CN103396087A - 新型高强度瓷绝缘子及其制备方法 - Google Patents

新型高强度瓷绝缘子及其制备方法 Download PDF

Info

Publication number
CN103396087A
CN103396087A CN2013103104347A CN201310310434A CN103396087A CN 103396087 A CN103396087 A CN 103396087A CN 2013103104347 A CN2013103104347 A CN 2013103104347A CN 201310310434 A CN201310310434 A CN 201310310434A CN 103396087 A CN103396087 A CN 103396087A
Authority
CN
China
Prior art keywords
parts
soil
novel high
strength
ceramic insulator
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103104347A
Other languages
English (en)
Inventor
朱文浩
刘少华
董显林
王根水
黄蕴君
罗杰
仲伯煊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU NANCI INSULATOR CO Ltd
Original Assignee
JIANGSU NANCI INSULATOR CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU NANCI INSULATOR CO Ltd filed Critical JIANGSU NANCI INSULATOR CO Ltd
Priority to CN2013103104347A priority Critical patent/CN103396087A/zh
Publication of CN103396087A publication Critical patent/CN103396087A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型高强度瓷绝缘子，包含由如下重量份数的原料配方制成：黑粘土2-5份，矾土35-45份，樟村土5-10份，泾阳土8-20份，左云土6-15份，青草岭7-15份，白胶泥11-20份，长石5-15份，宁海土1-5份，新会土1-5份。本发明瓷绝缘子机械性能好且生产成本低，易于工艺控制。所用原料均为现有的普通陶瓷矿物原料，采用泾阳土，缩短球磨时间，既减少了成本又能改善工艺性能。该配方另一特点是合理匹配不同矿物类型的粘土，是材料具有良好的工艺性能，特别是烧成性能，易于工艺控制，提高瓷件合格率。

