CN104045318A - 一种镁玉瓷 - Google Patents
一种镁玉瓷 Download PDFInfo
- Publication number
- CN104045318A CN104045318A CN201410297585.8A CN201410297585A CN104045318A CN 104045318 A CN104045318 A CN 104045318A CN 201410297585 A CN201410297585 A CN 201410297585A CN 104045318 A CN104045318 A CN 104045318A
- Authority
- CN
- China
- Prior art keywords
- parts
- magnesium
- jade porcelain
- firing
- porcelain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种镁玉瓷，包括下列重量份数的物质：镁质粘土10-25份，熔块20-40份，磷酸二氢钙3-7份，过磷酸钙2-9份，石粉20-30份，泥炭15-36份，麦饭石1-5份，滑石20-46份，萤石11-16份，二氧化钛2-8份，锡酸钡1-4份，碳酸钙11-21份，羧甲基纤维素钠1-3.5份，菱镁矿15-29份，钠长石7-21份，碳酸镁3-11份。本发明的有益效果是：实现了一次烧成，同时克服和提高因大量采用滑石材料带来烧成温度产生产品规整度及抗热震性差的问题；合理的原料和坯料配方及生产工艺，是实现镁玉瓷一次烧成的基础，同时也是解决挤压成型困难、烧制产品后强度低的问题的关键。
Description
技术领域
本发明涉及一种镁玉瓷。
背景技术
镁玉瓷具有白度高，半透明度好，瓷质细腻，釉面关泽的特点，在中外陶瓷器领域中属于高档瓷产品，是目前公认的高级宾馆、饭店的理想用瓷。镁玉瓷主要原料为滑石、长石等，滑石原属于工业陶瓷范畴主要应用于电瓷及电子行业作为绝缘电子器件，九十年代后逐渐扩展到日用瓷领域。
现有镁玉瓷的主要的原料为滑石，滑石为片状结构，在挤压成型过程中容易出现坯体中形成定向排列，使坯体产生各向异性排斥，在烧成冷却过程中会引起不同方向收缩不均匀，从而使产品产生较大的应力，将导致产品开裂，又因内应力大也会降低产品的强度和造成产品的后期龟裂。
现有烧制镁玉瓷的制造方法复杂，多采用两次烧成的方法解决该瓷种烧制控制狭窄的问题，即先高温1350℃素烧，再通过1050℃-1150℃釉烧，现有烧制技术不但工序复杂、而且大量采用滑石材料会带来烧成温度产生产品规整度及抗热震性差的问题。
发明内容
本发明所要解决的技术问题是提供一种镁玉瓷。
为解决上述技术问题，本发明采用的技术方案是：
一种镁玉瓷，包括下列重量份数的物质：镁质粘土10-25份，熔块20-40份，磷酸二氢钙3-7份，过磷酸钙2-9份，石粉20-30份，泥炭15-36份，麦饭石1-5份，滑石20-46份，萤石11-16份，二氧化钛2-8份，锡酸钡1-4份，碳酸钙11-21份，羧甲基纤维素钠1-3.5份，菱镁矿15-29份，钠长石7-21份，碳酸镁3-11份。
本发明的有益效果是：
实现了一次烧成，同时克服和提高因大量采用滑石材料带来烧成温度产生产品规整度及抗热震性差的问题；合理的原料和坯料配方及生产工艺，是实现镁玉瓷一次烧成的基础，同时也是解决挤压成型困难、烧制产品后强度低的问题的关键。
具体实施方式
实施例1
一种镁玉瓷，包括下列重量份数的物质：镁质粘土10-25份，熔块20-40份，磷酸二氢钙3-7份，过磷酸钙2-9份，石粉20-30份，泥炭15-36份，麦饭石1-5份，滑石20-46份，萤石11-16份，二氧化钛2-8份，锡酸钡1-4份，碳酸钙11-21份，羧甲基纤维素钠1-3.5份，菱镁矿15-29份，钠长石7-21份，碳酸镁3-11份。
Claims (1)
1.一种镁玉瓷，其特征在于，包括下列重量份数的物质：镁质粘土10-25份，熔块20-40份，磷酸二氢钙3-7份，过磷酸钙2-9份，石粉20-30份，泥炭15-36份，麦饭石1-5份，滑石20-46份，萤石11-16份，二氧化钛2-8份，锡酸钡1-4份，碳酸钙11-21份，羧甲基纤维素钠1-3.5份，菱镁矿15-29份，钠长石7-21份，碳酸镁3-11份。