CN1022619C - 钠长石质瓷 - Google Patents

钠长石质瓷 Download PDF

Info

Publication number
CN1022619C
CN1022619C CN 88105656 CN88105656A CN1022619C CN 1022619 C CN1022619 C CN 1022619C CN 88105656 CN88105656 CN 88105656 CN 88105656 A CN88105656 A CN 88105656A CN 1022619 C CN1022619 C CN 1022619C
Authority
CN
China
Prior art keywords
albite
porcelain
glaze
blank
firing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 88105656
Other languages
English (en)
Other versions
CN88105656A (zh
Inventor
罗德高
戴慕潜
刘春阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CERAMICS INST HUNAN PROV
Original Assignee
CERAMICS INST HUNAN PROV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CERAMICS INST HUNAN PROV filed Critical CERAMICS INST HUNAN PROV
Priority to CN 88105656 priority Critical patent/CN1022619C/zh
Publication of CN88105656A publication Critical patent/CN88105656A/zh
Application granted granted Critical
Publication of CN1022619C publication Critical patent/CN1022619C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

以钠长石作为主要熔剂原料的纳长石质瓷,坯料中钠长石的重量百分含量为22~35%。烧成温度为1190~1320℃,氧化焰、还原焰烧成均可。成本低,可快速烧成。成瓷效果好,胎体透明度高,釉面柔和适于生产高档日用瓷和艺术瓷。

