CN1037261C - 高透光度的硅灰石质瓷 - Google Patents

高透光度的硅灰石质瓷 Download PDF

Info

Publication number
CN1037261C
CN1037261C CN90105537A CN90105537A CN1037261C CN 1037261 C CN1037261 C CN 1037261C CN 90105537 A CN90105537 A CN 90105537A CN 90105537 A CN90105537 A CN 90105537A CN 1037261 C CN1037261 C CN 1037261C
Authority
CN
China
Prior art keywords
wollastonite
porcelain
transmittance
ceramic material
glaze
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN90105537A
Other languages
English (en)
Other versions
CN1059326A (zh
Inventor
杨子初
冯波
谢晓静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CERAMICS INST HUNAN PROV
Original Assignee
CERAMICS INST HUNAN PROV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CERAMICS INST HUNAN PROV filed Critical CERAMICS INST HUNAN PROV
Priority to CN90105537A priority Critical patent/CN1037261C/zh
Publication of CN1059326A publication Critical patent/CN1059326A/zh
Application granted granted Critical
Publication of CN1037261C publication Critical patent/CN1037261C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明是一种陶瓷新材质，利用硅灰石作为主要熔剂原料生产日用陶瓷(其中包括艺术瓷)。该瓷种烧成温度低，烧成范围宽(1180℃～1280℃)，不变形，透光性极强，在氧化焰气氛烧成时白里泛嫩黄；在还原焰烧成下呈现绿玉色。工艺易掌握、节能，具有大的经济效果。

