CN103756370A - 一种导电珠光颜料 - Google Patents

一种导电珠光颜料 Download PDF

Info

Publication number
CN103756370A
CN103756370A CN201410011012.4A CN201410011012A CN103756370A CN 103756370 A CN103756370 A CN 103756370A CN 201410011012 A CN201410011012 A CN 201410011012A CN 103756370 A CN103756370 A CN 103756370A
Authority
CN
China
Prior art keywords
electro
conductive
layer
mica
pearlescent pigment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410011012.4A
Other languages
English (en)
Inventor
郭俊怀
宋晓丽
谭丽颖
许田杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
OUKE FINE CHEMICAL INDUSTORY CO Ltd HEBEI
Original Assignee
OUKE FINE CHEMICAL INDUSTORY CO Ltd HEBEI
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by OUKE FINE CHEMICAL INDUSTORY CO Ltd HEBEI filed Critical OUKE FINE CHEMICAL INDUSTORY CO Ltd HEBEI
Priority to CN201410011012.4A priority Critical patent/CN103756370A/zh
Publication of CN103756370A publication Critical patent/CN103756370A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种导电珠光颜料，以云母为基质，在基质表面包覆有占导电珠光颜料质量45～60%的导电层，其中，所述导电层为二氧化锡与三氧化二锑的混合物。在基质表面与导电层之间还可有一层二氧化钛层。充分利用现有珠光颜料产生的细云母余料资源，与现有导电粉体相比，本发明的导电珠光颜料通过二氧化钛层可调节呈浅色或半透明，具有一定的光泽，非常有利于后期的配色，同时耐候性好，耐酸碱，不可燃，导电性好，电阻率为5～20Ω·cm。

