CN103805126A - 用于保护膜的有机硅胶粘剂 - Google Patents

用于保护膜的有机硅胶粘剂 Download PDF

Info

Publication number
CN103805126A
CN103805126A CN201410065939.6A CN201410065939A CN103805126A CN 103805126 A CN103805126 A CN 103805126A CN 201410065939 A CN201410065939 A CN 201410065939A CN 103805126 A CN103805126 A CN 103805126A
Authority
CN
China
Prior art keywords
organic silicon
silicon adhesive
silane coupling
coupling agent
silicone adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410065939.6A
Other languages
English (en)
Other versions
CN103805126B (zh
Inventor
金闯
包静炎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Sidike New Material Science and Technology Co Ltd
Original Assignee
Suzhou Sidike New Material Science and Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Sidike New Material Science and Technology Co Ltd filed Critical Suzhou Sidike New Material Science and Technology Co Ltd
Publication of CN103805126A publication Critical patent/CN103805126A/zh
Application granted granted Critical
Publication of CN103805126B publication Critical patent/CN103805126B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种用于保护膜的有机硅胶粘剂,所述有机硅胶粘剂由以下质量百分含量的物质经反应后制得:有机硅胶粘剂30~50%;羟基聚硅氧烷2~5%;铂金催化剂2~5%;硅烷偶联剂1-20%;马来醇0.5~5%;增粘树脂10~50%;异丁烷1~30%;所述羟基聚硅氧烷为α,ω-二羟基聚硅氧烷;所述硅烷偶联剂为硅烷偶联剂KH550;所述增粘树脂为MQ树脂。本发明有机硅胶粘剂具有排气性、吸附性,同时微孔是中空的,有吸附小分子的功能。

