一种镀铝钢板、热成形部件及制造方法
KR102904753B1 (ko) * 2022-12-30 2025-12-24 현대제철 주식회사 핫 스탬핑 부품
CN119824353A (zh) * 2025-01-03 2025-04-15 鞍钢股份有限公司 铝合金预镀层钢带的制造方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003166035A (ja) * 2001-11-28 2003-06-13 Nippon Steel Corp 成形加工後の耐遅れ破壊性に優れた高強度薄鋼板及びその製造方法並びに高強度薄鋼板により作成された自動車用強度部品
CN1553836A (zh) * 2001-09-14 2004-12-08 Ŧ�ƶ��� 铸造钢带
CN1782116A (zh) * 2004-11-29 2006-06-07 宝山钢铁股份有限公司 一种800MPa冷轧热镀锌双相钢及其制造方法
CN1890394A (zh) * 2003-12-12 2007-01-03 杰富意钢铁株式会社 汽车构造部件用钢材及其制造方法
WO2008066194A1 (en) * 2006-11-28 2008-06-05 Nippon Steel Corporation Free-cutting steel excellent in manufacturability

Family Cites Families (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3292671B2 (ja) * 1997-02-10 2002-06-17 川崎製鉄株式会社 深絞り性と耐時効性の良好な冷延鋼板用の熱延鋼帯
CA2231760A1 (en) * 1998-03-11 1999-09-11 Nisshin Steel Co., Ltd. Cold-rolled steel strip and hot-dip coated cold-rolled steel strip for use as building material and manufacturing method thereof
JP3410970B2 (ja) * 1998-07-02 2003-05-26 日本冶金工業株式会社 打抜き加工性に優れるＦｅ−Ｎｉ系合金の製造方法
JP3990554B2 (ja) * 2000-06-30 2007-10-17 新日本製鐵株式会社 形状凍結性に優れた鋼板およびその製造方法
CA2422753C (en) 2000-09-21 2007-11-27 Nippon Steel Corporation Steel plate excellent in shape freezing property and method for production thereof
RU2197542C1 (ru) * 2001-06-28 2003-01-27 Открытое акционерное общество "Северсталь" Способ производства листовой стали
JP2004068128A (ja) * 2002-08-09 2004-03-04 Daido Steel Co Ltd 切屑破砕性にすぐれた機械構造用鋼
EP1630244B2 (en) * 2003-04-23 2016-08-17 Nippon Steel & Sumitomo Metal Corporation Hot press formed product and method for production thereof
JP4317491B2 (ja) 2004-06-29 2009-08-19 新日本製鐵株式会社 熱間プレス用鋼板
JP4370991B2 (ja) 2004-07-15 2009-11-25 Ｊｆｅスチール株式会社 自動車構造部材用鋼材の耐遅れ破壊特性評価方法および耐遅れ破壊特性に優れた自動車構造部材用鋼材
JP4500124B2 (ja) * 2004-07-23 2010-07-14 新日本製鐵株式会社 ホットプレス用めっき鋼板の製造方法
CA2701559C (en) * 2004-09-15 2013-08-06 Nippon Steel Corporation High strength part and method of production of the same
RU2277594C1 (ru) * 2005-03-30 2006-06-10 Открытое акционерное общество "Северсталь" Способ производства холоднокатаных листов для глубокой вытяжки
SK288275B6 (sk) * 2005-12-01 2015-06-02 Posco Oceľová doska na tvarovanie lisovaním za horúca s tepelnou úpravou a rázovými vlastnosťami, za horúca lisovaný diel z nej vyrobený a spôsob ich výroby
KR100878614B1 (ko) * 2005-12-01 2009-01-15 주식회사 포스코 열처리 경화형 초고강도 강판, 이를 이용한 열처리 경화형부재와 그 제조방법
EP1832667A1 (fr) * 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
JP4846550B2 (ja) * 2006-12-12 2011-12-28 新日本製鐵株式会社 合金化溶融亜鉛めっき用鋼板及び合金化溶融亜鉛めっき鋼板
JP5079795B2 (ja) * 2007-04-11 2012-11-21 新日本製鐵株式会社 低温靭性に優れたプレス加工用溶融めっき高強度鋼板およびその製造方法
CA2729942C (en) * 2008-07-11 2013-08-06 Nippon Steel Corporation Aluminum plated steel sheet for rapid heating hot-stamping, production method of the same and rapid heating hot-stamping method by using this steel sheet
JP5126844B2 (ja) * 2008-08-19 2013-01-23 新日鐵住金株式会社 熱間プレス用鋼板およびその製造方法ならびに熱間プレス鋼板部材の製造方法
JP5316025B2 (ja) 2009-01-28 2013-10-16 Ｊｆｅスチール株式会社 熱間打抜き性に優れたダイクエンチ用鋼板
KR101141015B1 (ko) 2009-06-26 2012-05-02 현대제철 주식회사 수소지연파괴 저항성이 우수한 강판 및 그 제조방법
JP5457840B2 (ja) * 2010-01-07 2014-04-02 株式会社神戸製鋼所 伸びおよび伸びフランジ性に優れた高強度冷延鋼板
JP5064525B2 (ja) * 2010-02-18 2012-10-31 新日本製鐵株式会社 異方性が小さく焼入性に優れた高炭素鋼板及びその製造方法
JP5327106B2 (ja) 2010-03-09 2013-10-30 Ｊｆｅスチール株式会社 プレス部材およびその製造方法
JP5466576B2 (ja) * 2010-05-24 2014-04-09 株式会社神戸製鋼所 曲げ加工性に優れた高強度冷延鋼板
MX360249B (es) * 2011-03-09 2018-10-26 Nippon Steel & Sumitomo Metal Corp Laminas de acero para estampado en caliente, metodo para fabricar las mismas y metodo para fabricar partes con alta resistencia.

