CN103710103B - 冷挤压锌及锌合金材料的润滑剂 - Google Patents
冷挤压锌及锌合金材料的润滑剂 Download PDFInfo
- Publication number
- CN103710103B CN103710103B CN201310682291.2A CN201310682291A CN103710103B CN 103710103 B CN103710103 B CN 103710103B CN 201310682291 A CN201310682291 A CN 201310682291A CN 103710103 B CN103710103 B CN 103710103B
- Authority
- CN
- China
- Prior art keywords
- zinc
- lubricant
- agent
- oil
- cold extrusion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种冷挤压锌及锌合金材料的润滑剂,采用150号全损耗系统用油作为基础油,配合多种复合添加剂。它包括:油性剂、抗磨剂、摩擦改进剂、抗氧剂、抗氧防腐剂、补强剂、补充助剂。本发明的冷挤压锌及锌合金材料的润滑剂,具有粘度适中、附着力强,粘温特性好,提高冲压材料的耐拉力、抗破裂力,提高界限的深拉比,降低摩擦系数,油膜承压分布均匀,改善冲压成型效果,提高表面光滑、便于脱模,降低挤压力,从而减少能耗。
Description
技术领域
本发明属有色金属加工挤压工艺润滑剂、特别是冷挤压锌及锌合金材料的润滑剂领域。背景技术
锌是一种银白色略带淡蓝色的金属,密度为7.14g/cm3,熔点为419.5℃。在室温下,性较脆;100~150℃时,变软;超过200℃后,又变脆。锌的化学性质活泼,在常温下的空气中,表面生成一层薄而致密的碱式碳酸锌膜,可阻止进一步氧化。当温度达到225℃后,锌剧烈氧化。在现代工业中对于电池制造有不可磨灭的地位,为一相当重要的金属。锌主要用于钢铁、冶金、机械、电气、化工、轻工、军事和医药等领域。锌合金是以锌为基加入其他元素组成的合金。常加的合金元素有铝、铜、镁、镉、铅、钛等的低温锌合金。
挤压锌及锌合金材料是有色金属材质加工工艺的一种方法。它是采用挤压杆(或凸模)将放在挤压筒(或凹模)内的坯杆压出模孔,获得一定形状和尺寸的塑性加工方法。挤压时,由于锭坯表面几乎全部受工具的限制,在三向压应力作用下成形,也就是锭坯内部应力的承压均匀分布影响较大。因此,挤压具有提高金属材料的变形能力,提高材料的接合性,生产灵活性大,金属材料与工具密合性高等特点。特别对于多批次、多规格、小批量的断面复杂、超厚壁或薄壁的锌及锌合金管、棒、型材及线坯材料挤压非常有效。
发明内容
本发明要解决的技术问题是提供一种粘度适中、附着力强,粘温特性好,提高冲压材料的耐拉力、抗破裂力,提高界限的深拉比,降低摩擦系数,油膜承压分布均匀,改善冲压成型效果,提高表面光滑、便于脱模,降低挤压力,从而减少能耗的冷挤压锌及锌合金材料的润滑剂。
本发明以如下技术方案解决上述技术问题:采用150号全损耗系统用油作为基础油,配合多种复合添加剂,其各组分及质量百分数的成分组成为:
组分 | 含量(质量百分比) |
基础油 | 余量 |
油性剂 | 5.0%~15.0% |
抗磨剂 | 5.0%~8.0% |
摩擦改进剂 | 1.0%~3.0% |
抗氧剂 | 0.5%~1.0% |
抗氧防腐剂 | 0.5%~1.0% |
补强剂 | 3.0%~7.0% |
补充助剂 | 3.0%~5.0% |
基础油是150号全损耗系统用油。
油性剂是质量比50%~40%的硫化牛油与50%~60%的硫化猪油复合。
抗磨剂是硼化磷胺酯。
摩擦改进剂是硬脂酸锌。
抗氧剂是2,6-二叔丁基对甲酚。
抗氧防腐剂是硫磷丁辛基锌盐。
补强剂是质量比50%~40%的微晶蜡与50%~60%的碳五石油树脂复合。
补充助剂是羊毛脂。
本发明的冷挤压锌及锌合金材料的润滑剂,具有粘度适中、附着力强,粘温特性好,提高冲压材料的耐拉力、抗破裂力,提高界限的深拉比,降低摩擦系数,油膜承压分布均匀,改善冲压成型效果,提高表面光滑、便于脱模,降低挤压力,从而减少能耗。
具体实施方式
实施例1:
将下列组分按质量百分比调和而成:
组分 | 含量(质量百分比) |
150号全损耗系统用油 | 82.0% |
质量比50%的硫化牛油与50%的硫化猪油复合 | 5.0% |
硼化磷胺酯 | 5.0% |
硬脂酸锌 | 1.0% |
2,6-二叔丁基对甲酚 | 0.5% |
硫磷丁辛基锌盐 | 0.5% |
质量比40%的微晶蜡与60%的碳五石油树脂复合 | 3.0% |
羊毛脂 | 3.0% |
以上组分总和为100%。
实施例2:
将下列组分按质量百分比调和而成:
组分 | 含量(质量百分比) |
150号全损耗系统用油 | 60.0% |
质量比50%的硫化牛油与50%的硫化猪油复合 | 15.0% |
硼化磷胺酯 | 8.0% |
硬脂酸锌 | 3.0% |
2,6-二叔丁基对甲酚 | 1.0% |
硫磷丁辛基锌盐 | 1.0% |
质量比40%的微晶蜡与60%的碳五石油树脂复合 | 7.0% |
羊毛脂 | 5.0% |
以上组分总和为100%。
实施例3:
将下列组分按质量百分比调和而成:
组分 | 含量(质量百分比) |
150号全损耗系统用油 | 69.0% |
质量比50%的硫化牛油与50%的硫化猪油复合 | 12.0% |
硼化磷胺酯 | 6.5% |
硬脂酸锌 | 2.0% |
2,6-二叔丁基对甲酚 | 0.7% |
硫磷丁辛基锌盐 | 0.8% |
质量比40%的微晶蜡与60%的碳五石油树脂复合 | 5.0% |
羊毛脂 | 4.0% |
以上组分总和为100%。
实施例3产品的主要理化指标为:
项目 | 质量指标 |
水分,% | 痕迹 |
40℃运动粘度mm2/s | 162 |
闪点(开口)℃, | 220 |
机械杂质,% | 无 |
最大无卡咬负荷(Pb),Kg | 95 |
倾点,℃, | -5 |
水溶性酸或碱 | 无 |
腐蚀试验(铜片、100℃、3h),级 | 1 |
粘度指数,不小于 | 90 |
Claims (1)
1.一种冷挤压锌及锌合金材料的润滑剂,其特征在于采用150号全损耗系统用油作为基础油,配合多种复合添加剂,其各组分及质量百分数为:
其中:
油性剂是质量比50%~40%的硫化牛油与50%~60%的硫化猪油复合;
抗磨剂是硼化磷胺酯;
摩擦改进剂是硬脂酸锌;
抗氧剂是2,6-二叔丁基对甲酚;
抗氧防腐剂是硫磷丁辛基锌盐;
补强剂是质量比50%~40%的微晶蜡与50%~60%的碳五石油树脂复合;
补充助剂是羊毛脂。