CN103724774A - 一种可压延的合金性材料及制备合金性材料薄膜的方法 - Google Patents

一种可压延的合金性材料及制备合金性材料薄膜的方法 Download PDF

Info

Publication number
CN103724774A
CN103724774A CN201310753885.8A CN201310753885A CN103724774A CN 103724774 A CN103724774 A CN 103724774A CN 201310753885 A CN201310753885 A CN 201310753885A CN 103724774 A CN103724774 A CN 103724774A
Authority
CN
China
Prior art keywords
alloy material
parts
alloy
lubricant
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310753885.8A
Other languages
English (en)
Other versions
CN103724774B (zh
Inventor
李忠
丁明锦
李学武
曾宪垣
朱键宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FOSHAN SANSHUI CHANGFENG PLASTIC Ltd
FSPG Hi Tech Co Ltd
Original Assignee
FOSHAN SANSHUI CHANGFENG PLASTIC Ltd
FSPG Hi Tech Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FOSHAN SANSHUI CHANGFENG PLASTIC Ltd, FSPG Hi Tech Co Ltd filed Critical FOSHAN SANSHUI CHANGFENG PLASTIC Ltd
Priority to CN201310753885.8A priority Critical patent/CN103724774B/zh
Publication of CN103724774A publication Critical patent/CN103724774A/zh
Application granted granted Critical
Publication of CN103724774B publication Critical patent/CN103724774B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种可压延的合金性材料，按重量份数计，每100份包括下述组分：聚对苯二甲酸乙二醇酯0～60份；聚乙烯10～60份；聚丙烯5～45份；超高分子量聚乙烯0～15份；增强助剂0～10份。本发明主要是将单一结晶性材料进行共混改性，得到合金性材料，再添加润滑剂等，使得结晶性材料能够运用传统的压延工艺制造出薄膜和片材；其能提高材料的熔融强度，解决熔融状态下粘辊轮的弊端，从而达到用传统压延工艺能正常生产各种薄膜和片材；另外，本发明不添加可塑剂，弹性体，因而保证合金材料具备优秀的耐温性能；同时本发明所使用的材料不含有卤素成分，对环境无害。本发明同时提供了一种制备合金性材料薄膜的方法。

