CN103803951A - 一种陶瓷材料及其制备方法 - Google Patents

一种陶瓷材料及其制备方法 Download PDF

Info

Publication number
CN103803951A
CN103803951A CN201310715103.1A CN201310715103A CN103803951A CN 103803951 A CN103803951 A CN 103803951A CN 201310715103 A CN201310715103 A CN 201310715103A CN 103803951 A CN103803951 A CN 103803951A
Authority
CN
China
Prior art keywords
parts
stupalith
calcine
ceramic material
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310715103.1A
Other languages
English (en)
Other versions
CN103803951B (zh
Inventor
钱云春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU JINGYU PORCELAIN Co.,Ltd.
Original Assignee
SUZHOU HONGQUAN HIGH VOLTAGE CAPACITOR Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU HONGQUAN HIGH VOLTAGE CAPACITOR Co Ltd filed Critical SUZHOU HONGQUAN HIGH VOLTAGE CAPACITOR Co Ltd
Priority to CN201310715103.1A priority Critical patent/CN103803951B/zh
Publication of CN103803951A publication Critical patent/CN103803951A/zh
Application granted granted Critical
Publication of CN103803951B publication Critical patent/CN103803951B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种陶瓷材料及其制备方法，包括以下按重量份数计组分：聚丁二烯环氧树脂10-30份，氧化铝20-30份，高岭土10-25份，稳定剂5-10份，烧结助剂5-10份，环己烷溶液10-30份。本发明采用氧化铝陶瓷与环氧树脂混合制成陶瓷材料密度大于3.80g/cm3，熔点大于2030℃，介电常数大于9.0，抗弯强度大于300MPa，性能上都有所提高，拓展了陶瓷材料在电学领域的应用。

Description

一种陶瓷材料及其制备方法
技术领域
本发明涉及一种陶瓷材料及其制备方法。
背景技术
陶瓷材料是用天然或合成化合物经过成型或高温煅烧制成的一类无机非金属材料，陶瓷的种类很多，用途各异。电容器的外壳等大多都是陶瓷制成，所以对材料介电常数、抗压强度、熔点等都有一定的要求。现有技术中利用单一原料制成陶瓷材料，限制了此类材料的使用。
发明内容
针对现有技术的不足，本发明提供了一种陶瓷材料及其制备方法。
为解决现有问题本发明采用的技术方案为：一种陶瓷材料，包括以下按重量份数计组分：聚丁二烯环氧树脂10-30份，氧化铝20-30份，高岭土10-25份，稳定剂5-10份，烧结助剂5-10份，环己烷溶液10-30份。
优选的是，所述烧结助剂为La2O3。
优选的是，所述稳定剂为SiO2。
上述的一种陶瓷材料的制备方法包括以下步骤：
第一步，按重量份数称取原料；
第二步，将所称取的原料混匀注浆成毛坯件；
第三步，将毛坯件在温度为1000-1500℃下煅烧2-5小时，保温2-3小时候得半成品；
第四步，半成品在温度为800-1200℃下煅烧10-25小时，保温4-6小时候后，再重复煅烧2-4次，每次煅烧持续2-5小时得陶瓷材料。
有益效果：本发明采用氧化铝陶瓷与环氧树脂混合制成陶瓷材料密度大于3.80 g/cm3，熔点大于2030℃，介电常数大于9.0，抗弯强度大于300MPa，性能上都有所提高，拓展了陶瓷材料在电学领域的使用。
具体实施方式
下面通过具体实施例对本发明作进一步详细介绍。
实施例1
一种陶瓷材料，包括以下按重量份数计组分：聚丁二烯环氧树脂10份，氧化铝20份，高岭土10份，SiO25份，La2O35份，环己烷溶液10份。
上述的一种陶瓷材料的制备方法包括以下步骤：
第一步，按重量份数称取原料；
第二步，将所称取的原料混匀注浆成毛坯件；
第三步，将毛坯件在温度为1000℃下煅烧2小时，保温2小时候得半成品；
第四步，半成品在温度为800℃下煅烧10小时，保温4小时候后，再重复煅烧2次，每次煅烧持续2小时得陶瓷材料。
实施例2
一种陶瓷材料，包括以下按重量份数计组分：聚丁二烯环氧树脂30份，氧化铝30份，高岭土25份，SiO210份，La2O310份，环己烷溶液30份。
上述的一种陶瓷材料的制备方法包括以下步骤：
第一步，按重量份数称取原料；
第二步，将所称取的原料混匀注浆成毛坯件；
第三步，将毛坯件在温度为1500℃下煅烧5小时，保温3小时候得半成品；
第四步，半成品在温度为1200℃下煅烧25小时，保温6小时候后，再重复煅烧4次，每次煅烧持续5小时得陶瓷材料。
实施例3
一种陶瓷材料，包括以下按重量份数计组分：聚丁二烯环氧树脂20份，氧化铝25份，高岭土20份，SiO28份，La2O38份，环己烷溶液20份。
上述的一种陶瓷材料的制备方法包括以下步骤：
第一步，按重量份数称取原料；
第二步，将所称取的原料混匀注浆成毛坯件；
第三步，将毛坯件在温度为1200℃下煅烧3小时，保温2.5小时候得半成品；
第四步，半成品在温度为1100℃下煅烧20小时，保温5小时候后，再重复煅烧3次，每次煅烧持续4小时得陶瓷材料。
本发明对陶瓷材料的密度、熔点、介电常数、以及抗弯强度进行检测，结果如下表所述。
 
序号 密度（g/cm3） 熔点（℃） 介电常数 抗弯强度（MPa）
实施例1 3.98 2040 9.7 340
实施例2 4.20 2060 10.5 360
实施例3 4.08 2050 10.0 345
从上表可知：本发明提供的陶瓷材料密度大于3.80 g/cm3，熔点大于2030℃，介电常数大于9.0，抗弯强度大于300MPa。本发明陶瓷材料配方制成的陶瓷材料具有介电常数和抗弯强度。
另外，本发明不限于上述实施方式，只要在不超出本发明的范围内，可以采取各种方式实施本发明。

Claims (4)

1.一种陶瓷材料，其特征在于包括以下按重量份数计组分：聚丁二烯环氧树脂10-30份，氧化铝20-30份，高岭土10-25份，稳定剂5-10份，烧结助剂5-10份，环己烷溶液10-30份。
2.根据权利要求1所述的一种陶瓷材料，其特征在于：所述烧结助剂为La2O3。
3.根据权利要求1所述的一种陶瓷材料，其特征在于：所述稳定剂为SiO2。
4.权利要求1所述的一种陶瓷材料的制备方法，其特征在于包括以下步骤：
第一步，按重量份数称取原料；
第二步，将所称取的原料混匀注浆成毛坯件；
第三步，将毛坯件在温度为1000-1500℃下煅烧2-5小时，保温2-3小时候得半成品；
第四步，半成品在温度为800-1200℃下煅烧10-25小时，保温4-6小时候后，再重复煅烧2-4次，每次煅烧持续2-5小时得陶瓷材料。
CN201310715103.1A 2013-12-23 2013-12-23 一种陶瓷材料及其制备方法 Active CN103803951B (zh)