Description

一种导电珠光颜料
技术领域
本发明属于无机颜料领域，具体涉及一种导电珠光颜料。
背景技术
珠光颜料是一种极其美丽的具有珍珠光泽和金属光泽的颜料，它是由一种或数种金属氧化物薄层包覆于光洁透明的云母表面构成的，改变不同金属氧化物及其薄层的厚度，就能产生不同的珠光效果，具有无毒、不导电、耐热、耐光、耐化学腐蚀等优良特性，从而得到迅速发展，因此被广泛应用在涂料、塑料、皮革、橡胶、油墨、纸张印刷、纺织品印染、化妆品等领域。
珠光颜料在生产过程中会产生一定比例的粒径细，径厚比差的云母，然而径厚比越小，制成的珠光颜料光泽度越差，这就给其应用范围造成一定困扰，会造成了大量细粒径的云母积压，不仅占用大量空间进行保管，耗费人力物力，而且使资本流通变慢，阻碍了企业更好的发展。按现有技术，对于小于5微米的云母，由于径厚比太小一般是无法用于制备珠光颜料的，在生产过程中基本上是自然流失掉。如何变废为宝充分合理地利用不可再生的资源，成了很多珠光颜料企业面临的日益严重的问题。
传统的导电颜料是金属粉末，如金、银、铜等；还有炭黑，石墨等非金属粉末，这些颜料有的颜色很深，给后期的应用配色等造成了一定困难。而金属粉末造价高，耐酸碱性差，在涂料中分散性也不佳，制造金属粉末时，极细的金属粉末易燃、易爆也有很大的危险性。
发明内容
本发明的目的是克服现有技术的上述缺陷，提供一种导电珠光颜料。
本发明实现上述目的所采用的技术方案如下：
一种导电珠光颜料，以云母为基质，在基质表面包覆有占导电珠光颜料质量45～60%的导电层，其中，所述导电层为二氧化锡与三氧化二锑的混合物。
进一步，所述二氧化锡与三氧化二锑的质量比为（7～8）：1。
进一步，在基质表面与导电层之间还有一层二氧化钛层。
进一步，所述二氧化钛层占导电珠光颜料质量的10～20%。
进一步，所述云母的粒径≤15μm。
本发明充分利用现有珠光颜料产生的细云母余料资源，与现有导电粉体相比，本发明的导电珠光颜料通过薄薄的二氧化钛层可调节呈浅色或半透明，在物体表面铺展开来具有一定的反光效果，非常有利于后期的配色，同时耐候性好，耐酸碱，不可燃，导电性好，电阻率为5～20Ω·cm。
具体实施方式
以下结合实施例对本发明做进一步详细说明。
实施例1
1、取 5-15μm的云母粉30g，去离子水1000mL，投至反应釜中，搅拌均匀，制成悬浮溶液，调pH值至1.0，保持反应釜内温度75±5℃；
2、取80g/L的SnCl4溶液700mL，SbCl3 6.5g，加入到80mL浓度30%的HCl溶液，配制成锡盐和锑盐的混合溶液，在搅拌条件下将混合溶液匀速加入到上述反应釜中，此过程中保持反应釜中pH值保持在1.0～1.5，加完混合溶液后继续搅拌20分钟，调pH为7.0，搅拌20分钟后，放料，抽滤、洗涤，120℃烘干，600℃煅烧1小时，得到半透明的导电珠光颜料，其成分为云母45.1wt%，SnO2/Sb2O3 54.9wt%，电阻率9Ω·cm。
实施例2
1、取 5-15μm的云母粉30g，去离子水1000mL，投至反应釜中，搅拌均匀，制成悬浮溶液，调pH值为2.0，保持反应釜内温度75±5℃；
2、取250g/L的TiCl4溶液80mL，在搅拌条件下匀速加入到反应釜中，此过程保持pH值1.8～2.2，加完后继续搅拌20分钟；
3、取80g/L的SnCl4溶液700mL，SbCl3 6.5g， 加入60mL浓度30%的HCL溶液，配制成锡盐和锑盐的混合溶液，在搅拌条件下将混合溶液匀速加入到反应釜中，此过程中保持反应釜中pH值在1.3～1.7，加完混合溶液后继续搅拌20分钟，调pH为7.0，搅拌20分钟后放料，抽滤、洗涤，120℃烘干，600℃煅烧1小时，得到白中略带一点灰头的浅色导电珠光颜料，在物体表面展开后能反射亮光，其成分为云母40wt%，TiO2 11.2wt%，SnO2/Sb2O3 48.8wt%，电阻率10Ω·cm。
实施例3
1、沉淀池中的物料粒子有大有小，除了一些云母外，还有散落的半成品，经胶体磨研磨后，产物经分级处理，较大粒子可再回到胶体磨中研磨，得到较小粒径(5微米左右)的云母粒子，以其作为基质材料。取较细小粒径云母10g，去离子水800mL，投至反应釜中，搅拌均匀，制成悬浮溶液，调pH值为2.0，保持反应釜内温度75±5℃；
2、取250g/L的TiCl4溶液80mL，在搅拌条件下匀速加入到反应釜中，此过程保持pH值1.8~2.0，加完后继续搅拌20分钟；
3、取80g/L的SnCl4溶液500mL，SbCl3 5g， 加入60mL浓度30%的HCL溶液，配制成锡盐和锑盐的混合溶液，在搅拌条件下将混合溶液匀速加入到反应釜中，此过程中保持反应釜中pH值保持在1.2～1.5，加完混合溶液后继续搅拌20分钟，调pH为7.0，再搅拌20分钟后，放料，抽滤、洗涤，120℃烘干，600℃煅烧1小时，得到较细的浅色导电珠光颜料，其成分为云母22.3wt%，TiO2 18.8wt%，SnO2/Sb2O3 58.9 wt%，电阻率18Ω·cm。

Claims (5)

1.一种导电珠光颜料，以云母为基质，其特征在于：在基质表面包覆有占导电珠光颜料质量45～60%的导电层，其中，所述导电层为二氧化锡与三氧化二锑的混合物。
2.根据权利要求1所述导电珠光颜料，其特征在于：所述二氧化锡与三氧化二锑的质量比为（7～8）：1。
3.根据权利要求1所述导电珠光颜料，其特征在于：在基质表面与导电层之间还有一层二氧化钛层。
4.根据权利要求3所述导电珠光颜料，其特征在于：所述二氧化钛层占导电珠光颜料质量的10～20%。
5.根据权利要求1～4任一所述导电珠光颜料，其特征在于：所述云母的粒径≤15μm。
CN201410011012.4A 2014-01-10 2014-01-10 一种导电珠光颜料 Pending CN103756370A (zh)