Description

一种可压延的合金性材料及制备合金性材料薄膜的方法
技术领域
本发明涉及一种可压延的合金性材料及制备合金性材料薄膜的方法。
背景技术
结晶性材料熔融强度低，压延引出下垂，无法正常生产。目前结晶性材料（如PET、PE、PP等）的薄膜产品，均采用流延法生产，此类膜产品的耐温性和二次加工受热均匀性较差，厚度不均匀。且生产领域中采用压延法的较少。单独的结晶性材料如PET、PP、PE的熔融强度低而导致压延时无法剥离，牵引成膜，这是材料本身特性决定的。
中国专利200910139070.4专利中聚烯烃压延所制得的薄膜中加入了可塑剂、弹性体，这措施一方面提高了产品的柔软性，而另一方面却降低了制品的耐温性能。
发明内容
针对现有技术的缺点，本发明的目的之一在于克服现有技术中存在的缺点，提供一种可压延的合金性材料。
本发明的另一目的在于提供制备合金性材料薄膜的方法。
一方面，为了实现上述目的，本发明提供了一种可压延的合金性材料，按重量份数计，每100份包括下述组分：
Figure BDA0000451247550000011
根据本发明另一具体实施方式，增强助剂为MBS和/或ABS。
根据本发明另一具体实施方式，其进一步包括0.1～10份的润滑剂。
根据本发明另一具体实施方式，润滑剂选自如下一种、或两种以上的混合：硬脂酸、硬脂酸盐、蜡类。
根据本发明另一具体实施方式，其进一步包括0.1～10份的抗氧剂。
根据本发明另一具体实施方式，抗氧剂为1010和/或1076。
根据本发明另一具体实施方式，其进一步包括0.1～5份的抗紫外吸收剂。
根据本发明另一具体实施方式，抗紫外吸收剂为UV-531和/或P助剂。
根据本发明另一具体实施方式，其进一步包括0.1～50份的填充剂。
根据本发明另一具体实施方式，填充剂选自如下一种、或两种以上的混合：碳酸钙、云母、高岭土、滑石粉。
根据本发明另一具体实施方式，其进一步包括0～50份的着色剂。
另一方面，本发明提供了一种制备合金性材料薄膜的方法，其包括如下步骤：
（1）将PE、PP、UPE、PET、MBS、ABS中两种或两种以上按比例混合，加入抗氧剂、紫外线吸收剂；放入捏合机中，于低温混炼均匀，以得所需的各种合金材料；
（2）将步骤（1）所得的合金材料按比例添加润滑剂、抗氧剂、着色剂、紫外线吸收剂、填充剂，进行胶炼，得到胶料；
（3）将步骤（2）胶炼过的胶料依次经过120℃—180℃的轧轮机A、100℃—150℃的过滤机、130℃—160℃轧轮机B、160℃—210℃四辊压延机、厚度控制在0.05—0.65mm，成型为热熔胶布；
（4）经过引取、压花、冷却定型和卷取，获得所需薄膜、片材。
该方法进一步包括步骤（5），对步骤（4）所制得的薄膜、片材进行二次加热贴合或压纹的再加工工艺。
本发明主要是将单一结晶性材料进行共混改性，得到合金性材料，再添加润滑剂等，使得结晶性材料能够运用传统的压延工艺制造出薄膜和片材；其能提高材料的熔融强度，解决熔融状态下粘辊轮的弊端，从而达到用传统压延工艺能正常生产各种薄膜和片材；另外，本发明不添加可塑剂，弹性体，因而保证合金材料具备优秀的耐温性能；同时本发明所使用的材料不含有卤素成分，对环境无害。
具体实施方式
实施例1-7以及比较例1-3的组成如表1所示。
实施例1-7以及比较例1-3的物理性能如表2所示。
其中，实施例1中制备合金性材料薄膜的步骤如下：
通过捏合机对结晶材料合金处理；通过万马力合金材料、抗氧剂、填充剂胶炼；通过轧轮机A再一次均匀炼胶；通过过滤机过滤杂质；通过轧轮机B使胶料保温上料压延机；通过压延机抽出所需厚度薄膜片材；按所需压花纹；通过冷却对薄膜片材定型；卷取成品。
Figure BDA0000451247550000041
表1
Figure BDA0000451247550000051
表2
虽然本发明以较佳实施例揭露如上，但并非用以限定本发明实施的范围。任何本领域的普通技术人员，在不脱离本发明的发明范围内，当可作些许的改进，即凡是依照本发明所做的同等改进，应为本发明的范围所涵盖。

Claims (10)

1.一种可压延的合金性材料，按重量份数计，每100份包括下述组分： 
Figure FDA0000451247540000011
。
2.如权利要求1所述的合金性材料，其进一步包括0.1～10份的润滑剂。 
3.如权利要求1所述的合金性材料，其进一步包括0.1～10份的抗氧剂。 
4.如权利要求1所述的合金性材料，其进一步包括0.1～5份的抗紫外吸收剂。 
5.如权利要求1所述的合金性材料，其进一步包括0.1～50份的填充剂。 
6.如权利要求1所述的合金性材料，其进一步包括0～50份的着色剂。 
7.如权利要求1所述的合金性材料，其中，所述增强助剂为MBS和/或ABS。 
8.如权利要求1所述的合金性材料，其中，所述润滑剂选自如下一种、或两种以上的混合：硬脂酸、硬脂酸盐、蜡类。 
9.一种制备权利要求1-8之一所述合金性材料薄膜的方法，其包括如下步骤： 
（1）将PE、PP、UPE、PET、MBS、ABS中两种或两种以上按比例混合，加入抗氧剂、紫外线吸收剂；放入捏合机中，于低温混炼均匀，以得所需的各种合金材料； 
（2）将步骤（1）所得的合金材料按比例添加润滑剂、抗氧剂、着色剂、紫外线吸收剂、填充剂，进行胶炼，得到胶料； 
（3）将步骤（2）胶炼过的胶料依次经过120℃—180℃的轧轮机A、100℃—150℃的过滤机、130℃—160℃轧轮机B、160℃—210℃四辊压延机、厚度控制在0.05—0.65mm，成型为热熔胶布； 
（4）经过引取、压花、冷却定型和卷取，获得所需薄膜、片材。 
10.如权利要求9所述的方法，其进一步包括步骤（5），对步骤（4）所制得的薄膜、片材进行二次加热贴合或压纹的再加工工艺。 
CN201310753885.8A 2013-12-31 2013-12-31 一种可压延的合金性材料及制备合金性材料薄膜的方法 Active CN103724774B (zh)