Description

本发明属于陶瓷新材质。
到目前为止,日用陶瓷(包括艺术瓷)的瓷质基本上属于钾长石质瓷,即坯料所用的熔剂原料主要是钾长石,而没有以钠长石为主要熔剂原料的瓷质,即钠长石质瓷(见检索资料)。钠长石具有熔融温度低等优良性能,但过去人们普遍认为,钠长石膨胀系数大,高温粘度小,在陶瓷坯体中应用难度大,因而以钠长石作为主要熔剂原料而制成钠长石质瓷似乎是不可想象的事。而我国钠长石资源十分丰富,地质储量相当可观,这些宝贵的资源至今没有在陶瓷工业中得到广泛的利用。
本发明的目的,就是要研制一种能大量应用钠长石的低温新瓷质,使其具有低温烧成的特点,技术经济价值好,性能优良。
本发明技术内容,主要是解决坯釉配方问题。充分利用钠长石的优点,克服因钠长石膨胀系数大、高温粘度小,而影响制品热性能的缺点。由于陶瓷制品的热稳定性是由多方面因素决定的,各因素之间相互影响相互制约,本发明在配方中采取了一些措施,合理解决了这一问题。首先是利用钠长石高温粘度小、能熔解较多的游离石英,并有利于莫来石、堇青石的均匀生长的特点,从而提高制品的热稳定性。其次,提高坯釉的结合性能,以增加釉的弹性系数,增加抵抗由于热交换引起胎釉之间应力的能力,从而提高制品的热稳定性。再其次是利用钠长石高温粘度小,能熔解大量游离石英,玻璃体相应增多的性质,使胎体具有较高的透明度,同时又有利于莫来石、堇青石晶体的均匀生成,使坯体烧成温度范围拓宽。
在坯体中引入白云石,也是本发明的一项重要技术措施。在目前陶瓷行业中,熔剂原料除了使用钾长石和钾微斜长石矿物外,很少利用碳酸盐作为坯料熔剂原料。本发明打破了传统配方,大胆引入白云石矿物。白云石中MgO能使坯体在烧成过程中生成堇青石,这对降低坯体膨胀系数,提高热稳定性和增大烧成温度范围是十分有利的。
(一)坯料配方
a.坯料化学重量百分组成:
SiO265~70% Al2O320~25% Fe2O30.3~0.5%
CaO0.5~2% MgO0.5~1.3% K2O0.2~0.5%
Na2O2.5~4.2%
其中关键组成为:Na2O、SiO2、Al2O3
b.示性矿物重量百分组成:
高岭土40~50%    钠长石22~35%
石英20~25%    白云石1~6%
其中突出特征是钠长石的组成范围。本发明所用的钠长石,还包括钠长石的风化或半风化矿物。
烧成温度1190~1320℃,氧化焰或还原焰均可。
钠长石质瓷的坯料制备。产品制造工艺流程及工艺控制与其他普通日用瓷相同。即:
原料-配料-湿式球磨-过筛-除铁-抽浆-压滤-陈腐-练泥-成型-干燥-精坯-施釉-烧成-检验-装饰-彩烧-成品检验-包装-入库。
(二)釉料配方
根据钠长石质瓷的特点,风们选择了坯釉结合性能好、膨胀系数与钠长石质瓷胎匹配的钙釉。釉料以钾长石为主要熔剂。引入方解石,能促进坯釉结合,并提高釉面硬度和光泽。
此外,釉中还加入了少量滑石和工业氧化锌,以降低釉料烧成温度,增大烧成温度范围,并提高釉面光泽度和白度,增加釉层弹性系数,提高制品 热稳定性。
釉料的组成范围如下:
a.化学重量百分组成
SiO265~ 70% Al2O311~13% Fe2O30.1~0.5%
CaO5~10% MgO1.5~2% K2O5.5~6.5%
Na2O1~1.5%ZnO微量~5.0%
b.示性矿物重量百分组成
钾长石    40~45%    石英    25~28%
滑石    5~10%    方解石    5~15%
高岭土    8~10%    工业氧化锌微量~5.0%
烧成温度为1180~1320℃
试验证明:上述釉料与坯体结合良好,烧后釉面光亮,具有油脂光泽。
釉料制备工艺流程和工艺控制与其他日用陶瓷釉料相同,即:
原料-配料-湿式球磨-检验细度-过筛除铁-陈腐-备用。
本发明开辟了一种新瓷种。产品物理性能达到日用细瓷器“GB3532-83”标准。与现有国内外日用瓷比较,钠长石质瓷具有更突出的风格特点和优良的性能。
(1)烧成温度低,最低烧成温度为1190℃,可一次低温烧成。节能效果显著,与目前日用瓷(1300~1400℃烧成)比较,节能50%以上。为我国降低日用瓷烧成温度创出了一条新路。
(2)外观质量好,美感效果强。突出特点是透明度高、釉面柔和。
(3)适应品种范围广。适应于高档艺术瓷、高档日用细瓷。
(4)成本低。钠长石的价格是钾长石的40%左右,且原料丰富。
(5)钠长石在陶瓷工业中的应用开辟了新途径。
(6)生产易控制。产品适应氧化焰,也适应还原焰。可快速烧。易推广。
实施例:
本实施例为低温瓷。
坯釉配方列于表1,原料化学组成列于表2。
坯釉配方实例
单位:重量百分比    表1
名称    坯    釉
原    界牌桃红泥46    长石50    石英25
料    %    衡山半风化钠长石50    方解石10    界牌桃红泥10
组    白云石1    烧滑石5
成    膨润土3    外加烧ZnO5
SiO269.94 68.01
Al2O323.74 11.79
化 Fe2O30.29 0.12
学    CaO    1.09    6.04
组    MgO    0.59    1.70
成 K2O 0.28 6.01
% Na2O 4.09 1.34
ZnO    5.03
合计    100.02    100.04
坯釉原料化学重量百分比组成    表2
成份%
SiO2Al2O3Fe2O3CaO MgO K2O Na2O I.L 合计
名称
衡山半风化
钠长石    64.99    23.02    0.15    0.79    0.34    0.16    7.54    2.73    99.72
界牌桃红泥    68.09    22.12    0.37    0.63    0.22    0.25    0.11    8.68  100.47
耒阳膨润土    61.50    19.93    0.70    0.85    2.37    2.00    0.66    12.23  100.24
东安白去石    0.90    0.30    0.14    31.20    20.90    46.00    99.44
方解石    1.07    0.44    0.08    54.54    1.08    0.33    43.30    100.84
烧滑石    67.13    1.35    0.12    0.60    30.46    0.34    0.26    100.26
平江长石    65.15    18.51    0.11    0.73    11.7    2.62    0.56    99.44
汨罗石英    98.33    0.45    0.06    0.27    0.10    99.21
工艺流程:与一般日用陶瓷相同(前述)
工艺控制:
坯料细度:250目筛余<0.5%
釉料细度:250目筛余<0.02%
烧成温度:1190~1230℃
烧成气氛:氧化焰或还原焰。

Claims (2)

1、钠长石质瓷,其特征在于所说的钠长石质瓷由下述坯料制成,坯料的化学重量百分组成为:SiO265~70%,Al2O320~25%,Fe2O30.3~0.5%,CaO0.5~2.0%,MgO0.5~1.3%,K2O0.2~0.5%,Na2O2.5~4.2%;坯料示性矿物重量百分组成为:高岭土40~50%、石英20~25%、钠长石22~35%、白云石1~6%。
2、根据权利要求1所述的钠长石质瓷,其特征在于所说的钠长石质瓷釉,由下述釉料制成,釉料的化学重量百分组成为:SiO265~70%,Al2O311~13%,Fe2O30.1~0.5%,CaO5~10%,MgO1.5~2%,K2O5.5~6.5%,Na2O1.0~1.5%;ZnO微量~5.0%;釉料示性矿物重量百分组成为:钾长石40~45%,石英25~28%,方解石5~15%,滑石5~10%,ZnO微量~5.0%,高岭土8.0~10%。
CN 88105656 1988-01-16 1988-01-16 钠长石质瓷 Expired - Fee Related CN1022619C (zh)