Description

新型高强度瓷绝缘子及其制备方法
技术领域
本发明属于电瓷技术领域，，具体涉及一种新型高强度瓷绝缘子配方及其制备方法。
背景技术
电瓷坯料是指黏土原料和熔剂性原料及其他原料（石英、高铝原料或其他矿物原料）按一定比例组成的混合物，经磨细和混合成为可供制坯用泥料，这种制坯用的泥料就简称为坯料。
在确定各种原料比例时必须保证坯料能满足电瓷生产过程所要求的工艺性能和烧成后瓷质的物理性能要求。烧成前坯料的工艺性能只要取决于黏土原料的品质和用量，坯料的烧成工艺主要取决于熔剂原料。
机械强度一直是电瓷生产追求的最重要的性能，因为电瓷材料具有高强度时，在同等电压等级的条件下，可以提高材料的使用率，降低成本。传统的瓷绝缘子，机械强度不高，上釉后对提高电瓷的机、电、热性能效果不好，尤其是不能较大的提高瓷质的弯曲强度。
发明内容
为解决现有技术的不足，本发明的目的在于提供一种机械性能好，且生产成本低的新型高强度瓷绝缘子及其制备方法。
为达到上述目的，本发明是通过以下的技术方案来实现的：一种新型高强度瓷绝缘子，包含由如下重量份数的原料配方制成：黑粘土2-5份，矾土35-45份，樟村土5-10份，泾阳土8-20份，左云土6-15份，青草岭7-15份，白胶泥11-20份，长石5-15份，宁海土1-5份，新会土1-5份。
所述新型高强度瓷绝缘子无釉弯曲强度大于188Mpa，拉伸强度大于115MPa。
上述新型高强度瓷绝缘子的制备方法，首先将原料按配好的比例称料，加入基料原料总重量30%的水得到浆料，然后对浆料进行球磨9-10 h，得到的新浆料经过筛除铁后进行榨泥，得到的泥饼在真空练泥机内挤制，得到的泥段再进行电阴干，最后成型、干燥后即得到生坯；生坯经上釉、烧成、胶装后得到最后的成品。
本发明的有益效果是：本发明瓷绝缘子机械性能好且生产成本低，易于工艺控制。所用原料均为现有的普通陶瓷矿物原料，采用泾阳土，缩短球磨时间，既减少了成本又能改善工艺性能。该配方另一特点是合理匹配不同矿物类型的粘土，是材料具有良好的工艺性能，特别是烧成性能，易于工艺控制，提高瓷件合格率。
具体实施方式
以下结合具体实施例对本发明作具体的介绍。
本发明中所用原料均为现有的普通陶瓷矿物原料。
实施例1：
一种新型高强度瓷绝缘子，包含由如下重量份数的原料配方制成：黑粘土3份、矾土35、樟村土8份、泾阳土8份、左云土8份、青草岭11份、白胶泥15份、长石 8份、宁海土2份、新会土2份制备时，首先将原料按配好的比例称料，加入基料原料总重量30%的水得到浆料，然后对浆料进行球磨9h，得到的新浆料经过筛除铁后进行榨泥，得到的泥饼在真空练泥机内挤制，得到的泥段再进行电阴干，最后成型、干燥后即得到生坯；生坯经上釉、烧成、胶装后得到最后的成品。
本实施例新型高强度瓷绝缘子的性能如下：
体积密度：2.58 g/cm3；
开口孔隙率：0.098%；
闭口孔隙率：7.66%；
拉伸强度：86Mpa；
弯曲强度: 无釉146MPa  上釉182MPa。
实施例2：
一种新型高强度瓷绝缘子，包含由如下重量份数的原料配方制成：黑粘土3份、矾土38份、樟村土7份、泾阳土9份、左云土8份、青草岭9份、白胶泥15份、长石 7份、宁海土2份、新会土2份。制备时，首先将原料按配好的比例称料，加入基料原料总重量30%的水得到浆料，然后对浆料进行球磨10h，得到的新浆料经过筛除铁后进行榨泥，得到的泥饼在真空练泥机内挤制，得到的泥段再进行电阴干，最后成型、干燥后即得到生坯；生坯经上釉、烧成、胶装后得到最后的成品。
本实施例新型高强度瓷绝缘子的性能如下：
体积密度：2.59 g/cm3；
开口孔隙率：0.099%；
闭口孔隙率：7.65%；
拉伸强度：87Mpa；
弯曲强度: 无釉148MPa  上釉185Mpa。
实施例3：与实施例1基本相同，所不同的是新型高强度瓷绝缘子的原料配方，具体如下：
黑粘土2份，矾土45份，樟村土5份，泾阳土9份，左云土6份，青草岭15份，白胶泥11份，长石5份，宁海土1份，新会土1份。
实施例4：与实施例1基本相同，所不同的是新型高强度瓷绝缘子的原料配方，具体如下：
黑粘土5份，矾土35份，樟村土10份，泾阳土8份，左云土10份，青草岭7份，白胶泥14份，长石5份，宁海土3份，新会土3份。
实施例5：与实施例1基本相同，所不同的是新型高强度瓷绝缘子的原料配方，具体如下：
黑粘土2份，矾土36份，樟村土5份，泾阳土8份，左云土6份，青草岭7份，白胶泥11份，长石15份，宁海土5份，新会土5份。
实施例6：与实施例1基本相同，所不同的是新型高强度瓷绝缘子的原料配方，具体如下：
黑粘土2份，矾土35份，樟村土5份，泾阳土11份，左云土9份，青草岭8份，白胶泥20份，长石6份，宁海土2份，新会土2份。
实施例7：与实施例1基本相同，所不同的是新型高强度瓷绝缘子的原料配方，具体如下：
黑粘土2份，矾土36份，樟村土6份，泾阳土16份，左云土15份，青草岭7份，白胶泥11份，长石5份，宁海土1份，新会土1份。
实施例8：与实施例1基本相同，所不同的是新型高强度瓷绝缘子的原料配方，具体如下：
黑粘土2份，矾土35份，樟村土5份，泾阳土20份，左云土6份，青草岭9份，白胶泥15份，长石5份，宁海土2份，新会土1份。
以上所述仅是本发明的优选实施方式，应当指出：对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (3)

1.一种新型高强度瓷绝缘子，其特征在于，包含由如下重量份数的原料配方制成：黑粘土2-5份，矾土35-45份，樟村土5-10份，泾阳土8-20份，左云土6-15份，青草岭7-15份，白胶泥11-20份，长石5-15份，宁海土1-5份，新会土1-5份。
2.根据权利要求1所述的新型高强度瓷绝缘子，其特征在于，所述新型高强度瓷绝缘子无釉弯曲强度大于145MPa,上釉强度大于180MPa。
3.根据权利要求1所述的新型高强度瓷绝缘子的制备方法，其特征在于，
首先将原料按配好的比例称料，加入基料原料总重量30%的水得到浆料，然后对浆料进行球磨9-10h，得到的新浆料经过筛除铁后进行榨泥，得到的泥饼在真空练泥机内挤制，得到的泥段再进行电阴干，最后成型、干燥后即得到生坯；生坯经上釉、烧成、胶装后得到最后的成品。
CN2013103104347A 2012-09-05 2013-07-23 新型高强度瓷绝缘子及其制备方法 Pending CN103396087A (zh)