Description

本发明属于陶瓷新材质。
到目前为止，日用陶瓷(包括艺术瓷)的瓷质基本上属于钾长石、钠长石质瓷，即坯料所用的熔剂原料主要是钾长石或钠长石。但还没有人用硅灰石作为主要熔剂原料，且含量超过长石组分的瓷质，即硅灰石质瓷(见检索资料)，硅灰石一般都只作为精陶的成分，而精陶是一种半烧结产品，且硅灰石不是作为熔剂，我国硅灰石资源相当丰富，这种原料大量应用于日用陶瓷上产生高透光度的瓷质，从而提高日用陶瓷档次，特别是其艺术美感。
本发明的目的是研制出一种硅灰石为主要熔剂的、具有高透光度(其透光度为50-70)、烧成温度低且烧成范围宽的新瓷种。
本发明的技术内容主要是解决坯釉配方问题，充分利用硅灰石的优良特性，第一：硅灰石在高温下与高岭石反应生成钙长石和方石英，而生成的石英具有较强的活性，其溶解于长石中的速度及溶解的量都很大，从而能加快反应的进行，尽而达到促进烧结、降低烧成温度的目的。第二：由于硅灰石与高岭石反应生成的石英具有较强的活性，能较多地溶解于长石玻璃中，增强了坯体在高温下的抗变形能力，故坯料中可引入大量石英作为骨架，更进一步防止坯体内因大量液体出现而易倒塌的现象发生，即拓宽了烧成温度范围，第三：利用硅灰石阻止莫来石的生成，提高其透光性。因硅灰石与高岭石生成的钙长石与钾长石在任何情况下都不混熔，相当于钙长石将高岭石中的三氧化二铝络合了，相对而言莫来石生成量较少，而莫来石降低瓷胎的透光性能，所以该发明透发性较一般瓷质都强。
(一)坯料配方
a、坯料化学百分组成： SiO250～78％；Al2O310～29％；Fe2O3＜1％；CaO2.5～15％；MgO0.2～1％，(KNa)2O1～2％；TiO2＜0.5％.(wt％)
b、示性矿物百分组成：
高岭土25～70％；石英15～40％；
硅灰石5～30％，钾长石0～20％；
滑石0.5～3％.(wt％)
其中关键是引入的硅灰石量。
烧成温度1180℃～1280℃，氧化焰或还原焰均可。
高透光性硅灰石质瓷的坯料制备工艺，产品制造的工艺流程，以及工艺控制与其他普通日用瓷相同。即：原料—配料—湿式—球磨—过筛—除铁—抽浆—压滤—陈腐—练泥—成型—干燥—精坯—施釉—烧成—检验—装饰—彩烧—成品检验—包装—入库。
(二)釉料配方
根据高透光性硅灰石质瓷的特点，我们在釉配方中引入钾长石、滑石等提高坯釉结合性能，提高釉面硬度。引入锂辉石降低烧成温度及釉的膨胀系数，利用其硅灰石降低烧成温度，拓宽烧成范围，增强其透光性能。
釉料配方百分组成：(wt％)
a、化学百分组成： SiO255～70％；Al2O35～14％；Fe2O3＜0.5％；CaO2.5～10％；(KNa)2O4.5～7.5％； TiO2＜0.3％，Li2O微量-1.5％(wt％)
b、示性矿物组成：
高岭土5～11％；石英5～25％；
钾长石48～60％；硅灰石5～25％；
锂辉石0-10％，滑石0～15％。(wt％)
烧成温度为1180℃～1280℃
釉料制备工艺流程和工艺控制与其他日用陶瓷釉料相同。即：原料—配料—湿式球磨—检验细度—过筛除铁—除腐—备用。
该发明是一种陶瓷新瓷种，该瓷种与目前的普通陶瓷的优良点主要有如下几点：
1.该瓷种烧成温度低，可大量节能，最低为1180℃；
2.该瓷种中引入大量的硅灰石作为熔剂原料；
3.该瓷种具有较强的透光性能，透光度高达70度，而目前的瓷种具有40-50度；
4.该瓷种具有较宽的烧成温度范围(1180-1280℃)；
5.该瓷种在氧化焰下烧成泛嫩黄，柔洁如玉；在还原焰下烧成呈绿玉色，极富质感。
实施例：坯釉配方见表1，原料百分组成见表2。(表见文后)表1
                           坯釉配方实例
    名称     坯料     釉料
示性矿物百分组成(wt％)     界牌泥  50％硅灰石  17％钾长石  7％石英    24％滑石    1％     界牌泥  10％钾长石  48％硅灰石  14％锂辉石  4％石英    8％滑石    15％
       SiO2Al2O3化  学CaOMgO百  分(KNa)2OFe2O3组  成TiO2(w t％)Li2OI·L合计     77.58％10.32％5.7％0.80％1.80％0.20％微量/3.60％100.00     70.10％11.20％5.20％3.70％8.10％0.01％/0.50％0.60％99.41
表2
    名称    界牌泥    硅灰石    钾长石     滑石    锂辉石     石英
    SiO2     68.60     50.76     65.76     61.44     62.91     95.31
    Al2O3     21.40     0.91     18.91     0.5     28.42     1.93
    CaO     0.34     42.33     0.25     1.30     0.11     0.39
    MgO     0.05     1.27     0.14     31.31     0.13     0.40
  (KNa)2O     2.27     0.19     13.50     /     1.15     /
    Fe2O3     0.33     0.74     0.14     0.10     0.53     0.26
    TiO2     0.065     0.02
    Li2O     6.78
    I·L     8.94     3.83     0.50     5.52     0.28     1.74
工艺流程与普通日用瓷相同(如前述)。工艺控制：
坯料细度：250目筛余＜0.5％，
釉料细度：250目筛余＜0.3％，
烧成温度：1180～1280℃，
烧成气氛：氧化或还原均可。

Claims (1)

1.高透光度硅灰石质瓷，包含有矿物原料硅灰石、长石、高岭土、石英，其特征在于：
a、其坯体组成成分及配比为：
原料       配比(Wt％)
高岭土     25-70％
石英       15-40％
硅灰石     5-30％
钾长石     0-20％
滑石       0.5-3％
b、其釉料组成成分及配比为：
原料      配比(Wt％)
高岭土     5-11％
硅灰石     5-25％
钾长石     48-60％
锂辉石     0-10％
滑石       0-15％
CN90105537A 1990-08-29 1990-08-29 高透光度的硅灰石质瓷 Expired - Fee Related CN1037261C (zh)