CN103725147A - 一种铝线漆包线漆及其制备方法 - Google Patents
一种铝线漆包线漆及其制备方法 Download PDFInfo
- Publication number
- CN103725147A CN103725147A CN201310598864.3A CN201310598864A CN103725147A CN 103725147 A CN103725147 A CN 103725147A CN 201310598864 A CN201310598864 A CN 201310598864A CN 103725147 A CN103725147 A CN 103725147A
- Authority
- CN
- China
- Prior art keywords
- parts
- nylon
- wire
- aluminum wire
- enamel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝线漆包线漆,其特征在于,由下列重量份(公斤)的原料制成:酚醛树脂10-12、E-44环氧树脂10-12、尼龙1110-12、三羟甲基丙烷三丙烯酸酯6-8、氮化铝粉35-45、醋酸钾1-2、二苯甲烷二异氰酸酯2-3、硅烷偶联剂KH-5502-3、双丁基二氯化锡2-3、助剂7-9、间对甲酚100-120、二甲苯100-120;与现有技术相比,在生产中添加该,经过调配工艺处理后,可显著改善漆包线漆对铝材的附着力,用这种复配物改性处理过的漆包线绝缘漆涂制的铝漆包线各项性能指标均能满足国际电工IEC标准要求,并且耐热指数可提高到180级。
Description
技术领域
本发明涉及一种漆包线漆,尤其是一种铝线漆包线漆及其制备方法。
背景技术
漆包线是一种电工材料,它是在一根圆形的铜线表面加工一层薄薄的高强度绝缘层,起到与外界绝缘的作用。按规格可加工成比发丝还细的毛丝线,像拇指般粗的纱包线。漆包线具有很好的绝缘效果和防水能力。在电器方面应用很广泛,如电动机,发电机,水泵,电磁铁,电焊机,家用电器,无线通讯,扬声器,电报机,变压器等。漆包线漆是生产漆包线的必要绝缘材料,漆包线漆要求具有良好的附着性、机械强度、绝缘性能、耐热性能、耐磨性能、耐盐雾及耐恶劣环境性能等,但是普通的漆包线漆存在耐热性、耐磨性差、强度不够、耐热级低于120℃等问题,难以满足不同环境的要求。需要对漆包线漆的配方与生产工艺进行改进,进一步提高漆包漆的性能,降低其生产成本。
发明内容
本发明的目的就是提供一种铝线漆包线漆及其制备方法,以克服现有技术的不足。
本发明的目的是这样实现的:
一种铝线漆包线漆,其特征在于,由下列重量份(公斤)的原料制成:酚醛树脂10-12、E-44环氧树脂10-12、尼龙11 10-12、三羟甲基丙烷三丙烯酸酯6-8、氮化铝粉3-5、醋酸钾1-2、二苯甲烷二异氰酸酯2-3、硅烷偶联剂KH-550 2-3、双丁基二氯化锡2-3、助剂7-9、间对甲酚100-120、二甲苯100-120;
所述的助剂由下列重量份原料制成:纳米云母粉0.2-0.3、季戊四醇3-4、甘油3-4、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯2-3、交联剂TAC1-2、二季戊四醇六丙烯酸酯5-7、柠檬酸三乙酯7-10、没食子酸丙酯2-3、薏仁油3-4;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
所述的铝线漆包线漆的制备方法,其特征在于包括以下步骤:
(1)、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀,加热到50-55℃,加入尼龙11,搅拌并加热到155-190℃,至尼龙11完全溶解;
(2)、将步骤(1)反应物料降温至75-85℃,加入三羟甲基丙烷三丙烯酸酯、三羟甲基丙烷三丙烯酸酯、硅烷偶联剂KH-550 2-3、醋酸钾、助剂,保持温度,搅拌反应4.5-5小时;
(3)、再加入剩余物料,升温至150-120℃,继续搅拌反应1.5-2.5小时;
(4)、冷却物料至45-50℃,研磨至20-40μm浆料,过滤即得。
本发明具有以下有益效果:针对铜线漆包线绝缘漆设计的,经过调配工艺处理后,可显著改善漆包线漆对铝材的附着力,用这种复配物改性处理过的漆包线绝缘漆涂制的铝漆包线各项性能指标均能满足国际电工IEC标准要求,并且耐热指数可提高到180级。
具体实施方式
所述的一种铝线漆包线漆,其特征在于,由下列重量份(公斤)的原料制成:酚醛树脂10、E-44环氧树脂10、尼龙11 10、三羟甲基丙烷三丙烯酸酯6、氮化铝粉3、醋酸钾1、二苯甲烷二异氰酸酯3、硅烷偶联剂KH-550 3、双丁基二氯化锡2、助剂7、间对甲酚100、二甲苯100;
所述的助剂由下列重量份(公斤)原料制成:纳米云母粉0.2、季戊四醇3、甘油4、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯2、交联剂TAC2、二季戊四醇六丙烯酸酯7、柠檬酸三乙酯7、没食子酸丙酯2、薏仁油3;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
制备方法包括以下步骤:
(1)、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀,加热到50-55℃,加入尼龙11,搅拌并加热到155-190℃,至尼龙11完全溶解;
(2)、将步骤(1)反应物料降温至75-85℃,加入三羟甲基丙烷三丙烯酸酯、三羟甲基丙烷三丙烯酸酯、硅烷偶联剂KH-550 2-3、醋酸钾、助剂,保持温度,搅拌反应4.5-5小时;
(3)、再加入剩余物料,升温至150-120℃,继续搅拌反应1.5-2.5小时;
(4)、冷却物料至45-50℃,研磨至20-40μm浆料,过滤即得。
使用本发明漆制线材主要性能指标如下:
1、附着性好;
2、耐热等级≥180℃,热冲击达到220℃漆膜不开裂;
3、粘结强度:15N/mm2;
4、耐变压器油:1150小时/105℃,漆膜无损坏。
Claims (3)
1.一种铝线漆包线漆,其特征在于,由下列重量份(公斤)的原料制成:酚醛树脂10-12、E-44环氧树脂10-12、尼龙11 10-12、三羟甲基丙烷三丙烯酸酯6-8、氮化铝粉3-5、醋酸钾1-2、二苯甲烷二异氰酸酯2-3、硅烷偶联剂KH-550 2-3、双丁基二氯化锡2-3、助剂7-9、间对甲酚100-120、二甲苯100-120。
2.根据权利要求1所述的助剂由下列重量份原料制成:纳米云母粉0.2-0.3、季戊四醇3-4、甘油3-4、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯2-3、交联剂TAC1-2、二季戊四醇六丙烯酸酯5-7、柠檬酸三乙酯7-10、没食子酸丙酯2-3、薏仁油3-4;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
3.根据权利要求1所述的铝线漆包线漆的制备方法,其特征在于包括以下步骤:
(1)、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀,加热到50-55℃,加入尼龙11,搅拌并加热到155-190℃,至尼龙11完全溶解;
(2)、将步骤(1)反应物料降温至75-85℃,加入三羟甲基丙烷三丙烯酸酯、三羟甲基丙烷三丙烯酸酯、硅烷偶联剂KH-550 2-3、醋酸钾、助剂,保持温度,搅拌反应4.5-5小时;
(3)、再加入剩余物料,升温至150-120℃,继续搅拌反应1.5-2.5小时;
(4)、冷却物料至45-50℃,研磨至20-40μm浆料,过滤即得。