CN103695111A - 拉拔锌及锌合金线、棒材的润滑剂 - Google Patents
拉拔锌及锌合金线、棒材的润滑剂 Download PDFInfo
- Publication number
- CN103695111A CN103695111A CN201310682259.4A CN201310682259A CN103695111A CN 103695111 A CN103695111 A CN 103695111A CN 201310682259 A CN201310682259 A CN 201310682259A CN 103695111 A CN103695111 A CN 103695111A
- Authority
- CN
- China
- Prior art keywords
- zinc
- agent
- lubricant
- bar
- zinc alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种拉拔锌及锌合金线、棒材的润滑剂,采用32号全损耗系统用油作为基础油,配合多种复合添加剂。它包括:油性剂、抗磨剂、极压剂、抗泡剂、抗氧剂、补强剂、助剂。本润滑剂具有较强的渗透性,润滑膜强度大,抗磨性和粘温性好,极压性强、冷却和润滑性好,减少拉拔工具和拉模的磨损,有较小的流动剪切应力,提高金属的表面光洁度和规格精度,有一定的化学稳定性和防止出现白斑能力,便于使用和清理等特点。
Description
技术领域
本发明属有色金属加工拉拔加工、尤其是拉拔锌及锌合金线、棒材的润滑剂领域。
背景技术
锌是一种银白色略带淡蓝色金属,密度为7.14g/cm3,熔点为419.5℃。在室温下,性较脆;100~150℃时,变软;超过200℃后,又变脆。锌的化学性质活泼,在常温下的空气中,表面生成一层薄而致密的碱式碳酸锌膜,可阻止进一步氧化。当温度达到225℃后,锌剧烈氧化。锌在现代工业中对于电池制造有不可磨灭的地位,为一相当重要的金属。
拉拔锌及锌合金线、棒材是对锌及锌合金的金属坯料施以拉力,使之通过模孔以获得与模孔截面尺寸、形状相同的制品的塑性加工方法。在拉拔过程中,除材料、拉模和钢芯间的摩擦外,在接触面上由于拉拔速度提高,就会发生温度急剧上升。为了减少拉拔过程中发生严重磨损或烧结,因而要求润滑剂起到减磨和防止磨损、冷却及白斑生成的作用;同时得以提高拉拔速度和断面减小率,以提高产量和质量。
发明内容
本发明要解决的技术问题是提供一种有较强渗透性,润滑膜强度大,抗磨性和粘温性好,极压性强、冷却和润滑性好,减少拉拔工具和拉模的磨损,有较小的流动剪切应力,提高金属的表面光洁度和规格精度,有一定的化学稳定性和防止出现白斑能力,便于使用和清理等特点的拉拔锌及锌合金线、棒材的润滑剂。
本发明以如下技术方案解决上述技术问题:采用32号全损耗系统用油作为基础油,配合多种复合添加剂,其各组分及质量百分数为:
组分 | 含量(质量百分比) |
基础油 | 余量 |
油性剂 | 5.0%~15.0% |
抗磨剂 | 4.0%~6.0% |
极压剂 | 3.0%~6.0% |
抗氧剂 | 0.8%~1.5% |
抗泡剂 | 0.005%~0.01% |
补强剂 | 0.5%~1.0% |
助剂 | 0.5%~1.0% |
基础油是32号全损耗系统用油。
油性剂是质量比50%~40%的工业猪油与50%~60%的棕榈油复合。
抗磨剂是硫化异丁烯。
极压剂是烷基亚磷酸酯。
抗氧剂是质量比50%~40%的2,6-二叔丁基混合酯与50%~60%的双辛基二苯胺复合。