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1553836A (zh) * 2001-09-14 2004-12-08 Ŧ�ƶ��� 铸造钢带
JP2003166035A (ja) * 2001-11-28 2003-06-13 Nippon Steel Corp 成形加工後の耐遅れ破壊性に優れた高強度薄鋼板及びその製造方法並びに高強度薄鋼板により作成された自動車用強度部品
CN1890394A (zh) * 2003-12-12 2007-01-03 杰富意钢铁株式会社 汽车构造部件用钢材及其制造方法
CN1782116A (zh) * 2004-11-29 2006-06-07 宝山钢铁股份有限公司 一种800MPa冷轧热镀锌双相钢及其制造方法
WO2008066194A1 (en) * 2006-11-28 2008-06-05 Nippon Steel Corporation Free-cutting steel excellent in manufacturability

Also Published As

Publication number Publication date
MX2014010602A (es) 2014-09-18
US20150024237A1 (en) 2015-01-22
WO2013133270A1 (ja) 2013-09-12
US20180363109A1 (en) 2018-12-20
CA2865910C (en) 2017-10-17
KR20140138829A (ko) 2014-12-04
RU2587106C2 (ru) 2016-06-10
EP2824207A1 (en) 2015-01-14
JP5541421B2 (ja) 2014-07-09
KR101629594B1 (ko) 2016-06-13
JPWO2013133270A1 (ja) 2015-07-30
CA2865910A1 (en) 2013-09-12
US10161023B2 (en) 2018-12-25
IN2014DN08225A (https=) 2015-05-15
EP2824207A4 (en) 2016-03-09
BR112014021801B1 (pt) 2019-10-29
CN104160050A (zh) 2014-11-19
RU2014140161A (ru) 2016-04-27
MX366958B (es) 2019-08-01
ZA201406644B (en) 2016-09-28

Similar Documents

Publication Publication Date Title
CN104160050B (zh) 热冲压用钢板及其制造方法和热冲压钢材
EP3434801B1 (en) High strength steel sheet and high strength galvanized steel sheet
US9353424B2 (en) High strength steel sheet excellent in delayed fracture resistance and low temperature toughness, and high strength member manufactured using the same
EP2886674B1 (en) Steel sheet for hot stamping, method of manufacturing the same, and hot stamped steel sheet member
CN102639739B (zh) 耐氢脆化特性优异的最大拉伸强度为900MPa以上的高强度钢板及其制造方法
JP6540908B2 (ja) 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板およびその製造方法
CN113490758B (zh) 热压部件、热压用冷轧钢板及其制造方法
CN105308203B (zh) 冷轧钢板、镀锌冷轧钢板以及它们的制造方法
CN114207170B (zh) 高强度薄钢板及其制造方法
JP2007314817A (ja) 熱間プレス用鋼板および熱間プレス鋼板部材ならびにそれらの製造方法
CN107148486A (zh) 高强度钢板、高强度热镀锌钢板、高强度热镀铝钢板和高强度电镀锌钢板、以及它们的制造方法
JP4317491B2 (ja) 熱間プレス用鋼板
EP3572543A1 (en) Steel plate for hot stamping
CN108884534A (zh) 薄钢板和镀覆钢板、以及热轧钢板的制造方法、冷轧全硬钢板的制造方法、薄钢板的制造方法和镀覆钢板的制造方法
JP2022095819A (ja) 接合部品及びその製造方法
KR20230038239A (ko) 열간 프레스 부재 및 그 제조 방법
EP4600397A1 (en) Steel plate, resistance spot welding method, resistance spot welding member, and method for manufacturing steel plate
JP2004115843A (ja) 高張力合金化溶融亜鉛めっき鋼板およびその製造方法
TW201313916A (zh) 熱浸鍍鋅鋼板及其製造方法
KR20250150125A (ko) 강판, 부재 및 그들의 제조 방법

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
CP01 Change in the name or title of a patent holder
CP01 Change in the name or title of a patent holder

Address after: Tokyo, Japan, Japan

Patentee after: Nippon Iron & Steel Corporation

Address before: Tokyo, Japan, Japan

Patentee before: Nippon Steel Corporation