CN102408224A - 制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料 - Google Patents
制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料 Download PDFInfo
- Publication number
- CN102408224A CN102408224A CN2011102149233A CN201110214923A CN102408224A CN 102408224 A CN102408224 A CN 102408224A CN 2011102149233 A CN2011102149233 A CN 2011102149233A CN 201110214923 A CN201110214923 A CN 201110214923A CN 102408224 A CN102408224 A CN 102408224A
- Authority
- CN
- China
- Prior art keywords
- clay
- porcelain insulator
- shaped porcelain
- railway contact
- strong material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,包括如下重量百分比的成分:矾土粉25-28%、工业氧化铝8-12%、青草岭粘土25-28%、左云粘土9-13%、长石6-9%、樟村粘土13-18%、宁海粘土3-4%。本发明的优点是:减少普通高铝瓷配方中的铝矾土用量,用工业氧化铝代替部分矾土,从而提高原料中铝的含量,而且不需要增粗棒形瓷绝缘子的尺寸,实现超高强度的棒形瓷绝缘子,这样给生产、安装以及使用带来很大的方便。
Description
技术领域
本发明涉及一种绝缘子的生产原料,具体说是一种制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料。
背景技术
随着高速铁路行车速度的提高,为保证电力机车可靠运行,加大了接触线张力。当接触线 张力增大,支持导线的棒形瓷绝缘子必须具有较高的机械强度才能满足要求,开行速度250公 里/小时及以上的铁道线上对棒形瓷绝缘子的抗弯强度要求必须达到16KN以上。
众所周知,只要加粗棒形瓷绝缘子的尺寸,便可提高产品的机械强度,但是,由于现有的高铝瓷配方强度已经达到极限值,而且Al2O3的含量较低,因此要想提高产品的机械强度只能将棒形瓷绝缘子尺寸加粗,但是我们不能为了提高绝缘子机械强度,而一味增粗产品尺寸,否则棒形瓷绝缘子做得过大,重量将会很重,将给生产、安装以及使用带来一系列的麻烦,铁道线电气化接触网导线上的承重将无法得到有效控制。因此,我们还需在原料的配方中有所创新和突破,保证在不粗产品尺寸和重量的前提下进一步增强产品自身的机械强度性能。
发明内容
发明目的:为了克服现有技术的不足,本发明提供一种能提高机械强度的。
技术方案:为了解决上述技术问题,本发明所采用的技术方案为:一种制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,包括如下重量百分比的成分:矾土粉25-28%、工业氧化铝8-12%、青草岭粘土25-28%、左云粘土9-13%、长石6-9%、樟村粘土13-18%、宁海粘土3-4%。
优选方案:矾土粉27%、工业氧化铝10%、青草岭粘土27%、左云粘土10%、长石7%、樟村粘土15%、宁海粘土4%。
所述矾土粉为氧化铝含量84%以上,真密度3.5g/cm3以上,细度250目以上。
所述工业氧化铝的氧化铝含量98%以上,真密度3.9g/cm3以上,细度120目以上。
所述左云粘土的氧化铝含量22%以上,结合力1.5Mpa以上,可塑性指数18以上。
所述樟村粘土的氧化铝含量32%以上,氧化钾7~12%。
所述宁海粘土的氧化铝含量20%以上,结合力2.0Mpa以上,可塑性指数28以上。
有益效果:与现有技术相比,本发明的优点是:减少普通高铝瓷配方中的铝矾土用量,用工业氧化铝代替部分矾土,从而提高原料中铝的含量,而且不需要增粗棒形瓷绝缘子的尺寸,实现超高强度的棒形瓷绝缘子,这样给生产、安装以及使用带来很大的方便。
具体实施方式
下面结合实施例对本发明作进一步的详细说明。
实施例1:一种制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,包括如下重量百分比的成分:矾土粉27%、工业氧化铝10%、青草岭粘土27%、左云粘土10%、长石7%、樟村粘土15%、宁海粘土4%;
其中矾土粉为氧化铝含量84%以上,真密度3.5g/cm3以上,细度250目以上;工业氧化铝的氧化铝含量98%以上,真密度3.9g/cm3以上,细度120目以上;左云粘土的氧化铝含量22%以上,结合力1.5Mpa以上,可塑性指数18以上;樟村粘土的氧化铝含量32%以上,氧化钾7~12%;宁海粘土的氧化铝含量20%以上,结合力2.0Mpa以上,可塑性指数28以上。
设计原理:提高原料中Al2O3的含量是提高棒形瓷绝缘子机械强度的有效途径,而增加的Al2O3均以刚玉晶体的形态引入。
将上述高强度材料的各组分按配比混合均匀后依次经球磨、除铁、真空机制、制坯、干燥、上釉,最后在最高烧成温度为1240~1260℃的条件下烧成即得到所述的高强度材料;其中球磨细度为250目分析筛筛余为0.3~0.8%;通过除铁工序后的物料的要求是铁点为250目分析筛筛余不超过20粒;干燥后的物料水份1.0~1.8%(重量);上釉的釉层厚度0.2~0.6mm。
下面是绝缘子传统配方与本发明配方的比较:
配方名称 | 矾土(%) | 工业氧化铝(%) | 产品受力部位直径(mm) | 机械强度(kN) |
传统配方 | 37 | 0 | 125 | 19 |
本发明 | 27 | 10 | 125 | 25 |
从上表可以看出,采用本发明配方制成的绝缘子机械强度明显优于用传统配方制成的绝缘子。
实施例2:与实施例1基本相同,所不同的是高强度材料的组分:矾土粉28%、工业氧化铝8%、青草岭粘土25%、左云粘土11%、长石9%、樟村粘土18%、宁海粘土4%。
实施例3:与实施例1基本相同,所不同的是高强度材料的组分:矾土粉28%、工业氧化铝12%、青草岭粘土25%、左云粘土13%、长石6%、樟村粘土13%、宁海粘土3%。
实施例4:与实施例1基本相同,所不同的是高强度材料的组分:矾土粉26%、工业氧化铝10%、青草岭粘土28%、左云粘土9%、长石8%、樟村粘土16%、宁海粘土3%。
实施例5:与实施例1基本相同,所不同的是高强度材料的组分:矾土粉26%、工业氧化铝10%、青草岭粘土26%、左云粘土12%、长石8%、樟村粘土14%、宁海粘土4%。
Claims (7)
1.一种制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,其特征在于,包括如下重量百分比的成分:矾土粉25-28%、工业氧化铝8-12%、青草岭粘土25-28%、左云粘土9-13%、长石6-9%、樟村粘土13-18%、宁海粘土3-4%。
2.根据权利要求1所述的制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,其特征在于,矾土粉27%、工业氧化铝10%、青草岭粘土27%、左云粘土10%、长石7%、樟村粘土15%、宁海粘土4%。
3.根据权利要求1所述的制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,其特征在于,所述矾土粉为氧化铝含量84%以上,真密度3.5g/cm3以上,细度250目以上。
4.根据权利要求1所述的制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,其特征在于,所述工业氧化铝的氧化铝含量98%以上,真密度3.9g/cm3以上,细度120目以上。
5.根据权利要求1所述的制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,其特征在于,所述左云粘土的氧化铝含量22%以上,结合力1.5Mpa以上,可塑性指数18以上。
6.根据权利要求1所述的制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,其特征在于,所述樟村粘土的氧化铝含量32%以上,氧化钾7~12%。
7.根据权利要求1所述的制作高速电气化铁路接触网棒形瓷绝缘子用的高强度材料,其特征在于,所述宁海粘土的氧化铝含量20%以上,结合力2.0Mpa以上,可塑性指数28以上。