抗泡剂是二甲基硅油。
补强剂是硫磷丁辛基锌盐。
助剂是聚异丁烯。
本发明的拉拔锌及锌合金线、棒材的润滑剂,具有较强的渗透性,润滑膜强度大,抗磨性和粘温性好,极压性强、冷却和润滑性好,减少拉拔工具和拉模的磨损,有较小的流动剪切应力,提高金属的表面光洁度和规格精度,有一定的化学稳定性和防止出现白斑能力,便于使用和清理等特点。
具体实施方式
实施例1:
将下列组分按质量百分比调和而成:
组分 | 含量(质量百分比) |
32号全损耗系统用油 | 76.0% |
质量比50%的工业猪油与50%的棕榈油复合 | 14.0% |
硫化异丁烯 | 5.0% |
烷基亚磷酸酯 | 3.195% |
质量比45%的2,6-二叔丁基混合酯与55%的双辛基二苯胺复合 | 0.8% |
二甲基硅油 | 0.005% |
硫磷丁辛基锌盐 | 0.5% |
聚异丁烯 | 0.5% |
以上组分总和为100%。
实施例2:
将下列组分按质量百分比调和而成:
组分 | 含量(质量百分比) |
32号全损耗系统用油 | 69.5% |
质量比50%的工业猪油与50%的棕榈油复合 | 15.0% |
硫化异丁烯 | 6.0% |
烷基亚磷酸酯 | 5.99% |
质量比40%的2,6-二叔丁基混合酯与60%的双辛基二苯胺复合 | 1.5% |
二甲基硅油 | 0.01% |
硫磷丁辛基锌盐 | 1.0% |
聚异丁烯 | 1.0% |
以上组分总和为100%。
实施例3:
将下列组分按质量百分比调和而成:
组分 | 含量(质量百分比) |
32号全损耗系统用油 | 78.0% |
质量比40%的工业猪油与60%的棕榈油复合 | 10.0% |
硫化异丁烯 | 5.0% |
烷基亚磷酸酯 | 4.293% |
质量比50%的2,6-二叔丁基混合酯与50%的双辛基二苯胺复合 | 1.2% |
二甲基硅油 | 0.007% |
硫磷丁辛基锌盐 | 0.7% |
聚异丁烯 | 0.8% |
以上组分总和为100%。
实施例2产品的主要理化指标为:
项目 | 质量指标 |
水分,% | 痕迹 |
40℃运动粘度mm2/s | 33.3 |
闪点(开口)℃, | 180 |
机械杂质,% | 无 |
最大无卡咬负荷(Pb),Kg | 95 |
倾点,℃, | -10 |
水溶性酸或碱 | 无 |
腐蚀试验(铜片、100℃、3h),级 | 1 |
粘度指数,不小于 | 90 |
Claims (9)
1.一种拉拔锌及锌合金线、棒材的润滑剂,其特征在于采用32号全损耗系统用油作为基础油,配合多种复合添加剂,其各组分及质量百分数为:
2.如权利要求1所述的拉拔锌及锌合金线、棒材的润滑剂,其特征在于基础油是32号全损耗系统用油。
3.如权利要求1所述的拉拔锌及锌合金线、棒材的润滑剂,其特征在于油性剂是质量比50%~40%的工业猪油与50%~60%的棕榈油复合。
4.如权利要求1所述的拉拔锌及锌合金线、棒材的润滑剂,其特征在于抗磨剂是硫化异丁烯。
5.如权利要求1所述的拉拔锌及锌合金线、棒材的润滑剂,其特征在于极压剂是烷基亚磷酸酯。
6.如权利要求1所述的拉拔锌及锌合金线、棒材的润滑剂,其特征在于抗氧剂是质量比50%~40%的2,6-二叔丁基混合酯与50%~60%的双辛基二苯胺复合。
7.如权利要求1所述的拉拔锌及锌合金线、棒材的润滑剂,其特征在于抗泡剂是二甲基硅油。
8.如权利要求1所述的拉拔锌及锌合金线、棒材的润滑剂,其特征在于补强剂是硫磷丁辛基锌盐。
9.如权利要求1所述的拉拔锌及锌合金线、棒材的润滑剂,其特征在于助剂是聚异丁烯。