Description

用于保护膜的有机硅胶粘剂
技术领域
本发明涉及一种有机硅胶粘剂,特别涉及一种用于保护膜的有机硅胶粘剂,属于胶粘材料技术领域。
背景技术
有机硅胶粘剂的粘料是由一种或几种线型、环状或支链型的硅氧烷,在催化剂作用下,通过平衡、加成或缩合等反应制得的高分子质量的线型或交联型硅氧烷组成。有机硅胶粘剂主要有橡胶型和树脂型两类。有机硅胶粘剂具有耐高温、粘着力稳定、持久性好等特点,广泛应用于航空、航海、宇宙飞船、火箭导弹、原子能、电子电器工业等各个领域。随着有机硅胶粘剂系胶带的应用范围的逐步扩大,各行各业对有机硅胶粘剂系胶带的质量和性质方面的应用提出了新的要求。诸多不规则的和不同处理工艺的粘结面,使得有机硅胶粘剂系胶带的应用由简单向特殊的使用转变。一般有机硅胶粘剂系胶带的制备工艺是将有机硅胶粘剂涂布在胶带基材(如各种薄膜、纸等)的表面。有机硅胶粘剂系胶带的一大用途是制成保护膜,用于保护运输或使用过程的玻璃、金属板材、塑料板材等材料的表面,使其表面免受接触性污染或磨痕划伤。当有机硅胶粘剂系胶带保护膜保护电子产品表面时,由于这些表面会涂覆一些水性漆、光油等化学物质,在一般工艺中这些表面都有化学物质溶剂、小分子等残留,用现有的有机硅胶粘剂系保护膜贴合在表面进行保护时,由于有机硅胶粘剂层平整紧实,在被保护表面和有机硅胶粘剂之间没有排气通道,残留的小分子物质挥发时不能排出,长时间使用时会出现色差、圈印、异味等不良现象,这是因为硅胶超级平整性,无法透气导致。
发明内容
本发明提供一种用于保护膜的有机硅胶粘剂,用以制备有机硅胶粘剂保护膜,目的是解决现有的有机硅胶粘剂排气不畅的问题。
为达到上述目的,本发明采用的技术方案是:一种用于保护膜的有机硅胶粘剂,其特征在于:所述有机硅胶粘剂由以下质量百分含量的物质经反应后制得:
有机硅胶粘剂          30~50%;
羟基聚硅氧烷            2~5%;
铂金催化剂             2~5%;
硅烷偶联剂              1-20%;
马来醇                   0.5~5%;
增粘树脂                10~50%;
异丁烷                   1~30%。
上述技术方案中进一步改进的技术方案如下:
1、上述方案中,所述有机硅胶粘剂由以下质量百分含量的物质经反应后制得:
有机硅胶粘剂          30~45%;
羟基聚硅氧烷            2~5%;
铂金催化剂             2~5%;
硅烷偶联剂              2-3%;
马来醇                   0.5~2%;
增粘树脂                30~50%;
异丁烷                   10~15%。 
2、上述方案中,所述羟基聚硅氧烷为α,ω-二羟基聚硅氧烷。
3、上述方案中,所述硅烷偶联剂为硅烷偶联剂KH550,所述硅烷偶联剂是由硅氯仿(HSiCl3)和带有反应性基团的不饱和烯烃在铂氯酸催化下加成,再经醇解而得。
4、上述方案中,所述增粘树脂为MQ树脂,MQ树脂是由单官能团Si-O单元(M单元)与四官能团Si-O单元(SiQZ简称Q单元)组成的一种有机硅树脂,具有双层结构紧密球状物。
由于上述技术方案运用,本发明与现有技术相比具有下列优点和效果:
本发明用于保护膜的有机硅胶粘剂,实现了将一般的有机硅胶粘剂改造成具有微孔结构的微孔型有机硅胶粘剂,使有机硅胶粘剂具有排气性、吸附性,同时微孔是中空的,有吸附小分子的功能。有机硅胶粘剂的微孔结构大小可以调节,微孔分布排列可紧可松,可根据最终要求,来决定微孔的结构和粘性的大小。
具体实施方式
下面结合实施例对本发明作进一步描述:
实施例:一种用于保护膜的有机硅胶粘剂,所述有机硅胶粘剂由以下质量百分含量的物质经反应后制得:
有机硅胶粘剂          30%;
羟基聚硅氧烷            4%;
铂金催化剂             3%;
硅烷偶联剂              2%;
马来醇                  1%;
增粘树脂               50%;
异丁烷                   10%。
上述羟基聚硅氧烷为α,ω-二羟基聚硅氧烷。
上述硅烷偶联剂为硅烷偶联剂KH550。
上述增粘树脂为MQ树脂。
制备方法: 
第一步,选取一种有机硅胶粘剂,添加其他的助剂如有机硅增粘树脂、羟基聚硅氧烷4%、硅烷偶联剂2%、马来醇1%、异丁烷10%等,按照顺序一一添加,搅拌均匀。
第二步,根据发泡剂的种类,选择合适的温度,一般硅胶的固化温度>100度,选择在100度以内发泡的发泡剂,烤箱温度设置如下:50、80、100、120、140、140、70,在50-80度之间是先挥发溶剂,在85度与100度之间进行发泡,在120-180之间进行硅胶的固化。发泡的类型根据发泡剂的不同可以获得开孔的,也可以是闭孔的微孔型有机硅胶粘剂。从而使得微孔型有机硅胶粘剂具有良好的透气性能。
经过测量:微孔的孔径范围分布为1nm~5cm。微孔密度为高密度的,即大于或等于45 kg/m3
上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内。

Claims (5)

1. 一种用于保护膜的有机硅胶粘剂,其特征在于:所述有机硅胶粘剂由以下质量百分含量的物质经反应后制得:
有机硅胶粘剂          30~50%;
羟基聚硅氧烷            2~5%;
铂金催化剂             2~5%;
硅烷偶联剂              1-20%;
马来醇                   0.5~5%;
增粘树脂                10~50%;
异丁烷                   1~30%。
2. 根据权利要求1所述的有机硅胶粘剂,其特征在于:所述有机硅胶粘剂由以下质量百分含量的物质经反应后制得:
有机硅胶粘剂          30~45%;
羟基聚硅氧烷            2~5%;
铂金催化剂             2~5%;
硅烷偶联剂              2-3%;
马来醇                   0.5~2%;
增粘树脂                30~50%;
异丁烷                   10~15%。
3. 根据权利要求1或2所述的有机硅胶粘剂,其特征在于:所述羟基聚硅氧烷为α,ω-二羟基聚硅氧烷。
4. 根据权利要求1或2所述的有机硅胶粘剂,其特征在于:所述硅烷偶联剂为硅烷偶联剂KH550。
5. 根据权利要求1或2所述的有机硅胶粘剂,其特征在于:所述增粘树脂为MQ树脂。
CN201410065939.6A 2012-07-09 2012-07-09 用于保护膜的有机硅胶粘剂 Active CN103805126B (zh)